DE102004026515A1 - Ceramic armor plate, tank system and method of making a ceramic armor plate - Google Patents

Ceramic armor plate, tank system and method of making a ceramic armor plate Download PDF

Info

Publication number
DE102004026515A1
DE102004026515A1 DE102004026515A DE102004026515A DE102004026515A1 DE 102004026515 A1 DE102004026515 A1 DE 102004026515A1 DE 102004026515 A DE102004026515 A DE 102004026515A DE 102004026515 A DE102004026515 A DE 102004026515A DE 102004026515 A1 DE102004026515 A1 DE 102004026515A1
Authority
DE
Germany
Prior art keywords
armor plate
ceramic
ceramic armor
plate according
crack
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE102004026515A
Other languages
German (de)
Inventor
Bernhard Heidenreich
Martin Dr. Nedele
Rüdiger Schulte
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Deutsches Zentrum fuer Luft und Raumfahrt eV
Original Assignee
Deutsches Zentrum fuer Luft und Raumfahrt eV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Deutsches Zentrum fuer Luft und Raumfahrt eV filed Critical Deutsches Zentrum fuer Luft und Raumfahrt eV
Priority to DE102004026515A priority Critical patent/DE102004026515A1/en
Priority to PCT/EP2005/005172 priority patent/WO2005114089A1/en
Priority to EP05746412A priority patent/EP1747419B8/en
Priority to DE502005010042T priority patent/DE502005010042D1/en
Priority to AT05746412T priority patent/ATE476636T1/en
Publication of DE102004026515A1 publication Critical patent/DE102004026515A1/en
Priority to ZA200609276A priority patent/ZA200609276B/en
Priority to IL179146A priority patent/IL179146A/en
Priority to US11/561,144 priority patent/US20070125223A1/en
Withdrawn legal-status Critical Current

Abstract

A ceramic armor plate is proposed which is formed in one piece and which comprises a plurality of connected segments that are functionally separated by crack stoppers, whereby the crack stoppers serve to prevent the propagation of cracks from one segment to a neighboring segment.

Description

Die Erfindung betrifft eine keramische Panzerplatte.The The invention relates to a ceramic armor plate.

Ferner betrifft die Erfindung ein Panzersystem.Further The invention relates to a tank system.

Weiterhin betrifft die Erfindung ein Verfahren zur Herstellung einer keramischen Panzerplatte.Farther The invention relates to a method for producing a ceramic Armor plate.

Ein Panzersystem ist beispielsweise aus der EP 0 810 415 B1 ( DE 697 07 560 T2 ) bekannt; dieses umfaßt eine Mehrzahl von keramischen Fliesen, die in einer Fliesenschicht angeordnet sind. Die keramischen Fliesen haben die Aufgabe, aufgrund der Härte der Keramik den Kern eines auftreffenden Geschosses zu zerstören.A tank system is for example from the EP 0 810 415 B1 ( DE 697 07 560 T2 ) known; this includes a plurality of ceramic tiles arranged in a tile layer. The ceramic tiles have the task of destroying the core of an impacting bullet due to the hardness of the ceramic.

Davon ausgehend liegt der Erfindung die Aufgabe zugrunde, eine keramische Panzerplatte und ein Panzersystem bereitzustellen, welche auf einfache Weise herstellbar sind.From that Based on the object of the invention, a ceramic Armor plate and a tank system to provide, which on simple Way can be produced.

Diese Aufgabe wird erfindungsgemäß dadurch gelöst, daß die keramische Panzerplatte einstückig ausgebildet ist und eine Mehrzahl von zusammenhängenden Segmente umfaßt, welche durch Rißstopper funktionell getrennt sind, wobei die Rißstopper zur Verhinderung der Ausbreitung von Rissen von einem Segment auf ein benachbartes Segment dienen.These Task is inventively characterized solved, that the ceramic armor plate in one piece is formed and includes a plurality of contiguous segments, which by crack stopper are functionally separated, wherein the Rißstopper to prevent the Propagation of cracks from one segment to an adjacent segment serve.

Erfindungsgemäß wird eine einstückige Panzerplatte mit integral hergestellten Rißstoppern bereitgestellt. Dadurch ist die Herstellung stark vereinfacht, da nicht eine Mehrzahl von einzelnen Fliesen hergestellt werden muß, die dann noch gefügt werden müssen, sondern integral eine ganze Platte hergestellt wird, welche einen größeren Flächenbereich einnimmt. Da keine Fügung notwendig ist, sind auch die damit verbundenen Probleme vermieden. Beispielsweise kann bei der Herstellung von Keramikplatten ein Größenschwund und eine Verformung auftreten. Wenn Keramikfliesen zu fügen sind, dann erfordert dies eine aufwendige Herstellung, damit eine paßgenaue Fügung erreicht werden kann. Bei der erfindungsgemäßen keramischen Panzerplatte ist aber eine Fügung nicht notwendig, so daß die Herstellung weniger aufwendig ist.According to the invention is a one-piece Armor plate provided with integrally formed Rißstoppern. Thereby The production is greatly simplified, since not a plurality of individual tiles must be made, which are then still joined have to, but integrally a whole plate is made, which one occupies a larger surface area. There is no coincidence is necessary, the associated problems are avoided. For example, in the production of ceramic plates, a shrinkage in size and a deformation occur. If ceramic tiles are to be added, then this requires an elaborate production, so that an accurate fit coincidence can be achieved. In the ceramic armor plate according to the invention but a coincidence not necessary, so that the Production is less expensive.

Die Rißstopper lassen sich auf einfache Weise während der Herstellung ausbilden, beispielsweise über definiert erzeugte Risse oder über vor der Keramisierung eingebrachte Nuten. Dadurch wiederum ist es möglich, die funktionellen Segmente definiert für die gewünschte Anwendung zu erzeugen.The crack stopper can be easily while form the production, for example on defined cracks generated or over grooves introduced before ceramization. This in turn is it possible, to create the functional segments defined for the desired application.

Es ist auch möglich, eine keramische Panzerplatte für bestimmte Anwendungen mit einer definierten Krümmung herzustellen. Wenn einzelne Fliesen gefügt werden, dann ist die Krümmung erheblich schwieriger herzustellen, da Fliesen im Fliesenverbund unterschiedliche Krümmungen aufweisen können.It is possible, too, a ceramic armor plate for make certain applications with a defined curvature. If individual Tiles added be, then the curvature considerably more difficult to produce, since tiles in the tile composite different curvatures can have.

Im Vergleich zu einem Fliesenverbund ergeben sich durch die Integration von Rißstoppern in die Panzerplatte eine Vielzahl von Möglichkeiten zur Ausbildung der Panzerplatte. Diese läßt sich beispielsweise mehrlagig ausbilden, wobei in unterschiedlichen Lagen die Rißstopper unterschiedlich angeordnet sein können. Dadurch ergibt sich eine größere Anzahl an Steuerungs- und Einstellmöglichkeiten für die Eigenschaften der Panzerplatte.in the Compared to a tile composite result from the integration of tearstoppers in the armor plate a variety of ways to training the armor plate. This can be For example, form multi-layer, with different layers the tearstoppers can be arranged differently. This results in a larger number on control and adjustment options for the Properties of the armor plate.

Ganz besonders vorteilhaft ist es, wenn die Rißstopper in die Panzerplatte integriert sind. Dadurch läßt sich die Panzerplatte einfach herstellen und auch ein Panzersystem, welches mindestens eine erfindungsgemäße Panzerplatte umfaßt, läßt sich auf einfache Weise herstellen.All it is particularly advantageous if the crack stopper in the armor plate are integrated. This can be done The Panzerplatte easy to produce and also a tank system, which at least one armor plate according to the invention comprises let yourself in a simple way.

Insbesondere sind die Rißstopper in dem Vollmaterial der Panzerplatte gebildet, so daß keine getrennten und nachträglich zu fügenden Fliesen vorgesehen werden müssen. Dadurch ist die Herstellung der Panzerplatte stark vereinfacht, wobei sich ein großer Flächenbereich auf einfache Weise herstellen läßt.Especially are the tearstoppers formed in the solid material of the armor plate, so that no separate and afterwards to be joined Tiles must be provided. As a result, the production of the armor plate is greatly simplified, being a big one area can be produced in a simple manner.

Insbesondere werden die Rißstopper bei der Herstellung der Panzerplatte erzeugt.Especially become the crack stopper produced in the manufacture of the armor plate.

Bei einer Ausführungsform sind Rißstopper durch Ausnehmungen und/oder über Ausnehmungen gebildet. Die Ausnehmungen lassen sich insbesondere vor der Keramisierung eines Panzerplatten-Vorkörpers auf einfache Weise herstellen. Sie lassen sich definiert anordnen. Beispielsweise kann ein Gitter an Ausnehmungen erzeugt werden. Weiterhin lassen sich die Ausnehmungen mit definierter Tiefe herstellen. Bei der hergestellten Panzerplatte sind die Ausnehmungen nicht unbedingt mehr vorhanden. Beispielsweise werden diese vor Infiltrierung mit carbidbildenden Stoffen (wie Silicium für die Silicierung) mit einem Trennmittel gefüllt. Die Rißstopperfunktion bleibt dabei aber erhalten.at an embodiment are crack stops by Recesses and / or over Recesses formed. The recesses can be in particular before the ceramization of a Panzerplatten-Vorörpers produce in a simple manner. They can be arranged in a defined manner. For example, a grid be produced at recesses. Furthermore, the recesses can be produce with a defined depth. In the manufactured armor plate are the recesses do not necessarily exist anymore. For example are these before infiltration with carbide-forming substances (such Silicon for the siliconization) filled with a release agent. The Rißstopperfunktion remains but received.

Insbesondere sind die Ausnehmungen in der Dickenrichtung der Panzerplatte hergestellt. Dadurch wird die Panzerplatte in funktionelle Segmente unterteilt, wobei die Segmente zusammenhängend sind. Die Ausnehmungen verhindern eine Rißausbreitung über ein Segment hinaus, wenn ein Segment einen Impact beispielsweise durch Geschoßaufschlag erfährt.In particular, the recesses are made in the thickness direction of the armor plate. As a result, the armor plate is divided into functional segments, the segments are contiguous. The recesses prevent crack propagation beyond a segment when a segment impacts it, for example, by a bullet impact moves.

Es kann vorgesehen sein, daß die Ausnehmungen nichtdurchgehend sind. Beispielsweise werden Rißstopper durch Nuten und/oder über Nuten gebildet. Solche Nuten lassen sich auf einfache Weise herstellen, beispielsweise durch Fräsung oder Laserbearbeitung.It can be provided that the Recesses are non-continuous. For example, crack stops through grooves and / or over Grooves formed. Such grooves can be produced in a simple manner, for example by milling or laser processing.

Vorzugsweise liegt die Tiefe der Nuten im Bereich zwischen 0,05 bis 0,6 der Dicke der Panzerplatte. Dadurch läßt sich zum einen eine Rißstopwirkung erzielen und zum anderen eine einstückige Panzerplatte ausbilden.Preferably For example, the depth of the grooves ranges from 0.05 to 0.6 in thickness the armor plate. This can be done on the one hand, a crack stop effect achieve and on the other hand form a one-piece armor plate.

Es ist auch möglich, daß in der Dickenrichtung durchgehende Ausnehmungen vorgesehen sind. Beispielsweise werden dazu Rißstopper durch Perforationen und/oder über Perforationen gebildet.It is possible, too, that in the thickness direction through recesses are provided. For example become tearstoppers through perforations and / or over Perforations formed.

Es ist auch möglich, daß Rißstopper über Risse gebildet sind. Solche Risse lassen sich definiert herstellen, indem beispielsweise Deckplatten (Decklagen) auf einen Vollmaterial-Vorkörper aufgesetzt werden, welche einen unterschiedlichen Wärmeausdehnungskoeffizienten aufweisen als der Vollmaterial-Vorkörper. Bei anschließender Keramisierung wird ein integraler Werkstoffverbund mit Rißbildung erzeugt.It is possible, too, that crack stopper over cracks are formed. Such cracks can be produced in a defined way by For example, cover plates (cover layers) placed on a solid material preform which have a different thermal expansion coefficient have as the solid-material preform. With subsequent ceramization an integral composite material with cracking is generated.

Insbesondere verlaufen die als Rißstopper dienenden Risse zwischen einer Oberseite und einer Unterseite der Panzerplatte. Dadurch läßt sich die Panzerplatte in funktionelle Segmente unterteilen, wobei die Rißausbreitung über Segmente hinaus stopbar ist.Especially the crackers serve as crack stopper Cracks between a top and a bottom of the armor plate. This can be done divide the armor plate into functional segments, with the Crack propagation across segments is also out of the way.

Günstig ist es, wenn die Risse zumindest näherungsweise in der Dickenrichtung der Panzerplatte verlaufen. Dadurch läßt sich die Panzerplatte in Segmente unterteilen, die einem Fliesenverbund mit Fugen zwischen den Fliesen entsprechen, wobei jedoch die Panzerplatte einstückig ausgebildet ist.Cheap is it if the cracks at least approximately run in the thickness direction of the armor plate. This can be done subdivide the armor plate into segments that form a composite tile with joints between the tiles, but with the armor plate one piece is trained.

Günstig ist es, wenn Decklagen vorgesehen sind, zwischen welchen die Risse verlaufen. Dadurch wird die Panzerplatte zu ihrer Oberseite und Unterseite hindurch eine rißfreie Decklage abgedeckt. Über die Decklagen wiederum ist es möglich, während der Herstellung der Panzerplatte definiert Risse zu erzeugen.Cheap is it, when cover layers are provided, between which the cracks run. This will make the armor plate its top and bottom through a crack-free Covered cover. about the cover layers in turn it is possible while the manufacture of the armor plate defines creating cracks.

Beispielsweise werden die Decklagen aus C/C-SiC hergestellt. Dazu werden beispielsweise C/C-Vorkörper jeweils auf der Unterseite und der Oberseite eines porösen C-Vorkörpers aufgelegt und es wird eine anschließende Silicierung durchgeführt. Dadurch lassen sich Decklagen aus C-C-SiC bilden. Aufgrund der unterschiedlichen Materialeigenschaften läßt sich während der Silicierung eine Rißstruktur erzeugen, wobei die Risse zwischen den Decklagen verlaufen. Dadurch wiederum lassen sich die funktionellen Segmente erzeugen.For example the cover layers are made of C / C-SiC. For this purpose, for example, C / C preform each on the bottom and the top of a porous carbon precursor and it will be a subsequent one Silicification performed. Thereby Cover layers can be formed from C-C-SiC. Due to the different Material properties can be while to produce a crack structure of the siliconization, the cracks extend between the cover layers. This in turn The functional segments can be generated.

Grundsätzlich ist es möglich, als Rißstopper Fehlstellen wie beispielsweise Risse vorzusehen.Basically it is possible as crack stopper flaws such as cracks.

Es hat sich als günstig erwiesen, wenn der Abstand zwischen Rißstoppern im Bereich zwischen 5 mm und 50 mm liegt.It has been considered favorable proved when the distance between crack stops in the range between 5 mm and 50 mm.

Es kann günstig sein, einen mehrlagigen Aufbau vorzusehen. Die Lagen sind dabei einstückig aneinander gebildet. Beispielsweise werden mehrere Lagen bei der Keramisierung (wie beispielsweise über die Infiltration von flüssigem Silicium, d.h. Silicierung) einstückig (in situ) zusammengefügt.It can be cheap be to provide a multilayer structure. The layers are there in one piece educated. For example, several layers in the ceramization (such as over the infiltration of liquid Silicon, i. Siliconization) in one piece (in situ).

Beispielsweise ist die Panzerplatte aus einer Siliciumcarbid-Keramik hergestellt. Diese weist eine hohe Härte auf, so daß ein auftreffendes Geschoß zerstört wird. Es ist auch denkbar, die Panzerplatte über andere carbidbildende Metalle wie Titan oder Chrom herzustellen.For example The armor plate is made of a silicon carbide ceramic. This has a high hardness on, so that one striking bullet is destroyed. It is also conceivable, the armor plate on other carbide-forming metals how to make titanium or chrome.

Es ist günstig, wenn die Rißstopper in dem Keramikmaterial der Panzerplatte eingebracht sind und insbesondere dort eingebettet sind.It is cheap, when the tearstoppers are introduced in the ceramic material of the armor plate and in particular embedded there.

Die Panzerplatte läßt sich insbesondere aus einem kohlenstoffhaltigen Vorkörper herstellen. Ein solcher Vorkörper ist auf einfache Weise bearbeitbar. Er ist zumindest teilweise keramisierbar. Beispielsweise wird dieser Vorkörper mittels Graphitpulver und Bindemitteln hergestellt.The Armor plate lets itself in particular from a carbon-containing preform produce. Such a preforms is easy to edit. He is at least partially ceramizable. For example, this preform produced by means of graphite powder and binders.

Die erfindungsgemäße Panzerplatte läßt sich kostengünstig herstellen, wenn der keramische Werkstoff der Panzerplatte mittels eines biomorphen Materials und insbesondere eines Cellulose enthaltenden Materials hergestellt ist. Entsprechende Herstellungsverfahren sind in der nicht vorveröffentlichten deutschen Anmeldung Nr. 103 29 822.3 vom 30. Juni 2003 beschrieben. Auf diese Anmeldung wird ausdrücklich Bezug genommen.The armor plate according to the invention let yourself economical Produce when the ceramic material of the armor plate means a biomorphic material, and in particular a cellulose-containing material Material is made. Corresponding production methods are in the not pre-published German application no. 103 29 822.3 of 30 June 2003 described. This application is explicit Referenced.

Die erfindungsgemäße Panzerplatte läßt sich vorteilhaft in einem Panzersystem einsetzen, welches mindestens eine erfindungsgemäße Panzerplatte umfaßt.The armor plate according to the invention let yourself advantageous to use in a tank system, which at least an armor plate according to the invention includes.

Ein entsprechendes Panzersystem weist insbesondere einen mehrlagigen Aufbau auf. Ein Beispiel ist in der EP 0 810 415 B1 beschrieben, auf die ausdrücklich Bezug genommen wird. Anstatt einer Mehrzahl von Fliesen, wie dort beschrieben, läßt sich mindestens eine erfindungsgemäße Panzerplatte verwenden.A corresponding tank system has in particular a multilayer construction. An example is in the EP 0 810 415 B1 described, to which reference is expressly made. Instead of a plurality of tiles, as described there, at least one armor plate according to the invention can be used.

Insbesondere sitzt dann die mindestens eine Panzerplatte auf einem Backing (Strukturträgerschicht), die vorzugsweise aus einem Leichtbaumaterial wie Aluminium oder Kohle-Kevlar oder Aramid hergestellt ist.In particular, then sitting at least one Armor plate on a backing (Strukturträgerschicht), which is preferably made of a lightweight material such as aluminum or carbon Kevlar or aramid.

Der Erfindung liegt ferner die Aufgabe zugrunde, ein Verfahren zur Herstellung einer keramischen Panzerplatte bereitzustellen, welches auf einfache Weise durchführbar ist.Of the The invention is further based on the object, a process for the preparation to provide a ceramic armor plate, which is based on simple Way feasible is.

Diese Aufgabe wird erfindungsgemäß dadurch gelöst, daß in einem Panzerplatten-Vorkörper Rißstopper erzeugt werden und die Panzerplatte über die Rißstopper in zusammenhängende funktionelle Segmente unterteilt wird.These Task is inventively characterized solved, that in an armored plate preform crack stopper be generated and the armor plate on the crack stopper in coherent functional Segments is divided.

Erfindungsgemäß werden während der Herstellung der keramischen Panzerplatte die Rißstopper (für die herzustellende Panzerplatte) eingebracht, und zwar in einem Panzerplatten-Vorkörper, in dem die Einbringung unkompliziert erfolgen kann. Dadurch ergibt sich eine leichte Herstellbarkeit, wobei durch eine definierte Rißstoppererzeugung definierte funktionelle Segmente erstellbar sind.According to the invention while the production of the ceramic armor plate the crack stopper (for the armor plate produced), in an armored plate preform, in the introduction can be done easily. This results an easy manufacturability, whereby by a defined Rißstoppererzeugung Defined functional segments can be created.

Das erfindungsgemäße Verfahren weist die bereits im Zusammenhang mit der erfindungsgemäßen keramischen Panzerplatte erläuterten Vorteile auf.The inventive method has the already in connection with the ceramic according to the invention Armor plate explained Advantages.

Weitere vorteilhafte Ausgestaltungen des erfindungsgemäßen Verfahrens wurden ebenfalls bereits im Zusammenhang mit der erfindungsgemäßen keramischen Panzerplatte erläutert.Further advantageous embodiments of the method according to the invention were also already in connection with the ceramic armor plate according to the invention explained.

Insbesondere werden die Rißstopper vor der Keramisierung des Panzerplatten-Werkstoffes hergestellt. Es ist dann möglich, die Rißstopper beispielsweise durch spanabhebende Materialbearbeitung herzustellen. In dem Stadium vor der Keramisierung ist das Material weitaus weniger hart als nach der Keramisierung.Especially become the crack stopper produced before the ceramization of the armor plate material. It is then possible the tearstoppers For example, produce by machining material processing. At the stage before ceramization, the material is much less hard than after ceramization.

Beispielsweise werden die Rißstopper durch Herstellung von Ausnehmungen erzeugt. Diese lassen sich durch mechanische Materialbearbeitung, wie spanabhebende Materialbearbeitung (Fräsen, Bohren, Schleifen usw.), und/oder durch Strahlbearbeitung wie Laserbearbeitung oder Plasmastrahlbearbeitung auf einfache Weise in definierter Anordnung und Form herstellen.For example become the crack stopper produced by production of recesses. These can be through mechanical material processing, such as cutting material processing (Milling, drilling, Grinding, etc.), and / or by blasting such as laser machining or plasma jet machining in a simple manner in a defined arrangement and shape.

Es kann vorgesehen sein, daß die Ausnehmungen mit Trennmittel gefüllt werden. Das Trennmittel hat die Aufgabe, die Rißstopperfunktion für die fertige Panzerplatte (welche keramisiert ist) sicherzustellen. Insbesondere dient das Trennmittel dazu, eine Benetzung mit carbidbildendem Material während der Keramisierung zu verhindern.It can be provided that the Recesses filled with release agent become. The release agent has the task of the Rißstopperfunktion for the finished Armor plate (which is ceramized) to ensure. Especially the release agent serves to wetting with carbide-forming material while to prevent ceramification.

Es ist auch möglich, daß Risse als Rißstopper definiert erzeugt werden.It is possible, too, that cracks as a crack stopper be generated defined.

Beispielsweise werden die Risse über die Verbindung mit Deckplatten erzeugt. Diese Deckplatten werden vor der Keramisierung auf einen Vorkörper aufgelegt. Durch die Keramisierung beispielsweise durch Silicierung erfolgt eine einstückige Verbindung der Deckplatten, wobei Risse erzeugbar sind.For example the cracks are over creates the connection with cover plates. These cover plates will be placed on a preform before ceramization. By the ceramization For example, by siliconizing a one-piece compound the cover plates, wherein cracks are generated.

Insbesondere werden die Deckplatten C/C hergestellt, das heißt aus kohlefaserverstärktem Kohlenstoff hergestellt.Especially the cover plates C / C are made, that is, carbon fiber reinforced carbon produced.

Es ist auch günstig, einen mehrlagigen Aufbau vorzusehen, wobei die Lagen beim bei der Keramisierung in situ zur Bildung einer einstückigen Panzerplatte verbunden werden. Dadurch lassen sich die Eigenschaften der keramischen Panzerplatte definiert steuern bzw. einstellen. Beispielsweise lassen sich in individuelle Lagen jeweils Rißstopperstrukturen einbringen.It is also cheap to provide a multilayer structure, wherein the layers at the Ceramization connected in situ to form a one-piece armor plate become. This allows the properties of the ceramic armor plate defined control or adjust. For example, can be in individual layers each crack stopper structures contribute.

Die nachfolgende Beschreibung bevorzugter Ausführungsformen dient im Zusammenhang mit der Zeichnung der näheren Erläuterung der Erfindung. Es zeigen:The The following description of preferred embodiments is used in conjunction with the drawing of the closer explanation the invention. Show it:

1 eine schematische Darstellung eines ersten Ausführungsbeispiels einer erfindungsgemäßen keramischen Panzerplatte; 1 a schematic representation of a first embodiment of a ceramic armor plate according to the invention;

2 eine schematische Darstellung eines zweiten Ausführungsbeispiels; 2 a schematic representation of a second embodiment;

3 eine Schnittansicht der Panzerplatte gemäß 1; 3 a sectional view of the armor plate according to 1 ;

4 eine Schnittansicht eines dritten Ausführungsbeispiels; 4 a sectional view of a third embodiment;

5 eine Schnittansicht eines vierten Ausführungsbeispiels; 5 a sectional view of a fourth embodiment;

6 eine Schnittansicht eines fünften Ausführungsbeispiels; 6 a sectional view of a fifth embodiment;

7 eine Schnittansicht eines sechsten Ausführungsbeispiels und 7 a sectional view of a sixth embodiment and

8 eine perspektivische Teilschnittansicht eines Ausführungsbeispiels eines Panzersystems, welches eine erfindungsgemäße keramische Panzerplatte umfaßt. 8th a partial perspective sectional view of an embodiment of a tank system comprising a ceramic armor plate according to the invention.

Ein erstes Ausführungsbeispiel einer erfindungsgemäßen Panzerplatte ist in 1 schematisch gezeigt und dort als Ganzes mit 10 bezeichnet. Die Panzerplatte 10 ist aus einer Siliciumcarbid-Keramik hergestellt.A first embodiment of an armor plate according to the invention is in 1 shown schematically and there as a whole with 10 designated. The armor plate 10 is made of a silicon carbide ceramic.

Dazu wird ein kohlenstoffhaltiger Panzerplatten-Vorkörper hergestellt. Beispielsweise wird zur Herstellung des Panzerplatten-Vorkörpers ein cellulosehaltiger Werkstoff verwendet und dadurch ein poröser Vorkörper hergestellt. Der Vorkörper wird mittels Pyrolyse dann in einen offen porösen Kohlenstoffkörper umgewandelt. In diesen Vorkörper werden vor der Keramisierung Nuten 12 eingebracht. Beispielsweise wird ein rechteckförmiges Gitter 14 an Nuten 12 hergestellt. Durch die Nuten 12 sind Rißstopper gebildet, welche die Ausbreitung von Rissen verhindern.For this purpose, a carbonaceous armor plate preform is made. For example, a cellulosic material is used for the production of the armor plate preform body, thereby producing a porous preform. The preform is then converted by pyrolysis into an open porous carbon body. In this preform grooves are before the ceramization 12 brought in. For example, a rectangular grid 14 at grooves 12 produced. Through the grooves 12 Crackstoppers are formed which prevent the propagation of cracks.

Die Nuten 12 unterteilen die Panzerplatte 10 in einzelne Segmente 16, wobei die Segmente 16 zusammenhängend sind; die Panzerplatte 10 ist einstückig ausgebildet. Die Segmente 16 sind funktionell definiert. Sie sind durch Nuten 12 begrenzt. Die Nuten 12 verhindern, daß Risse, welche in einem Segment (beispielsweise in dem Segment 18 durch Aufprall eines Geschosses) entstehen, sich auf benachbarte Segmente 20a, 20b, 20c, 20d, 20e, 20f, 20g, 20h ausbreiten können.The grooves 12 divide the armor plate 10 into individual segments 16 , where the segments 16 are connected; the armor plate 10 is integrally formed. The segments 16 are functionally defined. They are through grooves 12 limited. The grooves 12 prevent cracks occurring in a segment (for example in the segment 18 by impact of a projectile) arise on adjacent segments 20a . 20b . 20c . 20d . 20e . 20f . 20g . 20h can spread.

Die Nuten 12 werden nach der Pyrolyse vor der Keramisierung des Panzerplatten-Vorkörpers eingebracht. Dies erfolgt beispielsweise durch spanabhebende Materialbearbeitung wie Fräsen und/oder durch Laserbearbeitung.The grooves 12 are introduced after the pyrolysis before the ceramization of the armor plates Vorkörpers. This is done for example by machining material processing such as milling and / or laser machining.

Die Nuten 12 erstrecken sich in einer Dickenrichtung d in der Panzerplatte 10. Die Panzerplatte 10 hat eine Dicke D (1). Die Tiefe der Nuten 12 liegt vorzugsweise im Bereich zwischen dem 0,05-fachen bis 0,6-fachen der Dicke D der Panzerplatte 10. Eine typische Tiefe der Nuten 12 liegt bei ca. 10 mm.The grooves 12 extend in a thickness direction d in the armor plate 10 , The armor plate 10 has a thickness D ( 1 ). The depth of the grooves 12 is preferably in the range between 0.05 times to 0.6 times the thickness D of the armor plate 10 , A typical depth of the grooves 12 is about 10 mm.

Die Segmente 16, definiert durch das Gitter 14 der Nuten 12, weisen typische Querabmessungen (senkrecht zur Dickenrichtung d) zwischen 10 mm und 40 mm auf.The segments 16 , defined by the grid 14 the grooves 12 , have typical transverse dimensions (perpendicular to the thickness direction d) between 10 mm and 40 mm.

Nach Einbringen der Nuten 12 erfolgt eine Silicierung des Panzerplatten-Vorkörpers; über Infiltration von Silicium umfassenden Materialien wird der Panzerplatten-Vorkörper in eine Siliciumcarbid-Panzerplatte umgewandelt.After inserting the grooves 12 a silicification of the armor plate preform takes place; By infiltrating materials comprising silicon, the armor plate preform is converted into a silicon carbide armor plate.

Es kann vorgesehen sein, daß zur Herstellung des Panzerplatten-Vorkörpers als Ausgangsbestandteil cellulosehaltiges Pulver verwendet wird. Ein entsprechendes Herstellungsverfahren (bei welchem aus einem cellulosehaltigen Werkstoff ein poröser Vorkörper hergestellt wird, der poröse Vorkörper mittels Pyrolyse in einen offenporösen Kohlenstoffkörper umgewandelt wird und der offenporöse Kohlenstoffkörper durch Infiltration von Silicium umfassenden Materialien in eine Silicium umfassende Carbid-Keramik, insbesondere Siliciumcarbid-Keramik, umgewandelt wird, wobei zur Herstellung des Vorkörpers als Ausgangsbestandteil mindestens cellullosehaltiges Pulver verwendet wird) ist in der nicht vorveröffentlichten deutschen Patentanmeldung Nr. 103 29 822.3 vom 30. Juni 2003 des gleichen Anmelders offenbart. In dieser Anmeldung sind auch Bauteile offenbart, welche einen mit Sillicium umfassende Materialien infiltrierten und dadurch im wesentlichen zu Silicium umfassenden Carbid, insbesondere Siliciumcarbid, keramisierten Kohlenstoffkörper umfassen, wobei der Kohlenstoffkörper eine durch Verwendung von mindestens cellulosehaltigem Pulver und Bindemittel als Ausgangsbestandteile im wesentlichen homogene Porenstruktur aufweist. Auf diese Anmeldung wird ausdrücklich Bezug genommen.It can be provided that the Production of the armor plate preform as an initial component cellulose-containing powder is used. A corresponding manufacturing process (In which made of a cellulosic material, a porous preform becomes, the porous preforms converted by pyrolysis in an open porous carbon body becomes and the open-porous one Carbon body by infiltrating silicon-containing materials into one Silicon carbide ceramic, in particular silicon carbide ceramic, converted is, wherein the preparation of the precursor as the starting ingredient at least cellullose-containing powder is used) is in the not pre-published German Patent Application No. 103 29 822.3 of June 30, 2003 of the same applicant disclosed. In this application are also components which infiltrated a Sillicium containing material and thereby substantially carbide comprising silicon, in particular Silicon carbide, ceramicized carbon body, wherein the carbon body a by using at least cellulose-containing powder and binder as starting components substantially homogeneous pore structure having. This application is expressly incorporated by reference.

Die Nuten 12 können vor der Silicierung mit einem Trennmittel wie Bornitrid befüllt werden; Silicium benetzt das Trennmittel nicht. Dadurch verbleiben beim Silicieren Fehlstellen, welche eben als Rißstopper dienen.The grooves 12 may be filled with a release agent such as boron nitride prior to siliconization; Silicon does not wet the release agent. As a result, defects remain in the siliconizing, which just serve as a crack stopper.

Erfindungsgemäß sind in die Panzerplatte 10 Rißstopper eingebracht. Bei dem Ausführungsbeispiel gemäß 1 sind diese Rißstopper die Nuten 12, welche gitterförmig eingebracht sind. Wenn ein Geschoß ein Segment, beispielsweise das Segment 18 (zur Veranschaulichung in 1 schraffiert) trifft, dann verhindern die das Segment 18 umgebenden Nuten 12 eine Ausbreitung von Rissen in die benachbarten Segmente 20a, b, c, d, e, f, g, h.According to the invention are in the armor plate 10 Crackstopper introduced. In the embodiment according to 1 these tearstoppers are the grooves 12 , which are introduced lattice-like. If a projectile is a segment, for example the segment 18 (for illustration in 1 hatched) hits, then prevent the segment 18 surrounding grooves 12 a spread of cracks in the adjacent segments 20a , b, c, d, e, f, g, h.

Die Panzerplatte 10 läßt sich integral herstellen und die Rißstopper sind integral in der Panzerplatte 10 gebildet. Beispielsweise ist es auch möglich, die Panzerplatte 10 mit entsprechenden Krümmungen herzustellen.The armor plate 10 can be made integral and the crack stops are integral in the armor plate 10 educated. For example, it is also possible the armor plate 10 produce with appropriate curvatures.

Bei dem Ausführungsbeispiel gemäß 1 sind durch die Nuten 12 nichtdurchgehende Ausnehmungen in einen Panzerplatten-Vorkörper eingebracht. Es ist auch möglich, wie anhand eines zweiten Ausführungsbeispiels 22 (2) gezeigt, daß vor der Keramisierung in einem Panzerplatten-Vorkörper durchgehende Ausnehmungen 24 in der Form von Perforationen eingebracht sind. Diese Perforationen dienen ebenfalls als Rißstopper, um die Ausbreitung von Rissen von einem Segment 26 auf benachbarte Segmente zu verhindern.In the embodiment according to 1 are through the grooves 12 non-continuous recesses introduced into an armored plate preform. It is also possible, as with a second embodiment 22 ( 2 ) showed that prior to ceramization in an armored plate pre-body continuous recesses 24 are introduced in the form of perforations. These perforations also serve as a crack stopper to prevent the spread of cracks from a segment 26 to prevent adjacent segments.

In 3 ist schematisch eine Schnittansicht durch die Panzerplatte gemäß 1 gezeigt. Man erkennt die oberflächlich eingebrachten Nuten 12 als Rißstopper. Eine Oberfläche 30, von welcher die Nuten 12 her eingebracht sind, liegt vorzugsweise einer Außenseite 28 der Panzerplatte 10 gegenüber. Bei einer Anwendung weist die Außenseite 28 vorzugsweise nach außen.In 3 is a schematic sectional view through the armor plate according to 1 shown. One recognizes the superficially introduced grooves 12 as a crack stopper. A surface 30 from which the grooves 12 are introduced ago, is preferably an outside 28 the armor plate 10 across from. In one application, the outside faces 28 preferably to the outside.

Es ist auch möglich, daß eine Panzerplatte, wie in 4 schematisch gezeigt und dort als Ganzes mit 32 bezeichnet, mehrlagig aufgebaut ist, beispielsweise mit einer ersten Lage 34a, einer zweiten Lage 34b und einer dritten Lage 34c. Die Lagen 34a, 34b, 34c sind integral miteinander verbunden, so daß die Panzerplatte 32 einstückig ausgebildet ist. Die Lagen 34a, 34b, 34c werden beispielsweise über getrennte pyrolysierte Vorkörper hergestellt, wobei die entsprechenden Lagen dann über die Silicierung miteinander einstückig verbunden werden.It is also possible that an armor plate, as in 4 shown schematically and there as Gan with 32 denotes multi-layered, for example, with a first layer 34a , a second location 34b and a third location 34c , The layers 34a . 34b . 34c are integrally connected to each other so that the armor plate 32 is integrally formed. The layers 34a . 34b . 34c are prepared, for example, via separate pyrolyzed preforms, wherein the corresponding layers are then integrally connected to one another via the siliconization.

In den Lagen 34a, 34b, 34c werden vor der Keramisierung (Silicierung) Nuten 36 als Rißstopper eingebracht. Die Einbringung erfolgt grundsätzlich so wie oben anhand des ersten Ausführungsbeispiels beschrieben. Dadurch werden in jeder Lage funktionelle Segmente 38a, 38b, 38c erzeugt. Die Segmente in jeder Lage sind dabei eben durch die Nuten 36 als Rißstopper funktionell getrennt.In the layers 34a . 34b . 34c become grooves before ceramification (siliconization) 36 introduced as a crack stopper. The introduction takes place in principle as described above with reference to the first embodiment. This will make functional segments in every situation 38a . 38b . 38c generated. The segments in each layer are just through the grooves 36 Functionally separated as a crack stopper.

Eine typische Tiefe der Nuten 36 liegt bei ca. 3 mm.A typical depth of the grooves 36 is about 3 mm.

Es kann vorgesehen sein, daß sich die Segmente benachbarter Lagen überdecken. Beispielsweise überdecken die Segmente 38b der Lage 34b jeweils die Segmente 38c und 38a der Lagen 34a und 34c.It can be provided that overlap the segments of adjacent layers. For example, cover the segments 38b the situation 34b each of the segments 38c and 38a the layers 34a and 34c ,

Bei einem weiteren Ausführungsbeispiel einer Panzerplatte, welche in 5 schematisch gezeigt und dort mit 40 bezeichnet ist, sind Nuten 42 und 44 von gegenüberliegenden Oberflächen 46, 48 her eingebracht. Die Nuten 42, 44 sind nichtdurchgehend und bezogen auf eine Richtung quer zur Dickenrichtung d versetzt zueinander. Auch dadurch werden funktionelle Segmente in der Panzerplatte 40 gebildet, wobei die Nuten 42, 44 als Rißstopper die Ausbreitung von Rissen über ein Segment hinaus verhindern, wenn das entsprechende Segment beispielsweise von einem Geschoß getroffen wird.In a further embodiment of an armor plate, which in 5 shown schematically and there with 40 is designated are grooves 42 and 44 from opposite surfaces 46 . 48 introduced. The grooves 42 . 44 are non-continuous and staggered with respect to a direction transverse to the thickness direction d. This also makes functional segments in the armor plate 40 formed, with the grooves 42 . 44 as a crack stopper prevent the propagation of cracks beyond a segment, for example, if the corresponding segment is hit by a projectile.

Bei einem weiteren Ausführungsbeispiel einer Panzerplatte, welche in 6 gezeigt und dort als Ganzes mit 50 bezeichnet ist, ist ein mehrlagiger Aufbau mit einer ersten Lage 52a, einer zweiten Lage 52b und einer dritten Lage 52c vorgesehen. Bei den Lagen handelt es sich beispielsweise um Siliciumcarbid-Lagen, welche über Silicierung integral miteinander verbunden sind. Es kann dabei vorgesehen sein, daß die mittlere Lage 52b Risse 54 aufweist, welche definiert hergestellt wurden. Die Risse verlaufen zumindest näherungsweise parallel zu einer Dickenrichtung der Panzerplatte 50. Die Risse 54 dienen als Rißstopper. Über sie wird die Panzerplatte 50 in funktionelle Segmente 56 unterteilt, wobei die entsprechenden Segmente durch Risse begrenzt sind. Die Risse 54 verhindern als eine Art von Sollbruchstellen die Ausbreitung von Rissen 56 über ein Segment hinaus, wenn beispielsweise durch Aufprall eines Geschosses in dem Segment 56 Risse entstehen.In a further embodiment of an armor plate, which in 6 shown and there as a whole with 50 is designated, is a multi-layer structure with a first layer 52a , a second location 52b and a third location 52c intended. The layers are, for example, silicon carbide layers, which are integrally connected to one another via siliconization. It can be provided that the middle layer 52b cracks 54 which have been produced in a defined manner. The cracks extend at least approximately parallel to a thickness direction of the armor plate 50 , The cracks 54 serve as crack stopper. Over them becomes the armor plate 50 into functional segments 56 divided, with the corresponding segments are limited by cracks. The cracks 54 prevent the spread of cracks as a kind of predetermined breaking points 56 beyond a segment, for example, when impacted by a projectile in the segment 56 Cracks arise.

Die Panzerplatte 50 ist mehrlagig mit den Rissen 54 als innenliegende Fehlstellen in situ gefügt, das heißt die Panzerplatte 50 ist einstückig ausgebildet.The armor plate 50 is multi-layered with the cracks 54 as internal defects in situ joined, that is the armor plate 50 is integrally formed.

Es ist auch möglich, wie in 7 anhand eines weiteren Ausführungsbeispiels einer Panzerplatte 58 gezeigt, daß Risse 60 als Rißstopper beispielsweise in einem Siliciumcarbid-Keramikvollmaterial 62 gebildet sind, wobei das Vollmaterial 62 zwischen Decklagen 64, 66 aus C/C-SiC liegt. Die Decklagen 64, 66 werden über Decklagen-Vorkörper beispielsweise aus C/C hergestellt, welche für die Silicierung mit dem Vollmaterial-Vorkörper verbunden werden. Beim Siliciervorgang können dadurch definiert Risse in dem Vollmaterial-Vorkörper erzeugt werden (das heißt in dem kohlenstoffhaltigen Werkstoff erzeugt werden), die dann auch in dem Siliciumcarbid-Keramikvollmaterial 62 gebildet sind.It is also possible, as in 7 based on a further embodiment of an armor plate 58 shown that cracks 60 as a crack stopper, for example in a silicon carbide ceramic material 62 are formed, wherein the solid material 62 between cover layers 64 . 66 made of C / C-SiC. The cover layers 64 . 66 are produced via cover layer preform, for example, from C / C, which are connected for the siliconization with the solid material preform. In the case of the siliconizing process, defined cracks can be generated in the solid material preform (that is to say produced in the carbonaceous material) which then also occur in the silicon carbide ceramic material 62 are formed.

Eine typische Dicke der Decklagen 64, 66 liegt bei ca. 1 mm.A typical thickness of the cover layers 64 . 66 is about 1 mm.

Erfindungsgemäß werden Panzerplatten bereitgestellt, welche sich auf einfache Weise herstellen lassen. Beispielsweise lassen sich technische Hölzer zur Herstellung einsetzen. Nach der Pyrolyse und vor der Keramisierung werden im Panzerplatten-Vorkörper Rißstopper hergestellt und dadurch die Panzerplatte in funktionelle Segmente unterteilt. Durch die funktionellen Segmente läßt sich eine räumliche Begrenzung der Schadenszone beim Impact, beispielsweise durch Auftreffen eines Geschosses, auf die Panzerplatte erreichen.According to the invention Armored plates provided, which can be produced in a simple manner. For example, technical woods can be used for the production. After the pyrolysis and before the ceramization crack stopper in the armor plate preform manufactured and thereby the armor plate in functional segments divided. Through the functional segments can be a spatial Limiting the damage zone during the impact, for example by impact of a projectile, reach the armor plate.

Die Panzerplatte selber wird mit den Rißstoppern integral hergestellt; es lassen sich dadurch relativ große Platten herstellen und verbauen. Die Platten können auch mit Krümmungen hergestellt werden, um so eine bessere Anpassung an eine Anwendung zu erreichen.The Armor plate itself is made integral with the Rißstoppern; It can thereby produce relatively large plates and obstruct. The plates can also with curvatures to be better adapted to an application to reach.

Die Rißstopper lassen sich auf einfache Weise vor der Keramisierung in dem Panzerplatten-Vorkörper herstellen, beispielsweise durch spanabhebende Materialbearbeitung und/oder Laserbearbeitung. Die funktionellen Segmente lassen sich dadurch mit definierten Abmessungen herstellen. Die entsprechenden Abstände lassen sich insbesondere so wählen, daß die sogenannte Drei-Treffer-Bedingung erfüllt wird.The crack stopper can be easily prepared before ceramization in the armor plate preform, for example, by machining material processing and / or Laser processing. The functional segments can be characterized produce with defined dimensions. Leave the appropriate distances to choose that way that the so-called three-hit condition is met.

Die erfindungsgemäßen Panzerplatten lassen sich in ein Panzersystem integrieren, wie es in der 8 schematisch gezeigt und dort als Ganzes mit 68 bezeichnet ist. Ein solches Panzersystem ist in der DE 697 07 560 T2 ( EP 0 810 415 B1 ) beschrieben. Auf dieses Dokument wird ausdrücklich Bezug genommen. Auf einer Strukturträgerschicht 70 (Backing) sitzt mindestens eine erfindungsgemäße keramische Panzerplatte 72. Die Strukturträgerschicht 70 kann beispielsweise aus Aluminium hergestellt sein oder aus Verbundwerkstoffen wie Kohle-Kevlar.The armor plates of the invention can be integrated into a tank system, as in the 8th shown schematically and there as a whole with 68 is designated. Such a tank system is in the DE 697 07 560 T2 ( EP 0 810 415 B1 ). This document is expressly incorporated by reference. On a textured carrier layer 70 (Backing) sits at least one kera invention mixed armor plate 72 , The structural carrier layer 70 may be made of aluminum, for example, or of composite materials such as carbon Kevlar.

Die (mindestens eine) Panzerplatte 72 ist beispielsweise über eine Klebstoffschicht 74 mit der Strukturträgerschicht 70 verklebt.The (at least one) armor plate 72 is for example via an adhesive layer 74 with the structural carrier layer 70 bonded.

Es kann auch noch eine Zertrümmerungsschicht 76 vorgesehen sein, auf welcher die Strukturträgerschicht 70 angeordnet ist. Die Zertrümmerungsschicht 76 dient dazu, die Zertrümmerung der Strukturträgerschicht 70 zu minimieren.It can also be a smash layer 76 be provided, on which the structural support layer 70 is arranged. The smash layer 76 this serves to disrupt the structure carrier layer 70 to minimize.

Die Panzerplatte 72 kann durch mehrere Abdeckschichten 78, 80, 82 abgedeckt sein. Nach oben ist das Panzersystem 68 durch ein Stahlplatte 84 begrenzt. Bezüglich des Aufbaus wird auf die EP 0 810 415 B1 verwiesen. Es läßt sich der gleiche Aufbau wie dort beschrieben verwenden, wobei anstatt einer Mehrzahl von Fliesen die mindestens eine erfindungsgemäße Panzerplatte eingesetzt wird.The armor plate 72 can through several cover layers 78 . 80 . 82 be covered. Upwards is the tank system 68 through a steel plate 84 limited. Regarding the construction is on the EP 0 810 415 B1 directed. It can be the same structure as described there use, instead of a plurality of tiles, the at least one armor plate according to the invention is used.

Claims (39)

Keramische Panzerplatte, welche einstückig ausgebildet ist und eine Mehrzahl von zusammenhängenden Segmenten (16) umfaßt, welche durch Rißstopper (12; 24; 60) funktionell getrennt sind, wobei die Rißstopper (12; 24; 60) der Verhinderung der Ausbreitung von Rissen von einem Segment (16) auf ein benachbartes Segment dienen.Ceramic armor plate integrally formed and a plurality of contiguous segments ( 16 ), which by crack stopper ( 12 ; 24 ; 60 ) are functionally separated, wherein the crack stopper ( 12 ; 24 ; 60 ) preventing the propagation of cracks from a segment ( 16 ) serve to an adjacent segment. Keramische Panzerplatte nach Anspruch 1, dadurch gekennzeichnet, daß die Rißstopper (12; 24; 60) in die Panzerplatte integriert sind.Ceramic armor plate according to claim 1, characterized in that the crack stops ( 12 ; 24 ; 60 ) are integrated into the armor plate. Keramische Panzerplatte nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die Rißstopper (12; 24; 60) in dem Vollmaterial der Panzerplatte gebildet sind.Ceramic armor plate according to claim 1 or 2, characterized in that the crack stops ( 12 ; 24 ; 60 ) are formed in the solid material of the armor plate. Keramische Panzerplatte nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, daß die Rißstopper (12; 24; 60) bei der Herstellung der Panzerplatte hergestellt sind.Ceramic armor plate according to one of the preceding claims, characterized in that the crack stops ( 12 ; 24 ; 60 ) are produced in the manufacture of the armor plate. Keramische Panzerplatte nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, daß Rißstopper durch Ausnehmungen (12; 24) und/oder über Ausnehmungen (12; 24) gebildet sind.Ceramic armor plate according to one of the preceding claims, characterized in that crack stopper is provided by recesses ( 12 ; 24 ) and / or recesses ( 12 ; 24 ) are formed. Keramische Panzerplatte nach Anspruch 5, dadurch gekennzeichnet, daß die Ausnehmungen (12; 24) in der Dickenrichtung (d) der Panzerplatte hergestellt sind.Ceramic armor plate according to claim 5, characterized in that the recesses ( 12 ; 24 ) in the thickness direction (d) of the armor plate. Keramische Panzerplatte nach Anspruch 5 oder 6, dadurch gekennzeichnet, daß nichtdurchgehende Ausnehmungen (12) vorgesehen sind.Ceramic armor plate according to claim 5 or 6, characterized in that non-penetrating recesses ( 12 ) are provided. Keramische Panzerplatte nach einem der Ansprüche 5 bis 7, dadurch gekennzeichnet, daß Rißstopper durch Nuten (12) und/oder über Nuten (12) gebildet sind.Ceramic armor plate according to one of claims 5 to 7, characterized in that crack stopper by grooves ( 12 ) and / or via grooves ( 12 ) are formed. Keramische Panzerplatte nach Anspruch 8, dadurch gekennzeichnet, daß die Tiefe der Nuten (12) im Bereich zwischen 0,05 bis 0,6 der Dicke (D) der Panzerplatte liegt.Ceramic armor plate according to claim 8, characterized in that the depth of the grooves ( 12 ) is in the range between 0.05 to 0.6 of the thickness (D) of the armor plate. Keramische Panzerplatte nach einem der Ansprüche 5 bis 9, dadurch gekennzeichnet, daß durchgehende Ausnehmungen (24) vorgesehen sind.Ceramic armor plate according to one of claims 5 to 9, characterized in that continuous recesses ( 24 ) are provided. Keramische Panzerplatte nach einem der Ansprüche 5 bis 10, dadurch gekennzeichnet, daß Rißstopper durch Perforationen (24) und/oder über Perforationen (24) gebildet sind.Ceramic armor plate according to one of claims 5 to 10, characterized in that crack stopper by perforations ( 24 ) and / or via perforations ( 24 ) are formed. Keramische Panzerplatte nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, daß Rißstopper über Risse (60) gebildet sind.Ceramic armor plate according to one of the preceding claims, characterized in that crack stopper is provided by cracks ( 60 ) are formed. Keramische Panzerplatte nach Anspruch 12, dadurch gekennzeichnet, daß die als Rißstopper dienenden Risse (60) zwischen einer Oberseite und einer Unterseite der Panzerplatte verlaufen.Ceramic armor plate according to claim 12, characterized in that the cracks serving as crack stopper ( 60 ) run between a top and a bottom of the armor plate. Keramische Panzerplatte nach Anspruch 13, dadurch gekennzeichnet, daß die Risse (60) zumindest näherungsweise in der Dickenrichtung (d) der Panzerplatte verlaufen.Ceramic armor plate according to claim 13, characterized in that the cracks ( 60 ) extend at least approximately in the thickness direction (d) of the armor plate. Keramische Panzerplatte nach Anspruch 13 oder 14, dadurch gekennzeichnet, daß Decklagen (64; 66) vorgesehen sind, zwischen welchen die Risse (60) verlaufen.Ceramic armor plate according to claim 13 or 14, characterized in that cover layers ( 64 ; 66 ) between which the cracks ( 60 ). Keramische Panzerplatte nach Anspruch 15, dadurch gekennzeichnet, daß die Decklagen (64; 66) aus C/C-SiC hergestellt sind.Ceramic armor plate according to claim 15, characterized in that the cover layers ( 64 ; 66 ) are made of C / C-SiC. Keramische Panzerplatte nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, daß als Rißstopper Fehlstellen vorgesehen sind.Ceramic armor plate according to one of the preceding Claims, characterized in that as crack stopper Defects are provided. Keramische Panzerplatte nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, daß der Abstand zwischen Rißstoppern (12; 24; 60) im Bereich zwischen 5 mm und 50 mm liegt.Ceramic armor plate according to one of the preceding claims, characterized in that the distance between crack stops ( 12 ; 24 ; 60 ) is in the range between 5 mm and 50 mm. Keramische Panzerplatte, gekennzeichnet durch einen mehrlagigen Aufbau.Ceramic armor plate, characterized by a multilayer construction. Keramische Panzerplatte, gekennzeichnet durch eine Herstellung aus einem Carbid-Keramikmaterial.Ceramic armor plate, characterized by a Manufacture from a carbide ceramic material. Keramische Panzerplatte nach einem der vorangehenden Ansprüche, gekennzeichnet durch eine Herstellung aus einer Siliciumcarbid-Keramik.Ceramic armor plate according to one of the preceding claims, characterized by a Manufactured from a silicon carbide ceramic. Keramische Panzerplatte nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, daß die Rißstopper (12; 24; 60) vor der Keramisierung eingebracht sind.Ceramic armor plate according to one of the preceding claims, characterized in that the crack stops ( 12 ; 24 ; 60 ) are introduced before the ceramization. Keramische Panzerplatte, gekennzeichnet durch eine Herstellung mittels eines kohlenstoffhaltigen Vorkörpers.Ceramic armor plate, characterized by a Production by means of a carbon-containing preform. Keramische Panzerplatte nach einem der vorangehenden Ansprüche, dadurch gekennzeichnet, daß der keramische Werkstoff der Panzerplatte mittels eines biomorphen Materials hergestellt ist.Ceramic armor plate according to one of the preceding Claims, characterized in that the ceramic material of the armor plate by means of a biomorphic material is made. Keramische Panzerplatte nach Anspruch 24, dadurch gekennzeichnet, daß das biomorphe Material Cellulose enthält.Ceramic armor plate according to claim 24, characterized characterized in that biomorphic material contains cellulose. Panzersystem, umfassend mindestens eine Panzerplatte gemäß einem der vorangehenden Ansprüche.A tank system comprising at least one armor plate according to one of the preceding claims. Panzersystem nach Anspruch 26, gekennzeichnet durch einen mehrlagigen Aufbau.A tank system according to claim 26, characterized by a multilayer construction. Panzersystem nach Anspruch 26 oder 27, dadurch gekennzeichnet, daß die mindestens eine Panzerplatte (72) auf einem Backing (70) angeordnet ist.A tank system according to claim 26 or 27, characterized in that the at least one armor plate ( 72 ) on a backing ( 70 ) is arranged. Verfahren zur Herstellung einer keramischen Panzerplatte, bei dem in einem Panzerplatten-Vorkörper Rißstopper erzeugt werden und die Panzerplatte über die Rißstopper in zusammenhängende funktionelle Segmente unterteilt wird.Method for producing a ceramic armor plate, in which are produced in an armored plate preform crack stopper and the armor plate over the tearstoppers in coherent functional Segments is divided. Verfahren nach Anspruch 29, dadurch gekennzeichnet, daß die Rißstopper vor der Keramisierung des Panzerplatten-Werkstoffs hergestellt werden.Method according to claim 29, characterized that the crack stopper be prepared before the ceramization of the armor plate material. Verfahren nach Anspruch 29 oder 30, dadurch gekennzeichnet, daß Rißstopper durch Herstellung von Ausnehmungen erzeugt werden.A method according to claim 29 or 30, characterized that tear stopper produced by the production of recesses. Verfahren nach Anspruch 31, dadurch gekennzeichnet, daß Ausnehmungen durch mechanische Materialbearbeitung hergestellt werden.Method according to claim 31, characterized in that that recesses be produced by mechanical material processing. Verfahren nach Anspruch 31 oder 32, dadurch gekennzeichnet, daß Ausnehmungen durch Strahlbearbeitung hergestellt werden.A method according to claim 31 or 32, characterized that recesses be prepared by jet machining. Verfahren nach einem der Ansprüche 29 bis 33, dadurch gekennzeichnet, daß Ausnehmungen mit Trennmittel gefüllt werden.Method according to one of Claims 29 to 33, characterized that recesses with Release agent filled become. Verfahren nach einem der Ansprüche 29 bis 34, dadurch gekennzeichnet, daß Risse als Rißstopper erzeugt werden.Method according to one of Claims 29 to 34, characterized that cracks as a crack stopper be generated. Verfahren nach Anspruch 35, dadurch gekennzeichnet, daß Risse über die Verbindung mit Decklagen erzeugt werden.Process according to claim 35, characterized in that that cracks over the Connection with cover layers are generated. Verfahren nach Anspruch 36, dadurch gekennzeichnet, daß die Decklagen aus C/C hergestellt werden.Method according to claim 36, characterized that the Cover layers made of C / C. Verfahren nach einem der Ansprüche 29 bis 37, dadurch gekennzeichnet, daß der Panzerplatten-Vorkörper ein kohlenstoffhaltiger Vorkörper ist.Method according to one of claims 29 to 37, characterized that the Armor plate preform a carbonaceous preform is. Verfahren nach einem der Ansprüche 29 bis 38, dadurch gekennzeichnet, daß ein mehrlagiger Aufbau vorgesehen wird, wobei die Lagen beim Keramisieren zur Bildung einer einstückigen Panzerplatte verbunden werden.Method according to one of Claims 29 to 38, characterized the existence multi-layer construction is provided, wherein the layers during ceramizing to form a one-piece Armor plate can be connected.
DE102004026515A 2004-05-19 2004-05-19 Ceramic armor plate, tank system and method of making a ceramic armor plate Withdrawn DE102004026515A1 (en)