DE10150600A1 - Two component hydraulically set (sic) adhesive mortar useful for application to nonwovens, plates, or natural stone as a cement-like base, emulsion coating, or paint - Google Patents

Two component hydraulically set (sic) adhesive mortar useful for application to nonwovens, plates, or natural stone as a cement-like base, emulsion coating, or paint

Info

Publication number
DE10150600A1
DE10150600A1 DE10150600A DE10150600A DE10150600A1 DE 10150600 A1 DE10150600 A1 DE 10150600A1 DE 10150600 A DE10150600 A DE 10150600A DE 10150600 A DE10150600 A DE 10150600A DE 10150600 A1 DE10150600 A1 DE 10150600A1
Authority
DE
Germany
Prior art keywords
adhesive mortar
mortar according
component
vinyl
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE10150600A
Other languages
German (de)
Inventor
Manfred Huber
Karl Frenkenberger
Robert Kaiser
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
PCI Augsburg GmbH
Original Assignee
PCI Augsburg GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by PCI Augsburg GmbH filed Critical PCI Augsburg GmbH
Priority to DE10150600A priority Critical patent/DE10150600A1/en
Publication of DE10150600A1 publication Critical patent/DE10150600A1/en
Withdrawn legal-status Critical Current

Abstract

A two component hydraulically set (sic) adhesive mortar obtained from a powder component A and a liquid component B, where the A component contains epoxide resin from bisphenol A or F, filler, cement containing binder, conventional additives, and component B, comprising amine curing agent, water, plasticizer, and an aqueous dispersion of vinyl or acrylate base. A two component hydraulically set (sic) adhesive mortar obtained from a powder component A and a liquid component B, where the A component contains (parts by wt.): epoxide resin from bisphenol A or F (0.5-10), filler (10-70), cement containing binder (5-20), conventional additives (0.1-5), and component B, comprising amine curing agent (0.5-0), water (2-0), plasticizer (0-5), and an aqueous dispersion of vinyl or acrylate base (10-50).

Description

Gegenstand der vorliegenden Erfindung ist ein zweikomponentiger, hydraulisch abbindender Klebemörtel, der aus einer Pulverkomponente (A) und einer Flüssigkomponente (B) hergestellt worden ist, und dessen Verwendung zum Verlegen von Fliesen, Platten oder Natursteinen auf zementären Untergründen oder auf Dispersionsbeschichtungen oder -anstrichen. The present invention relates to a two-component hydraulically setting adhesive mortar made from a powder component (A) and a liquid component (B) has been prepared, and its Use for laying tiles, slabs or natural stones on cementitious substrates or on dispersion coatings or -anstrichen.

Entsprechend dem Stand der Technik sind schon eine Vielzahl von ein- oder zweikomponentigen Klebemörteln bekannt bzw. im Handel, die sich in folgende vier Kategorien einteilen lassen:

  • 1. Zementäre Klebemörtel ohne oder mit nur einem geringen Anteil (< 1 Gew.-%) an Polymerpulver auf Vinyl- oder Acrvlat-Basis
    Diese Kleber eignen sich überwiegend für Wand- und Bodenfliesen im Innenbereich und insbesondere für unempfindliche Untergründe und geringe Belastung. Diese Systeme sind nach der Aushärtung vergleichsweise starr (geringe Elastizität) und nicht ohne Weiteres für jede Keramik (z. B. Feinsteinzeug) geeignet. Als besonders nachteilig muss jedoch die geringe Haftung, speziell bei Wärmebelastung, angesehen werden.
  • 2. Zementäre Klebemörtel mit einem größeren Anteil (bis 4.5 Gew.-%) an Polymerpulver auf Vinyl- oder Acrvlat-Basis (vgl. EP-A 722 917)
    Diese Mörtelsysteme sind sowohl für Innen- als auch für Außenbereiche gut geeignet. Sie weisen in der Regel eine gewisse Elastizität und Frühwasserbeständigkeit auf und sind für jede Art von Keramik geeignet. Problematisch ist jedoch die Haftung dieser Systeme, insbesondere bei nicht vollsatter Verlegung, im Außenbereich und vor allem Frost-, Tausalz- oder Wärmebelastung.
  • 3. Zweikomponentige zementäre Klebemörtel mit einer wässrigen Dispersion auf Vinyl- oder Acrvlat-Basis
    Diese zweikomponentigen Systeme besitzen eine gute Flexibilität und sind vor allem für vibrationsempfindliche Untergründe hervorragend geeignet. Ganz abgesehen davon, dass diese Klebemörtel vergleichsweise teuer und schwer zu verarbeiten sind, besteht bei dauernder Einwirkung von Alkalität eine deutliche Verseifungsgefahr, womit ein unerwünschter Haftungsverlust zur Keramik verbunden ist.
  • 4. Zweikomponentiger Klebemörtel auf Epoxidharz-Basis
    Die Klebemörtel auf Epoxidharz-Basis (sog. Epoxi-Kleber) besitzen normalerweise eine gute Haftung und eine ausgezeichnete Wasserfestigkeit. Als nachteilig bei den Epoxi-Klebern muss die Tatsache angesehen werden, dass sie vergleichsweise teuer sind, schwierig zu verarbeiten sind (Verätzungsgefahr) und im ausgehärteten Zustand zu vergleichsweise starren Systemen mit geringer Elastizität führen.
According to the state of the art, a large number of one- or two-component adhesive mortars are already known or commercially, which can be divided into the following four categories:
  • 1. Cementitious adhesive mortar without or with only a small proportion (<1% by weight) of polymer powder based on vinyl or acrylic
    These adhesives are mainly suitable for indoor wall and floor tiles and especially for insensitive substrates and low loads. After curing, these systems are comparatively rigid (low elasticity) and are not suitable for every ceramic (e.g. porcelain stoneware). However, the low adhesion, especially when exposed to heat, must be regarded as particularly disadvantageous.
  • 2. Cementitious adhesive mortar with a larger proportion (up to 4.5% by weight) of polymer powder based on vinyl or acrylic (see EP-A 722 917)
    These mortar systems are well suited for both indoor and outdoor areas. They usually have a certain elasticity and early water resistance and are suitable for all types of ceramics. However, the liability of these systems is problematic, especially when the installation is not fully saturated, outdoors and especially when exposed to frost, de-icing salt or heat.
  • 3. Two-component cementitious adhesive mortar with an aqueous dispersion based on vinyl or acrylic
    These two-component systems have good flexibility and are particularly suitable for vibration-sensitive substrates. Quite apart from the fact that these adhesive mortars are comparatively expensive and difficult to work with, there is a clear risk of saponification when alkaline is permanently exposed, which is associated with an undesirable loss of adhesion to the ceramic.
  • 4. Two-component adhesive mortar based on epoxy resin
    The adhesive mortars based on epoxy resin (so-called epoxy adhesive) normally have good adhesion and excellent water resistance. A disadvantage of epoxy adhesives is the fact that they are comparatively expensive, difficult to process (risk of chemical burns) and, when cured, lead to comparatively rigid systems with low elasticity.

Der vorliegenden Erfindung lag daher die Aufgabe zugrunde, einen universell einsetzbaren Klebemörtel für den Innen- und Außenbereich zu entwickeln, der die genannten Nachteile entsprechend dem Stand der Technik nicht aufweist, sondern der hervorragende Materialeigenschaften wie z. B. Elastizität, Haftung, Wasserfestigkeit, mechanische Stabilität und gute Verarbeitbarkeit besitzt. The present invention was therefore based on the object universal adhesive mortar for indoor and outdoor use develop the disadvantages mentioned according to the state of the art Technology does not have, but the excellent material properties such as B. elasticity, adhesion, water resistance, mechanical stability and has good processability.

Diese Aufgabe wurde erfindungsgemäß durch den zweikomponentigen, hydraulisch abbindenden Klebemörtel entsprechend Anspruch 1 gelöst. According to the invention, this object was achieved by the two-component hydraulically setting adhesive mortar according to claim 1 solved.

Es hat sich nämlich überraschenderweise gezeigt, dass durch gezielte Einstellung der Reaktivkomponenten die positiven Eigenschaften der Einzelkomponenten (wie z. B. die Nasshaftfestigkeit) sogar deutlich übertroffen und deren Nachteile überkompensiert wurden. Surprisingly, it has been shown that through targeted Setting the reactive components the positive properties of the Individual components (such as the wet adhesive strength) even clearly surpassed and their disadvantages were more than compensated for.

So konnte beim erfindungsgemäß vorgeschlagenen Mörtelsystem trotz des hohen Anteils der Polymerdispersion und des geringen Anteils an Epoxidharz eine sehr gute Wasserfestigkeit und Frost-Tausalz-Beständigkeit realisiert werden, was in diesem Ausmaß auf keinen Fall vorhersehbar war. Thus, in the mortar system proposed according to the invention, despite the high proportion of the polymer dispersion and the low proportion Epoxy resin very good water resistance and freeze-thaw resistance can be realized, which was by no means predictable to this extent.

Der zweikomponentige, hydraulisch abbindende Klebemörtel entsprechend der vorliegenden Erfindung ist aus einer Pulverkomponente (A) und eine Flüssigkomponente (B) hergestellt worden, wobei Komponente (A)

0,5 bis 10 Gew.-Teile eines Epoxidharzes vom Bisphenol A- oder F-Typ
10 bis 70 Gew.-Teile an Füllstoffen
5 bis 20 Gew.-Teile eines zementhaltigen Bindemittels
0,1 bis 5 Gew.-Teile an üblichen Additiven

enthält. The two-component, hydraulically setting adhesive mortar according to the present invention has been produced from a powder component (A) and a liquid component (B), component (A)

0.5 to 10 parts by weight of a bisphenol A or F type epoxy resin
10 to 70 parts by weight of fillers
5 to 20 parts by weight of a cement-containing binder
0.1 to 5 parts by weight of conventional additives

contains.

Bei den Epoxidharzen kann hierbei auf die üblichen Polymere vom Bisphenol A- oder F-Typ zurückgegriffen werden, die vorzugsweise eine Viskosität von 9000 bis 13 000 mPas und einen Epoxidwert (gemäß DIN 53188) von 0,52 bis 0,55 aufweisen. In the case of the epoxy resins, the usual polymers can be dated from Bisphenol A or F type can be used, preferably one Viscosity from 9000 to 13000 mPas and an epoxy value (according to DIN 53188) from 0.52 to 0.55.

Als Füllstoffe werden insbesondere Quarzsand, Quarzmehl, Schwerspat, Kalksteinmehl, Aluminiumoxid, Talkum oder Mischungen davon eingesetzt. In particular, quartz sand, quartz powder, heavy spar, Limestone powder, aluminum oxide, talc or mixtures thereof.

Als weiteren erfindungswesentlichen Zusatz enthält Komponente (A) ein zementhaltiges Bindemittel insbesondere aus der Gruppe Portlandzement, Tonerdeschmelzzement, Kompositzement oder HS-Zement bzw. Mischungen davon. Component (A) contains a further additive essential to the invention cement-containing binder, in particular from the Portland cement group, Alumina cement, composite cement or HS cement or Mixtures of these.

Schließlich enthält die Pulverkomponente (A) noch übliche Additive ausgewählt aus der Gruppe Verdickungsmittel, Fließmittel, Entschäumer, Verzögerer, Beschleuniger, Luftporenbildner und Schwundkompensationsmittel. Als Verdickungsmittel können hierbei die üblichen Celluloseether, wie z. B. Methylhydroxyethylcellulose oder Methylhydroxypropylcellulose, eingesetzt werden. Finally, the powder component (A) also contains conventional additives selected from the group of thickeners, flow agents, defoamers, Retarders, accelerators, air entraining agents and Fading compensation means. As a thickener, the usual cellulose ethers, such as. B. methylhydroxyethyl cellulose or Methyl hydroxypropyl cellulose can be used.

Um den erfindungsgemäß vorgeschlagenen Klebemörtel eine ausreichende Fließfähigkeit zu verleihen, kann die Pulverkomponente (A) ein Fließmittel auf der Basis von Melamin-Formaldehyd- oder Naphthalin- Formaldehyd-Kondensationsprodukten sowie Polymer-Verbindungen auf Vinyl- oder Acrylat-Basis enthalten. To the adhesive mortar proposed according to the invention to impart sufficient flowability, the powder component (A) a plasticizer based on melamine-formaldehyde or naphthalene Formaldehyde condensation products and polymer compounds Vinyl or acrylate base included.

Gemäß weiterer bevorzugter Ausführungsformen bestehen die Entschäumer aus Polyethylen- und/oder Polypropylenglykolen (ggf. mit einem Zusatz an amorpher Kieselsäure), die Verzögerer aus Citronensäure, Weinsäure und deren Salzen (insbesondere Phosphaten oder Glukonaten), die Beschleuniger aus Lithiumcarbonat oder Calciumformiat und die Schwundkompensationsmittel aus Calciumoxid, Aluminiumpulver, Polyethylenglykolen, nichtionischen Tensiden oder Neopentylglykol. According to further preferred embodiments, the Defoamer made of polyethylene and / or polypropylene glycols (if necessary with an addition of amorphous silica), the retarders made of citric acid, Tartaric acid and its salts (especially phosphates or gluconates), the accelerators made of lithium carbonate or calcium formate and the Shrinkage compensator made of calcium oxide, aluminum powder, Polyethylene glycols, non-ionic surfactants or neopentyl glycol.

Als Luftporenbildner können die üblichen Naturharze (wie z. B. Kieferwurzelharz) und/oder synthetischen Tenside auf Basis von Fettsäuresulfonaten eingesetzt werden. Insbesondere werden hierbei Vinsolharze verwendet, welche bei der Holzdestillation als Naturharz anfallen und ca. 85% Harzsäuren und ca. 15% vinsolische Produkte enthalten. The usual natural resins (such as, for example, Pine root resin) and / or synthetic surfactants based on Fatty acid sulfonates are used. In particular, here Vinsol resins used as a natural resin in wood distillation and approx. 85% resin acids and approx. 15% vinsolic products contain.

Die Teilchengröße der Pulverkomponente (A) kann in weiten Grenzen variiert werden, doch hat es sich aus Gründen der Verarbeitbarkeit als besonders vorteilhaft erwiesen, die mittlere Teilchengröße der Pulverkomponente (A) auf einen Wert von 10 bis 5 000 µm einzustellen. The particle size of the powder component (A) can be within wide limits can be varied, but it has turned out to be workable proven particularly advantageous, the average particle size of the Adjust powder component (A) to a value of 10 to 5,000 µm.

Es ist als erfindungswesentlich anzusehen, dass die Flüssigkomponente (B)

0,5 bis 10 Gew.-Teile eines Aminhärters
2 bis 10 Gew.-Teile Wasser
0 bis 5 Gew.-Teile eines Plastifizierungsmittels sowie
10 bis 50 Gew.-Teile einer wässrigen Polymerdispersion auf Vinyl- oder Acrylat-Basis

enthält. It is to be regarded as essential to the invention that the liquid component (B)

0.5 to 10 parts by weight of an amine hardener
2 to 10 parts by weight of water
0 to 5 parts by weight of a plasticizer and
10 to 50 parts by weight of an aqueous polymer dispersion based on vinyl or acrylate

contains.

Als Aminhärter können hierbei insbesondere Polyamidoamine und/oder Polyamine und/oder Polyamin-Epoxidharz-Addukte eingesetzt werden, die ggf. in gelöster Form in Wasser vorliegen können. Vorzugsweise besitzen die Aminhärter eine Viskosität (25°C) von 150 bis 1.200 mPas und eine Aminzahl von 250 bis 420. In particular, polyamidoamines and / or Polyamines and / or polyamine-epoxy resin adducts can be used possibly in dissolved form in water. Preferably own the amine hardeners have a viscosity (25 ° C) of 150 to 1,200 mPas and a Amine number from 250 to 420.

Als Plastifizierungsmittel werden vorzugsweise Polyalkylenglykolether eingesetzt, die aus den üblichen Ethylen- und/oder Propylenglykol- Einheiten sowie C1-C4-Alkyl- und Phenylresten aufgebaut sind. The plasticizers used are preferably polyalkylene glycol ethers which are composed of the customary ethylene and / or propylene glycol units and C 1 -C 4 -alkyl and phenyl radicals.

Bei der wässrigen Polymerdispersion auf Vinyl- oder Acrylatbasis, die einen bevorzugten Feststoffgehalt von 40 bis 60 Gew.-% aufweist, werden als Polymerverbindungen insbesondere solche auf Basis von Vinylacetat, Vinylpropionat, Vinyllaurat, Vinylversatat, Vinylchlorid, Vinylidenchlorid, geradkettigen oder verzweigten Vinylestern mit 3 bis 18 C-Atomen, Acryl- und Methacryl-Monomeren (insbesondere Estern) sowie Styrol, Butadien und Ethen eingesetzt. In the case of the aqueous polymer dispersion based on vinyl or acrylate, the has a preferred solids content of 40 to 60% by weight as polymer compounds, in particular those based on vinyl acetate, Vinyl propionate, vinyl laurate, vinyl versatate, vinyl chloride, vinylidene chloride, straight-chain or branched vinyl esters with 3 to 18 carbon atoms, acrylic and methacrylic monomers (especially esters) and styrene, butadiene and ethene.

Ein weiterer Gegenstand der vorliegenden Anmeldung ist die Verwendung des zweikomponentigen, hydraulisch abbindenden Klebemörtels zum Verlegen von Fliesen, Platten oder Natursteinen auf zementären Untergründen oder auf Dispersionsbeschichtungen oder -anstrichen. Another object of the present application is the use of the two-component, hydraulically setting adhesive mortar for Laying tiles, slabs or natural stones on cement Substrates or on dispersion coatings or paints.

Hierzu werden die Komponenten (A) und (B) homogen vermischt, mit den üblichen Vorrichtungen zu einem plastischen, knollenfreien Mörtel verrührt, anschließend wird das Klebebett auf den jeweiligen Untergrund aufgebracht und schließlich die Fliesen, Platten oder Natursteine nach bekannten Methoden verlegt. For this purpose, components (A) and (B) are mixed homogeneously with the usual devices for a plastic, lump-free mortar stirred, then the adhesive bed is on the respective surface applied and finally the tiles, slabs or natural stones after known methods relocated.

Die mit dem erfindungsgemäßen Klebemörtel ausgehärteten Systeme erfüllen hierbei alle Erforderungen im Hinblick auf die anwendungstechnischen Eigenschaften, wie Elastizität, Frühwasserbeständigkeit, Haftung, Wasserfestigkeit, Härte, Zugfestigkeit sowie Trocknungseigenschaften. The systems cured with the adhesive mortar according to the invention meet all requirements with regard to application properties, such as elasticity, Early water resistance, adhesion, water resistance, hardness, tensile strength as well as drying properties.

So können durch Variation der Bindemittelanteile alle Anforderungen der EN 12004 erfüllt werden, sowohl im Bereich der Dispersionskleber wie auch bei den zementären Klebemörteln. By varying the proportions of binder, all requirements of the EN 12004 are met, both in the field of dispersion adhesives as well for cementitious adhesive mortars.

Darüber hinaus ermöglicht der erfindungsgemäß vorgeschlagene Klebemörtel Nasshaftfestigkeiten von 1,0 bis 1,5 N/mm2, während bei den Systemen gemäß dem Stand der Technik die entsprechenden Werte lediglich bei 0,5 N/mm2 liegen. In addition, the adhesive mortar proposed according to the invention enables wet adhesive strengths of 1.0 to 1.5 N / mm 2 , while in the systems according to the prior art the corresponding values are only 0.5 N / mm 2 .

Die nachfolgenden Beispiele sollen die Erfindung näher erläutern. Beispiele Beispiel 1 (A) Pulverkomponente Gew.-Teile Epoxidharz: Europox 7101) (Bisphenol-A-Harz, Molmasse ≤ 700) 1,50 Kalksteinmehl 47,30 Portlandzement CEM I 42,5 R 10,60 Tonerdeschmelzzement 1,00 Verdickungsmittel: Culminal 200002) (Celluloseether) 0,20 Entschäumer: Agitan P 8033) 0,30 Beschleuniger: Lithiumcaxbonat 0,70 Verzögerer: Citronensäure 0,30 1) Hersteller: Witco GmbH 2) Hersteller: Hercules Inc. 3) Hersteller: Münzing Chemie GmbH (B) Flüssigkomponente Gew.-Teile wässrige Polymerdispersion: Cembond 0084) (Acrylatdispersion mit 54 Gew.-% Festkörpergehalt) 31,00 Plastifizierungsmittel: Plastilit 30605) (Polypropylenglykolalkylphenylether) 1,20 Wasser 4,70 Aminhärter: Polypox W 8006) (Polyaminaddukt 50%, gelöst in Wasser) 1,20 4) Hersteller: Vinamul Ltd. 5) Hersteller: BASF AG 6) Hersteller: U. Prümmer Polymer-Chemie GmbH Beispiel 2 (A) Pulverkomponente Gew.-Teile Epoxidharz: Europox 7101) (Bisphenol-A-Harz, Molmasse 700) 1,50 Quarzsand (0,06-0,2 mm) 37,30 Portlandzement CEM I 42,5 R 10,60 Tonerdeschmelzzement 1,00 Verdickungsmittel: Culminal 200002) (Celluloseether) 0,20 Entschäumer: Agitan P 8033) 0,30 Beschleuniger: Lithiumcarbonat 0,70 Verzögerer: Citronensäure 0,30 1) Hersteller: Witco GmbH 2) Hersteller: Hercules Inc. 3) Hersteller: Münzing Chemie GmbH (B) Flüssigkomponente Gew.-Teile wässrige Polymerdispersion: Cembond 0084) (Acrylatdispersion mit 54 Gew.-% Festkörpergehalt) 41,00 Plastifizierungsmittel: Plastilit 30605) (Polypropylenglykolalkylphenylether) 1,20 Wasser 4,70 Aminhärter: Polypox W 8006) (Polyaminaddukt 50%, gelöst in Wasser) 1,20 4) Hersteller: Vinamul Ltd. 5) Hersteller: BASF AG 6) Hersteller: U. Prümmer Polymer-Chemie GmbH The following examples are intended to explain the invention in more detail. Examples Example 1 (A) powder component Parts by weight Epoxy resin: Europox 710 1) (bisphenol A resin, molecular weight ≤ 700) 1.50 limestone 47.30 Portland cement CEM I 42.5 R 10.60 Aluminous cement 1.00 Thickener: Culminal 20000 2) (cellulose ether) 0.20 Defoamer: Agitan P 803 3) 0.30 Accelerator: lithium carbonate 0.70 Retarder: citric acid 0.30 1) Manufacturer: Witco GmbH 2) Manufacturer: Hercules Inc. 3) Manufacturer: Münzing Chemie GmbH (B) liquid component Parts by weight aqueous polymer dispersion: Cembond 008 4) (acrylic dispersion with 54% by weight solids content) 31.00 Plasticizer: Plastilit 3060 5) (polypropylene glycol alkylphenyl ether) 1.20 water 4.70 Amine hardener: Polypox W 800 6) (polyamine adduct 50%, dissolved in water) 1.20 4) Manufacturer: Vinamul Ltd. 5) Manufacturer: BASF AG 6) Manufacturer: U. Prümmer Polymer-Chemie GmbH (A) powder component Parts by weight Epoxy resin: Europox 710 1) (bisphenol A resin, molecular weight 700) 1.50 Quartz sand (0.06-0.2 mm) 37.30 Portland cement CEM I 42.5 R 10.60 Aluminous cement 1.00 Thickener: Culminal 20000 2) (cellulose ether) 0.20 Defoamer: Agitan P 803 3) 0.30 Accelerator: lithium carbonate 0.70 Retarder: citric acid 0.30 1) Manufacturer: Witco GmbH 2) Manufacturer: Hercules Inc. 3) Manufacturer: Münzing Chemie GmbH (B) liquid component Parts by weight aqueous polymer dispersion: Cembond 008 4) (acrylic dispersion with 54% by weight solids content) 41,00 Plasticizer: Plastilit 3060 5) (polypropylene glycol alkylphenyl ether) 1.20 water 4.70 Amine hardener: Polypox W 800 6) (polyamine adduct 50%, dissolved in water) 1.20 4) Manufacturer: Vinamul Ltd. 5) Manufacturer: BASF AG 6) Manufacturer: U. Prümmer Polymer-Chemie GmbH

Beispiel 3Example 3

Bewertung der Beispiele 1 und 2Evaluation of Examples 1 and 2

(1 = sehr gut; 6 = ungenügend) (1 = very good; 6 = insufficient)

Claims (19)

1. Zweikomponentiger, hydraulisch abbindender Klebemörtel, welcher aus einer Pulverkomponente (A) und einer Flüssigkomponente (B) hergestellt worden ist, dadurch gekennzeichnet, dass die Komponente (A)
0,5 bis 10 Gew.-Teile eines Epoxidharzes vom Bisphenol A- oder F-Typ
10 bis 70 Gew.-Teile an Füllstoffen
5 bis 20 Gew.-Teile eines zementhaltigen Bindemittels
0,1 bis 5 Gew.-Teile an üblichen Additiven
und die Komponente (B)
0,5 bis 10 Gew.-Teile eines Aminhärters
2 bis 10 Gew.-Teile Wasser
0 bis 5 Gew.-Teile eines Plastifizierungsmittels sowie
10 bis 50 Gew.-Teile einer wässrigen Polymerdispersion auf Vinyl- oder Acrylat-Basis
enthalten. 1. Two-component, hydraulically setting adhesive mortar which has been produced from a powder component (A) and a liquid component (B), characterized in that component (A)
0.5 to 10 parts by weight of a bisphenol A or F type epoxy resin
10 to 70 parts by weight of fillers
5 to 20 parts by weight of a cement-containing binder
0.1 to 5 parts by weight of conventional additives
and component (B)
0.5 to 10 parts by weight of an amine hardener
2 to 10 parts by weight of water
0 to 5 parts by weight of a plasticizer and
10 to 50 parts by weight of an aqueous polymer dispersion based on vinyl or acrylate
contain. 2. Klebemörtel nach Anspruch 1, dadurch gekennzeichnet, dass das Epoxidharz eine Viskosität von 9000 bis 13 000 mPas und einen Epoxidwert (DIN 53188) von 0,52 bis 0,55 aufweist. 2. adhesive mortar according to claim 1, characterized in that the Epoxy resin with a viscosity of 9000 to 13000 mPas and a Epoxy value (DIN 53188) from 0.52 to 0.55. 3. Klebemörtel nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass die Füllstoffe aus Quarzsand, Quarzmehl, Schwerspat, Kalksteinmehl, Aluminiumoxid, Talkum oder Mischungen davon bestehen. 3. adhesive mortar according to claim 1 or 2, characterized in that the fillers from quartz sand, quartz powder, heavy spar, limestone powder, Alumina, talc or mixtures thereof. 4. Klebemörtel nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass er als zementhaltiges Bindemittel Portlandzement, Tonerdeschmelzzement, Kompositzement oder HS- Zement oder Mischungen davon enthält. 4. adhesive mortar according to one of claims 1 to 3, characterized characterized as a cementitious binder Portland cement, alumina cement, composite cement or HS Contains cement or mixtures thereof. 5. Klebemörtel nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass das Additiv ein Zusatzmittel ausgewählt aus der Gruppe Verdickungsmittel, Fließmittel, Entschäumer, Verzögerer, Beschleuniger, Luftporenbildner und Schwundkompensationsmittel darstellt. 5. adhesive mortar according to one of claims 1 to 4, characterized characterized in that the additive is an additive selected from the Group of thickeners, flow agents, defoamers, retarders, Accelerators, air entraining agents and shrinkage compensators represents. 6. Klebemörtel nach Anspruch 5, dadurch gekennzeichnet, dass das Verdickungsmittel einen Celluloseether darstellt. 6. adhesive mortar according to claim 5, characterized in that the Thickener is a cellulose ether. 7. Klebemörtel nach Anspruch 5, dadurch gekennzeichnet, dass die Fließmittel aus Melamin-Formaldehyd- oder Naphthalin-Formaldehyd- Kondensationsprodukten, Polymer-Verbindungen auf Vinyl- oder Acrylat-Basis oder Casein bestehen. 7. adhesive mortar according to claim 5, characterized in that the Plasticizer made of melamine-formaldehyde or naphthalene-formaldehyde Condensation products, polymer compounds on vinyl or Acrylic base or casein exist. 8. Klebemörtel nach Anspruch 5, dadurch gekennzeichnet, dass er als Entschäumer ein Polyethylen- und/oder Polypropylenglykol, ggf. mit einem Zusatz an amorpher Kieselsäure, enthält. 8. adhesive mortar according to claim 5, characterized in that it as Defoamer a polyethylene and / or polypropylene glycol, if necessary with an addition of amorphous silica. 9. Klebemörtel nach Anspruch 5, dadurch gekennzeichnet, dass der Vexzögerer aus Citronensäure und Weinsäure und/oder deren Salzen, Phosphaten oder Glukonaten besteht. 9. adhesive mortar according to claim 5, characterized in that the Retarders from citric acid and tartaric acid and / or their salts, Phosphates or gluconates. 10. Klebemörtel nach Anspruch 5, dadurch gekennzeichnet, dass der Beschleuniger Lithiumcarbonat oder Calciumformiat darstellt. 10. adhesive mortar according to claim 5, characterized in that the Accelerator represents lithium carbonate or calcium formate. 11. Klebemörtel nach Anspruch 5, dadurch gekennzeichnet, dass die Luftporenbildner Naturharze und/oder synthetische Tenside auf Basis von Fettsäuresulfonaten sind. 11. adhesive mortar according to claim 5, characterized in that the Air entraining agents based on natural resins and / or synthetic surfactants of fatty acid sulfonates. 12. Klebemörtel nach Anspruch 5, dadurch gekennzeichnet, dass das Schwundkompensationsmittel aus Calciumoxid; Aluminiumpulver, Polyethylenglykolen, nichtionischen Tensiden oder Neopentylglykol besteht. 12. adhesive mortar according to claim 5, characterized in that the Calcium oxide shrinkage compensator; Aluminum powder, Polyethylene glycols, non-ionic surfactants or neopentyl glycol consists. 13. Klebemörtel nach einem der Ansprüche 1 bis 12, dadurch gekennzeichnet, dass als Aminhärter ein ggf. in Wasser gelöstes Polyamidoamin und/oder Polyamin und/oder Polyamin-Epoxidharz- Addukt eingesetzt wird. 13. adhesive mortar according to one of claims 1 to 12, characterized characterized in that the amine hardener is a solution which may be dissolved in water Polyamidoamine and / or polyamine and / or polyamine epoxy resin Adduct is used. 14. Klebemörtel nach einem der Ansprüche 1 bis 13, dadurch gekennzeichnet, dass der Aminhärter eine Viskosität (25°C) von 150 bis 1.200 mPas und eine Aminzahl von 250 bis 420 aufweist. 14. adhesive mortar according to one of claims 1 to 13, characterized characterized in that the amine hardener has a viscosity (25 ° C) of 150 up to 1,200 mPas and an amine number from 250 to 420. 15. Klebemörtel nach einem der Ansprüche 1 bis 14, dadurch gekennzeichnet, dass das Plastifizierungsmittel aus einem Polyalkylenglykolether besteht. 15. adhesive mortar according to one of claims 1 to 14, characterized characterized in that the plasticizer from a Polyalkylene glycol ether exists. 16. Klebemörtel nach einem der Ansprüche 1 bis 15, dadurch gekennzeichnet, dass die wässrige Polymer-Dispersion einen Feststoffgehalt von 40 bis 60 Gew.-% aufweist. 16. adhesive mortar according to one of claims 1 to 15, characterized characterized in that the aqueous polymer dispersion a Solids content of 40 to 60 wt .-%. 17. Klebemörtel nach einem der Ansprüche 1 bis 16, dadurch gekennzeichnet, dass Polymerverbindungen auf Vinyl- oder Acrylat- Basis solche aus Vinylacetat, Vinylpropionat, Vinyllaurat, Vinylversatat, Vinylchlorid, Vinylidenchlorid, geradkettigen oder verzweigten Vinylestern mit 3 bis 18 C-Atomen, Acryl- und Methacryl- Monomeren (insbesondere Estern) sowie Styrol, Butadien und Ethen eingesetzt werden. 17. adhesive mortar according to one of claims 1 to 16, characterized characterized in that polymer compounds on vinyl or acrylate Based on vinyl acetate, vinyl propionate, vinyl laurate, Vinyl versatate, vinyl chloride, vinylidene chloride, straight chain or branched vinyl esters with 3 to 18 carbon atoms, acrylic and methacrylic Monomers (especially esters) as well as styrene, butadiene and ethene be used. 18. Verwendung des Klebemörtels nach den Ansprüchen 1 bis 17 zum Verlegen von Fliesen, Platten oder Natursteinen auf zementären Untergründen oder auf Dispersionsbeschichtungen oder -anstrichen. 18. Use of the adhesive mortar according to claims 1 to 17 for Laying tiles, slabs or natural stones on cement Substrates or on dispersion coatings or paints. 19. Verwendung nach Anspruch 18, dadurch gekennzeichnet, dass man die Komponenten (A) und (B) vermischt, mit den üblichen Vorrichtungen zu einem plastischen, knollenfreien Mörtel verrührt, kurze Zeit später das Klebebett auf den Untergrund aufbringt und schließlich die Fliesen, Platten oder Natursteine verlegt. 19. Use according to claim 18, characterized in that one components (A) and (B) mixed with the usual Mixing devices into a plastic, lump-free mortar, a short time later applies the adhesive bed to the surface and finally the tiles, slabs or natural stones laid.
DE10150600A 2001-10-12 2001-10-12 Two component hydraulically set (sic) adhesive mortar useful for application to nonwovens, plates, or natural stone as a cement-like base, emulsion coating, or paint Withdrawn DE10150600A1 (en)