Abstract

The invented process for producing a decorative glass article with sealed spheres of garnets or another material is characterized in that at least one channel (2) with diameter being less than diameter of the spheres is made in a metallic matrix (1). Subsequently at least one sphere, most advantageously a series of spheres is put in said channel (2) of continuous or discontinuous shape. An external metallic jacket (3) copying the contour of the matrix (1) is put thereon, whereby the matrix fits exactly thereon, Then the jacket, the matrix and the spheres are heated up and glass is poured into a mold formed by the jacket and to the matrix. Further the matrix (1) is removed from the jacket (3) and glass is poured from the other side. After cooling, the product is removed from glass. Subsequently the glass article is dressed by grinding.

Description

Oblast technikyTechnical field

Vynález se týká způsobu výroby dekorativního výrobku ze skla se zatavenými kuličkami z granátu čí jiného materiálu.The invention relates to a method for manufacturing a decorative glass product with sealed beads of garnet or other material.

Dosavadní stav technikyBACKGROUND OF THE INVENTION

Je znám způsob výroby skleněného výrobku se zataveným vnitřním dekorem, který se provádí tak, že se vytvoří dvě části skleněného výrobku přičemž na jednu se aplikuje dekor obtiskem, zlacením či malováním a následně se obě části k sobě přilepí transparentním lepidlem, jehož index lomu je velmi blízký indexu lomu použitého skla. Nevýhodou tohoto řešení bývá často rozeznatelná hranice mezi oběma částmi právě způsobená přechodem lepidlo-sklo.There is known a method of manufacturing a glass article with a sealed interior decor, which is carried out by forming two parts of the glass product, one on which the decoration is applied by decal, gilding or painting, and then the two parts are glued together with a transparent adhesive. near the refractive index of the glass used. The disadvantage of this solution is often the recognizable boundary between the two parts due to the adhesive-glass transition.

Dále je znám způsob výroby skleněného výrobku, který spočívá v tom, že se na nosič přenese obtisk či dekor či jiná informace, která se včetně nosiče zataví do skla. Nevýhodou je, že nosič bývá ve skle viditelný a tímto způsobem se nedá do skla zatavit prostorový předmět.It is also known to produce a glass product by transferring a decal or decor or other information to the carrier, which is sealed into the glass including the carrier. The disadvantage is that the carrier is visible in the glass and in this way the spatial object cannot be sealed into the glass.

Je znám způsob umístění předmětu do skla tak, že se sklo naleje do formy, následně se do nalitého skla tento předmět umístí a skleněný výrobek se dále opracovává. Nevýhodou je, že se tímto způsobem může do skla umístit symetricky jenom jeden předmět.It is known to place the article in the glass by pouring the glass into a mold, then placing the article in the poured glass and processing the glass article. The disadvantage is that in this way only one object can be placed symmetrically in the glass.

Podstata vynálezuSUMMARY OF THE INVENTION

Způsob podle vynálezu spočívá v tora^že se do kovové matrice vytvoří alespoň jeden žlábek s průměrem menším než je průměr kuliček, spojitého či nespojitého tvaru, do kterého se umísti alespoň jedna kulička, nejlepe rada kuliček, na matrici se nasadí vnější kovový plást, který kopíruje tvar matrice , přičemž matrice do něho přesně zapadne, následně se plášť, matrice a kuličky zahřejí a do pláště se až k matrici naleje sklo, dále se matrice vyjme z pláště a sklo se naleje z druhé strany, po schlazení se výrobek ze skla vyjme.The method according to the invention consists in forming at least one groove in the metal matrix with a diameter smaller than the diameter of the balls, continuous or discontinuous in which at least one ball, preferably a series of balls, is placed. It follows the shape of the matrix, whereby the matrix fits exactly into it, then the shell, matrix and balls are heated and glass is poured into the shell up to the matrix, further the matrix is removed from the shell and the glass is poured from the other side. .

Nakonec se může skleněný výrobek přebrousit či vyleštit.Finally, the glass product may be reground or polished.

Výhodou tohoto řešení je, skleněného výrobku, který se oboru užitého umění. Dovoluje uvnitř skla z polodrahokamů, kuliček.The advantage of this solution is a glass product that is in the field of applied art. Allows inside the glass of semi-precious stones, balls.

Přehled obrázků na výkreseOverview of the drawings

Obrázek 1 znázorňuje formu vynálezu, obrázek 2 znázorňují že se docílí nového dekorativního svým provedením stává šperkem v vytváření různých dekorů a obrazců drahokamů či jiných materiálů tvaru k provádění způsobu výroby podle sklenici se zatavenými kuličkami.Figure 1 illustrates an embodiment of the invention; Figure 2 illustrates that a new decorative by its design becomes a jewel in creating various decors and patterns of gemstones or other shape materials to carry out the manufacturing process according to the sealed glass jar.

Příklad provedení vynálezuDETAILED DESCRIPTION OF THE INVENTION

Forma 4 se skládá ze dvou částí, jé vnějšího kovového pláště 3 a matrice 1. Do matrice 1 je vyfrézovaný jeden nebo více žlábku 2 spojitého tvaru přičemž průměr žlábku 2 je menší než průměr kuliček z granátu. Do žlábku 2 se vloží řada kuliček a následně se matrice 1 umístí do vnějšího kovového pláště 3. Plášť, matrice a kuličky se zahřejí a po zahřátí se do formy naleje sklo z přílepníkové tyče, posléze se vyjme matrice a sklo se naleje do formy z druhé strany. Po schlazení se sklo vyjme z formy a finálně se upravuje broušením nebo dalšími zušlechťovacími techn i kam i.The mold 4 consists of two parts, the outer metal sheath 3 and the die 1. One or more grooves 2 of continuous shape are milled into the die 1, the diameter of the groove 2 being smaller than the diameter of the garnet balls. A row of balls is inserted into the trough 2 and then the matrix 1 is placed in the outer metal sheath 3. The jacket, matrix and balls are heated and after heating the glass is poured into the mold from a rod, then the matrix is removed and the glass is poured into the mold. parties. After cooling, the glass is removed from the mold and finally treated by grinding or other finishing techniques.

Tímto uvedeným způsobem se vyrobí dekorativní výrobek zobrazený například podle obrázku 2, kde ve dně 6 sklenice 5 je zatavena spojitá řada 7 kuliček, výhodně z granátů či polodrahokamů č jiného materiálu. Z kuliček mohou být vytvářeny podle tvaru vyfrázovaného žlábku různé obrazce spojitého či nespojitého tvaru přičemž mohou být také vytvořeny v několika řadách nad sebou.In this way, the decorative product shown in FIG. 2 is produced, wherein a continuous row of 7 balls, preferably of garnets or semi-precious stones or other material, is sealed in the bottom 6 of the glass 5. Different shapes of continuous or discontinuous shape can be formed from the spheres according to the shape of the grooved groove and can also be formed in several rows one above the other.

Také umístění kuliček nemusí být vždy ve dně skleněného výrobku.Also, the placement of the beads need not always be in the bottom of the glass product.

Claims

PATENTOVÉ

Claims

Method for producing a decorative glass product with sealed beads of garnets or other material, characterized in that at least one groove (2) with a diameter less than the diameter of the balls of continuous shape is formed into the metal matrix (1). or a discontinuous shape into which at least one ball, preferably a row of balls, is placed, on the die (3) that follows the die shape, the outer metal sheath (1) is fitted, where the die fits exactly into it, into the sheath up to the matrix of sheath C3) and the glass is removed from the glass.

pour the glass, then remove the die C1) from the other side, after cooling

2.

The method of manufacturing a decorative article characterized by subsequent treatment is primarily characterized in that the glass article is ground by grinding or other finishing techniques.