CZ23869U1 - Composite material with natural fiber fillers based on sheep wool for manufacture of plastic parts - Google Patents
Composite material with natural fiber fillers based on sheep wool for manufacture of plastic parts Download PDFInfo
- Publication number
- CZ23869U1 CZ23869U1 CZ201125357U CZ201125357U CZ23869U1 CZ 23869 U1 CZ23869 U1 CZ 23869U1 CZ 201125357 U CZ201125357 U CZ 201125357U CZ 201125357 U CZ201125357 U CZ 201125357U CZ 23869 U1 CZ23869 U1 CZ 23869U1
- Authority
- CZ
- Czechia
- Prior art keywords
- natural
- plastic parts
- manufacture
- sheep wool
- natural fiber
- Prior art date
Description
Technické řešení se týká složení polymemího kompozitu s přírodními vlákennými plnivy na bázi ovčí vlny pro výrobu plastových dílů s vyššími užitnými vlastnostmi.The technical solution relates to the composition of a polymer composite with natural fibrous fillers based on sheep wool for the production of plastic parts with higher performance properties.
Dosavadní stav technikyBACKGROUND OF THE INVENTION
Polymemí materiály a jejich kompozity patří k nejprogresivněji se rozvíjejícím se materiálům, protože polymemí materiály představují nej významnější segment výroby a spotřeby podle objemu mezi všemi technickými materiály a nelze pochybovat o tom, že jsou klíčové pro moderní technickou společnost. Současný vývoj polymemích materiálů a jejich technologií zpracování bude pokračovat ve stále větším objemu a úspěch jednotlivých materiálů vyvinutých základním a aplikovaným výzkumem bude v rozhodující míře ovlivněn poměrem mezi cenou a užitnou hodnotou materiálu. Do této oblasti výzkumu patří i náhrada skelných vláken vlákny přírodními, které jsou z environmentálního hlediska předmětem zájmu polymemích zpracovatelů. Aplikace přírodních vláken je významnou materiálovou obměnou, která tradičně směřuje nejenom do automobilového průmyslu, ale i do oblastí spotřebního průmyslu, zdravotnických aplikací, apod. Výhodou přírodních vláken, pri srovnání s ostatními vláknitými materiály (používanými pri výrobě kompozitů), je jejich nízká hmotnost, nízká abraze (zabraňující opotřebení zpracovatelských strojů), spalitelnost, netoxičnost, biodegradabilita a především nízká cena, nezávislá na ceně ropy.Polymeric materials and their composites are among the most progressively developing materials, because polymeric materials represent the most important segment of production and consumption by volume among all technical materials and there is no doubt that they are key to a modern technical society. The current development of polymer materials and their processing technologies will continue to grow in volume, and the success of individual materials developed by basic and applied research will be influenced to a large extent by the price / utility value of the material. This area of research also includes the replacement of glass fibers with natural fibers, which are of environmental interest from polymer processors. The application of natural fibers is an important material variation, which is traditionally directed not only to the automotive industry, but also to the areas of consumer industry, medical applications, etc. The advantage of natural fibers compared to other fibrous materials (used in composites) is their low weight, low abrasion (preventing wear on processing machines), combustibility, nontoxicity, biodegradability and above all low price, independent of oil price.
Přírodní vlákna jsou v průmyslu používána nyní jako výztuž tvarovaných velkoplošných dílů, např. dřevěné piliny, obsahující vlákna celulózy a netkané lnové materiály s polypropylenem. Je však třeba zdůraznit, že se jedná prakticky pouze o výrobky vzniklé lisováním, nikoliv jejich vstřikováním, kde jsou kladeny vysoké nároky na kvalitu, rozměrovou a tvarovou přesnost vyrá25 běných dílů. Vstřikování syntetických kompozitů s přírodními plnivy je doposud velmi málo prozkoumanou oblastí s velkými možnostmi a potenciálem i předpokladem značného nárůstu a do této oblasti také směřuje toto navržené technické řešení,Natural fibers are now used in industry as reinforcement of shaped large-area parts, eg wood sawdust, containing cellulose fibers and polypropylene non-woven linen materials. It should be pointed out, however, that these are practically only injection molded products, not injection molding, where high demands are placed on the quality, dimensional and shape accuracy of manufactured parts. Injection of synthetic composites with natural fillers is a very poorly explored area with great potential and potential as well as a prerequisite for a significant increase, and this proposed technical solution is also directed to this area,
Z historického hlediska lze aplikaci kompozitů datovat od roku 1908, kdy bylo poprvé použito kompozitního materiálu na bázi fenolické pryskyřice zpevněné dřevěnou moučkou (L.Historically, the application of composites dates back to 1908, when it was first used composite material based on phenolic resin reinforced with wood flour (L.
Baekeland). Vývojem skelných vláken u firmy Owens-Illincis Glass Co. (1933) se postupně objevují první aplikace tzv. sklolaminátů, tj. polymemích kompozitů se skelnými vlákny, např. kryty radaru letadel (1942) nebo díly karosérie osobních automobilů (1956, íy. Citroen), apod. Kromě skelných vláken jsou během vývoje polymemích kompozitů aplikována jako výztuž také vlákna uhlíková, borová, keramická, aj. Skrytou realitou dneška je použití přírodních vláken a to pro výrobu polymemích kompozitů používaných k výrobě velkoplošných dílů vnitřního polstrování a vnějších dílů karoserií automobilů a dalších dopravních technologií. Podíl biokompozitů sice každoročně narůstá, ale technických řešení a možností je stále velmi málo. Nej používanějšími přírodními vlákny jsou především konopí, juta, len, bavlna, sisal a dřevo. Známými aplikacemi jsou díly v Mercedesu třídy C, Daimler AG. (např. výplně dveří a zvukové izolace), zadní kryt motoru autobusu vyrobený z rohože přírodních vláken, apod.Baekeland). Owens-Illincis Glass Co. developed glass fibers (1933), the first applications of so-called fiberglass, ie polymer composites with glass fibers, such as aircraft radar covers (1942) or body parts of passenger cars (1956, eg. Citroen), are gradually emerging. The hidden reality of today is the use of natural fibers for the production of polymer composites used for the production of large-area parts of inner padding and outer parts of car bodies and other transport technologies. The share of biocomposites is growing every year, but there are still few technical solutions and possibilities. The most used natural fibers are mainly hemp, jute, flax, cotton, sisal and wood. Well-known applications are parts in Mercedes C-Class, Daimler AG. (eg door panels and sound insulation), the rear engine cover made of natural fiber mats, etc.
Navržené technické řešení reaguje na vzrůstající poptávku a požadavky na tyto materiály, které jsou však v České republice doposud velmi málo rozšířené. Tlak na aplikace takovýchto materiálů neustále vzrůstá, a to nejenom v důsledku ekonomické situace (cena ropy se nejenom neustále mění, ale hlavně roste), nejenom v důsledku možností ovlivnění konečných a užitných vlastností výrobků, ale i z hlediska klimatických změn (téměř neřešená recyklace současných dílů ze syntetických plastů, spalování syntetických plastů, skládkování).The proposed technical solution responds to the increasing demand and requirements for these materials, which, however, have not been widely used in the Czech Republic. The pressure on the application of such materials is constantly increasing, not only because of the economic situation (the price of oil is not only constantly changing but also increasing), not only due to the possibility of influencing the final and utility properties of products, from synthetic plastics, combustion of synthetic plastics, landfilling).
-1 CZ 23869 Ul-1 CZ 23869 Ul
Podstata technického řešeníThe essence of the technical solution
Technické řešení si dává za cíl zlepšení výše uvedených nedostatků a vytvoření kompozitu s cíleným složením matrice, aditiva a plniva na bázi přírodních materiálů pro zlepšení konečných a užitných vlastností plastových dílů s vyšší přidanou hodnotou a ekologicky mnohem nižší zatí5 žitelností oproti 100% syntetickým produktům, tedy environmentálních výhod. Podstata technického řešení spočívá v tom, že kompozit obsahuje od 68,5 do 88,5 hmotnostních % polypropylenu, 10 až 30 hmotnostních % přírodních vláken ovčí vlny průměru od 16 do 40 pm (délka vláken od 0,2 do 2 mm) a 1 až 1,5 hmotnostního % aditiva na bázi silikonu a 0,1 až 0,5 hmotnostního % aditiva na bázi peroxidických dialkylů, které plní funkci chemického katalyzátoru.The aim of the technical solution is to improve the above mentioned drawbacks and to create a composite with a targeted composition of matrix, additive and filler based on natural materials for improving the final and utility properties of plastic parts with higher added value and ecologically much lower loadability compared to 100% synthetic products. environmental benefits. The essence of the invention is that the composite comprises from 68.5 to 88.5% by weight of polypropylene, 10 to 30% by weight of natural sheep wool fibers of 16 to 40 pm diameter (fiber length from 0.2 to 2 mm) and 1 up to 1.5% by weight of a silicone-based additive; and 0.1 to 0.5% by weight of a peroxide-dialkyl additive which functions as a chemical catalyst.
io Získaný kompozit je standardně dodáván ve formě granulí a je určen pro Širokou oblast technologií pro zpracování plastů, např. vstřikování.The composite obtained as a standard is supplied in the form of granules and is intended for a wide range of plastics processing technologies, eg injection molding.
Příklady provedení technického řešeníExamples of technical solution
Polymemí kompozit s přírodními vlákennými plnivy na bázi ovčí vlny je popsán na následujících příkladech včetně uvedení vhodné aplikace, přičemž složku A tvoří polypropylen, složku B pri15 rodní vlákna ovčí vlny průměru od 16 do 40 pm (délka vláken od 0,2 do 2 mm), složku C aditivum na bázi silikonu, složku D tvoří aditivum na bázi peroxidických dialkylů.The polymeric composite with natural fiber wool based fillers is described in the following examples, including an appropriate application, wherein component A is formed of polypropylene, component B is a natural sheep wool fiber of 16 to 40 µm diameter (fiber length of 0.2 to 2 mm) , component C is a silicone-based additive, component D is a peroxide-dialkyl-based additive.
Varianta 1:Option 1:
Složka A: 88,5 hmotnostních % polypropylenuComponent A: 88.5 wt% polypropylene
Složka B: 9,8 hmotnostních % přírodních vláken ovčí vlny průměru od 16 do 40 pmComponent B: 9.8 wt% natural sheep wool fibers with a diameter of 16 to 40 µm
Složka C: 1,5 hmotnostní % aditiva na bázi silikonuComponent C: 1.5% by weight silicone-based additive
Složka D: 0,2 hmotnostní % aditiva na bázi peroxidických dialkylů.Component D: 0.2 wt% peroxide dialkyl additive.
Varianta 2:Option 2:
Složka A: 78,5 hmotnostních % polypropylenuComponent A: 78.5 wt% polypropylene
Složka B: 19,8 hmotnostních % přírodních vláken ovčí vlny průměru od 16 do 40 pmComponent B: 19.8 wt.% Natural sheep wool fibers with a diameter of 16 to 40 µm
Složka C: 1,5 hmotnostní % aditiva na bázi silikonuComponent C: 1.5% by weight silicone-based additive
Složka D: 0,2 hmotnostní % aditiva na bázi peroxidických dialkylů.Component D: 0.2 wt% peroxide dialkyl additive.
Varianta 3:Option 3:
Složka A: 68,5 hmotnostních % polypropylenuComponent A: 68.5 wt% polypropylene
Složka B: 29,8 hmotnostních % přírodních vláken ovčí vlny průměru od 16 do 40 pmComponent B: 29.8 wt.% Natural sheep wool fibers with a diameter of 16 to 40 µm
Složka C: 1,5 hmotnostní % aditiva na bázi silikonuComponent C: 1.5% by weight silicone-based additive
Složka D: 0,2 hmotnostní % aditiva na bázi peroxidických dialkylů.Component D: 0.2 wt% peroxide dialkyl additive.
Polymemí kompozit s přírodními vlákennými plnivy na bázi ovčí vlny lze s výhodou použít pro výrobu plastových dílů rozdílnými technologickými procesy, které se vyznačují lepšími užitnými a konečnými vlastnostmi, např. mechanické vlastnosti, rozměrová stabilita, atd., ekonomickou úsporou, zkrácením výrobních cyklů, environmentálními aspekty, apod.Polymeric composites with natural fiber fillers based on sheep's wool can be advantageously used for production of plastic parts by different technological processes, which are characterized by better utility and final properties, eg mechanical properties, dimensional stability, etc., economical savings, shortening of production cycles, environmental aspects, etc.
Průmyslová využitelnostIndustrial applicability
Polymemí kompozit s přírodními vlákennými plnivy na bázi ovčí vlny podle předloženého technického řešení je vhodný pro výrobu plastových dílů rozdílnými technologickými procesy.The polymer composite with natural fiber fillers based on sheep wool according to the present invention is suitable for the production of plastic parts by different technological processes.
Claims (1)