CZ2014470A3 - Process for preparing expanded, clot-forming composite litter for cats and small animals - Google Patents
Process for preparing expanded, clot-forming composite litter for cats and small animals Download PDFInfo
- Publication number
- CZ2014470A3 CZ2014470A3 CZ2014-470A CZ2014470A CZ2014470A3 CZ 2014470 A3 CZ2014470 A3 CZ 2014470A3 CZ 2014470 A CZ2014470 A CZ 2014470A CZ 2014470 A3 CZ2014470 A3 CZ 2014470A3
- Authority
- CZ
- Czechia
- Prior art keywords
- expanded
- litter
- clay
- group
- cats
- Prior art date
Abstract
Způsob výroby lehčeného kompozitního silikátového steliva pro kočky a drobná zvířata, zejména bezprašného hrudkujícího steliva se sypnou hmotností kulovitých až oválných částic v rozsahu 200 až 800 kg/m.sup.3.n., kde vstupní pojivovou surovinou jsou částice s vysokým obsahem jílových minerálů ze skupiny kaolinitu, illitu, zeolitu a montmorillonitu a kde lehčeným kamenivem či plnidlem je látka vybraná ze skupiny zahrnující expandovaný perlit, expandovaný jíl, lehčený pálený kaolin, tvrdé dřevěné piliny a granule, křemelina, slídy a/nebo expandovaný vermikulit. Na vstupní surovinu nebo směs se po jejím vytřídění nebo namletí na požadovanou zrnitost a následném uvedení její předvlhčené sypké jemné frakce do vznosu rotací v uzavřeném prostoru působí jemně rozprašovanou kapalinou nebo suspenzí bez přídavků lepidel, vybranou ze skupiny látek, zahrnujících vodu, vodní roztok uhličitanu sodného, roztok tenzidu resp. saponátu, alkalický roztok, jemně vytříděnou a zahuštěnou natrifikovanou suspenzi kaolinu, jílu nebo bentonitu s obsahem užitného minerálu montmorillonitu 70 až 95 hm. % jako plastifikátoru, čímž se vlivem sorpční schopnosti a plasticity tohoto surového steliva, s využitím adhezních sil a aktivních center povrchu vznikajících při fyzikálně chemické adsorpci, vytvářejí nabalováním kuličky až oválky silikátového lehčeného steliva jako kompozitu složeného z lehčeného kameniva či plnidla a vysoce plastického práškového pojiva.A method for producing a lightweight composite silicate bedding for cats and small animals, especially dust-free clumping litter with bulk density of spherical to oval particles in the range of 200 to 800 kg / m.sup.3, where the high clay mineral content is the feed binder feedstock from the group of kaolinite, illite, zeolite and montmorillonite and wherein the expanded aggregate or filler is a substance selected from the group consisting of expanded perlite, expanded clay, expanded kaolin, hardwood filings and granules, diatomaceous earth, mica and / or expanded vermiculite. The feedstock or mixture is, after sorting or grinding it to the desired grain size and then bringing its pre-moistened bulk particulate fraction to a floating position by rotation in an enclosed space, with a finely atomized liquid or slurry without the addition of adhesives selected from the group consisting of water, sodium carbonate water solution , a surfactant solution, respectively. detergent, alkaline solution, finely sorted and thickened suspension of kaolin, clay or bentonite with a montmorillonite useful mineral content of 70 to 95 wt. % as a plasticizer, by virtue of the sorption ability and plasticity of this raw litter, by using adhesive forces and active surface centers generated by physicochemical adsorption, to form a ball of oval silicate lightweight bedding as a composite composed of expanded aggregate or filler and a highly plastic powder binder. .
Description
Oblast technikyField of technology
Předmětem vynálezu je způsob výroby lehčeného, hrudkujícího kompozitního steliva pro kočky a drobná zvířata, zejména kaolinového, jílového, bentonitového, zeolitového, z expandovaného perlitu, z expandovaného vermikulitu, muskovitu, biotitu, expandovaného cypřišového jílu a lehčeného páleného kaolinu nebo jejich směsi, a to bez využití lepidel s minimální prachovitostí.The present invention relates to a process for the production of expanded, clumping composite litter for cats and small animals, in particular kaolin, clay, bentonite, zeolite, expanded perlite, expanded vermiculite, muscovite, biotite, expanded cypress clay and expanded fired kaolin or mixtures thereof, without the use of adhesives with minimal dustiness.
Dosavadní stav technikyPrior art
Jako stelivo pro drobné domácí zvířectvo, zejména pro kočky, se používají granuláty, které slouží k zachycování a sorpci zvířecích odpadů. Na trhu jsou minerální granuláty různé zrnitosti s obsahem pojiv či jiných aditiv, které vytvářejí v přítomnosti tekutého odpadu aglomeráty, vlhké hrudky. Nevýhodou některých steliv je zvýšený podíl prachu, který se projevuje nejenom při výrobě a přepravě, ale i užití u spotřebitele, kde dochází ke znečišťování domácností. Velkou nevýhodou vyráběných komerčních steliv může být často jejich hmotnost, resp. sypná hmotnost steliva, která často limituje přepravu a jeho převzetí odběratelem.Granules are used as litter for small domestic animals, especially cats, which are used to capture and sorb animal waste. There are mineral granules on the market of various grain sizes containing binders or other additives, which form agglomerates, wet lumps in the presence of liquid waste. The disadvantage of some bedding is the increased proportion of dust, which manifests itself not only in production and transport, but also in consumer use, where household pollution occurs. A major disadvantage of commercially produced bedding can often be their weight, resp. bulk density of litter, which often limits transport and its acceptance by the customer.
Stelivo pro kočky a drobná zvířata jako přírodní hrudkující sorbent se vyrábí např. způsobem podle CZ patentu 299576, kdy se natěžená vhodná surovina na bázi bentonitu, zeolitu nebo jejich směsí aktivuje přídavkem iontů Na+ hnětením v kolovém mlýně nebo rychlomísidle, nechá se odležet a poté se suší, zdrobňuje a drtí, třídí na komerční zrnitostní frakci v rozmezí přibližně 0,5 až 7 mm, balí a expeduje jako přírodní stelivo pro kočky a drobná zvířata. Přitom má výrobek, podle použitých surovin, sypnou hmotnost nejčastěji v rozmezí 800 až 1200 kg/m3 a obsahuje velmi jemné prachovité částice. Cílem předloženého vynálezu je způsob výroby bezprašného, kuličkového nebo oválného silikátového, lehčeného kompozitního steliva, které je výrazné odlehčeno oproti normálnímu stelivu pro kočky drobná zvířata a vyznačuje se sypnou hmotností cca 200 až 800 kg/m3. Tím dochází ke snížení nákladů na přepravu tohoto zboží, které je pro spotřebitele elegantnější při ~2~ · : ··;· • ·· · ··· · manipulaci a nasypávání do nádoby při použití, kdy má minimální prachovitost.Litter for cats and small animals as a natural clumping sorbent is produced, for example, by the method according to CZ patent 299576, where the mined suitable raw material based on bentonite, zeolite or their mixtures is activated by addition of Na + ions by kneading in a wheel mill or quick mixer. is dried, crushed and crushed, sorted into a commercial grain fraction in the range of approximately 0.5 to 7 mm, packed and shipped as natural litter for cats and small animals. Depending on the raw materials used, the product most often has a bulk density in the range of 800 to 1200 kg / m 3 and contains very fine dusty particles. The object of the present invention is a method for the production of a dust-free, spherical or oval silicate, lightweight composite litter, which is significantly lightened compared to normal litter for small animals and is characterized by a bulk density of about 200 to 800 kg / m 3 . This reduces the cost of transporting these goods, which is more elegant for consumers when handled and poured into a container when used with minimal dustiness.
Podstata vynálezuThe essence of the invention
Předložený vynález se týká způsobu výroby lehčeného kompozitního silikátového steliva pro kočky a drobná zvířata, zejména bezprašného hrudkujícího steliva se sypnou hmotností kulovitých až oválných částic v rozsahu 200 až 800 kg/m3, kde vstupní pojivovou surovinou jsou částice s vysokým obsahem jílových minerálů ze skupiny kaolinitu, illitu, zeolitu a montmorillonitu a kde lehčeným kamenivem či plnidlem je látka vybraná ze skupiny zahrnující expandovaný perlit, expandovaný jíl, lehčený pálený kaolin, tvrdé dřevěné piliny nebo granule, křemelina, slídy a/nebo expandovaný vermikulit. Podstata vynálezu spočívá v tom, že na vstupní surovinu nebo směs se po jejím vytřídění nebo namletí na požadovanou zrnitost a následném uvedení její předvlhčené sypké jemné frakce do vznosu rotací v uzavřeném prostoru působí jemně rozprašovanou kapalinou nebo suspenzí bez přídavků lepidel, vybranou ze skupiny látek, zahrnujících vodu, vodní roztok uhličitanu sodného, roztok tenzidu resp. saponátu, alkalický roztok, jemně vytříděnou a zahuštěnou natrifikovanou suspenzi kaolinu, jílu nebo bentonitu s obsahem užitného minerálu montmorillonitu 70 až 95 hm.% jako plastifikátoru, čímž se vlivem sorpční schopnosti a plasticity tohoto surového steliva, s využitím adhezních sil a aktivních center povrchu vznikajících při fyzikálně chemické adsorpci, vytvářejí nabalováním kuličky až oválky silikátového lehčeného hrudkujícího steliva jako kompozitu složeného z lehčeného kameniva či plnidla a vysoce plastického práškového pojivá.The present invention relates to a process for the production of a lightweight composite silicate litter for cats and small animals, in particular a dust-free lumpy litter with a bulk density of spherical to oval particles in the range of 200 to 800 kg / m 3 , wherein the input binder raw material is high clay mineral particles from the group kaolinite, illite, zeolite and montmorillonite and wherein the expanded aggregate or filler is a substance selected from the group consisting of expanded perlite, expanded clay, expanded fired kaolin, hardwood sawdust or granules, diatomaceous earth, mica and / or expanded vermiculite. The invention is based on the fact that the feedstock or mixture is treated with a finely divided liquid or suspension without the addition of adhesives, selected from the group of substances, after it has been sorted or ground to the desired grain size and subsequently agitated by its pre-moistened free flowing fine fraction. comprising water, aqueous sodium carbonate solution, surfactant solution resp. detergent, alkaline solution, finely sorted and thickened stratified suspension of kaolin, clay or bentonite with a useful mineral content of montmorillonite 70 to 95 wt.% as a plasticizer, which due to the sorption capacity and plasticity of this raw litter, using adhesive forces and active surface centers arising in physicochemical adsorption, they form balls to ovals of silicate expanded clumping litter as a composite composed of expanded aggregate or filler and a highly plastic powder binder.
Kuličky až oválky silikátového lehčeného steliva, jako kompozitu složeného z lehčeného kameniva či plnidla a vysoce plastického práškového pojivá, podle tohoto vynálezu jsou vytvářeny bez využití lepidel a s minimální prachovitostí. Produktem jsou lehké a bezprašné, hrudkující kulovité útvary o velikosti v rozmezí přibližně od 0,01 až 10 mm, nejčastěji v komerční frakci 0,1 až 5 mm, 0,1 až 2 mm. Uvedený postup umožňuje i povrchovou úpravu steliva vzhledem na barvu, velikost adhezních sil a tedy hrudkovatelnost, úpravu pH výrobku, pevnost vytvořených hrudek, zářivost, lesk apod.Balls to ovals of silicate expanded bedding, as a composite composed of expanded aggregate or filler and a highly plastic powder binder, according to the present invention are formed without the use of adhesives and with minimal dustiness. The product is light and dust-free, lumpy spherical formations ranging in size from about 0.01 to 10 mm, most often in a commercial fraction of 0.1 to 5 mm, 0.1 to 2 mm. The mentioned procedure also enables surface treatment of litter with regard to color, size of adhesive forces and thus clumpingability, adjustment of product pH, strength of formed lumps, radiance, gloss, etc.
Příklady uskutečnění vynálezuExamples of embodiments of the invention
Příklad 1Example 1
Odprašek (prachovitý podíl frakce 0 až 1 mm) z výroby bentonitického steliva pro kočky a drobná zvířata nebo mletý aktivovaný bentonitický jíl se ve vznosu v rotační nádobě pomocí rozprašované vody s vytvořenou pěnou zpracovává na kuličky o zrnitosti 0,5 až 2,0 mm, případně 0,7 až 2,0 mm (ultra jemné stelivo) nebo o zrnitosti přibližně 0,7 až 5 mm. Produktem úpravy je vysoce kvalitní, lehké, hrudkující stelivo pro kočky a drobná zvířata se sorpčními vlastnostmi (pohlcuje tekutiny a pachy) se sypnou hmotností v rozmezí 500-800 kg/m3. Při klasické výrobě steliva pro kočky a drobná zvířata vzniká tak zvaný prachovitý podíl (obvykle zrnitostní frakce 0 až 1 mm, popř. 0 až 0,7 mm, resp. 0 až 0,5 mm), který se hůře využívá při výrobě sorbentů a lze ho pokládat za odpadní produkt (až 10 až 60 % hmot.). Jeho zpracováním peletizací lze zvýšit celkový výkon výrobní linky na výrobu steliva pro kočky a drobná zvířata. Navíc již aktivovaný prachovitý podíl obsahuje povrchově aktivní centra a látky, které zvýrazňují kvalitativní vlastnosti sorbentů.Dust (dust fraction 0 to 1 mm) from the production of bentonitic litter for cats and small animals or ground activated bentonitic clay is processed into balls with a grain size of 0.5 to 2.0 mm in suspension in a rotating vessel using sprayed water with the formed foam, optionally 0.7 to 2.0 mm (ultra-fine litter) or with a grain size of about 0.7 to 5 mm. The product of the treatment is a high-quality, light, clumping litter for cats and small animals with sorption properties (absorbs liquids and odors) with a bulk density in the range of 500-800 kg / m 3 . In the classic production of litter for cats and small animals, the so-called dust fraction is formed (usually a grain fraction of 0 to 1 mm, or 0 to 0.7 mm, or 0 to 0.5 mm), which is less used in the production of sorbents and it can be considered as a waste product (up to 10 to 60% by weight). By processing it by pelletizing, it is possible to increase the overall performance of the production line for the production of litter for cats and small animals. In addition, the already activated dust content contains surfactant centers and substances which enhance the qualitative properties of the sorbents.
Příklad 2Example 2
Mletý nebo jinak práškovitý kaolin (viz CZ patent 300585) s vysokým podílem lehké, muskovitické slídy (20-60 hm. %) se ve směsi s odpraškem světlého bentonitického jílu rotací zahaluje do kuliček a oválků zrnitosti přibližně 0,5 mm, případné 1 mm až přibližně 6 mm, po jeho ovlhčení jemně vytříděnou hustou suspenzí bílého bentonitu s obsahem montmorillonitu cca 80 hm.%. Produktem je lehké a světlé stelivo pro kočky a drobná zvířata se sypnou hmotností kolem 500 kg/m3 vhodný po dosušení na vlhkost asi 10 hm.% pro prodej. Další výhodou kulovitého kompozitního silikátového steliva se světlou muskovitickou slídou je malý obsah prachovitých částic a zářivý, stříbřitě lesknoucí se povrch steliva.Ground or otherwise powdery kaolin (see CZ patent 300585) with a high proportion of light, muscovitic mica (20-60 wt.%) In a mixture with a dusting of light bentonitic clay is rotated into balls and ovals with a grain size of approximately 0.5 mm or 1 mm. up to about 6 mm, after wetting with a finely sorted thick suspension of white bentonite with a montmorillonite content of about 80% by weight. The product is a light and light litter for cats and small animals with a bulk density of about 500 kg / m 3 suitable after drying to a moisture content of about 10% by weight for sale. Another advantage of the spherical composite silicate litter with light muscovite mica is the low content of dusty particles and the radiant, silvery shiny surface of the litter.
Příklad 3Example 3
Bílý, suchý expandovaný a velmi lehký kuličkovitý perlit (sypná hmotnost cca 80-200 kg/m3) o zrnitosti 0 až 5 mm se v nádobě s rotačním pohybem zpracovává suspenzí speciálně jemně vytříděného Na+ aktivovaného bílého bentonitu, upraveného v suspenzi na hydrocyklónu tak, aby obsahoval minimální množství balastních minerálů a 80 až 90 hm. % extrémně lepivého a jemného sorpčně aktivního minerálu montmorillonitu. Výsledkem jsou velmi lehké a hrudkující bílé kuličky a oválky kompozitního steliva o zrnitosti například 0,1 až 1 mm, resp. až 5 mm, které mají extrémně nízkou sypnou hmotnost asi 200 až 300 kg/m3. Produkt má vysokou nasákavost. Výrazné zvýšení kvality získaného produktu (například zvýšení nasákavosti přibližně na 200 až 350 %) má vliv na vysokou sorpční schopnost s možností mnohostranného využití v průmyslu (sorbenty, slévárenská pojivá, v chemickém průmyslu, stavebnictví, v zemědělství apod.).White, dry expanded and very light spherical perlite (bulk density approx. 80-200 kg / m 3 ) with a grain size of 0 to 5 mm is processed in a rotary vessel with a suspension of specially finely sorted Na + activated white bentonite, treated in suspension on a hydrocyclone so to contain a minimum amount of ballast minerals and 80 to 90 wt. % of extremely sticky and fine sorption active mineral montmorillonite. The result is very light and clumping white balls and ovals of composite litter with a grain size of, for example, 0.1 to 1 mm, resp. up to 5 mm, which have an extremely low bulk density of about 200 to 300 kg / m 3 . The product has a high absorbency. A significant increase in the quality of the obtained product (for example, an increase in absorbency to approximately 200 to 350%) has an effect on high sorption capacity with the possibility of versatile use in industry (sorbents, foundry binders, chemical industry, construction, agriculture, etc.).
Příklad 4Example 4
Směs jemných, lehkých a tvrdých dřevěných pilin o zrnitosti do přibližně 2 mm nebo dřevěných granulí a práškového, natrifikovaného bentonitu v zrnitostní frakci pod 20 mikrometrů v poměru 2:1 se po ovlhčení vodní mlhou zahaluje na lehké, kulovité stelivo o zrnitosti 0,5 až 5 mm se sypnou hmotností 500 až 800 kg/m3. Výhodou je v podstatě bezprašné stelivo pro kočky drobná zvířata na bázi přírodních materiálů, to je dřevěných pilin a upraveného bentonitu.A mixture of fine, light and hard wood sawdust with a grain size of up to about 2 mm or wood granules and powdered, natrified bentonite in a grain fraction below 20 micrometers in a ratio of 2: 1 is moistened to a light, spherical litter with a grain size of 0.5 to 5 mm with a bulk density of 500 to 800 kg / m 3 . The advantage is basically dust-free litter for cats, small animals based on natural materials, that is, wood sawdust and modified bentonite.
Příklad 5Example 5
Jemný prášek světlého žlutozeleného zeolitu Bartošova Lehčtka s příměsí světlého bentonitu (např. mletá frakce, odprašek, prachovitý podíl atd.) se ve směsi s koncentrátem světlé muskovitické slídy (poměr např. 2:1) rotací zahaluje do kuliček a oválků v kontinuálním zařízení zahuštěnou a ztekucenou suspenzí (pomocí uhličitanu sodného) za mokra vytříděného bentonitu, popř. jemného bentonitického jílu (montmorillonitický, iHiticko-montmorillonitický) s velmi vysokou sorpční schopností. Produktem úpravy je barevně stálé, odlehčené a hrudkující kompozitní stelivo pro kočky a drobná zvířata o zrnitosti například 0,5 až 2,0 mm, 0,5 až 3,0 mm, 0,5 až 4,0 mm, 0,5 až 5,0 mm apod. se sypnou hmotností 400 až 600 kg/m3, s vysokou pevností vytvořených hrudek a s velmi nízkou prašností (vysoká otěruvzdornost částic).The fine powder of light yellow-green zeolite Bartošova Lehčtka with an admixture of light bentonite (eg ground fraction, dust, dust, etc.) in a mixture with a concentrate of light muscovite mica (eg ratio 2: 1) is rotated into balls and ovals in a continuous device concentrated and a liquefied suspension (with sodium carbonate) of wet-sorted bentonite, or fine bentonitic clay (montmorillonite, iHitic-montmorillonite) with very high sorption capacity. The product of the treatment is a color-stable, lightweight and clumping composite litter for cats and small animals with a grain size of, for example, 0.5 to 2.0 mm, 0.5 to 3.0 mm, 0.5 to 4.0 mm, 0.5 to 5.0 mm etc. with a bulk density of 400 to 600 kg / m 3 , with high strength of formed lumps and very low dustiness (high abrasion resistance of particles).
Příklad 6Example 6
Odprašek nebo úlet o zrnitosti v oblasti 0 až 250 pm z drcení a třídění lehčeného bílého páleného kaolinu se ve směsi s úlety a odprašky z ultra jemného mletí bílého bentonitu upravuje v rotačním zařízení po ovlhčení roztokem sody na lehké kuličkovéDust or fly ash with a grain size in the range of 0 to 250 μm from the crushing and sorting of expanded white calcined kaolin, mixed with fly ash and dust from ultra-fine grinding of white bentonite, is treated in a rotary device after wetting with a solution of soda to light ball
kompozitní stelivo o zrnitosti například 0,5 až 3 mm nebo 0,5 až 5 mm. Výhodou je zpracování a využití odpadních práškových a prašných, úletových produktů.composite litter with a grain size of, for example, 0.5 to 3 mm or 0.5 to 5 mm. The advantage is the processing and utilization of waste powder and dust, flight products.
Příklad 7Example 7
Drcený, silně porézní a lehčený bílý metakaolin o zrnitosti 0,5 až 5 mm se jako kamenivo obaluje ve směsi s jemně namletým světlým aktivovaným (natrifikovaným) bentonitem ve frakci pod 20 mikrometrů zabaluje do kuličkového kompozitního steliva po jeho ovlhčení. Produkt úpravy je světlé kompozitní a odlehčené stelivo pro kočky a drobná zvířata.Crushed, strongly porous and lightened white metakaolin with a grain size of 0.5 to 5 mm is packed as an aggregate in a mixture with finely ground light activated (natrified) bentonite in a fraction below 20 micrometers and packed in a ball composite litter after its wetting. The product of the treatment is a light composite and lightweight litter for cats and small animals.
Příklad 8Example 8
Jemně namletý, natrifikovaný světlý bentonit o zrnitosti pod 100 mikrometrů je pojivém při výrobě kompozitního lehčeného steliva obsahují jako kamenivo silně porézní a nasákavý pálený lehčený kaolin KTM se sypnou hmotností 200 až 400 kg/m v zrnitostní frakci 0 až 1 mm, resp. 0-4 mm. Po ovlhčení tryskami vody vznikají rotací kulovité až oválné světlé částice hrudkujícího sorbentu.Finely ground, stratified light bentonite with a grain size below 100 micrometers is binding in the production of composite expanded bedding. It contains as aggregate strongly porous and absorbent fired expanded kaolin KTM with a bulk density of 200 to 400 kg / m in a grain fraction of 0 to 1 mm, resp. 0-4 mm. After wetting with water jets, spherical to oval light particles of clumping sorbent are formed by rotation.
Příklad 9Example 9
Kompozitní, odlehčené stelivo pro kočky a drobná zvířata lze vyrobit rotací po zabalení lehkého plnidla expandovaného vermikulitu se sypnou hmotností cca 80 kg/m3 vytříděnou suspenzí bentonitu s velmi vysokým obsahem minerálu montmorillonitu s extrémně vysokou sorpční schopností, vazností a lepivostí jako pojivá. Docílená sypná hmotnost tohoto lehkého hrudkujícího steliva činí podle poměru plnidla a pojivá (např. 50:50, 30:70, 70:30 atd.) 300 až 800 kg/m3.Composite, lightweight litter for cats and small animals can be produced by rotating after packaging a light filler of expanded vermiculite with a bulk density of about 80 kg / m3 sorted bentonite suspension with a very high content of montmorillonite mineral with extremely high sorption capacity, binding and tackiness as binders. The achieved bulk density of this light clumping litter is 300 to 800 kg / m 3, depending on the ratio of filler to binder (eg 50:50, 30:70, 70:30, etc.).
Příklad 10Example 10
Zamícháním velmi lehkého kuličkového kameniva z expandovaného cypřišového jílu typu keramzitu o granulometrii v rozmezí 0,1 až 10 mm s velmi plastickým a sorpčně aktivním jemným práškem bentonitu s vysokým měrným povrchem a s obsahem montmorillonitu nad 70 hm. % bylo připraveno velmi lehké a bezprašné stelivo pro kočky a drobná zvířata se sypnou hmotností kolem 400 kg/m3.By mixing very light spherical aggregate from expanded cypress clay of the expanded clay type with a granulometry in the range of 0.1 to 10 mm with a very plastic and sorption-active fine bentonite powder with a high specific surface area and a montmorillonite content above 70 wt. % very light and dust-free litter was prepared for cats and small animals with a bulk density of about 400 kg / m 3 .
Claims (1)