CS246531B1 - Livening agent with antistatic and softening effect - Google Patents
Livening agent with antistatic and softening effect Download PDFInfo
- Publication number
- CS246531B1 CS246531B1 CS586984A CS586984A CS246531B1 CS 246531 B1 CS246531 B1 CS 246531B1 CS 586984 A CS586984 A CS 586984A CS 586984 A CS586984 A CS 586984A CS 246531 B1 CS246531 B1 CS 246531B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- antistatic
- softening effect
- fabric
- cationic
- alkyl
- Prior art date
Description
Vynález se týká avivážního prostředku s antistatickým a změkčujícím účinkem, nízkou toxicitou a dobrou biologickou odbouratelností, který obsahuje směs kationaktivního a neionogenního tenzidu.The invention relates to a fabric softener having an antistatic and softening effect, low toxicity and good biodegradability, which comprises a mixture of a cationic and a non-ionic surfactant.
Avivážní prostředky zlepšují užitné vlastnosti tkanin, tj. zabraňují tvorbě elektrostatického náboje na textiliích nebo umožní jeho rychlejší odvedení, oživují vzhled, změkčují omak a usnadňují vypíratelnost v následujícím praní. Aplikují se v poslední máchací lázni na mokré vyprané prádlo po odstranění zbytků anionaktivních tenzidů z prací lázně.Fabric softeners improve the utility properties of fabrics, ie prevent the formation of electrostatic charges on fabrics or allow faster removal, revitalize the appearance, soften the touch and facilitate washability in subsequent washes. They are applied in the last rinse bath to wet washed laundry after removing residual anionic surfactants from the wash liquor.
Běžně užívané avivážní prostředky obsahují obvykle kvartérní amoniovou sloučeninu, která má antistatický a změkčovací účinek. Dále mohou obsahovat emulgátor, opticky zjasňující prostředek, barvivo, parfém či přísadu, způsobující perleťový vzhled.Commonly used fabric softeners typically contain a quaternary ammonium compound having antistatic and softening effects. They may further comprise an emulsifier, an optical brightener, a colorant, a perfume or a pearlescent agent.
Jako kvartérní soli se používají obvykle dimethyldistearylamoniové soli, substituované imidazoliniové soli, alkyltrimethylamoniové či alkylbenzyldimethylamoniové soli aj. K výrobě uvedených surovin jsou zapotřebí jako výchozí látky aminy, diaminy či triaminy, které se vyrábějí poměrně komplikovaným způsobem.The quaternary salts used are generally dimethyldistearylammonium salts, substituted imidazolinium salts, alkyltrimethylammonium or alkylbenzyldimethylammonium salts and the like. For the production of these raw materials amines, diamines or triamines are required as starting materials, which are produced in a relatively complicated manner.
Kvartérní amoniové sloučeniny mají kromě svých vynikajících užitných vlastností i řadu nevýhod, zejména vyšší toxicitu než neionogenní tenzidy a vyšší cenu.In addition to their excellent utility properties, quaternary ammonium compounds have a number of disadvantages, in particular higher toxicity than nonionic surfactants and higher cost.
Výše uvedené nevýhody nemá avivážní prostředek podle vynálezu s antistatickým a změkčujícím účinkem, nízkou toxicitou a dobrou biologickou odbouratelností, jehož podstata spočívá v tom, že obsahuje 1 až 38 % hmotnosti synergické směsi kationaktivního a neionogenního tenzidu v hmotnostním poměru 0,1 až 9:1, přičemž jako kationaktivní tenzid se použije kvartérní amoniová sůl obecného vzorce IThe above-mentioned disadvantages do not have the fabric softener composition according to the invention with antistatic and softening effect, low toxicity and good biodegradability, characterized in that it contains 1 to 38% by weight of a synergistic mixture of cationic and non-ionic surfactant in a weight ratio of 0.1 to 9: 1 wherein the quaternary ammonium salt of formula I is used as the cationic surfactant
R2 R 2
Rl—CONHCH2CHaCH2N +—R3 X~ I ve kterémRI CONHCH2CHaCH2N + -R3 X- I wherein
Rl značí alkylový zbytek se 7 až 22 atomy uhlíku,R1 represents an alkyl radical of 7 to 22 carbon atoms,
R2 alkylový zbytek s 1 až 4 atomy uhlíku,R 2 an alkyl residue with 1 to 4 carbon atoms,
R5 methylskupinu, ethylskupinu nebo benzýlskupinu aR 5 is methyl, ethyl or benzyl; and
X methoxysulfonylskupinu, ethoxysulfonylskupinu nebo atom chloru a jako neionogenní tenzid se použije acylpolyglykol obecného vzorce IIX a methoxy, ethoxy or chlorine atom and the nonionic surfactant used is an acyl polyglycol of formula II
R1 CO(OCH2CH2),;OH II nebo/a alkylpolyglykol obecného vzorce IIIR 1 CO (OCH 2 CH 2), OH II and / or an alkyl polyglycol of formula III
Rl (OCH2CH2)nOH ΙΠ ve kterých máR 1 (OCH 2 CH 2) n OH ΙΠ in which it has
R1 shora uvedený význam a n je přirozené číslo 3 až 36.R 1 as defined above and n is a natural number 3 to 36.
Výhodou avivážního prostředku je, že se žádaného antistatického účinku dosahuje s nižším množstvím kationaktivního tenzidu, neboť směs uvedeného kationaktivního tenzidu (KT) a neionogenního tenzidu (NT) vykazuje synergický efekt. Směs má až o 1 řád (podle poměru KT : NT) lepší antistatický účinek daný velikostí povrchového odporu upravených tkanin, než teoretický předpoklad vypočtený na základě lineárních kombinací povrchového odporu tkanin upravených samotnými výchozími tenzidy.An advantage of the fabric softener composition is that the desired antistatic effect is achieved with a lower amount of cationic surfactant, since the mixture of said cationic surfactant (KT) and nonionic surfactant (NT) exhibits a synergistic effect. The composition has up to 1 order (by KT: NT ratio) better antistatic effect given by the surface resistance of the treated fabrics than the theoretical assumption calculated on the basis of linear combinations of the surface resistance of fabrics treated with the starting surfactants themselves.
Avivážní prostředek podle vynálezu snižuje povrchový odpor z 1.1012 až 1. 1013 ohmu podle druhu tkaniny na 1.109 až 5 .1010 ohmu podle poměru kationaktivního tenzidu ku neionogennímu při koncentraci 0,4 g. . M 100% aktivní látky, což je běžná aplikační koncentrace. Komerční avivážní prostředky snižují povrchový odpor na hodnotu 2.101θ až 8.1O10 ohmu podle druhu tkaniny.Softening composition according to the invention reduces the surface resistance of 1.10 12 to 1 10 13 ohms according to the type of fabric to 10.1 9-5 .10 10 ohms according to the ratio of cationic: nonionic surfactant to at a concentration of 0.4 g.. M 100% active substance, which is the normal application concentration. Commercial fabric softeners reduce the surface resistance to 2.10 1θ to 8.1O 10 ohms depending on the fabric.
Synergický účinek je ukázán v následující tabulce pro aplikační koncentraci 0,4 g. L·1 100 % aktivní látky a kombinaci Ν,Ν,Ν-trimethyl-N-stearoylaminopropylamoniummethosulfátu (KT) a acylpolyglykolesteru (NTj.The synergistic effect is shown in the following table for an application concentration of 0.4 g. L · 1 100% active ingredient and a combination of Ν, Ν, trim-trimethyl-N-stearoylaminopropylammonium methosulfate (KT) and acyl polyglycol ester (NTj.
Povrchový odpor poměr PES PAD PANSurface resistance ratio PES PAD PAN
KT: NT teoreticky stanoveno teoreticky stanoveno teoreticky stanovenoKT: NT theoretically determined theoretically determined theoretically determined
Povrchový odpor se stanoví na tetraohmmetru Teralin III doplněném nerezovou nožovou sondou ve tvaru rovnoběžných 10 cm břitů vzdálených od sebe 0,7 cm. Měření se provádí při teplotě 20 až 22 °C a relativní vlhkosti vzduchu 60 až 65 %.Surface resistance is determined on a Teralin III tetraohmmeter supplemented with a stainless steel knife probe in the form of parallel 10 cm blades spaced 0.7 cm apart. The measurement is carried out at a temperature of 20 to 22 ° C and a relative humidity of 60 to 65%.
Avivážní prostředek podle vynálezu pro dosažení daného antistatického efektu obsahuje méně kvartérní amoniové sloučeniny, je tedy méně toxický a lépe biologicky odbouratelný, neboť pouitý neionogenní tenzid (zejména pokud je použit acylpolyglykol) je netoxický a dobře odbouratelný.The fabric softener composition of the present invention contains less quaternary ammonium compounds to achieve the antistatic effect, and is therefore less toxic and better biodegradable, since the nonionic surfactant used (especially when acyl polyglycol is used) is nontoxic and well degradable.
Hodnota LD50 uváděná pro alkyltrimethylamoniové sloučeniny je 250 až 1 000 mg. . kg-1 podle typu alkylu (Jungermann E.: Cationic Surfactants, New York 1970). Literatura (Blažej A. a kol.: Tenzidy, Bratislava 1977) uvádí pro alkylpolyglykoly LDso 2 000 až 12 500 mg . kg“1 a pro acylpolyglykoly LD50 12 500 až 50 200 mg . kg-1.The LD 50 value for the alkyltrimethylammonium compounds is 250 to 1000 mg. . kg -1 depending on the type of alkyl (Jungermann E .: Cationic Surfactants, New York 1970). The literature (Blazej A. et al., Tensides, Bratislava 1977) reported an LD 50 of 2000-12,500 mg for alkyl polyglycols. kg -1 and for acyl polyglycols LD50 12 500 to 50 200 mg. kg -1 .
Avivážní prostředek podle vynálezu je rovněž méně cenově náročný, neboť cena neionogenních tenzidů je průměrně 2X až 3X nižší než cena kationaktivních tenzidů.The fabric softener composition of the present invention is also less expensive since the cost of nonionic surfactants is on average 2X to 3X lower than the cost of cationic surfactants.
Pro hodnocení změkčujícího účinku není stanovena objektivní norma. Změkčující účinek se hodnotí subjektivně popsaným způsobem [Egan R. R: J. Am. Oil. Chem. Soc. 55, 118 (1978) ] skupinou 5 osob, které hodnotí omakem froté plátna a zařazují je do 5 tříd měkkosti, kde 1. třída značí nejtvrdší plátno a 5. nejměkčí.There is no objective standard for evaluating the softening effect. The emollient effect is evaluated subjectively as described [Egan R. R. J. Am. Oil. Chem. Soc. 55, 118 (1978)] by a group of 5 persons who evaluate the terry cloth and classify them into 5 softness classes, where the 1st class denotes the hardest linen and the 5th softest.
Jako srovnávací standardy se volí neupravené plátno a plátno upravené dimethyldistearylamoniumchloridem, který má výborný změkčovací účinek zařazený do třídy měkkosti 5. Bylo zjištěno, že omak pláten upravených avivážním prostředkem podle vynálezu, je srovnatelný s omakem dosaženým výše zmíněným chloridem.The untreated and dimethyldistearylammonium chloride treated canvas are selected as comparative standards and have an excellent softening effect classified in softness class 5. It has been found that the feel of the fabric conditioner treated fabrics of the present invention is comparable to that achieved by the aforementioned chloride.
Avivážní prostředek podle vynálezu se připraví snadno rozmícháním výchozích surovin při 30 až 60 °C ve vodě.The fabric softener composition of the invention is readily prepared by mixing the starting materials at 30 to 60 ° C in water.
Sloučeniny obsažené v avivážním prostředku jsou snadno přístupné. Kvartérní sůl se připraví kvarternisací reakčního produktu triglyceridu a 3-dialkylaminopropylaminu, acylpolyglykol respektive alkylpolyglykol se získá oxyethylací mastné kyseliny, respektive mastného alkoholu. Podle potřeby a druhu aplikace se přidá parfém, barvivo či opticky zjasňující prostředek.The compounds contained in the fabric softener are readily accessible. The quaternary salt is prepared by quaternizing the reaction product of triglyceride and 3-dialkylaminopropylamine, acyl polyglycol and alkyl polyglycol, respectively, by oxyethylating the fatty acid and fatty alcohol, respectively. Depending on the need and type of application, a perfume, colorant or optically brightener is added.
Příklady složení a výroby avivážního prostředku s antistatickým a změkčujícím účinkem podle vynálezu jsou blíže objasněny v následujících příkladech provedení, které však rozsah vynálezu nijak neomezují. Příklady provedeníExamples of the composition and manufacture of the fabric softener with antistatic and softening effect according to the invention are explained in more detail in the following non-limiting examples. Examples
Příklad 1Example 1
Do reaktoru o objemu 10 m3 opatřeného míchadlem a topným hadem se napustí 2 000 litrů vody, přidá se 457 kg 35%ního Ν,Ν,Ν-trimethyl-N-stearoylaminopropylamonium2463312,000 liters of water are charged into a 10 m 3 reactor equipped with a stirrer and a heating coil, 457 kg of 35% ní, Ν, Ν-trimethyl-N-stearoylaminopropylammonium are added 244633
S methosulfátu, 400 kg stearoylhexadekaethylenglykolu, směs se ohřeje na 60 °C a míchá se 2 hodiny. Pak se během 30 minut přidá 5 103 1 vody, 40 kg parfému a směs se míchá 2 hodiny. Získá se perleťově bílý avivážní prostředek s dobrým antistatickým účinkem a změkčujícím účinkem vhodný pro použití v automatických pračkách. Prostředek při aplikační koncentraci 0,4 g. I1 100% aktivní látky snižuje povrchový odpor na 8.109 až 4.10i° ohm podle druhu tkaniny. Změkčující účinek je hodnocen třídou měkkostiWith methosulfate, 400 kg stearoylhexadecaethylene glycol, the mixture was warmed to 60 ° C and stirred for 2 hours. 5 103 L of water, 40 kg of perfume are then added over 30 minutes and the mixture is stirred for 2 hours. A pearlescent softener with good antistatic and softening effect is obtained, suitable for use in automatic washing machines. Means at an application concentration of 0.4 g. I, 1100% of the active ingredient reduces the surface resistivity at 8.10 to 4.10 ° 9 ohm by fabric type. The softening effect is evaluated by the softness class
5.5.
Příklad 2Example 2
Stejným způsobem jako v příkladu 1 se smísí 2 000 kg 40%ního N-ethyl-N,N-dimethyl-N-lauroylaminopropylamoniumethosulfátu s 2 000 1 vody, 320 kg palmitoyloktadekaethylenglykolu. Přidá se 3 620 1 vody a 60 kilogramů parfému. Získá se luxusní avivážní prostředek s výborným antistatickým a změkčujícím účinkem vhodný pro úpravu jemných syntetických tkanin při ručním máchání.In the same manner as in Example 1, 2,000 kg of 40% N-ethyl-N, N-dimethyl-N-lauroylaminopropylammonium ethosulfate were mixed with 2,000 L of water, 320 kg of palmitoyl octadecaethylene glycol. 3,620 L of water and 60 kg of perfume are added. A luxury fabric softener with excellent antistatic and softening effect is obtained, suitable for the treatment of fine synthetic fabrics during hand rinsing.
Prostředek při aplikační koncentraci 0,4 gramu. I-1 100%ní aktivní látky snižuje povrchový odpor na 1. 109 až 5 . 109 ohm podle druhu tkaniny. Změkčující účinek je hodnocen třídou měkkosti 4.The formulation at an application concentration of 0.4 grams. I- 1 100% of the active substance reduces the surface resistance to 1. 10 9 to 5. 10 9 ohm depending on the type of fabric. The softening effect is evaluated by softness class 4.
Příklad 3Example 3
Do reaktoru o objemu 10 m3 opatřeného míchadlem a topným hadem se napustí 2 400 litrů vody, přidá se 914 kg 35%ního Ν,Ν,Ν-trimethyl-N-palmitoylaminopropylamoniummethosulfátu, 180 kg myristoyldodekaethylenglykolu a 140 kg laurylhexadekaethylenglykolu, směs se ohřeje na 60 °C a míchá se 2 hodiny. Pak se přidá během 30 minut 4 326 litrů vody, 40 kg parfému a směs se míchá 2 hodiny. Získá se avivážní prostředek s výborným antistatickým a změkčujícím účinkem vhodný i pro použití v automatických pračkách. Prostředek při aplikační koncentraci 0,4 g. I“1 100% aktivní látky snižuje povrchový odpor na 2.109 až 1.1010 ohm podle druhu tkaniny. Změkčující účinek je hodnocen třídou měkkosti 4 až 5.2400 liters of water are charged to a 10 m 3 reactor equipped with a stirrer and a heating coil, 914 kg of 35% Ν, Ν, Ν-trimethyl-N-palmitoylaminopropylammonium methosulfate, 180 kg of myristoyldodecethylene glycol and 140 kg of laurylhexadecethylene glycol are added. 60 ° C and stirred for 2 hours. 4,326 liters of water, 40 kg of perfume are then added over 30 minutes and the mixture is stirred for 2 hours. A fabric softener with excellent antistatic and softening effect is obtained, suitable also for use in automatic washing machines. The composition at an application concentration of 0.4 g. 1 100% active ingredient reduces the surface resistance to 2.10 9 to 1.10 10 ohm depending on the fabric type. The softening effect is evaluated by softness class 4 to 5.
Příklad 4Example 4
Do reaktoru o objemu 10 m3 (podle příkladu lj se napustí 3 847 kg 30%ního N-ethyl-N,N-dimethyl-N-stearoylaminopropylamoniumethosulfátu, ohřeje se na 50 °C, přidá se 1 646 kg stearylhexakosylenethylenglykolu a po dokonalém rozmíchání při 50 stupních Celsia se přidá 50 kg parfému a 2 457 kg vody. Získá se 8 000 kg pastovitého avivážního prostředku, vhodného pro ruční máchání. V koncentraci 0,4 g. L·1 100%ní aktivní látky snižuje prostředek povrchový odpor na 3 .109 až 2.1010 ohmu podle druhu použité tkaniny. Změkčující účinek je hodnocen třídou měkkosti 5.In a 10 m 3 reactor (according to Example 1j) 3,847 kg of 30% N-ethyl-N, N-dimethyl-N-stearoylaminopropylammonium ethosulphate are charged, heated to 50 ° C, 1,646 kg of stearylhexacosylene ethylene glycol are added and mixed thoroughly. at 50 degrees Celsius was added 50 kg of perfume and 2,457 kg water. There were obtained 8000 kg of pasty softener composition suitable for hand rinsing. at a concentration of 0.4 g. of L · 1 100% active ingredient composition reduces the surface resistance to 3 .10 9 to 2.10 10 ohms depending on the type of fabric used The softening effect is evaluated by softness class 5.
Příklad 5Example 5
Stejným postupem jako v příkladu 1 se smísí 2 650 kg 50%ního N,N,N-trimethyl-N-lauroylaminopropylamoniummethosulfátu a 320 kg myristoyloktadekaethylenglykolu. Přidá se 40 kg parfému a 4 990 kg vody. Získá se avivážní prostředek pro ruční máchání s vynikajícím antistatickým účinkem na PES — tkaniny. Prostředek v aplikační koncentraci 0,4 g. 1_1 snižuje povrchový odpor až na 9.108 u PES — tkanin.In the same manner as in Example 1, 2,650 kg of 50% N, N, N-trimethyl-N-lauroylaminopropylammonium methosulfate and 320 kg of myristoyl octadecaethylene glycol are mixed. 40 kg of perfume and 4,990 kg of water are added. A fabric rinse aid fabricator with excellent antistatic effect on PES fabrics is obtained. The composition at the application concentration 0.4 g. 1 _1 reduces surface resistance of up to 10.9 8 by PES - fabrics.
Příklad 6Example 6
Stejným postupem jako v příkladu 1 se smísí 1 543 kg 40%ního N-benzyl-N,N-dimethyl-N-stearoylaminopropylamonium chloridu a 343 kg stearylhexakosylenethylenglykolu. Přidá se 40 kg parfému a 6 074 kg vody. Získá se 8 000 kg avivážního prostředku, vhodného zejména pro použití v automatických pračkách. Prostředek snižuje v aplikační koncentraci 0,4 g. I1 povrchový odpor na 2.109 až 9.109 podle druhu použité tkaniny. Změkčující účinek je hodnocen třídou měkkosti 4 až 5.1543 kg of 40% N-benzyl-N, N-dimethyl-N-stearoylaminopropylammonium chloride and 343 kg of stearylhexacosylene ethylene glycol are mixed in the same manner as in Example 1. 40 kg of perfume and 6 074 kg of water are added. 8,000 kg of fabric softener are obtained, particularly suitable for use in automatic washing machines. The composition reduces the application concentration at 0.4 g. I 1 surface resistance to 2.10 9 to 9.10 9 depending on the type of fabric used. The softening effect is evaluated by softness class 4 to 5.
Claims (1)