CS195993B1 - Agent for hardening and frost resistance of ceramic and wooden material - Google Patents
Agent for hardening and frost resistance of ceramic and wooden material Download PDFInfo
- Publication number
- CS195993B1 CS195993B1 CS522477A CS522477A CS195993B1 CS 195993 B1 CS195993 B1 CS 195993B1 CS 522477 A CS522477 A CS 522477A CS 522477 A CS522477 A CS 522477A CS 195993 B1 CS195993 B1 CS 195993B1
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- ceramic
- sodium
- hardening
- agent
- frost resistance
- Prior art date
Description
Vynález se týká prostředku pro zpevnění a mrazuvzdornost keramického a dřevěného materiálu a řeéí zvýšení jejich statických a dynamických pevností se současným získáním mrazuvzdornosti. Jde o keramické a dřevěné materiály a výrobky vystavené účinkům namáhání a celoroční povětrnoati. Dosud známé prostředky jsou jednoúčelové, buč uvedené materiály pouze zpevňují nebo čelí účinkům dešťů a mrazů impregnací chemickými roztoky a izolačními nátěry. Soudobé zkušenosti ukazují, že tyto prostředky nesplňují své poslání. Dochází k rozpadání střešních krytin již během prvního přezimování, dřevěné výrobky vystavené mokru a mrazu při namáhání praskají a lámou se za snížené pevnosti, jako například hokejové hole, lyže, sáně apod.BACKGROUND OF THE INVENTION The present invention relates to a means for strengthening and frost resistance of ceramic and wood materials and to improving their static and dynamic strengths while at the same time obtaining frost resistance. These are ceramic and wood materials and products exposed to stress and year-round weather. The prior art compositions are single-purpose, either reinforcing or facing the effects of rain and frost by impregnation with chemical solutions and insulating coatings. Current experience has shown that these funds do not fulfill their mission. The roof coverings break down during the first hibernation, wood products exposed to wet and frost burst under stress and break at reduced strength, such as hockey sticks, skis, sleds, etc.
Uvedené nedostatky odstraňuje prostředek pro zpevnění a mrazuvzdornost keramického a dřevěného materiálu podle vynálezu, jehož podstata spočívá v tom, že je směsí vodních roztoků vodního skla sodného NagSiO^ nebo draselného KgSiO^ s hustotou od 15° do 30° Bé a silikonové hydrofobizační látky, například methylsilanolátu sodného/(CHjSiCOHgO.)^ Na s hustotou od 20° do 35° Bé v mísícím poměru 1,5 až 5 % roztoku silikonové hydrofobizační látky v celkovém obsahu roztoku vodního skla, do které jako lázně, ae keramický nebo dřevěný materiál vloží nebo se opatří jejími nátěry, případně postřiky. Účinky infuze,difúze, případně i hydrostatického tlaku proniká prostředek podle vynálezu vrstvami keramického nebo dřevěného materiálu. Působení vodního skla sodného NagSiOj, případně draselnéhoThe above-mentioned drawbacks are eliminated by the solidification and frost-resistance of the ceramic and wood-based material according to the invention, which consists of a mixture of aqueous water glass solutions of sodium NagSiO4 or potassium KgSiO4 with a density of 15 ° to 30 ° Be. sodium methylsilanolate / (CH3SiCOHgO.) ^ Na having a density of from 20 ° to 35 ° B in a mixing ratio of a 1.5 to 5% solution of silicone hydrophobizing agent in the total water glass solution content into which the ceramic or wood material is placed; shall be coated or sprayed. The effects of infusion, diffusion and possibly hydrostatic pressure penetrate the composition according to the invention through layers of ceramic or wood material. Influence of water glass of sodium NagSiOj or potassium
195 993195 993
195 993195 993
KgSiOj, spočívá v tom, že jejich zásaditý roztok reaguje se vzdušným kysličníkem uhličitým CO2 za uvolnění polymerní kyseliny křemičité SiO2 dle rovnice tKgSiOj is that their basic solution reacts with airborne carbon dioxide CO 2 to liberate polymeric silica SiO 2 according to equation t
Na2SiOj + C02 —!* Si02 + Na2CO3, případně k2 sío3 + co2—► sío2 ♦ k2co3, přičemž kyselina křemičitá SiO2 vytváří kostru a utěsňuje póry keramického a dřevěného materiálu. Produkovaný uhličitan sodný Na2CO3, případně draselný KgCOp nemají při použití uvedeného zředění roztoku Škodlivý vliv na materiál. Podobně reaguje se vzdušným kysličníkem uhličitým C02 methyleilanolát sodný [cH3Si(OH)2oJ Na za tvorby methylpolysiloxanolu CHjSí(OH)3, který je ve vodě nerozpustný a silně bydrofobní :Na 2 SiO 2 + CO 2 -! * SiO 2 + Na 2 CO 3 , optionally k 2 sieve 3 + co 2 —► sieve 2 ♦ k 2 co 3 , the SiO 2 forming the skeleton and sealing the pores of the ceramic and wood material. The produced sodium carbonate Na 2 CO 3 or potassium KgCOp does not have a detrimental effect on the material when using the above dilution solution. Similarly, it reacts with carbon dioxide CO 2 sodium methyleilanolate sodium [cH 3 Si (OH) 2 O Na to form methyl polysiloxanol CH 3 Si (OH) 3 , which is insoluble in water and strongly bydrophobic:
[ÓH3Si(OH)2oJ Na + C02 —» CH3Si(OH)3 + Na2CO3 a dále ch3sí(oh)3 —* [ca3sioljJ χ y h2o.[OH 3 Si (OH) 2 oJ Na + CO 2 -> CH 3 Si (OH) 3 + Na 2 CO 3 and ch 3 Si (oh) 3 - * [ca 3 sio lj J χ yh 2 o.
K této reakci dochází v pórech keramického a dřevěného materiálu, která byly prostředkem podle vynálezu napuštěny, za velmi pevné vazby mezi organokřemičitým polymerem a hydrofilním povrchem pórů napuštěného materiálu, poněvadž se předpokládá vazba Si-O-Si, resp. Si-O-Me, tedy přes kyslíkový můstek. Tudíž celkovým výsledkem chemických pochodů, vyvolaných použitím prostředku podle vynálezu, je současná zpevněni a vytvoření mrazuvzdomosti uzavřením a hydrofobizací obsahu pórů materiálů proti nasáklivosti vodou, při zachování průdušnosti, nebol bydrofobní povlaky pórů jsou průchodné pro páry, tudíž pouze jedním prostředkem podle vynálezu, což je jeho nový účinek. Vyšší kvantita účinku je dána uvedenou velmi silnou vazbou mezi organokřemičitým polymerem a hydrofilnlm povrchem pórů keramického a dřevěného materiálu, prokázanou výsledky zkoušek v Technickém a zkušebním ústavu stavebním.This reaction occurs in the pores of the ceramic and wood material impregnated with the composition according to the invention, with a very strong bond between the organosilicon polymer and the hydrophilic surface of the pores of the impregnated material, since the Si-O-Si or Si-O-Si bond is assumed. Si-O-Me, through the oxygen bridge. Thus, the overall result of the chemical processes induced by the composition of the invention is the simultaneous solidification and frost-resistance by closing and hydrophobising the pore content of the materials against water absorption, while maintaining air permeability since the pore coatings are permeable to vapors. its new effect. The higher quantity of effect is given by said very strong bond between the organosilicon polymer and the hydrophilic pore surface of the ceramic and wood material, as evidenced by the results of tests at the Technical and Testing Institute of Building.
Příklady užití vynálezu:Examples of application of the invention:
1. Střešní keramické tašky se narovnají nastojato v nádobě, která se naplní do výše1. Roof ceramic tiles are straightened upright in a container that is filled up
3-4 cm nad jejich horní okraj prostředkem podle vynálezu složeným z 98 % vodního skla sodného Na2SiO3 s hustotou 20° Bé a 2 % methylsilanolátu sodného CH3Si(OH)2O Na s hustotou 30° Bé. Po uplynutí 20 minut se prostředek podle vynálezu z nádoby vypustí a tašky se osuší a použijí.3-4 cm above their upper edge with a composition of the invention composed of 98% Na 2 SiO 3 water glass with a density of 20 ° Bé and 2% sodium methylsilanolate CH 3 Si (OH) 2 O Na with a density of 30 ° Bé. After 20 minutes, the composition of the invention is drained from the container and the bags are dried and used.
2. Stávající střešní tašková krytina se očistí od prachu a pak se třikrát bohatě natře, např. zednickou štětkou, nebo třikrát bohatě nastříká prostředkem podle vynálezu ve složení jako v příkladu prvním. Opakování nátěru se provede před zaschnutím předcházejícího.2. The existing roof tile is cleaned of dust and then three times richly coated, for example with a masonry brush, or three times richly sprayed with the composition according to the invention as in the first example. Repeat the coating before the previous one has dried.
3. Díly dřevěných konstrukcí, násady, dřevěná sportovní nářadí, jako hokejky, lyže, díly saní apod. se ponoří do lázně prostředku podle vynálezu ve složeni 98,5 % vodního skla sodného Na2SiO3 s hustotou 18° Bé a 1,5 % roztoku methylsilanolátu sodného ^CH3Si(OH)2O~l Na s hustotou 25° Bé. Po výjmutí z lázně se osuší a použijí po vyschnutí.3. Parts of wooden structures, handles, wooden sports equipment such as hockey sticks, skis, sledge parts and the like are immersed in a bath of the composition according to the invention in a composition of 98.5% sodium water Na 2 SiO 3 with a density of 18 ° Bé and 1.5 % of a solution of sodium methylsilanolate-CH 3 Si (OH) 2 O-1N with a density of 25 ° Bé. After removal from the bath, they are dried and used after drying.
19S 9919S 99
Možnost využití vynálezu je široká. V dřevařském průmyslu ke zkvalitnění a k zvýšení doby užívání všech dřevěných výrobků vystavených vlivům povětmosti nebo vlhkosti ve spoje ní s namáháním, jako jsou skříně vagonů a nákladních aut, dřevo na stavbu lodí, díly dřevě ných nezakrytých staveb, dřevěné stožáry, tribuny, rámy oken dveří a vrat. Ve stavebním průmyelu pro úpravy střešních krytin, dřevěných pilot, plotů, štětových stěn, špalíkovýeh dlažeb, dřevěných podlah apod.The scope of the invention is broad. In the timber industry to improve and increase the use time of all timber products exposed to weather or moisture in connection with stress, such as wagons and lorries, shipbuilding timber, exposed wooden parts, wooden poles, grandstands, door window frames and gates. In the construction industry for the treatment of roofing, wooden piles, fences, sheet walls, block paving, wooden floors, etc.
Claims (1)