CO4410418A1 - NEW PRECIPITATED SILICE PREPARATION PROCEDURE AND NEW PRECIPITATED SILICES. - Google Patents
NEW PRECIPITATED SILICE PREPARATION PROCEDURE AND NEW PRECIPITATED SILICES.Info
- Publication number
- CO4410418A1 CO4410418A1 CO94050178A CO94050178A CO4410418A1 CO 4410418 A1 CO4410418 A1 CO 4410418A1 CO 94050178 A CO94050178 A CO 94050178A CO 94050178 A CO94050178 A CO 94050178A CO 4410418 A1 CO4410418 A1 CO 4410418A1
- Authority
- CO
- Colombia
- Prior art keywords
- silice
- precipitated
- silicate
- amount
- sio2
- Prior art date
Abstract
1. PROCEDIMIENTO DE PREPARACION DE SILICE PRECIPI- TADA DEL TIPO QUE COMPRENDE LA REACCION DE UN SI- LICATO DE METAL ALCALINO M CON UN AGENTE ACIDIFI- CANTE POR MEDIO DEL CUAL SE OBTIENE UNA SUSPENSION DE SILICE PRECIPITADO, LUEGO LA SEPARACION Y EL SECADO DE ESTA SUSPENSION, CARACTERIZADO EN QUE SE REALIZA LA PRECIPITACION DE LA MANERA SIGUIENTE: (i) SE FORMA UNA MEDIDA INICIAL QUE CONLLEVA UNA PARTE DE LA CANTIDAD TOTAL DEL SILICATO DE METAL ALCALINO M INVOLUCRADA DENTRO DE LA REACCION, LA CONCENTRACION EN SILICATO (EXPRESADA EN SiO2) DEN- TRO DE DICHA MEDIDA INICIAL SIENDO INFERIOR A 20 g/l, (ii) SE AGREGA EL AGENTE ACIDIFICANTE A LA MEDIDA INICIAL HASTA QUE AL MENOS 5% DE LA CANTIDAD DE M20 PRESENTE DENTRO DE DICHA MEDIDA INICIAL SEA NEUTRALIZADA, (iii) SE AGREGA EL MEDIO REACCIONAL SIMULTANEAMEN- TE EL AGENTE ACIDIFICANTE Y LA CANTIDAD RESTANTE DE SILICATO DE METAL ALCALINO M TAL QUE LA PROPOR- CION CANTIDAD DE SILICATO AGREGADO (EXPRESADO EN SiO2)/CANTIDAD DE SILICE PRESENTE EN LA MEDIDA INICIAL (EXPRESADO EN SiO2) SEA SUPERIOR A 4 Y A LO MAXIMO 100. 19. UN SILICE PRECIPITADO CARACTERIZADO EN QUE ES- TE POSEE: - UNA SUPERFICIE ESPECIFICA CTAB (S*CTAB*) COM- PRENDIDA ENTRE 140 Y 240 m2/g, - UN FACTOR DE DESAGLOMERACION AL ULTRASONIDO (F* D*) SUPERIOR A 11 ml, - UN DIAMETRO MEDIO (PHI 50), DESPUES DE DESAGLO- MERACION AL ULTRASONIDO, INFERIOR A 2,5 mm.1. PRECIPITATED SILICE PREPARATION PROCEDURE OF THE TYPE WHICH INCLUDES THE REACTION OF A METAL ALKALINE M SILICATE WITH AN ACIDIFYING AGENT BY WHICH A SUSPENSION OF PRECIPITATED SILICE IS OBTAINED, THEN THE SEPARATION AND DRYING OF THIS SUSPENSION, CHARACTERIZED IN WHICH PRECIPITATION IS CARRIED OUT AS FOLLOWS: (i) AN INITIAL MEASURE IS FORMED WHICH CONTAINS A PART OF THE TOTAL AMOUNT OF ALKALINE METAL SILICATE INVOLVED WITHIN THE REACTION, THE CONCENTRATION IN SILICATE ( SiO2) WITHIN SUCH INITIAL MEASURE BEING LESS THAN 20 g / l, (ii) THE ACIDIFYING AGENT IS ADDED TO THE INITIAL MEASURE UNTIL AT LEAST 5% OF THE AMOUNT OF M20 PRESENT WITHIN SUCH INITIAL MEASURE IS NEUTRALIZED, ( iii) THE REACTIONAL MEDIA IS ADDED SIMULTANEOUSLY THE ACIDIFYING AGENT AND THE REMAINING AMOUNT OF ALCALINE METAL SILICATE M AS THE PROPORTION AMOUNT OF ADDED SILICATE (EXPRESSED IN SiO2) / AMOUNT OF SILICE PRESENT IN L INITIAL SIZE (EXPRESSED IN SiO2) IS GREATER THAN 4 AND MAXIMUM 100. 19. A PRECIPITATED SILICON CHARACTERIZED IN WHICH IT HAS: - A SPECIFIC SURFACE CTAB (S * CTAB *), INCLUDED BETWEEN 140 AND 240 m2 / g, - A ULTRASOUND BREAKDOWN FACTOR (F * D *) GREATER THAN 11 ml, - A MEDIUM DIAMETER (PHI 50), AFTER BREAKDOWN- ULTRASOUND MERRATION, LESS THAN 2.5 mm.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FR9410046A FR2723581B1 (en) | 1994-08-12 | 1994-08-12 | NEW PROCESS FOR PREPARING PRECIPITATED SILICA |
Publications (1)
Publication Number | Publication Date |
---|---|
CO4410418A1 true CO4410418A1 (en) | 1997-01-09 |
Family
ID=9466329
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CO94050178A CO4410418A1 (en) | 1994-08-12 | 1994-11-02 | NEW PRECIPITATED SILICE PREPARATION PROCEDURE AND NEW PRECIPITATED SILICES. |
Country Status (5)
Country | Link |
---|---|
CO (1) | CO4410418A1 (en) |
FR (1) | FR2723581B1 (en) |
MY (1) | MY115160A (en) |
TW (1) | TW307741B (en) |
ZA (1) | ZA948071B (en) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2928363B1 (en) * | 2008-03-10 | 2012-08-31 | Rhodia Operations | NOVEL PROCESS FOR THE PREPARATION OF PRECIPITED SILICES, PRECIPITED SILITIES WITH SPECIAL MORPHOLOGY, GRANULOMETRY AND POROSITY AND THEIR USES, IN PARTICULAR FOR THE STRENGTHENING OF POLYMERS |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2731326A (en) * | 1951-08-31 | 1956-01-17 | Du Pont | Process of preparing dense amorphous silica aggregates and product |
FR2649089B1 (en) * | 1989-07-03 | 1991-12-13 | Rhone Poulenc Chimie | CONTROLLED POROSITY SILICA AND PROCESS FOR OBTAINING SAME |
FR2678259B1 (en) * | 1991-06-26 | 1993-11-05 | Rhone Poulenc Chimie | NOVEL PRECIPITATED SILICA IN THE FORM OF GRANULES OR POWDERS, METHODS OF SYNTHESIS AND USE FOR REINFORCING ELASTOMERS. |
-
1994
- 1994-08-12 FR FR9410046A patent/FR2723581B1/en not_active Expired - Lifetime
- 1994-10-14 ZA ZA948071A patent/ZA948071B/en unknown
- 1994-11-02 CO CO94050178A patent/CO4410418A1/en unknown
- 1994-11-10 MY MYPI94002989A patent/MY115160A/en unknown
-
1995
- 1995-01-12 TW TW084100244A patent/TW307741B/zh not_active IP Right Cessation
Also Published As
Publication number | Publication date |
---|---|
ZA948071B (en) | 1995-06-06 |
TW307741B (en) | 1997-06-11 |
MY115160A (en) | 2003-04-30 |
FR2723581B1 (en) | 1996-11-08 |
FR2723581A1 (en) | 1996-02-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR9405616A (en) | Process of preparation of precipitated silica, precipitated silica, and use of a silica | |
AR001454A1 (en) | A new procedure for the preparation of precipitated silica which has a very good dispersibility and very satisfactory reinforcing properties. | |
AR001453A1 (en) | New procedure for the preparation of precipitated silica. | |
FI943648A0 (en) | Process for the preparation of silicic acid | |
EA199900001A1 (en) | SILICON DIOXIDE USED IN TOOTH CARE COMPOSITIONS | |
KR950704194A (en) | Precipitated Silica (PRECIPITATED SILICA) | |
HK1054186A1 (en) | High cleaning dentifrice. | |
CA2289105A1 (en) | Improved silica product for use in elastomers | |
BR0200743A (en) | silicic acid by precipitation with constant alkaline content and its use | |
DE69816233D1 (en) | FALLING SILICONE USED AS A REINFORCING FILLER IN ELASTOMERS | |
DK1490301T3 (en) | Nonoscale zinc oxide, process for its preparation and use | |
ATE225161T1 (en) | PRECIPITATED SILICIC ACID WITH IMPROVED PERFORMANCE PROPERTIES IN DENTAL CARE PRODUCTS | |
WO2006010438A3 (en) | Dispersion containing titanium dioxide | |
ATE142987T1 (en) | SILICIC ACIDS | |
AU2001266117A1 (en) | Use of a high structure and dispersible precipitated silica as thickening or texturing agent in toothpaste compositions | |
CO4410418A1 (en) | NEW PRECIPITATED SILICE PREPARATION PROCEDURE AND NEW PRECIPITATED SILICES. | |
WO2004046255A3 (en) | Dispersion, coating composition, and recording medium containing silica mixture | |
AR033172A1 (en) | COMPOSITIONS FOR HAIR TREATMENT | |
CO4410249A1 (en) | NEW PRECIPITATED SILICES AND THEIR PREPARATION PROCEDURE | |
JPS5590560A (en) | Powder metal pigment composition and its manufacture | |
HUP0104911A2 (en) | Liquid tooth cleaning agents | |
JPS55135173A (en) | Manufacture of stable metal powder pigment composition | |
TH35864B (en) | New type of precipitated silica Methods for preparation and use for strengthening elastomers | |
TH65637A3 (en) | Improved dental abrasives | |
TH19080A (en) | New type of precipitated silica Methods for preparation and use for strengthening elastomers |