CN86101965A - Process for making non-radioactive luminous colored glaze - Google Patents
Process for making non-radioactive luminous colored glaze Download PDFInfo
- Publication number
- CN86101965A CN86101965A CN 86101965 CN86101965A CN86101965A CN 86101965 A CN86101965 A CN 86101965A CN 86101965 CN86101965 CN 86101965 CN 86101965 A CN86101965 A CN 86101965A CN 86101965 A CN86101965 A CN 86101965A
- Authority
- CN
- China
- Prior art keywords
- glaze
- luminous
- night
- ceramic glaze
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is manufacturing technology, performance and the application thereof of non-radioactive luminous colored ceramic glaze.
The low-temperature glaze of forming with regulation with the zinc of mixing rare earth, cadmium or alkaline earth sulfide luminescent powder mixes, and through the luminous ceramic glaze of 700~850 ℃ of manufacturings, is that the photochromic bonded new ceramics of ideal is decorated and the night-mark(ing) material.
The pottery made from luminous glaze, except that having general ceramic glaze performance, still have "dead", send out characteristics such as colorama, brightness height, time of persistence be long.In the dark or send night colored gorgeous photochromicly, twilight sunset keeps being used for industry, daily and craft artistic pottery and porcelain more than two hours after visible light or uviolizing.
Description
The invention relates to the manufacturing technology of "dead" luminous ceramic glaze, characteristic and other application.
The used luminescent powder of the present invention is for mixing rare earth material Er
+++: Ga
+++With with Cu
++(copper) activated sulfide luminescent material stores energy absorption under visible light, uviolizing, stop irradiation after, discharge with the form of light.In the dark or send colorama night, twilight sunset keeps more than two hours.
The used ceramic glaze of the present invention is formed content range:
SiO
240~50% Al
2O
34~5.5%
H
3BO
330~40% CaCO
30.1~0.2%
ZnO 2~3.6% K
2CO
32~3%
Na
2CO
310~15% ZrO
20.05~0.15%
1100~1350 ℃ of material firing temperatures, fusion and the low melting point glaze made, this glaze and the luminescent powder formed noctilucence glaze behind blackening that is mixed, have acid-alkali-corrosive-resisting, wear-resisting wiping, condition of surface is smooth, chemical stability good, luminosity is high, time of persistence is long, "dead", can send redness, orange, lemon yellow, yellowish green orchid is green is characteristics such as colorama.
The colorful noctilucent ceramic glaze that the present invention makes can be used for industrial ceramics, domestic ceramics, architectural pottery and craft artistic pottery and porcelain etc.Can be in the dark after visible light or uviolizing or send night bright and colourful photochromicly, be photochromic bonded china ornament of ideal and sign device.
Embodiment:
The compound method of A, low-temperature glaze
By following ratio of components, take by weighing various raw materials:
SiO
245.53 gram Al
2O
34.65 gram
H
3BO
333.98 gram CaCO
30.14 gram
ZnO 2.94 gram K
2CO
32.39 gram
Na
2CO
313.24 gram ZrO 0.08 gram
To prepare burden and drop in the ball grinder, put on the ball mill ball milling 4~6 hours, take out in pack into bique ware or the crucible, place 1200~1350 ℃ of heating and meltings, and take out to pour in the cold water and scrap sieving for standby after grinding.
B: the manufacture method of noctilucence glaze
Get above-mentioned low-temperature glaze 100 weight parts and luminescent powder 30 weight parts that pass through 180 mesh sieves, mix, water glass melt furnishing paste uses for coating ceramic.
C: the method for cooking of Noctilucent ceramics goods
The uniform luminous glaze slip of modulated is stuck with paste, by the design requirements pattern, be applied to or be printed on the ceramic form surface, behind the oven drying at low temperature, putting into kiln burns till under 700~850 ℃ of temperature, taking-up can form slick luminous glaze layer on ceramic surface, after visible light or uviolizing, in the dark or send colorama night.
Claims (1)
- The present invention is characterised in that used luminescent material is "dead", and mixing rare earth material is Er +++.Ga +++Be 10 of matrix weight -5~10 -7.Gu +++10 -3~10 -5Luminous colour powder.Ceramic glaze compositing range of the present invention is:SiO 240~50% Al 2O 34~5.5%H 3BO 330~40% CaCO 30.1~0.2%ZnO 2~3.6% K 2CO 32~3%Na 2CO 310~15% ZrO 20.05~0.15%1200~1350 ℃ of melt temperatures, prepared glaze maturing temperature is 700~850 ℃, chemical reaction does not take place being lower than 850 ℃ of temperature in glaze and luminescent powder, does not reduce luminescent properties.Luminous glaze is applied to the ceramic batch surface, forms the Vitrea luminous glaze layer of uniform surface after 700~850 ℃ of maturations, constitutes the Noctilucent ceramics goods.