CN2564968Y - Metal smelting furnace - Google Patents
Metal smelting furnace Download PDFInfo
- Publication number
- CN2564968Y CN2564968Y CN 02247553 CN02247553U CN2564968Y CN 2564968 Y CN2564968 Y CN 2564968Y CN 02247553 CN02247553 CN 02247553 CN 02247553 U CN02247553 U CN 02247553U CN 2564968 Y CN2564968 Y CN 2564968Y
- Authority
- CN
- China
- Prior art keywords
- metal
- melting
- mentioned
- molten metal
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to a smelting furnace with a material proportioning apparatus. The utility model is used for smelting metal. The metal smelting furnace can smelt an alloy material A to obtain a continuous smelting furnace of a metal smelted liquid A. The metal smelting furnace has the functions that the metal smelting furnace can smelt more than two kinds of pure metal materials and obtain the metal smelted liquid A. The utility model with the material proportioning function comprises a first apparatus, a second apparatus, a third apparatus and a fourth apparatus, wherein the first apparatus determines the smelted liquid output amount Q#-< Out > of the smelting furnace; the second apparatus sets the input amount Q#-< INA > of the alloy material A to smelt the alloy material to obtain a metal smelted liquid Y#-< A >; the third apparatus figures out the input amount Q#-< INl > of a pure metal material X#-< 1 > of a main raw material in a pure metal material group X#-< n > to smelt the pure metal material in the metal smelted liquid Y#-< A > to obtain a metal smelted liquid Y#-< 1 >; the fourth apparatus figures out the respective input amount Q#-< INm > of at least more than one kind of pure metal material which is added with the raw material to smelt the pure metal material in the metal smelted liquid Y#-< 1 > to obtain the metal smelted liquid A.
Description
Technical field
The smelting furnace that the utility model relates to and is used for Metal Melting, possesses proportioner.In more detail, relate to have can cooperate certain simple metal material obtain with the desirable molten metal of melting standard material gained with the function of the molten metal of forming, except standard material and with standard material roughly with the foundry returns of forming (comprising the old metal material) is can also be with certain simple metal material as raw material and can be with the Metal Melting furnace of any material in these material as the raw material use.
Background technology
All goods all have shape preferably, in order to obtain such shape, can carry out following processing: with fluid pour into mold cured the fluid processing and forming, with viscoid heating make its viscoid processing and forming that reduces cooling curing after viscosity, with powder pack into the mould compression the powder processing and forming, reinforcing makes the solid forming processing of its plastic deformation etc. to solid.Wherein, the melting solid metal becomes fluid, pours the fluid processing and forming that metal pattern solidifies again into and is widely used, as casting or casting die and by known.
Generally the metal charges that use are smelted into the fluid that is called molten metal as raw material with metal charge more in the fluid processing and forming, pour the metal pattern moulding again into.At this moment, require mostly to form by certain standard as the molten metal of raw material.This is because the variation that molten metal is formed may make the flowability of molten metal descend, thereby in the generation defective in shape of processing and forming product, perhaps makes the mechanical performance of processing and forming product not good.
For example, cast the situation of aluminium wheel for example with casting as goods, as the metal charge of raw material, the A356 aluminium alloys that use according to AA Standard more.So-called A356 aluminium alloy, be in Al (aluminium), to contain Si (silicon) 6.5～7.5 quality %, Mg (magnesium) 0.30～0.45 quality %, the alloy below Ti (titanium) the 0.20 quality %, owing to constitute such composition, can give good mechanical performance and the good anti-corrosion of goods that processing and forming obtains, in addition, because castability is good, so realize various designs and requirement attractive in appearance easily, suitable conduct is in the alloy material that the aluminium wheel raw material under the strict behaviour in service is used.
In using the such scope of standard compliant alloy material (standard material) as raw material, can give the desired performance of goods of moulding, be difficult to have problems.
In addition, when for example making goods with casting, in casting process, the part of moulding in the die cavity of article shape molding space, as the ingate moulded products, attaching unnecessary portions and constituting the moulding product, but this unnecessary part is removed before finishing goods, can be used as raw material and utilize again.Perhaps in inspection, regard as underproof goods, become the old metal material, also can be used as raw material and utilize again.Because they and standard material be by roughly the same forming, so can directly constitute raw material, comprise the foundry returns of old metal material by utilization, can cut down raw material cost, seek the reduction of goods cost.
; owing to consider that recently the discharge meeting that suppresses waste material is more favourable to environment; or, wish except above-mentioned foundry returns, the material outside standard material lower cost, that definite composition is arranged to be used as raw material because the person of needs requires further to reduce cost.
For example,, compare as raw material, can seek to make expense of raw materials to reduce quite a few cost with buying standard compliant alloy material if the simple metal material is used as raw material.In more detail, when making aluminium wheel goods, if with high-purity Al as main material replacing above-mentioned A356 aluminium alloy, and with Si, Mg, Ti the melting of preparing burden obtains desirable molten metal as the interpolation raw material, just can further seek cost degradation.
Because various simple metal material are preferably highly purified, so in the simple metal material, the also material that can adopt some to meet certain standard is even if but in this case, usually, also be more cheap because have a standard material of definite composition.If can and then in this simple metal material or standard material, use smear metal, then can further seek cost degradation, refuse is reused simultaneously, is ideal.
Yet in the continuous smelting stove, the main material input amount generally is not certain, owing to can't catch amount by the main material of melting thermal source melting, therefore, the amount of the interpolation raw material that sneak into also is difficult to hold, and the molten metal that the melting of preparing burden also stably obtains definite composition is difficult.Thereby mainly the standard material of typings such as ingot is used as raw material.
In addition, smear metal is meant the smear metal that machined produces, and is easy oxidation, the also poor material of the melting rate of recovery.
But, the batch process smelting furnace can be set, in this batch process smelting furnace with various simple metal material as the raw material melting of preparing burden, can be used as the means that obtain the desirable molten metal suitable with standard material, but because batch process smelting furnace smelting efficiency is poor, during operation in the method for being used loss also many, the disposal cost height, therefore promptly enable to lower raw material cost, also be difficult to obtain the effect that totle drilling cost lowers.Only be the supplier who has replaced standard material, and the result about equally, can not deal with problems.
Summary of the invention
The present invention is exactly the problem in view of above-mentioned prior art, its purpose is, provide a kind of except carrying out the melting as raw material with the standard material and the foundry returns of prior art, can also obtain the molten metal of desired composition with the simple metal material as raw material, through the batching melting, but also can take in simple metal material and standard material by the suitable smear metal of forming as raw material prepare burden the Metal Melting furnace of melting and batching method of smelting.Another object of the present invention is to, can go on foot the forming processing device such as casting device, die casting equipment of operation by this backward, supply with low-cost and stay-in-grade molten metal, thereby can produce the goods such as processing and forming such as for example cast product, die cast product etc. flawless, that mechanical performance is good with lower cost.
On above basis, the structure of continuous smelting stove and the method for smelting of preparing burden have been carried out more detailed further investigation, found that, adopt following means just can reach above-mentioned purpose.
That is, according to the present invention, providing a kind of Metal Melting furnace, it is characterized in that, is the continous way smelting furnace that can molten alloy material A obtains molten metal A, has melting to be included in the simple metal material group X that multiple simple metal material constitutes
nIn the simple metal material more than at least 2 kinds and obtain the batching function of above-mentioned molten metal A.
Preferably, the device with this batching function comprises: obtain smelting furnace and go out liquation amount Q
OUtThe 1st device, set the input amount Q of alloy material A
INA, carry out melting, obtain molten metal Y
AThe 2nd the device, calculate and be included in simple metal material group X
nIn the simple metal material X of main material
1Input amount Q
IN1, at molten metal Y
AIn melting, obtain molten metal Y
1The 3rd device and calculate and be included in by simple metal material group X
nThe simple metal material group X that constitutes of the interpolation raw material more than at least a kind of inscape
mIn the input amount Q of simple metal material more than a kind
INm, at molten metal Y
1In melting, obtain molten metal A the 4th the device.Q
INAAlso can be 0.In addition, Q
IN1And Q
INmAlso can be 0.
In addition, the simple metal material X in device this moment the 3rd
1Input amount Q
IN1Can represent by following formula (1):
Q
IN1＝Q
OUt-Q
INA …… (1)
In addition, be included in the simple metal material group X of the 4th device
mIn the input amount Q of simple metal material more than a kind
INm, in containing of this simple metal material than being P
mWhen (quality %), can represent by following formula (2):
Q
INm＝Q
IN1×P
m/100 …… (2)
In Metal Melting furnace of the present invention, preferably, possesses the simple metal of being included in material group X
mIn the agitating device of simple metal material melting more than a kind.
In addition, at alloy material A and/or be included in simple metal material group X
nIn more than at least 2 kinds in the simple metal material, preferably contain smear metal.And the melting agitating device that possesses this smear metal is necessary to effective melting.
Metal Melting furnace of the present invention is applicable to that main primary raw material is the melting by the molten metal A of any light metal that constitutes of aluminium, zinc, magnesium.Be applicable to that more its main primary raw material is an aluminium, siliceous 4～24 quality %, contain the melting of the molten metal A of magnesium 0.3～0.5 quality %, titaniferous 0.05～0.25 quality %.
Metal Melting furnace of the present invention preferably possesses the composition analysis device of the molten metal A of melting.
In addition, preferably, Metal Melting furnace of the present invention is to possess to obtain molten metal A and melting simple metal material X by molten alloy material A
1Obtain the working chamber of molten metal Y1, can be at molten metal Y
1Middle melting is included in simple metal material group X
mIn simple metal material more than a kind obtain molten metal A moist closet and can be with alloy material A and simple metal material X
1Pack into the tower smelting furnace of tower shape introduction part of working chamber, the radiator structure of working chamber and/or moist closet makes used heat discharge through tower shape introduction part, by this can preheating alloy material A or simple metal material X
1
In addition, in Metal Melting furnace of the present invention, can roughly use as raw material with alloy material A with the foundry returns of forming, or with alloy material A and usefulness, with replace alloy material A.
In the present invention, preferably, possess and to drop into machine for typing raw material and at least 2 kinds of corresponding respectively raw materials of indefinite form raw material.
In addition, according to the present invention, a kind of batching method of smelting is provided, it is to use smelting furnace, molten alloy material A and/or be included in simple metal material more than at least 2 kinds among the simple metal material group Xn that is made of multiple simple metal material, obtain the batching method of smelting of molten metal A is characterized in that, comprises with the operation of coming off duty, that is, obtain smelting furnace and go out liquation amount Q
OUtThe 1st operation, set the input amount Q of alloy material A
INA, carry out melting, obtain molten metal Y
AThe 2nd operation, calculate and be included in simple metal material group X
nIn the simple metal material X of main primary raw material
1Input amount Q
IN1, at molten metal Y
AIn melting, obtain molten metal Y
1The 3rd operation and calculating be included in by simple metal material group X
nThe simple metal material group X that constitutes of the interpolation raw material more than at least a kind of inscape
mIn the input amount Q of simple metal material more than a kind
INm, at molten metal Y
1In melting, obtain the 4th operation of molten metal A.
In batching method of smelting of the present invention, the simple metal material X in the 3rd operation
1Input amount Q
IN1Can be by Q
IN1=Q
OUt-Q
INAExpression in addition, is included in simple metal material group X in the 4th operation
mIn the input amount Q of simple metal material more than a kind
INm, in containing of this simple metal material than being P
mWhen (quality %), can be by Q
INm=Q
IN1* P
m/ 100 expressions.
In batching method of smelting of the present invention, be preferably included in after the 4th operation, carry out the 5th operation of the composition analysis of molten metal A.
Description of drawings
Fig. 1 is the figure of an embodiment of expression Metal Melting furnace of the present invention, is the horizontal sectional drawing of smelting furnace body.
Fig. 2 is the figure of an embodiment of expression Metal Melting furnace of the present invention, is the vertical cross section of the BB section of expression smelting furnace body shown in Figure 1.
Fig. 3 is the figure of an embodiment of expression Metal Melting furnace of the present invention, is the vertical cross section of the AA section of expression smelting furnace body shown in Figure 1.
Fig. 4 is the block flow diagram of expression with metallic article manufacturing process one example of the casting that comprises Metal Melting furnace of the present invention
Fig. 5 is the block flow diagram of expression Metal Melting furnace general structure one example of the present invention.
The specific embodiment
Below, for Metal Melting furnace of the present invention and batching method of smelting, specify its embodiment, but explanation of the present invention is not limited to these, in the limit that does not exceed scope of the present invention, can apply all changes, correction, improvement based on those skilled in the art's knowledge.
For example, in this manual, it is the typical example of alloy material A that aluminium alloy material A356 is got as standard material, has disclosed Al, the Si, Mg, the Ti conduct that constitute this A356 and has been included in the simple metal material group X that is made of multiple simple metal material
nIn an example of the simple metal material more than at least 2 kinds, will be included in simple metal material group X
nIn the simple metal material X of primary raw material
1Be recited as Al, being included in the inscape of simple metal material group by adding the simple metal material group X that raw material constitutes
mIn simple metal material more than a kind be recited as Si, Mg, Ti, but the present invention fundamentally is being the continous way smelting furnace that can the molten alloy material obtains molten metal, relates to possess the batching function, can the certain simple metal material of melting obtain the Metal Melting furnace and the batching method of smelting of desirable molten metal; Certainly, as the metal of standard material, also can be the aluminium alloy beyond the A356 alloy, or the alloy of titanium or magnesium, zinc etc. for example of other light metal beyond the aluminium alloy, do not limit.Also can select the simple metal material and make it be combined as the composition of alloy, do not limited.
Metal Melting furnace of the present invention, be not only can melting meet the alloy material of certain standard and also be can with the simple metal material as raw material prepare burden melting, obtain the molten metal of desired composition and supply with the general casting device of back step operation or the smelting furnace of forming processing device such as die casting equipment.Metal Melting furnace of the present invention will be with lower device as main constituent apparatus: pack into standard material or foundry returns or simple metal material are at interior main material and the working chamber that carries out melting, molten metal that obtains in the insulation working chamber and the moist closet that adds raw material or smear metal by necessary melting.
In addition, in this manual, the simple metal material refers to the metal of total impurities below certain proportion.And when concentrating the talk of standard material, only refer to the alloy material that in advance multiple metal is cooperated with certain proportion.
Metal Melting furnace of the present invention has following feature: be the continous way smelting furnace on the one hand, possess by for example simple metal material more than 2 kinds on the one hand, obtain being equivalent to the batching function of molten metal of the composition of the resulting molten metal of the desirable alloy material of melting.Also has following feature in addition: can mix and carry out the melting of alloy material and the melting of simple metal material more than 2 kinds with existing.Owing to possess this feature, can seek the further reduction of raw material cost, can not only give the metallic article made through Metal Melting furnace of the present invention with cost competitiveness, and so long as become to distinguish one from the other, just effectively utilize waste materials such as for example smear metal easily, can lower the chance that waste material is discharged and placed, prevent ecological deterioration.
Below with reference to the accompanying drawings Metal Melting furnace of the present invention is elaborated.
Metal Melting furnace of the present invention is the device that is arranged in initial stage in the manufacturing process of the metallic article casting of finishing Metal Melting, pureization, insulation, mould molding operation, comprises the Metal Melting processing use of batching.
Fig. 5 is the block flow diagram of expression Metal Melting furnace general structure one example of the present invention.As shown in Figure 5, Metal Melting furnace 11, preferably by smelting furnace body 10, the composition analysis device 20 of 4 subsidiary system's raw material dispensers and the molten metal 3 that goes out molten metal constitutes.And 4 system's raw material dispensers add raw material dispenser 33 and smear metal raw material dispenser 34 formations preferably by 2 kinds of main material dispensers 31,32.
At first the raw material dispenser is described.
So-called typing material 25 is the material bodies that for example bar-shaped ingot one-piece unit become definite shape, should be the alloy material 8 that is suitable for certain standard usually, or as the simple metal material 1 of the main material that is used to prepare burden.
The shape of main material does not limit, can drop into and check underproof goods, that is, and when old metal material 6 or casting outside the goods die cavity moulding and the foundry returns 2 such as no materials 5 in cutting operation, removed.The indefinite form of non-ingot body but be fit to the alloy material 8 of certain standard or as the simple metal material 1 of the main material of batching usefulness, also can be with in these main material dispenser 32 input smelting furnace bodies 10.
Adding raw material dispenser 33 and possess hopper 64 and doser 65, is the equipment that trace meter material 9 is dropped into smelting furnace body 10.The standby in hopper 64 of a certain amount of trace meter material 9 by the necessary amount of doser 65 meterings corresponding to main material, adds the teeter chamber 53 of smelting furnace body 10.The mode of hopper 64 and doser 65 does not limit.For example, can adopt shape at the bottom of the mortar the handstand cone, be equipped in the hopper 64 vibra feeder feed of bottom peristome, or in container, possess force cell, in feed, subtract calculation up to set amount, the doser 65 that can measure and drop into a constant volume.
Trace meter material 9, the small pieces or the fritter of normally different with main material simple metal material 12 for example are in main material during with simple metal material 1, for making molten metal that melting obtains by the desirable material that adds its necessary amount of forming.
Smear metal raw material dispenser 34 possesses hopper 66 and doser 67, is the equipment that smear metal 4 is dropped into smelting furnace body 10.A certain amount of smear metal 4 standby in hopper 66 by doser 67 metering input amounts, adds the teeter chamber 54 of smelting furnace body 10.The mode of hopper 66 and doser 67 etc. does not limit, and can adopt the mode same with above-mentioned hopper 64 and doser 65.
Smear metal 4 is mach smear metals, usually should be with the alloy material that is suitable for certain standard.Though obtainable amount is limited, if use, then can reduce spillage of material, raw material cost is greatly cut down.
In Metal Melting furnace 11 of the present invention, possess above-mentioned 4 system's raw material dispensers 31～34, can distinguish independently operation arbitrarily.Thereby, for a Metal Melting furnace 11, as long as it is same that the raw material that is dropped into simultaneously by main material dispenser 31,32 is formed, just can implement individually or simultaneously with the general melting of the alloy material 8 that is fit to certain standard as raw material, with certain simple metal material more than 2 kinds 1,12 as the batching melting of raw material with the melting of smear metal as raw material.
That is to say, can be with all material such as typing such as ingot alloy material 8, indefinite form foundry returns 2, smear metals 4, though shape as the raw material input, can be with the shape of the corresponding raw material of optimum means.Because can be by 4 system's raw material dispensers 31～34 simultaneously to smelting furnace body 10 base feeds, so can carry out the batching melting of main material, interpolation raw material, at this moment, even at main material or add in any of raw material and contain smear metal 4, the melting of also can preparing burden.In addition, moved the main material dispenser at the same time at 31,32 o'clock, the composition of the preferred main material that drops into is same.The composition of the main material that moves main material dispenser 31,32 simultaneously but drop into must be provided with metering device not simultaneously in addition, obtains the input amount of each main material.
Then, except Fig. 5,, the smelting furnace body is described also with reference to Fig. 1～Fig. 3.
Fig. 1 is the figure of an embodiment of expression Metal Melting furnace of the present invention, is the horizontal sectional drawing of smelting furnace body 10.In addition, Fig. 2 is the vertical cross section of the BB section of expression smelting furnace body 10 shown in Figure 1, and Fig. 3 is the vertical cross section of the AA section of expression smelting furnace body 10 shown in Figure 1.
Smelting furnace body 10 connects the working chamber 51 of tower shape introduction part 55 by tower shape introduction part 55, and connects moist closet 52 formations of working chamber 51.In moist closet 52, in order to promote the melting of trace meter 9 and smear metal 4, prevent that melting is bad, teeter chamber 53,54 preferably is set.
If by tower shape introduction part 55 input typing raw materials 25 or indefinite form raw material 26 is main material, then by the melting thermal source, for example in working chamber 51, carry out melting by melting burner 71 shown in Figure 2, for example flow into moist closet again because of gravity, mix with the trace meter material 9 of pressing necessity 53 interpolation raw materials that drop into or with the smear metal 4 of 54 main materials that drop into or conduct interpolation raw material, obtain desirable molten metal 3 through the teeter chamber through the teeter chamber.Molten metal 3 by being incubated thermal source, for example keeping certain temperature by insulation burner shown in Figure 3 72, behind the delay certain hour, is emitted liquation to going on foot operation down by the liquation mouth 56 that goes out shown in Figure 1 in moist closet 52.
Shape, the size of tower shape introduction part 55 and working chamber 51 do not limit, but preferably, its structure wants successively main material to be dropped into tower shape introduction part 55, in working chamber 51 by the melting of melting thermal source.In Fig. 2 and example shown in Figure 3, as main material, for example the typing material 25 of the ingot of component alloy material 8 is deposited in working chamber 51 and the tower shape introduction part 55.Main material by near the bottom of the melting burner 71 of melting thermal source by melting, flow into moist closet 52.Like this, make tower shape introduction part 55 and working chamber 51 integrated, tower shape introduction part 55 is preferably made more elongated tower shape so long as can receive the main material of maximum profile.This is can more effectively reclaim used heat because the preheating zone of material increases.Thereby can do the area that is provided with of Metal Melting furnace 11 less.
In addition, in tower shape introduction part 55, photo switch etc. is set preferably, so that the main material amount that can perception drops into, thereby the charge level that material is filled can be held.If the main material amount is few, then preferably can drop into alloy material 8 etc. automatically by main material dispenser 31,32.
In addition, preferably establish exhaust outlet 57 on the top of tower shape introduction part 55.This is because the used heat of working chamber 51 and moist closet 52 is also discharged through tower shape introduction part 55, and this used heat is treated sequential scheduling in the tower shape introduction part 55 the main material preheating of melting the hot generating capacity of the needed melting thermal source of melting to be reduced, and can manifest more energy-conservation effect.By tower shape introduction part 55 is made big capacity, with the capacity adaptation of moist closet 52, play the effect of buffering, even if go out the liquation amount change is arranged, also can make the main material input amount more balanced.
The size of moist closet 52 does not limit, but because the molten metal of working chamber's melting is lower than the melt temperature of moist closet, the liquation of moist closet causes the liquation face to change repeatedly because of going out liquation repeatedly again, so must be the capacity that can keep the appropriateness of holding temperature in the shortest time.In addition, the shape of moist closet does not limit, but its structure optimization bottom surface is roughly the plane, the side is a vertical plane, and make horizontal profile as far as possible be shaped as simple shape such as quadrangle.This be because, as long as the depth direction basal area is roughly constant, the area of liquation liquid level is known, then by the change of liquid level in the liquid level meter instrumentation moist closet 52 is installed in moist closet 52, just can be poor by the change of liquid level area * liquid level, easily calculate out the liquation amount.Because molten metal and liquation face top all are high temperature, so the liquid level meter preferably adopts the non-contact type that is made of laser sensor etc.
Melting thermal source and insulation thermal source are not limited to burner, and for example also can use resistance, electric induction, electric arc etc. electric in the melting thermal source is thermal source, perhaps the heating means of Department of Electronics such as laser, electron beam.
In addition, in the insulation thermal source, also can use heater.At this moment, because can be to the molten metal direct heat transfer, higher in order to make efficient, the preferred use flooded heater.
In addition, the fuel that produces heat does not limit yet, no matter be liquid, solid, gas.Use any fuel or any thermal source, be not with for example alloy material 8 direct meltings of normal temperature main material, but preferably utilize used heat to carry out preheating as mentioned above, reduce manufacturing cost so that do one's utmost to suppress heat loss, therefore preferable.
In teeter chamber 53,54, possesses agitating device respectively.In teeter chamber 53, stir the speed of melting that can improve the trace meter material 9 that drops into, thereby the early stage of composition that can realize out the liquation 3 of liquation stablized.In addition, in teeter chamber 54, stir and can quicken smear metal is involved in the molten metal, one side prevents oxidational losses, and one side can promote the melting of smear metal 4.
The agitating device that is arranged in the teeter chamber 53,54 does not limit, but in order to prevent the oxidation of molten metal 3, preferably mix with the inert blowing gas gas mixing, perhaps as shown in Figure 1, the agitator 73,74 that the installation of 53,54 approximate centre position for example has the motor of slender lobule wheel to drive in the teeter chamber turns round stirring.Perhaps preferably be involved in mechanism with the contour speed of electromagnetic induction.
Following with reference to Fig. 5, the composition analysis device is described.
Adopt composition analysis device 20, the molten metal 3 after the melting of can preparing burden reaches the composition analysis of the molten metal 3 of being emitted by moist closet 52.For carrying out quality management, preferably composition analysis device 20 is provided in after the moist closet 52 and with molten metal deliver to down go on foot before the operation between.For example,, obtain the ratio that constitutes metal components, just can monitor whether mensuration molten metal 3 is defective in quality in going out before the liquation mouth 56 of moist closet 52 to molten metal 3 samplings.If there is problem just to give the alarm, stop to emit molten metal 3, and then preferably, before becoming problem, in moist closet 52, only drop into the simple metal material or the trace meter material as main material of necessary amount, regulate making it reach desirable component ratio automatically again.
As long as possessed the composition analysis device, emitted the quality monitoring of liquation 3, just can not only be with the alloy material 8 of definite composition and simple metal material 1,12 as raw material, and be easy to smear metal material such as so-called old metal material 6 that other factory is produced and no materials 5 and recycle as raw material.Much less, should preferably investigate the generation source of old metal material 6 and no materials 5 this moment, with clear and definite original material category, even but the material that supposition is not contemplated to sneak into, also can prevent the molten metal 3 quality instability that becomes by composition analysis device 20.As composition analysis device 20, for example can use spectral analysis device.
One example of the metallic article manufacturing process that comprises Metal Melting furnace 11 of the present invention then, is described.
Fig. 4 is the block flow diagram of expression with metallic article manufacturing process one example of casting, and Metal Melting furnace 11 is arranged on the initial period of manufacturing process.Manufacturing process 41 shown in Figure 4, except Metal Melting furnace 11, at least also possess: the temperature of the molten metal 3 that maintenance Metal Melting furnace obtains and the holding furnace 13 that stores, molten metal 3 is carried out the casting device 14 of processing and forming with casting, remove the shear 18 of the nonuseable part that does not constitute casting product goods and make the annealing device 19 of the mechanical performance raising of goods.In addition, preferably also have the preceding goods of confirming to dispatch from the factory flawless testing fixture 21 is arranged.
Be close to holding furnace 13 after the Metal Melting furnace 11, possess heater usually, molten metal 3 is incubated, up to giving casting device 14.
Casting device 14 is that molten metal 3 is injected casting mold, obtains the device of the product of casting after solidifying.In casting device 14, can boost productivity owing to finish solidifying of molten metal 3 as early as possible, so in casting mold, use the higher material of pyroconductivity.
Resulting casting product generally are separated into prefabrication and no materials 5 with shear after cooling.Apply heat treatment with 19 pairs of prefabrications of annealing device then,, become final metallic article 7 to seek the raising of mechanical property.The no materials 5 that separated by shear 18 return Metal Melting furnace 11, are re-used as prepared using.In addition, final metallic article 7 is found defective in testing fixture 21, also returns Metal Melting furnace 11 as old metal material 6, is re-used as prepared using.Though not shown but certain is that the no materials and the old metal material that produce beyond shear 18 and testing fixture 21 also can be received by Metal Melting furnace 11, are re-used as raw material and use.
Below, illustrate and use all method of smelting Metal Melting furnace of the present invention, that comprise batching.
Use the Metal Melting furnace 11 of general structure shown in Figure 5, for example make it and consist of and contain Si7 quality %, Mg0.4 quality %, the aluminium wheel of the Al alloy of Ti0.15 quality % (quite A356 aluminium alloy).Wherein, establish the liquid level meter in the moist closet 52 of Metal Melting furnace 11, the instrumentation liquid level can detect liquid level H (high position) and liquid level L (low level) at least continuously.The section configuration of moist closet 52 depth directions is certain, and the liquid level area is known.
At this moment, for example can be as follows for the raw material that 4 systems' raw material dispensers of Metal Melting furnace 11 are operated.
Can drop into the main material dispenser 31 of typing material 25, with A356 alloy pig, pure Al ingot as operand.Can drop into the main material dispenser 32 of indefinite moulding mixture 26, take turns defective work (old metal material 6) as operand with aluminium.Also can operate no materials 5 or non-ingot A356 alloy, pure Al metal, but in this example its row be done outside the object.In addition, add raw material dispenser 33, with as the pure Si slug of the trace meter material 9 of simple metal material 12, pure Mg slug, pure Ti slug as operand.Smear metal raw material dispenser 34, with the A356 alloy smear metal of smear metal 4, pure Si smear metal, pure Mg smear metal, pure Ti smear metal as operand.
First kind of situation below is described.
Drop into the A356 alloy pig by main material dispenser 31 and carry out melting as raw material.Without other raw material.Handle equally with general continous way smelting furnace.
Also can be not to going out liquation amount Q
OUtManage.Do not depend on liquation amount Q
Out, in moist closet 52, one side finishes instrumentation liquid level H with the liquid level meter, and one side is with 71 igniting of melting burner, and the melting of beginning A356 alloy pig in case the liquid level meter detects liquid level H, just stops melting burner 71.Repeat aforesaid operations, melt raw material obtains molten metal 3, emits liquation.
Second kind of situation below is described.
Drop into the A356 alloy pig by main material dispenser 31 and carry out melting, drop into the smear metal of A356 alloy by smear metal raw material dispenser 34 and carry out melting as raw material as raw material.Without other raw material.According to first kind of processing of situation.
Also can be not to going out liquation amount Q
OUtManage.Do not depend on liquation amount Q
Out, in moist closet 52, one side finishes instrumentation liquid level H with the liquid level meter, and one side is with 71 igniting of melting burner, and the melting of beginning A356 alloy pig in case the liquid level meter detects liquid level H, just stops melting burner 71.Repeat aforesaid operations, melt raw material obtains molten metal 3, emits liquation.In addition, when the liquid level of moist closet 52 is discontented with liquid level H, A356 alloy smear metal input is provided in the teeter chamber 54 of moist closet 52.The smear metal of A356 alloy be trapped in moist closet 52 in by the insulation burner 72 keep high temperature liquation 3 stirrings, mix, melting.Can implement the input of A356 alloy pig and the input of A356 alloy smear metal independently.
The third situation below is described.
Drop into pure Al ingot by main material dispenser 31 and carry out melting as raw material, raw material dispenser 33 drops into pure Mg slug, pure Ti slug carries out melting as raw material by adding, and drops into pure Si slug by smear metal raw material dispenser 34 and carries out melting as raw material.Without other raw material.
Must manage out liquation amount Q
OutTo prepare burden.Go out liquation amount Q
OutObtain with following (3) formula by liquid level area S and liquid level H, L.
Q
OUt＝S×(H-L) …… (3)
In moist closet 52, in a single day the liquid level meter detects liquid level L, just with 71 igniting of melting burner, begins the melting of pure Al ingot.Then, measure pure Si slug, with the input amount Q shown in following (4) formula
INSiDrop in the teeter chamber 53 of moist closet 52 outfits, carry out melting.Wherein contain proportional P
MSi=7 (quality %).
Q
INSi＝Q
OUt×P
mSi/100 ……?(4)
Pure Si slug with keep being in liquation stirring in the moist closet 52, mixing of high temperature, melting by insulation burner 72.The input of pure Si slug preferably follows the rising of the melting complexed metal liquation face height of pure Al ingot to carry out several times.
What carry out side by side is to measure pure Mg slug, pure Ti slug respectively, with the input amount Q shown in following (5), (6) formula difference
INMg, Q
INTiCarry out melting in the teeter chamber 53 that input moist closet 52 is equipped with.Wherein contain proportional P
MMg=0.4 (quality %), P
MTi=0.15 (quality %).
Q
INMg＝Q
OUt×P
mMg/100 ……?(5)
Q
INTi＝Q
OUt×P
mTi/100 ……?(6)
Pure Mg slug, pure Ti slug and keep being in liquation stirring in the moist closet 52, mixing of high temperature, melting by insulation burner 72.The input of pure Mg slug, pure Ti slug preferably follows the rising of the melting complexed metal liquation face height of pure Al ingot to carry out several times.
In a single day the liquid level meter detects liquid level H, just stops melting burner 71.Repeat this operation, make the feed proportioning melting, obtain molten metal 3.If the composition of the molten metal 3 that obtains with composition analysis device 20 inspection no problem, then begins liquation for well.If problem is arranged, suitable way is to give the alarm, only drop into simultaneously the pure Al ingot as main material of necessary amount, or as the pure Si slug, pure Mg slug, the pure Ti slug that add raw material, regulate again automatically, make it reach desirable component ratio.
The 4th kind of situation below is described.
Drop into pure Al ingot by main material dispenser 31 and carry out melting as raw material, carry out melting by the pure Si slug of interpolation raw material dispenser 33 inputs, pure Mg slug, pure Ti slug as raw material, drop into the smear metals of A356 alloy by smear metal raw material dispenser 34 and carry out melting as raw material.Without other raw material.
Must manage out liquation amount Q
OutTo prepare burden.Go out liquation amount Q
OutBy liquid level area S and liquid level, obtain with above-mentioned (3) formula.
In moist closet 52, in a single day the liquid level meter detects liquid level L, just with 71 igniting of melting burner, begins the melting of pure Al ingot.Then measure the smear metal of A356 alloy, drop in the teeter chamber 53 of moist closet 52 outfits, carry out melting.The smear metal of A356 alloy with keep being in liquation stirring in the moist closet 52, mixing of high temperature, melting by insulation burner 72.The input amount of A356 alloy smear metal is taken as Q
INAThe input of A356 alloy smear metal can independently be carried out with the melting of pure Al ingot.If the amount of A356 alloy smear metal surpasses liquation amount Q
OUt, then can adopt following countermeasure, that is, only the smear metal of melting A356 alloy makes it and goes out liquation amount Q
OUtQuite.
Then, obtain the input amount Q of pure Al metal charge by above-mentioned (1) formula
IN1, measure pure Si slug, pure Mg slug, pure Ti slug then respectively, with the input amount Q shown in following (7), (8), (9) formula difference
INsi, Q
INMg, Q
INTiCarry out melting in the teeter chamber 53 that input moist closet 52 is equipped with.
Q
INSi＝Q
IN1×P
mSi/100 …… (7)
Q
INMg＝Q
IN1×P
mMg/100 …… (8)
Q
INTi＝Q
IN1×P
mTi/100 …… (9)
Pure Si slug, pure Mg slug, pure Ti slug and keep being in liquation stirring in the moist closet 52, mixing of high temperature, melting by insulation burner 72.The input of pure Si slug, pure Mg slug, pure Ti slug is preferably followed the melting of pure Al ingot, the smear metal of A356 alloy, and the rising of complexed metal liquation face height is carried out several times.
In a single day the liquid level meter detects liquid level H, just stops melting burner 71.At liquid level is the moment of H, finishes to be fit to the batching of composition, obtains molten metal 3.About the composition analysis of the molten metal 3 of gained and the corresponding situation of analysis result, according to the content of the third situation.
The 5th kind of situation below is described.
Drop into Al wheel defective work by main material dispenser 32 and carry out melting as raw material, carry out melting by the pure Si slug of interpolation raw material dispenser 33 inputs, pure Mg slug, pure Ti slug as raw material, drop into pure Al borings by smear metal raw material dispenser 34 and carry out melting as raw material.Without other raw material.
Preferably manage out liquation amount Q
OutTo prepare burden.Go out liquation amount Q
OutBy liquid level area S and liquid level, obtain with above-mentioned (3) formula.
In moist closet 52, one side finishes liquid level meter instrumentation liquid level H, and one side is with 71 igniting of melting burner, and beginning Al takes turns the melting of defective work.Then measure pure Al borings, drop in the teeter chamber 54 of moist closet 52 outfits, carry out melting.The input amount of pure Al borings is taken as Q
IN1Pure Al borings with keep being in liquation stirring in the moist closet 52, mixing of high temperature, melting by insulation burner 72.The input of pure Al borings can independently be carried out with the melting that aluminium is taken turns defective work.If the amount of aluminium wheel defective work surpasses liquation amount Q
OUt, then can adopt to make following countermeasure, that is, only melting aluminium wheel defective work makes it and goes out liquation amount Q
OUtQuite.
Then, measure pure Si slug, pure Mg slug, pure Ti slug respectively, with the input amount Q shown in above-mentioned (7), (8), (9) formula difference
INsi, Q
INMg, Q
INIiCarry out melting in the teeter chamber 53 that input moist closet 52 is equipped with.
Pure Si slug, pure Mg slug, pure Ti slug and keep being in liquation stirring in the moist closet 52, mixing of high temperature, melting by insulation burner 72.The input of pure Al borings and pure Si slug, pure Mg slug, pure Ti slug is preferably carried out respectively several times.
In a single day the liquid level meter detects liquid level H, just stops melting burner 71.At liquid level is the moment of H, finishes to be fit to the batching of composition, obtains molten metal 3.About the composition analysis of the molten metal 3 of gained and the corresponding situation of analysis result, according to the content of the third situation.
As mentioned above, in a Metal Melting furnace, in order to obtain desirable molten metal, can implement to meet of the general melting of the alloy material of certain standard individually or simultaneously as raw material, with certain simple metal material more than 2 kinds as the batching melting of raw material with the melting of smear metal as raw material.Certainly be not limited to above-mentioned situation first～5th kind of situation.
Below the material that constitutes equipment of the present invention is described.
The temperature of molten metal is for example with the occasion of aluminum series alloy as raw material, owing to be to remain on the high temperature that reaches about 720 ℃, so will give special heed to corrosivity for well.
At the body of heater inner face that contacts with molten metal, preferred typing refractory material or the amorphous refractory etc. of using.The equipment class that is provided with in the Metal Melting furnace for example in burner or the agitator, can be used pottery or graphite etc.Not directly in the raw material dispenser of contacting metal liquation etc., can use iron plate, but preferably be applied with hear resistance, corrosion proof coating.As described above, according to Metal Melting furnace of the present invention and batching method of smelting, obtain the molten metal except carrying out melting as raw material with standard material same as the prior art and foundry returns, can also obtain the liquation of desired composition with the simple metal material as the raw material melting of preparing burden.In addition, even the smear metal that reception, utilization and simple metal material or standard material are quite formed also can obtain the molten metal of desired composition as raw material.
Thereby show following good effect: can cut down raw material cost on the one hand, forming processing devices such as the casting device of step operation, die casting equipment after stay-in-grade molten metal being supplied with on the one hand.
Claims (13)
1. Metal Melting furnace, it is the continous way smelting furnace that molten alloy material A obtains molten metal A, it is characterized in that, has melting to be included in the simple metal material group X that is made of multiple simple metal material
nIn the simple metal material more than at least 2 kinds and obtain the batching function of above-mentioned molten metal.
2. according to the described Metal Melting furnace of claim 1, it is characterized in that the device with above-mentioned batching function comprises:
Obtain smelting furnace and go out liquation amount Q
OUtThe 1st the device,
Set the input amount Q of above-mentioned alloy material A
INACarry out melting, obtain molten metal Y
AThe 2nd the device,
Calculate and be included in above-mentioned simple metal material group X
nIn the simple metal material X of main material
1Input amount Q
IN1, at above-mentioned molten metal Y
AMiddle melting obtains molten metal Y
1The 3rd the device and
Calculate and be included in by above-mentioned simple metal material group X
nThe simple metal material group X that constitutes of the interpolation raw material more than at least a kind of inscape
mIn the input amount Q of simple metal material more than a kind
INm, at molten metal Y
1In melting, obtain molten metal A the 4th the device.
3. according to the described Metal Melting furnace of claim 2, it is characterized in that the simple metal material X in above-mentioned the 3rd device
1Input amount Q
IN1Can be expressed from the next.
Q
INI＝Q
Out-Q
INA
4. according to the described Metal Melting furnace of claim 3, it is characterized in that, be included in simple metal material group X in above-mentioned the 4th device
mIn the input amount Q of simple metal material more than a kind
INm, in containing of this simple metal material than being P
mThe time, can be expressed from the next.
Q
INm＝Q
INI×P
m/100
5. according to claim 1 or 2 described Metal Melting furnaces, it is characterized in that possessing and be included in above-mentioned simple metal material group X
mIn the agitating device of the melting of simple metal material more than a kind.
6. according to claim 1 or 2 described Metal Melting furnaces, it is characterized in that, at above-mentioned alloy material A and/or be included in above-mentioned simple metal material group X
nIn more than at least 2 kinds in the simple metal material, comprise smear metal.
7. according to the described Metal Melting furnace of claim 6, it is characterized in that possessing the agitating device of the melting of above-mentioned smear metal.
8. according to the described Metal Melting furnace of claim 1, it is characterized in that the principal component of above-mentioned molten metal is by any light metal that constitutes in aluminium, zinc, the magnesium.
9. according to each described Metal Melting furnace in the claim 1～8, it is characterized in that above-mentioned its principal component of molten metal A is an aluminium, contain silicon 4～24 quality %, magnesium 0.3～0.5 quality %, titanium 0.05～0.25 quality %.
10. according to each described Metal Melting furnace in the claim 1～9, it is characterized in that possessing the composition analysis device of above-mentioned molten metal A.
11., it is characterized in that, be to possess to obtain molten metal A and the above-mentioned simple metal material of melting X by the above-mentioned alloy material A of melting according to each described Metal Melting furnace in the claim 2～10
1Obtain molten metal Y
1The working chamber, can be at molten metal Y
1Middle melting is included in simple metal material group X
mIn simple metal material more than a kind obtain above-mentioned molten metal A moist closet and can be with above-mentioned alloy material A and above-mentioned simple metal material X
1Pack into the tower smelting furnace of tower shape introduction part of above-mentioned working chamber,
The used heat of above-mentioned working chamber and/or above-mentioned moist closet constitutes like that according to discharging through tower shape introduction part, by this can above-mentioned alloy material A of preheating or above-mentioned simple metal material X
1
12., it is characterized in that, will roughly use as raw material with above-mentioned alloy material, in order to replace above-mentioned alloy material A or also to use with above-mentioned alloy material A with the foundry returns of forming according to each described Metal Melting furnace in the claim 1～11.
13., it is characterized in that possessing 2 kinds of raw materials input machines that typing raw material and indefinite form raw material are used at least according to each described Metal Melting furnace in the claim 1～12.