CN2383500Y - Hydrogel composite wound dressing - Google Patents
Hydrogel composite wound dressing Download PDFInfo
- Publication number
- CN2383500Y CN2383500Y CN 99217930 CN99217930U CN2383500Y CN 2383500 Y CN2383500 Y CN 2383500Y CN 99217930 CN99217930 CN 99217930 CN 99217930 U CN99217930 U CN 99217930U CN 2383500 Y CN2383500 Y CN 2383500Y
- Authority
- CN
- China
- Prior art keywords
- layer
- hydrogel
- hydrogel layer
- film
- gas permeable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model relates to a hydrogel composite wound dressing. One side of a hydrogel layer 2 is covered with a layer of air permeable polymer film 1, and an adhesion layer 3 can be arranged between the hydrogel layer 2 and the air permeable polymer film 1. The other side of the hydrogel layer 2 is covered with a layer of mold release paper 5 or a release film 8 coated with silicone 4. The utility model has the advantages of good transparence, high water absorbability, high air permeability, high moisture permeability and no water permeability. The utility model can be used for preventing wound infection and accelerating healing. The utility model is suitable for the protection and the treatment of wound surfaces of burn, scald, bed sore and traumatic wounds. In addition, the utility model can be stored for a long time after radiation sterilization.
Description
This utility model relates to a kind of wound dressing that is applicable to burn, scald, decubital ulcer and traumatic wounds protecting wound surface and treatment, specifically is a kind of hydrogel compounded dressing for wound.
Present hydrogel compounded dressing for wound is composited by several parts such as ventilative continuous film, non-woven fabrics or fabric skeleton, hydrogel, adhesive usually.
CN1044405 discloses and a kind ofly can absorb wound fluid, and can be with water transport to airborne binder.This binder be by thin film such as polyester, polyethylene as the protection backing, pasting one deck on the protection backing is that the hydrogel of skeleton is made with fabric or non-woven fabrics.The base material of hydrogel comprises sodium carboxymethyl cellulose, various polypropylene amine, polyacrylonitrile and acrylate copolymer etc.The shortcoming of this hydrogel is opaque.
CN1095916 discloses a kind of wound dressing that can absorb wound fluid.It forms the sealing top layer by polyurethane film and polymer filament net, absorbed layer is composited by mixture, the polypropylene fibre second layer of polypropylene fibre ground floor, hydrocolloid and superabsorbents, is the polymer base coat made of polyvinylpyrrolidone or polyvinyl alcohol and moisturely separates colloidal adhesive phase with skin directly contacts.This invention weighing-appliance has excellent water absorption, but it is to reach multi-layer compound structure that ideal intensity and water absorption design to have sacrificed and be beneficial to the transparency of observing wound.
CN2292547 discloses a kind of water absorption medical dressing of not sticking wound, and water accepting layer that it is made by the micropore non-woven fabrics that scribbles acrylic compounds water-absorbing resins film and the basic unit made from fabric or breathability non-woven fabrics form.This dressing except that have aforesaid opaque, do not intercept the shortcoming such as antibacterial, also lack ideal performances such as pliability that wound dressing should possess and elasticity, in addition, the residual monomer of acrylic resin usually has skin to stimulate or slight toxic and side effects.
Though existing these aquogel type wound dressings have solved problems such as absorption transudate, breathability, obstruct antibacterial, waterproof, wound comfort level, but for the intensity that increases hydrogel, the cohesive that strengthens hydrogel and waterproof and breathable notacoria, majority has all adopted fabric or non-woven fabrics as enhancement Layer, and has taked the complicated technology of MULTILAYER COMPOSITE.Like this, goods are opaque structure, have influenced the observation of wound healing situation.
The purpose of this utility model is to provide a kind of can absorb transudate, can intercept antibacterial; have transparent, ventilative, waterproof, not with characteristics such as tissue adhesion, pliability be good, be applicable to the hydrogel compounded dressing for wound of burn, scald, decubital ulcer, traumatic wounds protecting wound surface and treatment.
The technical solution of the utility model is as follows:
A kind of hydrogel compounded dressing for wound is the one side covering one deck gas permeable polymers film at hydrogel layer.
Further scheme is to be provided with adhesion layer between hydrogel layer and gas permeable polymers film.
Further the another side of scheme hydrogel layer covers release paper or the stripping film that one deck scribbles silicone.
Wherein, the overall dimensions unanimity of dressing, unified square, rectangle, circle or the elliptical shape of cutting into.
Wherein, the overall dimensions of gas permeable polymers film is consistent with release paper that scribbles silicone or stripping film, greater than the composite bed that all the other each layers constituted, the gas permeable polymers film be not coated with the medical pressure-sensing glue-line by the coated clear area of composite bed, the gas permeable polymers film with scribble the release paper of silicone or stripping film, composite bed can be made square, rectangle, circle or elliptical shape respectively.
Wherein, the thickness of hydrogel layer is 0.5 to 10mm; Preferred thickness is 2 to 4mm.
Wherein, the thickness of gas permeable polymers film is 25 to 100 microns; Preferred thickness is 25 to 50 microns.
Owing to adopt above scheme, the utlity model has good transparency, high-hydroscopicity, breathability, poisture-penetrability, but waterproof, can prevent wound infection, quicken recovery from illness.Be applicable to the protecting wound surface and the treatment of burn, scald, decubital ulcer and traumatic wounds.Pass through radiation sterilization in addition, but long term store.
Below in conjunction with drawings and Examples this utility model is further specified.
Fig. 1 is the sectional structural map of the sectional structural map of the present utility model and first embodiment.
Fig. 2 is the sectional structural map of second embodiment of the present utility model.
Fig. 3 is the sectional structural map of the 3rd embodiment of the present utility model.
Fig. 4 is the sectional structural map of the 4th embodiment of the present utility model.
Fig. 5 is the sectional structural map of the 5th embodiment of the present utility model.
Fig. 6 is the A--A cutaway view of Fig. 5.
Fig. 7 is the sectional structural map of the 6th embodiment of the present utility model.
Fig. 8 is the B--B cutaway view of Fig. 7.
Embodiment 1
In Fig. 1, hydrogel compounded dressing for wound is the one side covering one deck gas permeable polymers film 1 at hydrogel layer 2.1 pair of hydrogel layer 2 of the polymeric film of breathability shields, and under the prerequisite of keeping the skin eupnea, prevents the moisture excessive vaporization of hydrogel, prevents the antibacterial intrusion, has air permeability and good, the transparency, and plays the potentiation of hydrogel.This film is a kind of continuous film of better softness, and material can be chosen from polymer such as polyethylene, polrvinyl chloride, silicone rubber, polyurethane, polyimides.Preferred material is a polyurethane, and its moisture-vapor transmission is greater than 300g/m
224h.The thickness of film is selected 25 to 100 microns; Preferred thickness is 25 to 50 microns.Hydrogel layer 2 has high-hydroscopicity, and water absorption rate is up to 200-400%.The thickness of hydrogel layer is 0.5 to 10mm; Preferred thickness is 2 to 4mm.
As shown in Figure 2, on the basis of embodiment 1, in order to improve the bond properties of hydrogel layer 2 and gas permeable polymers film 1, can carry out surface treatment to gas permeable polymers film 1, at its surface-coated medical adhesive adhesion layer 3, or the adhesion layer 3 that has viscosity in hydrogel layer 2 surface-coated.Adopt one of above-mentioned method or several method to be used in combination, can obtain satisfied bonding force.
Embodiment 3
As shown in Figure 3; on the basis of embodiment 1; in order to protect hydrogel layer 2; the another side of hydrogel layer 2 covers release paper 5 or the stripping film 8 that one deck scribbles silicone 4; release paper 5 relies on silicone 4 and hydrogel layer 2 that certain bonding force is arranged; or stripping film 8 is directly bonding with hydrogel layer 2, is easy to during use take off.Stripping film 8 can be selected polyethylene film, polypropylene screen, polychloroethylene film etc. for use.
See shown in Figure 4ly, on the basis of embodiment 3, between hydrogel layer 2 and gas permeable polymers film 1, be provided with adhesion layer 3.
In above-described embodiment 1 to 4, the overall dimensions unanimity of each of dressing layer, the unified shapes such as square, rectangle, circle or ellipse that cut into.With transparent gas-pervious medical adhesive tape dressing is fixed in the wound during use, can makes it bonding more firm, and keep its waterproof, function such as ventilative.
In following embodiment 5,6, the overall dimensions of gas permeable polymers film 1 is consistent with release paper 5 that scribbles silicone 4 or stripping film 8, but greater than composite bed 6 that all the other each layers constituted.Wherein described in the composite bed 6 expression front embodiment 1 to 4 with gas permeable polymers film 1 bonded two kinds of layer structures, or be hydrogel layer 2, or be the composite bed of adhesion layer 3 and hydrogel layer 2.Be not coated with medical pressure-sensing glue-line 7 at gas permeable polymers film 1 by composite bed 6 coated clear areas.Throw off release paper 5 or the stripping film 8 that scribbles silicone 4 when product uses, directly rely on pressure-sensitive adhesive layer 7 that whole dressing paste is spread on the wound.Gas permeable polymers film 1 and the release paper 5 that scribbles silicone 4 or stripping film 8, composite bed 6 can be made shapes such as square, rectangle, circle or ellipse respectively, but combination in any between each shape.
Fig. 5,6 is depicted as the profile of gas permeable polymers film 1 and release paper 5 that scribbles silicone 4 or stripping film 8 for circular, and composite bed 6 also be the situation of circle.
Fig. 7,8 is depicted as gas permeable polymers film 1 and scribbles the release paper 5 of silicone 4 or the profile of stripping film 8 is square, and composite bed 6 also is quadrate situation.
Remaining combination of shapes does not remake one by one and gives unnecessary details.
Claims (7)
1. hydrogel compounded dressing for wound, it is characterized in that: the one side of gas permeable polymers film (1) covers one deck hydrogel layer (2), the overall dimensions of gas permeable polymers film (1) is greater than the overall dimensions of hydrogel layer (2), the white space that is not covered by hydrogel layer (2) at gas permeable polymers film (1) is coated with medical pressure-sensing glue-line (7), scribbles the release paper (5) or the stripping film (8) of silicone (4) at another side covering one deck of hydrogel layer (2) and medical pressure-sensing glue-line (7).
2. wound dressing according to claim 1 is characterized in that between hydrogel layer (2) and the gas permeable polymers film (1) adhesion layer (3) being arranged, and its overall dimensions is identical with hydrogel layer (2).
3. according to claim 1,2 described wound dressings, the thickness that it is characterized in that hydrogel layer (2) is 0.5 to 10mm, and the thickness of gas permeable polymers film (1) is 25 to 100 microns.
4. a hydrogel compounded dressing for wound is characterized in that the one side of hydrogel layer (2) covers one deck gas permeable polymers film (1).
5. wound dressing according to claim 4 is characterized in that between hydrogel layer (2) and the gas permeable polymers film (1) adhesion layer (3) being arranged.
6. according to claim 4,5 described wound dressings, it is characterized in that the another side of hydrogel layer (2) covers release paper (5) or the stripping film (8) that one deck scribbles silicone (4).
7. wound dressing according to claim 6, the thickness that it is characterized in that hydrogel layer (2) are 0.5 to 10mm, and the thickness of gas permeable polymers film (1) is 25 to 100 microns.