CN2283688Y

CN2283688Y - Building decorative material-colour glass block

Info

Publication number: CN2283688Y
Application number: CN 96209736
Authority: CN
Inventors: 谢林丰
Original assignee: Xie Linxing
Current assignee: Xie Linxing
Priority date: 1996-05-06
Filing date: 1996-05-06
Publication date: 1998-06-10
Anticipated expiration: 2006-05-06

Abstract

The utility model relates to a building decorative material-colour glass block, composed of a colour glass of a surface layer, a porcelain block of a bottom layer and adhesive for adhering the surface layer and the bottom layer together. The building decorative material-colour glass block is firmly combined with the bottom layers of buildings, having beautiful surface and high colour durability.

Description

A kind of building decoration material coloured glass tile

The utility model relates to a kind of building decoration material coloured glass tile.

At present, architecturally make surperficial ornament materials with glass, fastness is relatively poor, and the time one is long, and it is a lot of to come off, and the habitual building with the facing glass decoration, its surface color be through exposing to the weather for a long time, peels off seriously, influences attractive in appearance.

The object of the present invention is to provide a kind of combine with building firm, the coloured glass tile that color is lasting.

A kind of coloured glass tile of the present invention is characterized in that described vitrified brick by surface color glass, bottom porcelain piece and the binding agent that surface layer and bottom are glued together formed.

Described vitrified brick is a color metallized glass, and described plated film face is an adhesive surface.

Described porcelain piece is after soaking 1 hour with 0.5% hydrochloric acid solution, to clean, dry.

Described vitrified brick is to be coated with one deck binding agent on the shiny surface of porcelain piece on the plated film face that sticks on glass under the pressure, puts into temperature after the extruding again and be 100-200 ℃ heat-treatment furnace, and is modified, solidified 1 hour, come out of the stove, continue to solidify the goods after the arrangement 24 hours at 30-40 ℃.

Described color metallized glass specification is all size by building requirements, and its color is as required shades of colour.

But describedly stick on porcelain piece monoblock on the coating film on glass face, also piecemeal, its shape is a different shape as required.

The preferred CH-31 type of described cementing agent cementing agent.Below in conjunction with description of drawings the utility model

Fig. 1 is the rear elevation of the utility model coloured glass tile.The survey view of Fig. 2 coloured glass tile of the present utility model.

Referring to Fig. 1,2, wherein code name 1 is a color metallized glass, the 2nd, the porcelain piece, the 3rd, adhesive, diagram A face is the plated film face of stained glass.

Totally 6 of porcelain pieces shown in Figure 1, can be as required monoblock, also piecemeal is square, rhombus, circular or other shape.

Described color metallized glass specification is all size of building requirements, for example: and dull and stereotyped, cambered surface, square, rhombus, other shape circular or that require according to architectural decoration.Its color is as required shades of colour.

Described cementing agent 3 is CH-31.

Color metallized glass of the present utility model is mainly used in building and ornament materials, and using method is as follows;

1, be put on building surface with 1: 3 cement mortar and do bottom, floating;

2, be put on the vitrified brick back side (with porcelain piece adhesive surface) with 1: 1 cement mortar, thickness 0.5-0.8cm is under pressure, vitrified brick is sticked on building surface, extruding, the slit is the smaller the better, after solidifying 1-2 hour, use pointing with cement mortar again, continue to solidify 24 hours.

3, arrangement, drying is cleaned in scrubbing.

Claims

1, a kind of coloured glass tile is characterized in that described vitrified brick by surface color glass, bottom porcelain piece and the binding agent that surface layer and bottom are glued together formed.

2, according to the vitrified brick of claim 1, it is characterized in that described vitrified brick is a color metallized glass, described plated film face is an adhesive surface.

3, according to the vitrified brick of claim 1, it is characterized in that described porcelain piece is to soak with 0.5% hydrochloric acid solution, clean, dry.

4, vitrified brick according to claim 1, it is characterized in that described vitrified brick is to be coated with one deck binding agent on the shiny surface of porcelain piece on the plated film face that sticks on glass under the pressure, put into temperature after the extruding again and be 100-200 ℃ heat-treatment furnace, modified, solidified 1 hour, come out of the stove, continue to solidify the goods after the arrangement 24 hours at 30-40 ℃.

5, according to the vitrified brick of claim 1-4, it is characterized in that described color metallized glass specification is all size by building requirements, its color is as required shades of colour.

6, according to the vitrified brick of claim 1-4, it is characterized in that described to stick on porcelain piece on the coating film on glass face whole, also piecemeal, its shape is a different shape as required.

7, according to the vitrified brick of claim 1-4, it is characterized in that the preferred CH-31 type of described cementing agent cementing agent.

8, according to the vitrified brick of claim 5, it is characterized in that the preferred CH-31 type of described cementing agent cementing agent.

9, according to the vitrified brick of claim 6, it is characterized in that the preferred CH-31 type of described cementing agent cementing agent.