CN219685979U - Fixed-length compacting plate based on high frequency - Google Patents

Abstract

The utility model relates to a high-frequency-based sizing compaction plate, wherein the sizing compaction plate (1) comprises a plurality of longitudinal spliced compaction wood plates (2) with the same size, wherein the longitudinal spliced compaction wood plates are in compression joint in the width direction, each longitudinal spliced compaction wood plate (2) comprises a plurality of compaction wood strips (3) in compression joint in the length direction, and each compaction wood strip (3) comprises a plurality of soft wood strips (4) in compression joint in the thickness direction through a high-frequency hot pressing step. The high-frequency-based sizing compaction plate has the beneficial effects that the high-frequency-based sizing compaction plate has better processing performances such as screw holding force, bending strength, bending elasticity and the like, and excellent accelerated aging resistance, and the preparation method is easy for mass production and low in cost.

Description

Fixed-length compacting plate based on high frequency

Technical Field

The utility model belongs to the technical field of wood board processing, and particularly relates to a sizing compaction plate based on high frequency waves.

Background

The density boards, chipboards, multi-layer boards and log boards used in the panel furniture are basically fixed-length boards, such as 48-length (1220 mm in length and width dimension by 2440 mm) and 49-length (1220 mm in length and width dimension by 2745 mm) which are commonly used. The related art does not disclose cut-to-length pressed wood for use in the custom furniture industry. CN111347511A (2020.06.30) is based on a process for the preparation of a high-frequency hybrid glue-free composite material by mixing at least two blocks of material having a density not exceeding 0.7kg/m ³ The wood boards are heated and pressed through high frequency waves to form a degenerated connecting layer between two adjacent wood boards, and the preparation method specifically comprises the following steps: pretreatment, lamination treatment, heating and pressurizing treatment, curing treatment, cooling treatment and health-preserving treatment, however, the multilayer compaction plate manufactured by the patent is not a transverse splicing compaction plate, and the multilayer compaction plate is not easy to produce in mass and has higher cost when manufactured into a sizing plate. CN112847694 a (2021.05.28) discloses a glue-free transverse splicing compaction apparatus (refer to fig. 1, wherein 1-lower platen, 2-upper platen, 4-lower pad, 5-upper pad, 6-hydraulic rod, 30-transverse splicing) and glue-free transverse splicing compaction method, the method comprising the steps of:

(1) A plurality of transverse jointed boards are sequentially arranged on a plane, a resin film is clamped between two adjacent transverse jointed boards, and the contact surface of the two adjacent transverse jointed boards forms an angle of 45-135 degrees with the plane, so that a arranging board is manufactured; (2) Applying a first acting force F1 to the horizontal direction of the arrangement plate, wherein F1 is 1.5-2MPa; (3) Heating the arrangement plate to 60-170 ℃, applying a second acting force F2 in the vertical direction of the arrangement plate, wherein F2 is not less than 0.7MPa, and maintaining the pressure for 8-10min; (4) F2 is kept unchanged, F1 is increased to F3, F3 is 2.5-4MPa, and the pressure is kept to the temperature of the arrangement plate to 40-70 ℃. Although the patent is to heat the transverse splice compacting plates in the molding process, the transverse splice compacting plates are still not easy to produce in mass and have high cost when being made into sizing plates.

Disclosure of Invention

At least in view of the above technical problems, various embodiments of the present utility model provide a high frequency-based sizing compaction plate, in which the sizing compaction plate 1 includes a plurality of longitudinally spliced compaction wood boards 2 of the same size that are crimped in the width direction, each longitudinally spliced compaction wood board 2 includes a plurality of compaction wood strips 3 that are crimped in the length direction, and each compaction wood strip 3 includes a plurality of cork strips 4 that are crimped in the thickness direction by a high frequency hot-pressing step.

Further fixed-length compacting plates, vertical splicing lines 5 are formed at the splicing positions of the adjacent compacting wood strips 3, transverse splicing lines 6 are formed at the splicing positions of the adjacent longitudinal splicing compacting wood strips, and a plurality of high-frequency hot embossing lines 7 are formed at the splicing positions of the adjacent soft wood strips.

Further, the vertical splicing lines 5 of the adjacent longitudinal splicing pressing boards 2 are not on the same straight line.

Further sizing compaction plates, each high frequency hot embossing 7 of adjacent cork strips 4 is in the same direction but does not intersect.

The transverse splicing contact surface of each longitudinal splicing compaction wood board adjacent to each other in the width direction of each fixed-length compaction board 1 is a plane or an inclined plane, and the inclined plane comprises an inclined plane or an inclined curved surface; preferably, the oblique curved surface is a serrated surface;

the longitudinal splicing contact surface of each longitudinal splicing pressed wood board 2 adjacent to each other in the length direction of the pressed wood board 3 is a curved surface or an inclined surface, and the inclined surface comprises an inclined plane or an inclined curved surface; preferably, the curved surface or the oblique curved surface is a serrated surface.

Further, the resin layers 8 are arranged between the adjacent transverse splicing contact surfaces or the adjacent longitudinal splicing contact surfaces, and the resin layers comprise one or more of PVA resin layers, PVB resin layers and PVC resin layers. The resin used for the resin layer comprises any one or a mixture of a plurality of ethylene-vinyl acetate copolymers or polyolefin materials, wherein the polyolefin materials are any one or a mixture of at least two of polyethylene, polypropylene, modified polyethylene, modified polypropylene or ethylene elastomer containing ethylene units.

And a printing layer is arranged on the surface of the fixed-length compaction plate 1 in the thickness direction.

Further fixed-length compacting plates, each fixed-length compacting plate 1 comprises a plurality of longitudinal spliced compacting wood plates 2 with the same size positioned in the middle of the fixed-length compacting plates;

the widths of a plurality of compaction wood strips (3) of each longitudinal-spliced compaction wood plate (2) are equal.

Further scale compaction board, scale compaction board 1 is: the density is a fixed-length compacting plate with 0.58-0.6; and/or the plate surface holds the fixed-length compacting plate with the screw force of 1400N-1600N; and/or a fixed-length compacting plate with the bending strength of 50-65 MPa; and/or the fixed-length compaction plate with the bending resistance elasticity of 6500MPa to 7500MPa.

The sizing compacting plate 1 is a poplar sizing compacting plate.

The high-frequency-based sizing compaction plate has the beneficial effects that the high-frequency-based sizing compaction plate has better processing performances such as screw holding force, bending strength, bending elasticity and the like, and excellent accelerated aging resistance, and the preparation method is easy for mass production and low in cost.

Drawings

FIG. 1 is a prior art cross-piece compaction apparatus;

FIG. 2 illustrates a fixed-length compaction plate according to an embodiment of the utility model;

FIG. 3 is a longitudinal split press wood board of an embodiment of the present utility model;

FIG. 4 is a schematic cross-sectional view.

Detailed Description

The following examples further illustrate the utility model but are not to be construed as limiting the utility model. Modifications and substitutions to methods, procedures, or conditions of the present utility model without departing from the spirit and nature of the utility model are intended to be within the scope of the present utility model.

Interpretation of the terms

Sizing refers to preparing a sheet, for example, according to the length and width specified by the product standards. It can be appreciated that the sizing board is more suitable for robot and assembly line operation, and can be manufactured into mass production boards so as to reduce cost.

Single press refers to hot press of a layer of wood board by a hot press.

By press-fitting, it is meant that the press presses the multi-layered wood board, for example, the press presses the three-layered wood board, which is called "three-press-fitting".

Longitudinal splicing, also known as longitudinal splicing or fixed-length direct pressing, refers to splicing wood boards adjacent in the length direction.

Transverse splicing, also known as transverse splicing or fixed-length side pressing, refers to splicing of wood boards adjacent in the width direction, and is shown with reference to fig. 4.

Splice end face, see fig. 4, the end face of the wood board includes 6 faces, and splice end face 9 is one end face of the wood board for splicing. After splicing, the spliced end surfaces can also be called longitudinal spliced contact surfaces or transverse spliced contact surfaces.

Resin layer, see fig. 4, the resin layer 8 is located between the splice end faces 9.

The first force, referred to as the first force F1 applied in the horizontal direction, is referred to in chinese patent application CN112847694 a, and may be implemented by a pneumatic compacting device, for example.

The second acting force refers to applying a second acting force F2 in the vertical direction, see Chinese patent application CN 112847694A; such as may be realized by a high frequency thermo-compressor. The use of the sizing compaction plate is not particularly limited, and for example, the sizing compaction plate can be used as a floor substrate, namely, a substrate of a decorative artificial board besides a substrate for manufacturing plate furniture.

Alternative devices for use with embodiments of the present utility model include, but are not limited to: a slicer; an infrared preheating device; an attaching water layer device (which may be a coating device or a spraying device); a high frequency hot press; liquid nitrogen refrigerating equipment; four-edge planing; a sorting system; tooth punching equipment; roller type coating device; pneumatic compaction devices (including hydraulic press-based compaction devices for various plate assembly lines); a woodworking cutting machine; a board printer. The optional citation chinese patent application CN 201811592197-is based on high frequency glue-free compacting equipment, chinese patent application CN 201910181348-high frequency compacting wood combination production line, chinese patent application CN 201922120903-a glue-free transverse splicing compacting equipment, chinese patent application CN 202010100409-equipment for discharging compressed water vapor on the surface of compacting wood in a balanced manner and equipment for the assembly line of compacting wood equipment, and in addition, the equipment or production line reconstructed according to the inventive concept is also within the scope of protection of the present utility model.

The optional infrared preheating equipment in the embodiment of the utility model is a plurality of sections of infrared preheating boxes which can be arranged on a conveying device (which can be a conveying chain or a roller) of a production line, namely the conveying device can carry boards to pass through from the lower part in the box body of the plurality of sections of infrared preheating boxes, each section of infrared preheating box comprises an infrared heating preheating pipe arranged above the inner part of the box body, the wattage of the infrared heating preheating pipes is adjustable, so that the space temperature in the infrared preheating box is usually kept at about 150 ℃, the length of the infrared preheating box on the production line can be set according to the process requirement, and when the length of the infrared preheating box on the production line is fixed, the speed of the conveying device (such as the conveying chain) can be adjusted, so that the preheating temperature of the boards is between 60 ℃ and 100 ℃, for example, the preheating temperature is reduced by 100 ℃, and the preheating temperature is increased by 60 ℃.

The optional water layer attaching device provided by the embodiment of the utility model is a plurality of water layer coating machines which can be arranged on a conveying device (which can be a conveying chain or a roller) of a production line, namely, the conveying device can carry boards to pass through from the lower part in a box body of the plurality of coating machines, each water layer coating machine comprises a coating roller set (comprising a driving roller and a driven roller) and a water supply device, wherein the water supply device can spray water on the coating roller set, and the coating roller set can coat water on a wood board, so that the wood board attaches to the water layer. The number of the water layer coating machines or the number of the roller sets can be set according to the process requirements, for example, 1 set of coating roller sets can be set for each water layer coating machine, and 2 sets of coating roller sets can be set for each water layer coating machine, and obviously if the coating is carried out 2 times, 2 coating roller sets are needed for the former and 1 coating roller set is needed for the latter. The coating speed (rotational speed of the roller set) is typically consistent with the travel speed of the conveyor.

The optional liquid nitrogen refrigerating equipment in the embodiment of the utility model is a plurality of liquid nitrogen refrigerating cabinets which can be arranged on a conveying device (which can be a conveying chain or a roller) of a production line, namely, the conveying device can carry plates to pass through the lower part of the inner parts of the plurality of liquid nitrogen refrigerating cabinets. The temperature in the liquid nitrogen refrigeration cabinet is about-150 ℃ to-130 ℃.

The corresponding designs of the mechanical structure, the electrical structure and the like of the infrared preheating box, the liquid nitrogen refrigerating equipment and the water layer coating machine can be realized by adopting the known technology, and the utility model is not repeated one by one.

The present utility model is described below with reference to the embodiments, wherein the methods of the cited chinese patent applications are all cited in full, and those skilled in the art can make direct reference or indirect reference after slightly modifying the concept of the present utility model, and the present utility model is not limited to the specific manner of reference.

Embodiment one preparation of a Soft wood slat

The method for preparing the cork strip used in the embodiments of the present utility model may be prepared by any known technique, such as a saw blade processing method, a slicing method for controlling the moisture content to be 60-80% (slicing is adopted instead of saw blades, poplar with higher moisture content is more suitable for slicing without pretreatment and drying, and substrate loss may be reduced), a cooking slicing method (including the steps of selecting materials, cooking, slicing, and air drying). The dimensions of the cork strips used in the embodiments of the present utility model are determined according to the dimensions of the sizing compaction plates, for example, 48-gauge (4-gauge by 8-gauge) sizing compaction plates are prepared, the cork strips may have a thickness of 1-4 cm, a width of 22cm or 44cm, and cork is typically poplar. The moisture content of the cork strip is generally 10% -20%.

Second embodiment preparation of the adhered Water layer Soft wood slat

According to some embodiments of the utility model, the surface of the preheated cork strip irradiated by infrared rays is coated with a water layer for 2-4 times by the water layer coating machine, so that a plurality of cork strips with the water layer are obtained. Although the water layer coating machine is more convenient to arrange on the assembly line, a spraying device can be used for enabling the surface of the preheated cork strip to be attached with the water layer in alternative embodiments. Of course, in small scale preparations, the surface of the pre-heated cork strip may also be coated with a thin layer of water by hand. The soft wood strip attached with the water layer generates hot steam at the instant of high-frequency hot pressing, so that the wood property of the subsequently obtained compacted wood strip is changed (the beef hairline is reduced), and other implementation modes based on the conception of the utility model are also within the protection scope of the utility model.

Embodiment preparation of three-pressed wooden lath (Single press)

The method for preparing the compacted wood veneer (single-pressure) used in the embodiment of the utility model at least comprises the steps of heating, compressing and solidifying, and optionally comprises the steps of cooling and curing. The following is a method of referring to chinese patent application CN109465932a, as an alternative method of preparing the compacted wood veneer (single press) according to the embodiments of the present utility model:

and (3) heating and compressing: heating wood by high frequency until the average temperature of the wood is 100-110 ℃, preserving heat for 5-7min, and compressing according to a first compression rate.

Curing: heating the wood subjected to the heating and compression treatment by using high frequency until the average temperature of the wood is 180-220 ℃, and preserving heat for 5-8min to carry out curing treatment.

And (3) cooling treatment: cooling the surface of the wood subjected to the solidification treatment by using a water cooling technology at a speed of 5-15 ℃/min until the average temperature of the wood is 70-90 ℃; the water flow rate of the water cooling technology is 0.9-1.3m/s; in the cooling treatment process, when the surface temperature of the wood is cooled to 85-90 ℃, wind cooling is carried out, the wind speed is 9.2-9.7m/s, and the wind temperature is 55-60 ℃.

And (3) health preserving treatment: placing the cooled wood at room temperature, and preserving for 13-15 days to obtain the glue-free compacted hardwood; the specific method for health care treatment comprises the following steps: placing the cooled wood on a horizontal drying surface, applying pressure of 5.5-7.2Mpa to the upper surface of the wood, preserving for 3 days, reducing pressure of 1.2-1.5Mpa every day until the pressure is 0, and preserving for 10-12 days.

Embodiment preparation of four-pressed wooden lath (three-ply pressing)

The method for preparing the compacted wood veneer (three-in-one) used in the embodiment of the utility model at least comprises the steps of heating and compressing treatment (also called heating and pressurizing treatment) and solidifying treatment, and optionally comprises cooling treatment (also called cooling treatment) and curing treatment. The following is a method of referring to chinese patent application CN111347511a, as an alternative method of preparing the compacted wood veneer (three-in-one) according to the embodiment of the present utility model:

lamination treatment: taking 2 or more than 2 boards, and stacking according to at least one stress direction to obtain a laminated board, wherein the stress direction comprises a direct pressure direction and an indirect pressure direction;

heating and pressurizing treatment: heating the degenerated connecting layer of the laminated wood board to 80-100 ℃, preserving heat for 4-6min, and then carrying out pressurization treatment according to the stress direction and the preset compression rate;

curing: heating the wood board subjected to heating and pressurizing treatment by using high frequency until the temperature of the wood board is 180-220 ℃, preserving heat for 5-8min, and curing to obtain a cured wood board;

and (3) cooling treatment: cooling the surface of the solidified wood board at a speed of 5-15 ℃/min to 70-90 ℃ by water cooling technology, wherein the water flow rate of the water cooling technology is 0.9-1.5m/s, and when the surface temperature of the wood board is cooled to 85-90 ℃, carrying out air cooling at an air speed of 9.2

-9.7m/s, the temperature of the wind being 55-60 ℃;

and (3) health preserving treatment: and (3) placing the cooled wood board for 15-20 days at normal temperature to obtain the high-frequency mixed material-based glue-free composite material.

The fixed-length compaction plate prepared based on the compaction wood batten (three-in-one compaction) has three layers in the thickness direction, two joints are formed in the width direction, and the adjacent laminated wood boards can interact transverse stress and longitudinal stress to offset each other, so that the rebound prevention performance of the structure is reflected. In addition, the woodiness of different slices is necessarily different, and unique lines (corresponding to anti-counterfeiting lines) of the fixed-length compaction plate are formed on the side edges after hot pressing, and the fixed-length compaction plate is equivalent to natural wood and is the characteristic which other products such as a shaving board do not have.

Fifth embodiment preparation of longitudinally-spliced pressed wood board

The preparation method of the longitudinally spliced pressed wood board used in the embodiment of the utility model comprises, but is not limited to, the method of Chinese patent application CN201911193101, namely, the method of clamping resin films between wood boards and then hot pressing is needed. In addition, some embodiments of the present utility model use the following clamp resin mix method:

splicing the cooled compressed wood strips adjacent in the length direction to obtain a plurality of longitudinally spliced compressed wood boards, wherein the method specifically comprises the following steps of:

a) Mixing materials, heating and hot-melting resin to obtain a resin hot melt; adding 20-40 mesh resin particles, and stirring to obtain a resin mixture (also called pasty hot melt resin); the resin includes, but is not limited to, one or more of PVA, PVB, PVC, and the resin particles include, but are not limited to, one or more of PVA particles, PVB particles, and PVC particles.

b) The fixed length three-ply pressing plate is sawn by the comb teeth (finger joint) (compacting assembly line), so as to obtain a three-ply plate after the comb teeth;

c) Coating resin on the comb teeth of the three-ply board after combing the comb teeth by using a roller machine; on the assembly line, the comb teeth of the comb tooth three-ply plates dipped with resin are contacted end to end, the comb teeth of the front comb tooth three-ply plate and the rear comb tooth three-ply plate can be pressurized while walking at the pneumatic compacting device of the assembly line, and the three-ply plates after comb tooth connection are transferred to the fixed-length direct-pressure pneumatic compacting device.

d) And (3) connecting the comb teeth with the rear three-ply board by fixed-length direct-compression, and placing the three-ply board on a fixed-length direct-compression pneumatic compacting device for pressing to obtain the fixed-length direct-compression compacting board.

Embodiment six-transverse-spliced pressed wood board preparation

The preparation method of the longitudinally spliced pressed wood board used in the embodiment of the utility model comprises, but is not limited to, the method of Chinese patent application CN201911193101, namely, the method of clamping resin films between wood boards and then hot pressing is needed. In addition, some embodiments of the present utility model use the following clamped resin hot melt method:

a) Heating and hot-melting resin to obtain resin hot melt;

b) And coating resin hot melt between longitudinally spliced compacting wood boards adjacent in the width direction, applying acting force by using a pneumatic compacting device, and finishing splicing by using a fixed-length side pressure pneumatic compacting device to obtain a plurality of transversely spliced compacting wood boards (also called fixed-length side pressure compacting boards).

Preparation of seventh-embodiment sizing compaction plate

As shown in fig. 2 and 3, the fixed-length press plate 1 of the present utility model comprises a plurality of longitudinally spliced press-fit wood boards 2 of the same size which are crimped in the width direction, each longitudinally spliced press-fit wood board 2 comprises a plurality of press-fit wood strips 3 which are crimped in the length direction, and each press-fit wood strip 3 comprises a plurality of cork strips 4 which are crimped in the thickness direction through a high-frequency hot-pressing step.

The splicing parts of the adjacent compressed wood strips 3 form vertical splicing lines 5, the splicing parts of the adjacent longitudinal splicing compressed wood strips form transverse splicing lines 6, and the splicing parts of the adjacent soft wood strips form a plurality of high-frequency hot embossing lines 7.

The vertical-spliced lines 5 of adjacent vertical-spliced pressed wood boards 2 are not on the same straight line.

Each high frequency heat embossing 7 of adjacent cork strips 4 is in the same direction but does not intersect. Specifically, since the high-frequency hot embossing 7 is formed by high-frequency compression, the unique lines (corresponding to anti-counterfeiting lines) of the fixed-length compacting plate are formed on the side after hot pressing, as shown in fig. 2, due to the necessarily different lignification of different cork strips 4.

Among the longitudinal spliced pressing boards 2 of each fixed-length pressing board 1, the longitudinal spliced pressing boards 2 with the same size are positioned in the middle;

the widths of the plurality of compacting wood strips 3 of each longitudinal-spliced compacting wood board 2 are equal.

The fixed-length compaction plate has the following properties of 0.58-0.6 in density, has the strength equivalent to that of pine, and can be used as a cabinet plate to replace a shaving board, a multilayer board and a density board; the screw holding force of the plate surface is 1400N-1600N; the bending strength is 50 MPa-65 MPa; the bending resistance is 6500MPa to 7500MPa.

The preparation process of the fixed-length compacting plate comprises the following steps:

the first preheating step is to heat up a plurality of soft wood battens with the water content of 10-20% to 80-90 ℃ by infrared irradiation to obtain a plurality of preheated soft wood battens;

the step of attaching the water layer is to attach the water layer on the surface of the preheated cork strip irradiated by infrared rays, so as to obtain a plurality of cork strips with the water layer;

the high-frequency hot pressing step is to heat, compress and solidify the soft wood batten attached with the water layer under the high-frequency condition according to the method of the embodiment 2 or the embodiment 3, and a plurality of compact wood battens are obtained;

and (3) cooling treatment: cooling a plurality of compacted wood veneer strips to an average wood temperature of 70-90 ℃ according to the method of example 2 or example 3;

the longitudinal splicing step is used for splicing the cooled pressed wood strips adjacent in the length direction to obtain a plurality of longitudinal spliced pressed wood boards;

the transverse splicing step is to splice the longitudinally spliced pressed compact boards adjacent to each other in the width direction, and a plurality of transverse spliced pressed compact boards are obtained by referring to the figure 4;

the sizing step is to cut a plurality of transverse spliced compacting plates into a plurality of sizing compacting plates by a woodworking material cutting machine.

The screw holding force of the fixed-length compaction plates of some embodiments of the utility model can be improved by at least 30%, the density of the fixed-length compaction plates is 0.58-0.6 by taking poplar as an example, the fixed-length compaction plates have the strength equivalent to pine, and the fixed-length compaction plates can be used as cabinet plates to replace shaving boards, multi-layer boards and density boards.

Embodiment eight-faced artificial board preparation

In some alternative embodiments, the fixed-length compaction plate is used as a substrate for facing the artificial board, and further comprises the following steps:

and the pattern printing step is to print patterns (printing layers) on the fixed-length compacting plates by a wood plate printer to obtain a plurality of decorative artificial boards.

The present utility model will be further described with reference to specific examples and comparative examples.

Example 1 preparation of a fixed-size compaction plate

1. Preparation of a Soft wood slat according to the method of the first embodiment, a fixed-length poplar slat (also referred to as a Soft wood slat) having a length of 50cm to 120cm and a width of 22cm was prepared, and the moisture content was 15.+ -. 3%.

2. And in the first preheating step, a plurality of soft wood strips with the water content of 15+/-3% are heated to 80-90 ℃ by infrared irradiation through the infrared preheating box, and the temperature of an infrared irradiation space is 130 ℃ to obtain a plurality of preheated soft wood strips.

3. In the third step of adhering the water layer, the water layer is coated 2 times by 2 coating roller group water layer coating machines with 1 group, and the surface of the preheated cork strip irradiated by infrared rays is adhered with the water layer, so as to obtain a plurality of cork strips with the water layer.

4. The high-frequency hot pressing step is to heat, compress and solidify the soft wood batten attached with the water layer under the high-frequency condition according to the method of the third embodiment mode, so as to obtain a plurality of compact wood battens;

5. and (3) cooling treatment: cooling the plurality of compacted wood veneer strips according to the method of embodiment three to an average wood temperature of 70-90 ℃;

6. the longitudinal splicing step refers to a method of Chinese patent application CN201911193101, and the cooled compressed wood strips adjacent in the length direction are spliced to obtain a plurality of longitudinal spliced compressed wood boards;

7. the transverse splicing step refers to a method of Chinese patent application CN201911193101, and longitudinally spliced pressed wood boards adjacent in the width direction are spliced to obtain a plurality of transverse spliced pressed wood boards;

8. and in the sizing step, a woodworking material cutting machine is used for cutting a plurality of transverse spliced compacting plates into a plurality of sizing compacting plates to prepare a 48-scale (4-scale multiplied by 8-scale) sizing compacting plate (length, width and thickness are 2440mm x 1220mm x 20 mm).

Example 2 preparation of a fixed-size compaction plate

Substantially the same as in example 1, except that:

in the first preheating step, the temperature of the infrared irradiation space is 140 ℃.

In the step of attaching the water layer, the total coating is performed 3 times by 3 coating roller group water layer coating machines with 1 group of coating roller groups;

example 3 preparation of a fixed-size compaction plate

Substantially the same as in example 1, except that:

in the first preheating step, the temperature of the infrared irradiation space is 150 ℃.

In the step of attaching the water layer, the water layer coater is coated for 3 times by 3 coating roller sets which are arranged in the step of arranging 1 group;

the high frequency hot pressing step is carried out after the second preheating step on the soft wood strip with the water layer,

and the second preheating step is to maintain the temperature of the plurality of adhered water layer cork strips to 80-90 ℃ by infrared irradiation.

Example 4 preparation of a fixed-size compaction plate

Substantially the same as in example 1, except that:

the longitudinal splicing step refers to the method for clamping resin mixture in the fifth embodiment, and the cooled compacted wood planks adjacent in the length direction are spliced to obtain a plurality of longitudinal spliced compacted wood planks; wherein, the longitudinal splicing contact surface of each longitudinal splicing pressed wood plank is a serrated surface.

A transverse splicing step refers to a resin hot melting method in the sixth embodiment, and a plurality of transverse spliced pressed wood boards are obtained by splicing longitudinally spliced pressed wood boards adjacent in the width direction; wherein, the transverse splicing contact surface of each transverse splicing pressed wood plank is a plane.

Adjacent two longitudinal splicing contact surfaces or adjacent transverse splicing contact surfaces are in pressure connection through PVB resin layers.

The steps of forming the longitudinally spliced PVB resin layer are as follows:

s1, processing and forming the spliced end surfaces of the compacted wood battens into serrated surfaces;

s2, after the PVB resin is hot melted, 20-40 mesh PVB resin particles are added, stirring is carried out, PVB resin mixture is obtained, the PVB resin mixture is coated on the splicing end face (longitudinal splicing contact face) of the fixed-length compact wood, and the weight ratio of the PVB resin to the PVB resin particles is 8:1.

And S3, extruding the spliced end surfaces of the adjacent compacted wood strips by using a pneumatic compacting device.

The steps of forming the layer of the horizontally spliced PVB resin are as follows:

s1, machining and forming the spliced end surfaces of the compacted wood battens into planes (the steps are omitted for the planes);

s2, carrying out hot melting on the PVB resin to obtain PVB resin hot melt, and coating the PVB resin mixture on the splicing end face (transverse splicing contact face) of the compact wood with the fixed length.

And S3, extruding the spliced end surfaces of the adjacent compacted wood strips by using a pneumatic compacting device.

Example 5 preparation of a fixed-size compaction plate

Substantially the same as in example 4, except that:

in the step of forming the longitudinal joint contact surface:

s1, processing and forming the spliced end surfaces of the compacted wood battens into serrated surfaces;

the weight ratio of S2 PVB resin to PVB resin particles was 10:1.

In the step of forming the transverse joint contact surface:

s1, machining and forming the spliced end faces of the compacted wood battens into inclined planes.

Example 6 preparation of a fixed-size compaction plate

Substantially the same as in example 4, except that:

in the step of forming the longitudinal joint contact surface:

s1, processing and forming the spliced end surfaces of the compacted wood battens into serrated surfaces;

the weight ratio of S2 PVB resin to PVB resin particles was 12:1.

In the step of forming the transverse joint contact surface:

s1, processing and forming the spliced end surfaces of the compacted wood laths into planes.

Example 7 preparation of a fixed-size compaction plate

Substantially the same as in example 4, except that:

a high-frequency hot pressing step (three-in-one pressing) is carried out on the soft wood batten attached with the water layer under the high-frequency condition by referring to the method in the fourth embodiment, and the three-in-one pressing plate with burrs is obtained; the front, back, left and right edges of the three-in-one pressing plate with burrs are cut by using a four-edge planer to obtain a plurality of pressing wood strips (also called three-in-one pressing plates). Wherein, the liquid crystal display device comprises a liquid crystal display device,

lamination treatment: stacking 3 soft wood strips with water layers according to a stress direction to obtain a laminated wood board; and arranging 6-8 laminated boards on a compacting disc/supporting plate of the hot press according to a matrix, wherein the stress direction is a direct pressure direction.

The high frequency conditions are as follows: the compression rate was 25 seconds/time and the compression ratio was 25%.

Example 8 preparation of a fixed-size compaction plate

Substantially the same as in example 7, except that:

the high frequency conditions are as follows: the compression rate was 27 seconds/time and the compression ratio was 30%.

Example 9 preparation of a fixed-size compaction plate

Substantially the same as in example 7, except that:

the high frequency conditions are as follows: the compression rate was 30 seconds/time, and the compression ratio was 28%.

Example 10 preparation of a fixed-size compaction plate

Substantially the same as in example 7, except that:

and (3) cooling treatment: and (3) placing a plurality of compacted wood strips in an environment of minus 130 ℃ by using a liquid nitrogen refrigeration technology, cooling for 15min to room temperature, and then performing longitudinal splicing. Typically, a number of compressed wood strips are cooled to room temperature using liquid nitrogen refrigeration techniques and then left in the liquid nitrogen refrigeration cabinet. In other embodiments, "room temperature" refers to the temperature before the longitudinal splice is made, for pipeline operation, cooled in an environment of-130 ℃ to a temperature of 3-5 ℃ for the compacted wood veneer, and then fed out of the pipeline into the longitudinal splice device.

EXAMPLE 11 preparation of a fixed-size compaction plate

Substantially the same as in example 10, except that:

and (3) cooling treatment: and (3) placing a plurality of compacted wood strips in an environment of-140 ℃ by using a liquid nitrogen refrigeration technology, cooling for 12min to room temperature, and then performing longitudinal splicing.

Example 12 preparation of a fixed-size compaction plate

Substantially the same as in example 10, except that:

and (3) cooling treatment: and (3) placing a plurality of compacted wood strips in an environment of-150 ℃ by using a liquid nitrogen refrigeration technology, cooling for 9min to room temperature, and then performing longitudinal splicing.

Comparative example 1 preparation of a fixed-size compaction plate

Substantially the same as in example 1, except that: the step of attaching the water layer is omitted.

Comparative example 2 preparation of a fixed-size compaction plate

Substantially the same as in example 1, except that: the step of attaching the water layer is omitted, and the first preheating step is performed through a high-frequency hot press instead.

Comparative example 3 preparation of a fixed-size compaction plate

Substantially the same as in example 1, except that:

in the first preheating step, the temperature of the infrared irradiation space is 160 ℃, and a plurality of preheated cork strips are obtained.

In the step of adhering the water layer, the total coating is performed 1 time by 1 coating roller set water layer coater with 1 set of coating roller set.

Comparative example 4 preparation of a fixed-size compaction plate

Substantially the same as in example 4, except that:

in the step of forming the longitudinal joint contact surface:

s1, processing and forming the spliced end surfaces of the compacted wood laths into planes;

in the step of forming the transverse joint contact surface:

s1, machining and forming the spliced end faces of the compacted wood battens into inclined planes.

Comparative example 5 preparation of a fixed-size compaction plate

Substantially the same as in example 4, except that:

in the step of forming the longitudinal joint contact surface:

s1, processing and forming the spliced end surfaces of the compacted wood laths into inclined planes;

in the step of forming the transverse joint contact surface:

s1, machining the spliced end faces of the compacted wood veneers into serrated faces.

Comparative example 6 preparation of a fixed-size compaction plate

Substantially the same as in example 4, except that:

in the step of forming the longitudinal joint contact surface:

the weight ratio of S2 PVB resin to PVB resin particles was 14:1.

In the step of forming the transverse joint contact surface:

s1, machining and forming the spliced end faces of the compacted wood battens into inclined planes.

Comparative example 7 preparation of a fixed-size compaction plate

Substantially the same as in example 7, except that:

the high frequency conditions are as follows: the compression rate was 40 seconds/time.

Comparative example 8 preparation of a fixed-size compaction plate

Substantially the same as in example 7, except that:

the high frequency conditions are as follows: the compression rate was 10 seconds/time.

Comparative example 9 preparation of a fixed-size compaction plate

Substantially the same as in example 7, except that:

the high frequency conditions are as follows: the compression ratio was 20%.

The following experiments were performed in conjunction with examples and comparative examples.

Test example 1 cattle hairline assay

The wood board was sawed in the thickness direction to remove a surface layer (a surface layer receiving infrared irradiation) 3mm thick to expose an inner layer, and the density and the water content were measured, and then 4 pieces were cut at four corners and 2 pieces were cut at the center in total of 6 test pieces.

Test piece size: the length is 150+/-1 mm; 50+ -0.5 mm wide;

the testing method comprises the following steps: the surface of the test piece was examined for hairline with normal vision (or corrected to normal vision) and a 6-fold magnifying glass at an illuminance of 800lx to 1000 lx.

Grade of cowhair grain: 5 stages: no cow hair line; 4 stages: cattle hairline is only arranged under a 6-time magnifying glass; 3 stages: the presence of the hairline was visually observed, and the hairline of one wood board was expressed as an arithmetic average of the total test piece hairline grades, approximated to an integer, and the results are shown in Table 1.

Table 1 results of measurement of the level of hairline in cattle

As can be seen from the test results, the beef hairline of examples 1 to 3 is significantly smaller than that of comparative examples 1 to 3. The possible reason is that the adhered water layer cork strip generates hot steam at the instant of high frequency hot pressing, thereby changing the lignification. As can be seen from a comparison of examples 1 to 3 with comparative example 2, the combination of infrared preheating and high frequency hot pressing of the adhered water layer cork strip was substantially the same as the grade of the cowhair pattern preheated and cured by high frequency, but the former is more suitable for the production line and has lower cost than the latter to complete preheating by a high frequency hot press. As is clear from a comparison of examples 1 to 3 with comparative examples 1 and 3, the infrared preheating or the unsuitable adhering of the water layer causes the occurrence of beef hairline in the vicinity of the infrared-irradiated surface layer of the fixed-size press plate of poplar of 2mm to 4mm, and it is shown by test example 1 that the method of examples 1 to 3 can substantially solve this problem.

Test example 2 flexural Strength, flexural modulus of elasticity test

The flexural strength detection method is GB/T1936.1-2009 "method for testing flexural strength of wood", the flexural modulus detection method is GB/T1936.2-2009 "method for measuring flexural modulus of wood", and the test results are shown in tables 2 and 3.

TABLE 2 flexural Strength test results

TABLE 3 flexural modulus of elasticity test results

As is clear from the test results, the flexural strength and flexural modulus of examples 1 to 6 are both superior to those of comparative examples 4 to 6. Examples 4 to 6 were better in flexural strength and flexural modulus. It can be seen that three-in-one compression is more advantageous. As is clear from a comparison between examples 4 to 6 and comparative example 4, in the step of forming the longitudinal joint contact surface, the joint end surface of the compacted wood veneer is processed and formed into a serrated surface, the resin loading amount is increased, and the improvement effect on the flexural strength and the flexural elastic modulus performance is large. As is clear from a comparison between examples 4 to 6 and comparative example 5, in the step of forming the transverse butt joint contact surface, the butt joint end surfaces of the pressed wooden lath were formed into the saw tooth surfaces, but the improvement in the flexural strength and flexural modulus of elasticity was not greatly affected. As is clear from a comparison of examples 4 to 6 with comparative example 6, the weight ratio of PVB resin to PVB resin particles in the step of forming the longitudinal joint contact surface has a large influence on the improvement of the flexural strength and flexural elastic modulus properties.

Test example 3 screw holding force test

The detection method of the screw holding force is GB/T17657-2013 method for testing the physicochemical properties of artificial boards and decorative artificial boards, and the test results are shown in Table 4.

Table 4 screw grip test results

/>

From the test results, the screw holding force of the boards of examples 4 to 9 is superior to that of the medium density boards, the joinery boards and the common chipboards. The panel holding screw forces of examples 7-9 are close to the veneable directional structural panel. The plate edge holding screw forces of examples 4-9 are substantially the same, but the plate splice holding screw forces of examples 7-9 are superior to examples 4-6. Comparison of examples 4 to 6 with examples 7 to 9 shows that there is no significant difference in compression speed and compression ratio.

Test example 4 determination of formaldehyde content

Determination basis of formaldehyde (mg/L): GB 18584-2001 "limit of harmful substances in Wood furniture as interior Material", the test results are shown in Table 5.

TABLE 5 Formaldehyde test results

	Detecting items	Detection basis	Index requirements	Detection result
					Example 1	Formaldehyde, mg/L	GB 18584-2001	≤1.5	0.3
Example 4	Formaldehyde, mg/L	GB 18584-2001	≤1.5	0.3
					Example 7	Formaldehyde, mg/L	GB 18584-2001	≤1.5	0.3
Example 10	Formaldehyde, mg/L	GB 18584-2001	≤1.5	0.3

Test results: examples 1, 4, 7 and 10 all meet the index requirements on formaldehyde in GB 18584-2001 limit of harmful substances in wooden furniture as an interior decoration material.

Test example 5 accelerated aging Property measurement

1. The test piece is soaked in hot water, sprayed, steamed, frozen, dried, sprayed, steamed and dried, and after 6 cycles, the screw holding force and the water absorption thickness expansion rate performance of the test piece are measured.

2. The equipment and instrument adopt an artificial board steam accelerated aging test box which meets the requirements of 'accelerated aging performance measurement' on equipment and instrument in GB/T17657-2013 'method for testing physical and chemical properties of artificial boards and veneers'.

3. Test piece size:

static bending strength test piece size (length 450+ -1 mm, width 50+ -1 mm, thickness 20+ -1 mm);

screw holding force test piece dimensions (75+ -1 mm long, 50+ -1 mm wide, 20+ -1 mm thick);

the water absorption thickness expansion rate test piece size (length 50+ -1 mm, width 50+ -1 mm);

4. test piece balancing treatment

The test piece was placed in an environment with a relative humidity of 65.+ -. 5% at 20.+ -. 2 ℃ until the mass was constant (the secondary weighing was performed 24 hours apart, and the difference in mass between the two weighing was less than 1% of the mass of the compacted material, which was considered to be the mass constant).

5. Test method

The aging cycle is accelerated. The test pieces were subjected to 6 cycle tests. Each cycle comprises the steps of:

a) The test piece was immersed in hot water at (49.+ -. 2) ℃ for 1 hour.

b) The test piece is sprayed in steam at the temperature of (93+/-3) ℃ for 3 hours.

c) The test pieces were frozen in a freezer at (-12.+ -. 3) ℃ for 20h.

d) The test pieces were dried in a forced air drying oven at (99.+ -. 2) ℃ for 3 hours.

e) The test piece was steamed in steam at (93.+ -. 3) C for 3 hours.

f) The test pieces were dried in a forced air drying oven at (99.+ -. 2) ℃ for 18 hours.

After the 6-cycle accelerated aging test was completed, the test piece was subjected to conditions of (20.+ -. 2) ℃ and relative humidity (65.+ -. 5)% for at least 48 hours, and then performance test was performed, and the test results are shown in Table 6.

TABLE 6 accelerated aging Performance determination

As can be seen from the test results, the screw holding force of each of examples 4, 7 and 10 was reduced after accelerated aging, but was still superior or equivalent to that of the medium density board, the joinery board and the ordinary particle board. The water absorption thickness expansion ratio of examples 7 and 10 is lower than that of example 4, and thus the three-in-one technique exhibits structural rebound prevention performance. The lowest water absorption thickness expansion ratio of example 10 indicates that the quench bounce prevention and the structural bounce prevention properties can be synergistic.

While the utility model has been described in detail in the foregoing general description, embodiments and experiments, it will be apparent to those skilled in the art that modifications and improvements can be made thereto. Accordingly, such modifications or improvements may be made without departing from the spirit of the utility model and are intended to be within the scope of the utility model as claimed.

Claims (11)

1. The fixed-length compacting plate based on the high frequency is characterized in that the fixed-length compacting plate (1) comprises a plurality of longitudinal spliced compacting plates (2) with the same size and in a width direction in a compression joint mode, each longitudinal spliced compacting plate (2) comprises a plurality of compacting wood strips (3) in a compression joint mode in a length direction, and each compacting wood strip (3) comprises a plurality of soft wood strips (4) in a thickness direction in a compression joint mode through the high frequency hot pressing step.

2. The fixed-length compacting plate according to claim 1, characterized in that the joints of adjacent compacting wood strips (3) form vertical splitted lines (5), the joints of adjacent vertical splitted compacting wood boards form horizontal splitted lines (6), and the joints of adjacent soft wood strips form a plurality of high-frequency hot embossing lines (7).

3. A fixed-length press-fit board as claimed in claim 2, characterized in that the vertical corrugations (5) of adjacent longitudinally-spliced press-fit boards (2) are not collinear.

4. The fixed-length compaction plate according to claim 2, wherein,

each high-frequency hot embossing (7) of adjacent cork strips (4) has the same direction but does not intersect.

5. The fixed-length compaction plate according to any one of claims 1 to 4, wherein,

the transverse splicing contact surface of each longitudinal splicing compaction wood board adjacent to each fixed-length compaction board (1) in the width direction is a plane or an inclined plane, and the inclined plane comprises an inclined plane or an inclined curved surface;

the longitudinal splicing contact surface of each longitudinal splicing pressed wood board (2) adjacent to each other in the length direction of the pressed wood board (3) is a curved surface or an inclined surface, and the inclined surface comprises an inclined plane or an inclined curved surface.

6. The fixed-length compaction plate according to any one of claims 1 to 4, wherein,

the transverse splicing contact surfaces of the longitudinal splicing compaction wood boards adjacent to each other in the width direction of each fixed-length compaction board (1) are planes or inclined planes, the inclined planes comprise inclined curved surfaces, and the inclined curved surfaces are serrated surfaces;

the longitudinal splicing contact surface of each longitudinal splicing pressed wood board (2) adjacent to each other in the length direction of the pressed wood board (3) is a curved surface or an inclined surface, the inclined surface comprises an inclined curved surface, and the curved surface or the inclined curved surface is a serrated surface.

7. The fixed-length compaction plate according to any one of claims 1 to 4, wherein,

and a resin layer (8) is arranged between the adjacent transverse splicing contact surfaces or the adjacent longitudinal splicing contact surfaces, and the resin layer comprises one or more of PVA resin layers, PVB resin layers and PVC resin layers.

8. A sizing press plate according to any one of claims 1 to 4, characterized in that the thickness-direction surface of the sizing press plate (1) has a printed layer.

9. The fixed-length compaction plate according to any one of claims 1 to 4, wherein,

each fixed-length compacting plate (1) comprises a plurality of longitudinal spliced compacting wood plates (2) with the same size positioned in the middle;

the widths of a plurality of compaction wood strips (3) of each longitudinal-spliced compaction wood plate (2) are equal.

10. A sizing compaction plate according to any one of claims 1 to 4, wherein the sizing compaction plate (1) is: the density is a fixed-length compacting plate with 0.58-0.6; and/or the plate surface holds the fixed-length compacting plate with the screw force of 1400N-1600N; and/or a fixed-length compacting plate with the bending strength of 50-65 MPa; and/or the fixed-length compaction plate with the bending resistance elasticity of 6500MPa to 7500MPa.

11. A sizing press according to any one of claims 1 to 4, wherein the sizing press (1) is a poplar sizing press.