CN212925174U - Coating structure for plating rose gold on zinc alloy die casting - Google Patents
Coating structure for plating rose gold on zinc alloy die casting Download PDFInfo
- Publication number
- CN212925174U CN212925174U CN202020426589.2U CN202020426589U CN212925174U CN 212925174 U CN212925174 U CN 212925174U CN 202020426589 U CN202020426589 U CN 202020426589U CN 212925174 U CN212925174 U CN 212925174U
- Authority
- CN
- China
- Prior art keywords
- plating
- plating layer
- rose gold
- zinc alloy
- nickel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a zinc alloy die casting rose gold's cladding material structure, including the zinc alloy base member and with alkaline zinc-nickel alloy cladding material, chemical nickel coating, pyrophosphate copper plate, acid copper cladding material, bright nickel cladding material, palladium steel cladding material, rose gold cladding material that from inside to outside prepare in proper order on the zinc alloy base member. The utility model discloses a rose gold's cladding material structure is plated to environment-friendly, preparation technology environmental protection carries out neutral salt fog test 120 hours according to GB/T10125 + 2012 "artificial atmosphere corrosion test salt fog test", plates a surperficial no corrosive substance and generates, has good corrosion resistance.
Description
Technical Field
The utility model belongs to the metal plating field, concretely relates to zinc alloy die casting plates cladding material structure of rose gold.
Background
The rose gold plating layer is a thin and hard rose gold copper alloy plating layer, has bright color, high wear resistance and good ductility, is durable and does not change color, and is generally used as a decorative plating layer of high-end products such as jewelry and the like.
The traditional process for plating rose gold on zinc alloy die castings uses cyanide copper plating as a pre-plating layer, and since cyanide is a highly toxic compound, the use of cyanide is strictly prohibited by governments in various countries, and cyanide electroplating processes such as cyanide copper plating and the like are gradually eliminated in the global scope.
The zinc alloy die casting surface has more pores, the prior art adopts cyanide copper plating to seal the pores on the zinc alloy die casting surface, and the cyanide copper plating is used as a pre-plating layer of pyrophosphate copper plating. Under the background that cyanide is prohibited, how to adopt environment-friendly electroplating technology to replace cyanide copper plating is an urgent problem to be solved in the industry.
SUMMERY OF THE UTILITY MODEL
Including the problem of using the cyanide copper facing technology of high toxicity in order to solve the zinc alloy die casting rose gold plating, the utility model provides a zinc alloy die casting rose gold plating's cladding material structure. In order to achieve the purpose, the utility model adopts the following technical scheme:
a coating structure for plating rose gold on a zinc alloy die casting comprises a zinc alloy substrate, and an alkaline zinc-nickel alloy coating, a chemical nickel plating layer, a pyrophosphate copper plating layer, an acid copper coating, a bright nickel coating, a palladium steel coating and a rose gold coating which are sequentially prepared on the zinc alloy substrate from inside to outside.
In some embodiments, the thickness of the alkaline zinc-nickel alloy coating is 5-15 μm.
In some embodiments, the electroless nickel layer has a thickness of 1-5 μm.
In some embodiments, the pyrophosphate copper plating layer has a thickness of 5 to 10 μm.
In some embodiments, the thickness of the acid copper plating layer is 5-20 μm.
In some embodiments, the bright nickel coating has a thickness of 5-15 μm.
In some embodiments, the palladium steel plating layer has a thickness of 0.1 to 1 μm.
In some embodiments, the thickness of the rose gold coating is 0.1-0.5 μm.
The alkaline zinc-nickel alloy plating solution has higher dispersing capacity and deep plating capacity, the plating layer has higher corrosion resistance, and the alkaline zinc-nickel alloy plating on the zinc alloy die casting can effectively seal holes and improve the corrosion resistance. Chemical nickel plating can be carried out on the zinc-nickel alloy plating layer, pyrophosphate copper plating can be carried out on the chemical nickel plating layer, and the bonding force between the plating layers is good, so the zinc-nickel alloy plating layer and the chemical nickel plating layer can replace a cyanide copper plating layer.
The palladium steel plating layer is used as the bottom layer of the rose gold plating layer, so that gold atoms can be prevented from diffusing into bottom layer metal, and the thickness of the gold plating layer is reduced.
Compared with the prior art, the utility model discloses following beneficial effect has:
1. the utility model discloses a coating structure of rose gold plated on zinc alloy die castings, which adopts the electroplating alkaline zinc-nickel alloy to prepare a bottom coating, can effectively seal the pores on the surface layer of the zinc alloy die castings, and obviously improve the corrosion resistance of the coating;
2. the process of electroplating alkaline zinc-nickel alloy and chemically plating nickel to replace a cyanide copper plating process is adopted, so that the limitation of using highly toxic cyanide and potential safety hazard caused by the use of the highly toxic cyanide in the prior art are eliminated;
3. the palladium steel plating layer is used as the bottom layer of the rose gold plating layer, so that the thickness of the rose gold plating layer can be reduced, and the electroplating cost is reduced.
Drawings
The accompanying drawings, which are included to provide a further understanding of the invention and are incorporated in and constitute a part of this application, do not constitute a limitation of the invention, and in which:
FIG. 1 is a schematic diagram of the structure of the plating layer in examples 1 and 2 of the present invention.
Detailed Description
The invention will be described in detail with reference to the drawings and specific embodiments, wherein the exemplary embodiments and descriptions are provided to explain the invention, but not to limit the invention.
Example 1:
as shown in figure 1, the coating structure for rose gold plating of the zinc alloy die casting comprises a zinc alloy base body 1, and an alkaline zinc-nickel alloy coating 2, an electroless nickel coating 3, a pyrophosphate copper coating 4, an acid copper coating 5, a bright nickel coating 6, a palladium steel coating 7 and a rose gold coating 8 which are sequentially prepared on the zinc alloy base body 1 from inside to outside.
The thickness of the alkaline zinc-nickel alloy coating 2 is 5-7 mu m, and the alkaline zinc-nickel alloy coating is prepared by adopting the existing alkaline zinc-nickel alloy electroplating process.
The thickness of the chemical nickel-plating layer 3 is 2-3 mu m, and the chemical nickel-plating layer is prepared by adopting GG-182 alkaline chemical nickel-plating process of ultra-bonding chemical industry. The plating solution components and the operation conditions are as follows: 40-60 mL/L of GG-182A additive, 30-50 mL/L of GG-182B reducing agent, 30-50 mL/L of GG-182C stabilizer, 30-50 ℃ of operation temperature, 8.5-9.5 of pH range and 8-15 min of time.
The pyrophosphate copper plating layer 4 is 7-8 microns thick and is prepared by adopting the existing pyrophosphate copper plating process.
The thickness of the acid copper plating layer 5 is 13-15 mu m, and the acid copper plating layer is prepared by adopting the existing acid copper plating process.
The thickness of the bright nickel plating layer 6 is 10-12 mu m, and the bright nickel plating layer is prepared by adopting the existing bright nickel plating process.
The thickness of the palladium steel plating layer 7 is 0.3-0.5 mu m, and the palladium steel plating layer is prepared by a PALLASDIO 720 INOX palladium steel plating process of ultra-high chemical engineering. The plating solution components and the operation conditions are as follows: 995mL/L of PALLASDIO 720 INOX MPM palladium steel cylinder opening agent, 5mL/L of 50% ammonium chloride palladium solution by mass fraction, wherein the palladium content is 3.0-4.0 g/L, the pH range is 8.0-8.5, and the operation temperature is 3545 ℃ below zero and the cathode current density is 0.7A/dm DEG C2The cathode moves 3-5 m/min, and the electroplating time is 2-4 min.
The thickness of the rose gold plating layer 8 is 0.2-0.3 mu m, and the rose gold plating layer is prepared by adopting an RS-18 rose gold electroplating process of ultra-high chemical engineering. The plating solution is prepared from the following components under the operating conditions: the RS-18M rose gold jar opener agent is prepared, only a small amount of warm water is needed to dissolve potassium gold cyanide and then the potassium gold cyanide is added into the jar opener agent, RS-18CU rose gold copper water containing 10g/L copper is added according to the needed color tone to adjust the color of a plating layer, the gold content in the plating solution is 0.8-1.2 g/L, the copper content is 0.1-0.35 g/L, the pH range is 7.3-7.8, the operating temperature is 35-50 ℃, and the cathode current density is 1A/dm2The cathode moves for 4-6 m/min, and the electroplating time is 2-3 min.
The operation of the embodiment is divided into the following steps:
1. pretreatment: the zinc alloy part 1 is subjected to the steps of "chemical wax removal → water washing → ultrasonic wax removal → water washing → chemical degreasing → water washing → acid salt activation → water washing".
2. Electroplating alkaline zinc-nickel alloy: preparing an alkaline zinc-nickel alloy coating 2 on the pretreated zinc alloy substrate 1.
3. Chemical nickel plating: and preparing a chemical nickel-plating layer 3 on the zinc-nickel alloy plating layer 2 by adopting a GG-182 alkaline chemical nickel-plating process.
4. Pyrophosphate copper plating: a pyrophosphate copper plating layer 4 was prepared on the electroless nickel plating layer 3.
5. Acid copper plating: an acid copper plating layer 5 is prepared on the pyrophosphate copper plating layer 4.
6. Plating bright nickel: a bright nickel plating layer 6 is prepared on the acid copper plating layer 5.
7. Plating palladium steel: and preparing a palladium steel plating layer 7 on the bright nickel plating layer 6 by adopting a PALLASDIO 720 INOX palladium steel plating process.
8. Plating rose gold: and preparing a rose gold plating layer 8 on the palladium steel plating layer 7 by adopting an RS-18 rose gold electroplating process.
Example 2:
as shown in figure 1, the coating structure for rose gold plating of the zinc alloy die casting comprises a zinc alloy substrate 1, and an alkaline zinc-nickel alloy coating 2, an electroless nickel coating 3, a pyrophosphate copper coating 4, an acid copper coating 5, a bright nickel coating 6, a palladium steel coating 7 and a rose gold coating 8 which are sequentially prepared on the zinc alloy substrate 1 from inside to outside.
The thickness of the alkaline zinc-nickel alloy coating 2 is 8-10 mu m, and the alkaline zinc-nickel alloy coating is prepared by adopting the existing alkaline zinc-nickel alloy electroplating process.
The thickness of the chemical nickel-plating layer 3 is 2-3 mu m, and the chemical nickel-plating layer is prepared by adopting GG-178 alkaline chemical nickel-plating process of ultra-high chemical industry. The plating solution components and the operation conditions are as follows: 25-50 mL/L of GG-178A additive, 25-40 mL/L of GG-178B reducing agent, 30-60 mL/L of GG-178C stabilizer, 25-38 ℃ of operation temperature, 8.5-9.5 of pH value and 8-15 min of time.
The pyrophosphate copper plating layer 4 is 5-6 microns thick and is prepared by adopting the existing pyrophosphate copper plating process.
The thickness of the acid copper plating layer 5 is 15-18 mu m, and the acid copper plating layer is prepared by adopting the existing acid copper plating process.
The thickness of the bright nickel plating layer 6 is 8-10 mu m, and the bright nickel plating layer is prepared by adopting the existing bright nickel plating process.
The thickness of the palladium steel plating layer 7 is 0.5-0.7 mu m, and the palladium steel plating layer is prepared by a PALLASDIO 720 INOX palladium steel plating process of ultra-high chemical engineering. The plating solution components and the operation conditions are as follows: 995mL/L of PALLASDIO 720 INOX MPM palladium steel cylinder opening agent, 5mL/L of 50% ammonium chloride palladium solution by mass fraction, wherein the palladium content is 4.0-5.0 g/L, the pH range is 8.0-8.5, the operating temperature is 35-45 ℃, and the cathode current density is 0.9A/dm2The cathode moves 3-5 m/min, and the electroplating time is 2.5-4 min.
The thickness of the rose gold plating layer 8 is 0.3-0.5 mu m, and the rose gold plating layer is prepared by an RS-18 rose gold electroplating process of ultra-high chemical engineering. The plating solution is prepared from the following components under the operating conditions: the RS-18M rose gold jar opener agent is prepared, only a small amount of warm water is needed to dissolve potassium gold cyanide and then the potassium gold cyanide is added into the jar opener agent, RS-18CU rose gold copper water containing 10g/L copper is added according to the needed color tone to adjust the color of a plating layer, the gold content in the plating solution is 1.0-1.5 g/L, the copper content is 0.1-0.35 g/L, the pH range is 7.3-7.8, the operating temperature is 35-50 ℃, and the cathode current density is 1.5A/dm2The cathode moves for 4-6 m/min, and the electroplating time is 3-5 min.
The operation of the embodiment is divided into the following steps:
1. pretreatment: the zinc alloy die casting 1 is subjected to the steps of "chemical wax removal → water washing → ultrasonic wax removal → water washing → chemical degreasing → water washing → acid salt activation → water washing".
2. Electroplating zinc-nickel alloy: preparing an alkaline zinc-nickel alloy coating 2 on the pretreated zinc alloy substrate 1.
3. Chemical nickel plating: and preparing a chemical nickel-plating layer 3 on the zinc-nickel alloy plating layer 2 by adopting a GG-178 alkaline chemical nickel-plating process.
4. Pyrophosphate copper plating: pyrophosphate copper plating 4 was prepared on the electroless nickel plating layer 3.
5. Acid copper plating: an acid copper plating layer 5 is prepared on the pyrophosphate copper plating layer 4.
6. Plating bright nickel: a bright nickel plating layer 6 is prepared on the acid copper plating layer 5.
7. Plating palladium steel: and preparing a palladium steel plating layer 7 on the bright nickel plating layer 6 by adopting a PALLASDIO 720 INOX palladium steel plating process.
8. Plating rose gold: and preparing a rose gold plating layer 8 on the palladium steel plating layer 7 by adopting an RS-18 rose gold electroplating process.
The plated articles prepared in examples 1 and 2 were tested for plating adhesion by thermal shock test according to JB 2111-. And (3) heating the plated part to 190 ℃ in a heating furnace, taking out the plated part, and placing the plated part into water at room temperature for sudden cooling, wherein the plated layer does not generate bubbles and fall off, and the plated layer has good bonding force.
The electroplated parts prepared in the embodiments 1 and 2 are subjected to a neutral salt spray test for 120h according to GB/T10125-2012 salt spray test for artificial atmosphere corrosion test, and no corrosive substances are generated on the surfaces of the electroplated parts.
The technical solutions provided by the embodiments of the present invention are described in detail above, and the principles and embodiments of the present invention are explained herein by using specific examples, and the descriptions of the above embodiments are only applicable to help understand the principles of the embodiments of the present invention; meanwhile, for a person skilled in the art, according to the embodiments of the present invention, there may be variations in the specific implementation manners and application ranges, and in summary, the content of the description should not be construed as a limitation to the present invention.
Claims (7)
1. The utility model provides a zinc alloy die casting plates cladding material structure of rose gold which characterized in that: the zinc alloy plating layer is characterized by comprising a zinc alloy substrate, and an alkaline zinc-nickel alloy plating layer, a chemical nickel plating layer, a pyrophosphate copper plating layer, an acid copper plating layer, a bright nickel plating layer, a palladium steel plating layer and a rose gold plating layer which are sequentially prepared on the zinc alloy substrate from inside to outside;
the thickness of the rose gold coating is 0.1-0.5 mu m.
2. The coating structure for rose gold coating of zinc alloy die castings according to claim 1, characterized in that: the thickness of the alkaline zinc-nickel alloy coating is 5-15 mu m.
3. The plating structure of rose gold plating of zinc alloy die casting of claim 1, wherein: the thickness of the chemical nickel-plating layer is 1-5 mu m.
4. The plating structure of rose gold plating of zinc alloy die casting of claim 1, wherein: the pyrophosphate copper plating layer is 5-10 μm thick.
5. The plating structure of rose gold plating of zinc alloy die casting of claim 1, wherein: the thickness of the acid copper plating layer is 5-20 mu m.
6. The plating structure of rose gold plating of zinc alloy die casting of claim 1, wherein: the thickness of the bright nickel coating is 5-15 mu m.
7. The plating structure of rose gold plating of zinc alloy die casting of claim 1, wherein: the thickness of the palladium steel coating is 0.1-1.0 mu m.