CN212340833U - Be used for mandrel to weave carbon-carbon composite material ultra-high temperature tensile test anchor clamps - Google Patents
Be used for mandrel to weave carbon-carbon composite material ultra-high temperature tensile test anchor clamps Download PDFInfo
- Publication number
- CN212340833U CN212340833U CN202021668030.7U CN202021668030U CN212340833U CN 212340833 U CN212340833 U CN 212340833U CN 202021668030 U CN202021668030 U CN 202021668030U CN 212340833 U CN212340833 U CN 212340833U
- Authority
- CN
- China
- Prior art keywords
- joint
- shaped
- shaped joint
- carbon
- sample
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses an ultra-high temperature tensile test fixture for weaving carbon-carbon composite material by a mandrel, which consists of a cylindrical joint, a T-shaped joint, positioning tiles and heat-insulating rubber; the cylindrical joint is connected with the material testing machine through a pin; the lower part of the cylindrical joint is provided with a T-shaped groove for installing the T-shaped joint, and the wall surface of the T-shaped groove is pasted with heat insulation rubber for protecting heat transferred by the T-shaped joint when a sample is heated, and meanwhile, the T-shaped groove can play an insulating role. The T-shaped joint is used for being matched with the positioning tile, the positioning tile is of a semicircular platform structure, the outer conical surface is matched with the inner conical surface at the lower part of the T-shaped joint, and the inner side surface is matched with the outer conical surface of the sample clamping section; the fixture was used to test the tensile strength of the material. The tensile test fixture is simple in structure, convenient to install and disassemble, capable of accurately installing the sample in place, capable of improving the coaxiality of the axis of the sample and the axis of the fixture during installation and capable of improving the accuracy of measurement. The fixture has strong universality and can be suitable for ultra-high temperature tensile tests of other composite materials.
Description
Technical Field
The utility model relates to a be used for the mandrel to weave carbon-carbon composite material ultra-high temperature tensile test anchor clamps, specifically speaking relates to an ultra-high temperature tensile test anchor clamps that is used for the mandrel to weave carbon-carbon composite material, tests tensile strength, belongs to solid rocket engine design and tensile test equipment technical field.
Background
In the prior art, the temperature of key thermal structure components such as a throat insert, an expansion section and the like of a solid rocket engine is up to 2200 ℃ or above during working, the used material is a carbon-carbon composite material, the measurement of the tensile strength of the carbon-carbon composite material at 2200 ℃ is a key test technology, and the carbon-carbon composite material plays an important role in the design of the solid rocket engine.
The Chinese invention patent CN104931342A discloses a multifunctional high-temperature tensile clamp, which has no positioning function for the installation of a sample, cannot ensure the coaxiality of the axis of the sample and the clamp, can generate an additional bending moment on the sample to influence the test result, and the sample contacts at the corners of a clamping groove 6 and a lead groove 7 to generate stress concentration, and can be damaged at the chamfers of the clamping section and the test section of the sample during the test to make the test result invalid.
The invention patent CN209979394U discloses a ceramic matrix composite ultra-high temperature stretching combined clamp, wherein a sample of the ultra-high temperature stretching combined clamp cannot ensure the coaxiality with the clamp after being installed, so that an additional bending moment is generated on the sample to influence the test result, the sample is a thin plate, the coaxial positioning requirement after being installed is higher, the clamp can only be used for the plate, and a shaft rod woven carbon/carbon composite material can only be processed into a cylindrical sample for testing due to the structural particularity of the plate.
The clamp and the clamping method for testing the ultrahigh-temperature tensile property of the conductor material, which are provided by the invention patent CN107894365A, adopt a cooling system, increase the complexity of the clamp, make the installation of the sample more complicated and the positioning effect poor, need to liner graphite paper for centering and positioning, and the graphite paper has lower strength of only about 4MPa, is easy to damage during the test, and on one hand, the centering and positioning effect is lost, and on the other hand, the clamping section of the sample is damaged due to uneven heating and increased thermal stress.
Therefore, an ultrahigh-temperature tensile test fixture for testing tensile strength of the carbon-carbon composite material woven by the mandrel needs to be developed, so that the defects and limitations of the ultrahigh-temperature tensile test of the carbon-carbon composite material woven by the mandrel in the prior art are avoided, and the development of the ultrahigh-temperature tensile test is guaranteed.
SUMMERY OF THE UTILITY MODEL
In order to avoid the defects of the prior art, the utility model provides an ultra-high temperature tensile test fixture for weaving carbon-carbon composite material by using a shaft rod; the fixture is used for testing the tensile strength of materials, has simple structure, convenient processing, convenient installation and disassembly, can accurately install a sample in place, improves the coaxiality of the axis of the sample and the axis of the fixture during installation, and improves the accuracy of measurement.
The technical scheme adopted by the utility model for solving the technical problems is that the device comprises a cylindrical joint, a T-shaped joint, a positioning tile and heat-insulating rubber, wherein a round through hole is arranged at the upper part of the cylindrical joint, the cylindrical joint is connected with a material testing machine through a pin, a T-shaped groove is arranged at the lower part of the cylindrical joint for installing the T-shaped joint, and the heat-insulating rubber is pasted on the wall surface of the T-shaped groove and used for protecting heat transferred by the T-shaped joint when a sample is heated, protecting the cylindrical joint and playing a role of insulation; the T-shaped joint is matched with the T-shaped groove of the cylindrical joint;
the upper part and the lower part of the T-shaped joint are of an integral structure, the upper part of the T-shaped joint is a cuboid, the middle part of the cuboid is provided with a circular through hole, the lower part of the T-shaped joint is a cylinder, a round table-shaped through hole is arranged in the cylinder, the centers of the upper part and the lower part of the T-shaped joint through hole are positioned on a central axis of the T-shaped joint, the T-shaped joint is used for being matched with a positioning tile, the diameter of the minimum section of the T-shaped joint is larger than the maximum diameter of;
the positioning tile is of a semicircular table arc-shaped structure, the taper of the positioning tile is 5 degrees, the outer conical surface of the positioning tile is matched with the inner conical surface of the circular table hole in the lower portion of the T-shaped joint, and the inner side surface of the positioning tile is matched with the outer conical surface of the sample clamping section.
The positioning tiles are made of high-strength graphite T705.
The heat insulation rubber is made of silicon rubber, and the thickness of the rubber layer is 5 mm.
The axes of the cylindrical joint and the T-shaped joint are coaxial.
Advantageous effects
The utility model provides a carbon-carbon composite material ultra-high temperature tensile test fixture for shaft weaving, which consists of a cylindrical joint, a T-shaped joint, positioning tiles and heat-insulating rubber; wherein, the cylinder connects and is used for being connected with material testing machine, and the cylinder connects the lower part to have T type groove installation T type to connect, and the wall in cylinder joint T type groove is pasted thermal insulation rubber for the heat by T type joint transmission when the protection sample heats can play insulating effect simultaneously. The T-shaped joint and the cylindrical joint are matched with the positioning tiles, and the diameter of the T-shaped joint and the cylindrical joint at the minimum section is larger than the maximum diameter of the test sample, so that the test sample can pass through the T-shaped joint and the cylindrical joint. The positioning tile is of a semicircular platform structure, the outer conical surface is matched with the inner conical surface at the lower part of the T-shaped joint, and the inner side surface is matched with the outer conical surface of the sample clamping section.
The utility model discloses anchor clamps simple structure, processing is convenient, and it is convenient to install, dismantle, can install the sample accuracy in place, and the axiality of sample axis and anchor clamps axis improves the measuring accuracy when improving the installation, and the frock has insulating and thermal-insulated characteristics simultaneously, can protect operating personnel and test instrument.
The utility model discloses the anchor clamps commonality is strong, and its structure size that only changes the location tile can be tested the test sample of unidimensional not, still can be applicable to other combined material's ultra-temperature tensile test.
Drawings
The following provides a further detailed description of the clamp for the ultra-high temperature tensile test of carbon-carbon composite material woven by the mandrel, in conjunction with the accompanying drawings and the embodiments.
Figure 1 is the utility model discloses tensile test anchor clamps's cylinder connects the schematic diagram.
Fig. 2 is the T-shaped joint structure diagram of the tensile test fixture of the present invention.
(a) T-joint axonometric view (b) T-joint axonometric view.
Figure 3 is the utility model discloses tensile test anchor clamps's location tile structure chart.
FIG. 4 is a schematic view of the fixture for ultra-high temperature tensile test of carbon-carbon composite material woven by mandrel bars according to the present invention;
(a) fixture installation schematic diagram (b) fixture installation cross-sectional diagram (c) fixture installation axis mapping.
In the drawings
1. Cylindrical joint 2, T-shaped joint 3, positioning tile 4, heat-insulating rubber 5 and sample
Detailed Description
The embodiment is a clamp for a shaft rod weaving carbon-carbon composite material ultra-high temperature tensile test.
Referring to fig. 1 to 4, the fixture for the ultra-high temperature tensile test of the carbon-carbon composite material woven by the mandrel in the embodiment is composed of two cylindrical joints 1, two T-shaped joints 2, four positioning tiles 3 and heat insulation rubber 4; wherein, the upper part of the cylindrical joint 1 is provided with a cylindrical through hole which is connected with a material testing machine through a pin; the lower part of the cylindrical joint 1 is provided with a T-shaped groove for installing the T-shaped joint 2, the depth of the groove of the T-shaped groove is a set value, the rear view surface of the T-shaped groove is a positioning surface, and after the T-shaped joint 2 is installed in place, the T-shaped groove is attached to the back surface of the T-shaped groove, and the cylindrical joint 1 and the T-shaped joint 2 are coaxial in axis. The wall in T type groove is pasted thermal insulation rubber 4, and thermal insulation rubber 4's material is the silicon rubber, and thickness is 5mm, and thermal insulation rubber 4 is used for preventing that the heat that the sample produced when heating is transmitted for cylindrical joint 1 by T type joint 2, prevents that cylindrical joint 1 high temperature from becoming invalid, and it still has the insulating effect, and when the heating method of sample was ohmic heating, can prevent that too big electric current from causing the damage to test instrument. The material of the cylindrical joint 1 is heat-resistant alloy.
In this embodiment, 2 upper portions and the lower part combination structure as an organic whole are connected to the T type, 2 upper portions are connected to the T type and are the cuboid, the cuboid middle part is opened there is circular through-hole, 2 lower parts are connected to the T type and are the cylinder, the inside round platform shape through-hole that is equipped with of cylinder, and 2 upper portions and the lower part through-hole center that connect of T type are located the T type and connect the axis, the T type connect 2 be used for with location tile 3 cooperation, the diameter of its minimum cross-section department is greater than the maximum diameter of sample, can make location tile 3 pass from it. The lower cylinder of the T-shaped joint 2 is internally provided with a circular truncated cone-shaped through hole, and the taper of the side conical surface of the through hole is 5 degrees and is used for being matched with the positioning tile 3. The material of the T-shaped joint 2 is high-strength graphite T705.
The positioning tile 3 is of a semicircular table structure, the taper of the positioning tile is 5 degrees, an outer conical surface is matched with a conical surface in a circular table hole at the lower part of the T-shaped joint, and the inner side surface of the positioning tile is matched with an outer conical surface of the sample holding section; the material of the positioning tiles 3 is high-strength graphite T705.
Mode of operation
Two cylindrical joints 1 are respectively fixed at two ends of a material testing machine, and the distance between the two cylindrical joints 1 is adjusted. Inserting a sample 5 from the lower part of a T-shaped joint 2, inserting a pair of positioning tiles 3 from the upper part of the T-shaped joint 2 after inserting, installing the positioning tiles on the outer conical surface of the sample 5, then pulling back the positioning tiles in the opposite direction of the insertion of the sample 5, fixing one end of the positioning tiles 3 and one end of the sample 5 on one T-shaped joint 2, fixing the other end of the sample 5 on the other T-shaped joint 2 according to the method, and then slowly pushing the two T-shaped joints 2 with the sample 5 installed into the T-shaped groove of a cylindrical joint 1 until the side surfaces of the T-shaped joints 2 are attached to the back surface of the T-shaped groove, wherein the distance between the two cylindrical joints 1 is required to enable the sample 5 not to be pulled. Then slowly adjusting the distance between the two ends of the testing machine, and slightly shaking the sample 5 to ensure that the testing machine displays 10N of tensile force; by means of the positioning effect of the positioning tile 3, the sample 5 and the T-shaped joint 2 in conical surface fit, the sample 5 can be ensured to be coaxial with the clamp, and the sample 5 is installed in place at the moment.
Claims (4)
1. The clamp for the ultra-high-temperature tensile test of the carbon-carbon composite material woven by the mandrel is characterized by comprising a cylindrical joint, a T-shaped joint, positioning tiles and heat-insulating rubber, wherein a round through hole is formed in the upper part of the cylindrical joint, the cylindrical joint is connected with a material testing machine through a pin, a T-shaped groove is formed in the lower part of the cylindrical joint and used for mounting the T-shaped joint, and the heat-insulating rubber is adhered to the wall surface of the T-shaped groove and used for protecting heat transferred by the T-shaped joint when a sample is heated and protecting the cylindrical joint and playing a role in insulation; the T-shaped joint is matched with the T-shaped groove of the cylindrical joint;
the upper part and the lower part of the T-shaped joint are of an integral structure, the upper part of the T-shaped joint is a cuboid, the middle part of the cuboid is provided with a circular through hole, the lower part of the T-shaped joint is a cylinder, a round table-shaped through hole is arranged in the cylinder, the centers of the upper part and the lower part of the T-shaped joint through hole are positioned on a central axis of the T-shaped joint, the T-shaped joint is used for being matched with a positioning tile, the diameter of the minimum section of the T-shaped joint is larger than the maximum diameter of;
the positioning tile is of a semicircular table arc-shaped structure, the taper of the positioning tile is 5 degrees, the outer conical surface of the positioning tile is matched with the inner conical surface of the circular table hole in the lower portion of the T-shaped joint, and the inner side surface of the positioning tile is matched with the outer conical surface of the sample clamping section.
2. The fixture for the ultra-high temperature tensile test of the carbon-carbon composite material woven by the mandrel as claimed in claim 1, wherein the positioning tiles are made of high-strength graphite T705.
3. The fixture for the ultra-high temperature tensile test of the carbon-carbon composite material woven by the mandrel as claimed in claim 1, wherein the heat-insulating rubber is made of silicon rubber, and the thickness of the rubber layer is 5 mm.
4. The fixture for the ultra-high temperature tensile test of the carbon-carbon composite material woven by the mandrel as claimed in claim 1, wherein the axis of the cylindrical joint is coaxial with the axis of the T-shaped joint.