CN209920697U - Crease-resistant high elasticity blending tweed surface fabric - Google Patents
Crease-resistant high elasticity blending tweed surface fabric Download PDFInfo
- Publication number
- CN209920697U CN209920697U CN201920080378.5U CN201920080378U CN209920697U CN 209920697 U CN209920697 U CN 209920697U CN 201920080378 U CN201920080378 U CN 201920080378U CN 209920697 U CN209920697 U CN 209920697U
- Authority
- CN
- China
- Prior art keywords
- layer
- wrinkle
- tweed
- elasticity
- warp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a crease-resistant high elasticity blending tweed surface fabric, including basic unit, close skin layer, elastic layer and fire-retardant layer, the basic unit includes first warp and second woof, and first warp weaves into plain weave with first woof, and the basic unit bottom surface is sewed up with close skin layer through the thin spinning silk thread, the utility model discloses a ventilative layer is made up for thin tweed fine hair, and the texture is slim and graceful, the feel is smooth, the hygroscopicity is good, and is provided with the bleeder vent on ventilative layer, and the gas permeability is better, is convenient for the heat to scatter and disappear; the first anti-wrinkle layer and the second anti-wrinkle layer are both woven into a mesh shape by the PPT fibers, the mesh diameter is 2 mm, the elongation recovery performance of the anti-wrinkle high-elasticity blended tweed fabric can be improved, the 2 mm meshes can effectively recover a wrinkle area, and the anti-wrinkle effect is greatly improved.
Description
Technical Field
The utility model relates to a textile fabric technical field that is relevant specifically is an anti-wrinkle high elasticity blending tweed surface fabric.
Background
With the continuous improvement of living standard and the continuous development of science and technology, the textile fabrics meeting different requirements of people emerge endlessly, the requirements of people on the performance of clothes are also continuously improved, and the surface crease resistance, the soft hand feeling and the wearing comfort of the fabrics are more and more concerned by people. Various tights with elasticity and novel styles sold in the market are very depended by young people, but the existing fabrics have insufficient elasticity and poor air permeability, so that the clothes are very uncomfortable to wear, the phenomena of sultriness, moist underwear and the like are caused, and the comfort level of a human body is seriously influenced. And the clothes processed by part of the fabrics can have wrinkles after being washed and aired, so that the attractiveness of the clothes to be worn next time is influenced, the anti-wrinkle fabrics are good in extensibility and poor in soft handfeel, the comfortableness is greatly influenced, and the anti-wrinkle performance needs to be further improved, so that the anti-wrinkle high-elasticity blended tweed fabric is provided for solving the problems.
SUMMERY OF THE UTILITY MODEL
In order to solve the defects existing in the prior art, the utility model provides a crease-resistant high elasticity blending tweed surface fabric.
In order to solve the technical problem, the utility model provides a following technical scheme:
the utility model relates to an anti-wrinkle high elasticity blending tweed fabric, including basic unit, skin-friendly layer, elastic layer and fire-retardant layer, the basic unit includes first warp and second woof, first warp is woven with first woof and is plain weave, the basic unit underrun is sewed up with skin-friendly layer through thin spinning silk thread, basic unit upper surface hot pressing complex has first anti-wrinkle layer, first anti-wrinkle layer upper surface bonds through hot melt adhesive and elastic layer, elastic layer includes nylon fiber and spandex, and nylon fiber and spandex spiral weaving, elastic layer upper surface bonds through the hot melt adhesive has the anti-wrinkle layer of second, the anti-wrinkle layer upper surface hot pressing complex of second has ventilative layer, ventilative layer upper surface is sewed up through thin spinning line and fire-retardant layer.
As an optimized technical solution of the present invention, the first warp yarn is composed of the australian hair with an average fineness of 16.5 micrometers and an average length of 86 millimeters, and the first warp yarn accounts for 80% of the total mass of the base layer.
As an optimized technical scheme of the utility model, first woof comprises triangle dysmorphism silk, and first woof accounts for 20% of basic unit's total mass.
As an optimal technical scheme of the utility model, this surface fabric still includes second warp, second woof and third warp, the second warp is the bamboo fibre, the second woof is hydrophilicity polyester fiber, the third warp is mulberry silk, and the total mass ratio of second warp, second woof and third warp is 3: 4: 3.
as an optimal technical scheme of the utility model, the elastic layer upper and lower two sides all are provided with the buffer layer with first anti-wrinkle layer and the anti-wrinkle layer junction of second, and just two sets of buffer layers constitute by sponge fiber.
As an optimized technical scheme of the utility model, first anti-wrinkle layer and second anti-wrinkle layer are woven into netted by the PPT fibre, and the mesh diameter is 2 mm.
As a preferable technical solution of the present invention, the thickness of the first anti-wrinkle layer is 0.3 mm, and the thickness of the second anti-wrinkle layer is 0.15 mm.
As an optimized technical scheme of the utility model, ventilative layer is constituteed for thin tweed fine hair, and is provided with the bleeder vent on ventilative layer.
As an optimal technical scheme of the utility model, fire-retardant layer includes FBI fibre and chlorine silk thread, FBI fibre hot pressing is compound in chlorine silk thread top, and FBI fibre and the reverse winding of chlorine silk thread.
Compared with the prior art, the beneficial effects of the utility model are that:
(1) the utility model discloses a second warp is bamboo fibre, and the second woof is hydrophilicity polyester fiber, and the third warp is mulberry silk, and the total mass ratio of second warp, second woof and third warp is 3: 4: 3, bamboo fibre is hygroscopic, ventilative and have antibiotic effect, and hydrophilicity polyester fiber has fine hygroscopicity, the heat dissipation of being convenient for, and mulberry silk texture is soft, and the sense of touch is good, and the close skin layer travelling comfort that the three warp and weft interweaved and form is strong.
(2) The utility model discloses a ventilative layer comprises for thin tweed fine hair, and the texture is slim and graceful, feels smooth, the hygroscopicity is good, and is provided with the bleeder vent on ventilative layer, and the gas permeability is better, and the heat of being convenient for scatters and disappears.
(3) The utility model discloses a two sides all are provided with the buffer layer with first anti-wrinkle layer and the anti-wrinkle layer junction of second about the elastic layer, and two sets of buffer layers constitute by sponge fiber, can play fine cushioning effect, and effectual protection elastic layer does not receive the damage, and life is longer.
(4) The utility model discloses a first anti-wrinkle layer is knitted into netted by the PPT fibre with the anti-wrinkle layer of second, and the mesh diameter is 2 mm, can improve the extension recovery nature of this anti-wrinkle high elasticity blending tweed surface fabric, and 2 mm's mesh can effectively resume the fold district, and anti-wrinkle effect improves greatly.
(5) The utility model discloses a fire-retardant layer includes FBI fibre and chlorine silk thread, and FBI fibre hot pressing is compound in chlorine silk thread top, and FBI fibre and the reverse winding of chlorine silk thread, can play fine flame retardant efficiency, avoids external combustion gas to permeate in this crease-resistant high elasticity blending tweed surface fabric simultaneously.
Drawings
The accompanying drawings are included to provide a further understanding of the invention, and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention, and together with the description serve to explain the invention and not to limit the invention. In the drawings:
FIG. 1 is a schematic structural view of the present invention;
FIG. 2 is a schematic diagram of the basic structure of the present invention;
fig. 3 is a schematic view of the structure of the skin-friendly layer of the present invention;
FIG. 4 is a schematic view of the elastic layer structure of the present invention;
fig. 5 is a schematic view of the structure of the flame retardant layer of the present invention.
In the figure: the base layer 1, the first warp yarn 11, the first weft yarn 12, the skin-friendly layer 2, the second warp yarn 21, the second weft yarn 22, the third warp yarn 23, the first anti-wrinkle layer 3, the elastic layer 4, the nylon fiber 41, the spandex 42, the buffer layer 5, the second anti-wrinkle layer 6, the breathable layer 7, the air vents 8, the flame retardant layer 9, the FBI fiber 91 and the polyvinyl chloride wire 92.
Detailed Description
The preferred embodiments of the present invention will be described in conjunction with the accompanying drawings, and it will be understood that they are presented herein only to illustrate and explain the present invention, and not to limit the present invention.
Example (b):
referring to fig. 1, fig. 2, fig. 3, fig. 4 and fig. 5 show, the utility model relates to an anti-wrinkle high elasticity blending tweed surface fabric, including basic unit 1, skin-friendly layer 2, elastic layer 4 and fire-retardant layer 9, basic unit 1 includes first warp 11 and first woof 12, first warp 11 is woven with first woof 12 and is plain weave, basic unit 1 bottom surface is sewed up with skin-friendly layer 2 through fine spinning thread, basic unit 1 upper surface hot-pressing complex has first anti-wrinkle layer 3, first anti-wrinkle layer 3 upper surface bonds with elastic layer 4 through the hot melt adhesive, elastic layer 4 includes nylon fiber 41 and spandex 42, and nylon fiber 41 and spandex 42 spiral weaving, elastic layer 4 upper surface bonds through the hot melt adhesive has second anti-wrinkle layer 6, second anti-wrinkle layer 6 upper surface hot-pressing complex has ventilative layer 7, ventilative layer 7 upper surface is sewed up through fine spinning line and fire-retardant layer 9.
Referring to fig. 2, the first warp yarn 11 has a composition with an average fineness of 16.5 μm and an average length of 86 mm, and the first warp yarn 11 accounts for 80% of the total mass of the base layer 1.
Referring to fig. 2, the first weft yarns 12 are composed of delta shaped yarns, and the first weft yarns 12 account for 20% of the total mass of the base layer 1.
Referring to fig. 3, the second warp 21 is a bamboo fiber, the second weft 22 is a hydrophilic polyester fiber, the third warp 23 is a mulberry silk, and the total mass ratio of the second warp 21, the second weft 22, and the third warp 23 is 3: 4: 3, bamboo fiber 21 absorbs moisture, ventilative and have antibiotic effect, and hydrophilicity polyester fiber 22 has fine hygroscopicity, the heat dissipation of being convenient for, 23 soft texture of mulberry silk, the sense of touch is good, and the close skin layer travelling comfort that the three warp and weft interweaved and form is strong.
Referring to fig. 1, the buffer layers 5 are arranged at the joints of the upper surface and the lower surface of the elastic layer 4, the first anti-wrinkle layer 3 and the second anti-wrinkle layer 6, and the two groups of buffer layers 5 are made of sponge fibers, so that a good buffering effect can be achieved, the elastic layer 4 is effectively protected from being damaged, and the service life is longer.
Referring to fig. 1, the first anti-wrinkle layer 3 and the second anti-wrinkle layer 6 are both woven by PPT fibers into meshes, and the mesh diameter is 2 mm, so that the elongation recovery performance of the anti-wrinkle high-elasticity blended tweed fabric can be improved, the 2 mm mesh can effectively recover a wrinkle region, and the anti-wrinkle effect is greatly improved.
Referring to fig. 1, the first anti-wrinkle layer 3 has a thickness of 0.3 mm, and the second anti-wrinkle layer 6 has a thickness of 0.15 mm.
Referring to fig. 1, the air permeable layer 7 is made of tweed, has light texture, smooth hand feeling and good hygroscopicity, and the air permeable holes 8 are arranged on the air permeable layer 7, so that the air permeability is better and the heat dissipation is facilitated.
Referring to fig. 1 and 5, the flame retardant layer 9 includes FBI fibers 91 and polyvinyl chloride fiber yarns 92, the FBI fibers 91 are hot-pressed and compounded on the polyvinyl chloride fiber yarns 92, and the FBI fibers 91 are reversely wound with the polyvinyl chloride fiber yarns 92, so that a good flame retardant effect can be achieved, and external combustion gas is prevented from permeating into the anti-wrinkle high-elasticity blended tweed fabric.
The working principle is as follows: the base layer 1 is woven by Australian wool and triangular special-shaped silk into plain weave, the texture is soft, the gloss is bright, the bamboo fiber 21 absorbs moisture, is breathable and has an antibacterial effect, the hydrophilic polyester fiber 22 has good moisture absorption and is convenient to dissipate heat, the mulberry silk 23 is soft in texture and good in touch feeling, a skin-friendly layer formed by interweaving the three warps and wefts is high in comfort, the elastic layer 4 comprises nylon fibers 41 and spandex 42, the nylon fibers 41 and the spandex 42 are spirally woven, the elasticity is sufficient in moisture absorption, the buffer layer 5 formed by two groups of sponge fibers can play a good buffering role, the elastic layer 4 is effectively protected from being damaged and is longer in service life, the first anti-wrinkle layer 3 and the second anti-wrinkle layer 6 are both woven into meshes by the nylon fibers, the mesh diameter is 2 mm, the elongation recovery performance of the anti-wrinkle high-elasticity blended tweed fabric can be improved, and the mesh opening of 2 mm can effectively recover a, the crease-resistant effect is greatly improved, the breathable layer 7 is composed of tweed velvet, the texture is light, the hand feeling is smooth, the moisture absorption is good, the breathable holes 8 are formed in the breathable layer 7, the breathability is better, heat dissipation is facilitated, a good flame-retardant effect can be achieved through the flame-retardant layer 9 composed of the FBI fibers 91 and the polyvinyl chloride fiber silk threads 92, external combustion gas is prevented from permeating into the crease-resistant high-elasticity blended tweed fabric, the using method of the crease-resistant high-elasticity blended tweed fabric is the same, and the content which is not described in detail in the description belongs to the prior art which is well known by professionals in the field.
Finally, it should be noted that: although the present invention has been described in detail with reference to the foregoing embodiments, it will be apparent to those skilled in the art that modifications may be made to the embodiments described in the foregoing embodiments, or equivalents may be substituted for elements thereof. Any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (9)
1. The utility model provides an anti-wrinkle high elasticity blending tweed fabric, includes basic unit (1), skin-friendly layer (2), elastic layer (4) and fire-retardant layer (9), its characterized in that: the base layer (1) comprises first warp yarns (11) and first weft yarns (12), the first warp yarns (11) and the first weft yarns (12) are woven into plain weave, the bottom surface of the base layer (1) is sewn with a skin-friendly layer (2) through fine spinning threads, a first crease-resistant layer (3) is compounded on the upper surface of the base layer (1) in a hot pressing mode, the upper surface of the first crease-resistant layer (3) is bonded with an elastic layer (4) through hot melt glue, the elastic layer (4) comprises nylon fibers (41) and spandex (42), the nylon fibers (41) and the spandex (42) are woven in a spiral mode, a second crease-resistant layer (6) is bonded on the upper surface of the elastic layer (4) through hot melt glue, a ventilation layer (7) is compounded on the upper surface of the second crease-resistant layer (6) in a hot pressing mode, and the upper surface of the ventilation layer (7) is sewn with a flame-retardant layer (9) through fine spinning threads.
2. The anti-wrinkle high-elasticity blended tweed fabric according to claim 1, wherein the anti-wrinkle high-elasticity blended tweed fabric comprises the following components in percentage by weight: the first warp (11) is made of Australian wool with the average fineness of 16.5 micrometers and the average length of 86 millimeters, and the first warp (11) accounts for 80% of the total mass of the base layer (1).
3. The anti-wrinkle high-elasticity blended tweed fabric according to claim 1, wherein the anti-wrinkle high-elasticity blended tweed fabric comprises the following components in percentage by weight: the first weft yarns (12) are composed of triangular profiled filaments, and the first weft yarns (12) account for 20% of the total mass of the base layer (1).
4. The anti-wrinkle high-elasticity blended tweed fabric according to claim 1, wherein the anti-wrinkle high-elasticity blended tweed fabric comprises the following components in percentage by weight: the fabric further comprises second warp yarns (21), second weft yarns (22) and third warp yarns (23), wherein the second warp yarns (21) are bamboo fibers, the second weft yarns (22) are hydrophilic polyester fibers, the third warp yarns (23) are mulberry silks, and the total mass ratio of the second warp yarns (21), the second weft yarns (22) and the third warp yarns (23) is 3: 4: 3.
5. the anti-wrinkle high-elasticity blended tweed fabric according to claim 1, wherein the anti-wrinkle high-elasticity blended tweed fabric comprises the following components in percentage by weight: buffer layers (5) are arranged at the joints of the upper surface and the lower surface of the elastic layer (4) and the first anti-wrinkle layer (3) and the second anti-wrinkle layer (6), and the two groups of buffer layers (5) are composed of sponge fibers.
6. The anti-wrinkle high-elasticity blended tweed fabric according to claim 1, wherein the anti-wrinkle high-elasticity blended tweed fabric comprises the following components in percentage by weight: the first anti-wrinkle layer (3) and the second anti-wrinkle layer (6) are both woven into a mesh shape by PPT fibers, and the diameter of the mesh is 2 mm.
7. The anti-wrinkle high-elasticity blended tweed fabric according to claim 1, wherein the anti-wrinkle high-elasticity blended tweed fabric comprises the following components in percentage by weight: the thickness of the first anti-wrinkling layer (3) is 0.3 mm, and the thickness of the second anti-wrinkling layer (6) is 0.15 mm.
8. The anti-wrinkle high-elasticity blended tweed fabric according to claim 1, wherein the anti-wrinkle high-elasticity blended tweed fabric comprises the following components in percentage by weight: the breathable layer (7) is composed of thin tweed velvet, and the breathable layer (7) is provided with breathable holes (8).
9. The anti-wrinkle high-elasticity blended tweed fabric according to claim 1, wherein the anti-wrinkle high-elasticity blended tweed fabric comprises the following components in percentage by weight: the flame-retardant layer (9) comprises FBI fibers (91) and a polyvinyl chloride filament (92), the FBI fibers (91) are hot-pressed and compounded on the polyvinyl chloride filament (92), and the FBI fibers (91) are reversely wound with the polyvinyl chloride filament (92).