CN209352791U - Three-dimensional imaging coated glass - Google Patents
Three-dimensional imaging coated glass Download PDFInfo
- Publication number
- CN209352791U CN209352791U CN201821848590.3U CN201821848590U CN209352791U CN 209352791 U CN209352791 U CN 209352791U CN 201821848590 U CN201821848590 U CN 201821848590U CN 209352791 U CN209352791 U CN 209352791U
- Authority
- CN
- China
- Prior art keywords
- film layer
- glass
- layer
- glue
- coated glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model belongs to coated glass technical field, more particularly to a kind of three-dimensional imaging coated glass, the functional film layer that the UV glue-line of space pattern is set in the glass substrate and had including glass substrate, transfer and is covered on UV glue-line and makes the outer surface of glass substrate that space pattern imaging effect be presented, functional film layer are offline solar control coated glass membrane system layer or offline low-emission coated membrane system layer.The outer surface that the utility model realizes coated glass can show apparent three-dimensional pattern effect according to demand, the true qualities and performance of plated film functional layer are not influenced simultaneously, have good sunshade, translucency, not only having met does not influence film plating layer performance but also have both to meet space pattern demand, the not particular/special requirements such as tempering demand, high transparency demand, sun-shading requirements, ecological requirements.And then replaces the pattern patch printed on previous coated glass using stickup or carry out the imaging mode and product of the coating covering treatments such as ink, paint in glass surface.
Description
Technical field
The utility model belongs to coated glass technical field more particularly to a kind of three-dimensional imaging coated glass.
Background technique
Coated glass is in glass surface coating one or more layers metal, alloy or metal compound film, to change glass
The optical property of glass meets certain particular requirement.Coated glass kind currently on the market is more, and architectural design is also more and more
Sample, personalization.Coated glass daylighting, masking, heat transfer, color, in terms of have apparent progress, plate simultaneously
The dog-eat-dog of film glass power savings advantages is also gradually reducing, and with the development of building decoration aesthetics, people are in building energy conservation
Except demand, to the special decorative effect of architectural decorative glass or building glass, more stringent requirements are proposed.
Coated glass currently on the market is mostly that film layer covering is directly carried out on plate glass, in terms of display effect
Color diversity based on planar imaging effect, reflected intensity diversity are mainly reflected in, through intensity diversity, for a small amount of
The product for having pattern displaying to require is generally to carry out pasting the pattern patch printed in glass surface or carry out in glass surface
The coating covering treatment such as ink, paint.And pasting patterns patch is easy to appear bubble, there is also aging after of long duration, falls off, moves back
Situations such as color, at the same pasting patterns patch certain reduction can be caused to influence original glass transmission rate, cause glass translucent or
Person is opaque, blocks sight or causes the fuzzy and distortion through observation object;And the glass of the coating such as ink, paint processing is then
Just film layer can be made Nian Jie with glass by glass tempering or heating, drying, while glass surface covering ink, paint can also be made
It is translucent or opaque at glass, and coating has certain environmental contamination, is unfavorable for the popularization of environment-friendly products.In addition,
It is unfavorable that use of this two kinds of coverage modes on coated glass can cause film plating layer imaging effect and film performance on glass
It influences, reduces the functionality of film plating layer.It is had both again for neither influencing film plating layer performance and meets space pattern demand, not tempering need
It asks, the product of the Special displays such as high transparency demand, sun-shading requirements, ecological requirements or requirement, then above method can not achieve, and grind
Hair meets the product of these particular demands, is of great significance to the functionality for changing building glass with diversity.
Utility model content
The purpose of this utility model is to provide a kind of three-dimensional imaging coated glasses, it is intended to solve glass in the prior art
The technical issues of three-dimensional imaging pattern that surface is formed will affect plated film function.
A kind of in order to achieve the above purposes, the technical solution adopted by the utility model is: three-dimensional imaging coated glass, comprising:
Glass substrate;
UV glue-line, transfer are set in the glass substrate and have space pattern;
Functional film layer, be covered on the UV glue-line and make the outer surface of the glass substrate show space pattern at
As effect, the functional film layer is offline solar control coated glass membrane system layer or offline low-emission coated membrane system layer.
Preferably, the glass substrate is float flat glass substrate.
Preferably, the UV glue-line is the highly resistance scratch-type ultraviolet curing glue layer of clear, colorless.
Preferably, the functional film layer is made of one or more kinds of film layers.
Specifically, the film layer is SiO2Layer, Si3N4Film layer, AZO film layer, TZO film layer, ITO film layer, TCO film
Layer, Cu film layer, NiCr film layer, Ag film layer, MgF2Film layer, Al2O3Film layer, ZnO film layer, TiO2Film layer, SnO2Film layer, ZrO2Film
Layer or ZnSnO3Film layer.
Preferably, the functional film layer is covered in the UV glue-line by offline vacuum magnetron sputtering coating film process deposits
On.
Preferably, the space pattern is CD line, drawing pattern, cloudy surface, irregular decorative pattern or male and fomale(M&F).
Preferably, the three-dimensional imaging coated glass is by the glass substrate, the UV glue-line and the functional film layer structure
At.
The utility model has the beneficial effects that the three-dimensional imaging coated glass of the utility model, sharp on a glass substrate first
The various UV glue-lines with required transparent space pattern are transferred with UV roller mould, transfer glue, transfer printing process, secondly
The covering setting functional film layer on UV glue-line, using the body color of functional film layer, reflection, the adjusting of transmission, so that UV is transferred
Good space pattern shows apparent space pattern imaging effect, while the color shape of its pattern in the outer surface of glass substrate
State, bright-dark degree, depth degree can be controlled by the function of functional film layer.So it is achieved that the outer surface energy of coated glass
It is enough to show apparent three-dimensional pattern effect according to demand, while the true qualities and performance of plated film functional layer are not influenced, have good
Sunshade, translucency, not only met not influence film plating layer performance but also have both meet space pattern demand, tempering demand, it is high thoroughly
The particular/special requirements such as light rate demand, sun-shading requirements, ecological requirements.And then replace the figure printed on previous coated glass using stickup
Case patch carries out the imaging mode and product of the coating covering treatments such as ink, paint in glass surface, and improves and thus bring
The drawbacks of.To promote the upgrading of coated glass, realize that large area has the batch metaplasia of coated glass of three-dimensional imaging effect
It produces.
Detailed description of the invention
It, below will be to embodiment or the prior art in order to illustrate more clearly of the technical scheme in the embodiment of the utility model
Attached drawing needed in description is briefly described, it should be apparent that, the accompanying drawings in the following description is only that this is practical new
Some embodiments of type for those of ordinary skill in the art without any creative labor, can be with
It obtains other drawings based on these drawings.
Fig. 1 is the structural schematic diagram of three-dimensional imaging coated glass provided by the embodiment of the utility model.
Fig. 2 is the Section View of three-dimensional imaging coated glass provided by the embodiment of the utility model.
Wherein, each appended drawing reference in figure:
10-glass substrate 20-UV, 21-space patterns of glue-line
30-functional film layers.
Specific embodiment
The embodiments of the present invention are described below in detail, examples of the embodiments are shown in the accompanying drawings, wherein from beginning
Same or similar element or element with the same or similar functions are indicated to same or similar label eventually.Below by ginseng
The embodiment for examining the description of attached drawing 1~2 is exemplary, it is intended to for explaining the utility model, and should not be understood as practical to this
Novel limitation.
In the description of the present invention, it should be understood that term " length ", " width ", "upper", "lower", " preceding ",
The orientation or positional relationship of the instructions such as " rear ", "left", "right", "vertical", "horizontal", "top", "bottom" "inner", "outside" is based on attached
Orientation or positional relationship shown in figure, is merely for convenience of describing the present invention and simplifying the description, rather than indication or suggestion
Signified device or element must have a particular orientation, be constructed and operated in a specific orientation, therefore should not be understood as to this
The limitation of utility model.
In addition, term " first ", " second " are used for descriptive purposes only and cannot be understood as indicating or suggesting relative importance
Or implicitly indicate the quantity of indicated technical characteristic.Define " first " as a result, the feature of " second " can be expressed or
Implicitly include one or more of the features.The meaning of " plurality " is two or two in the description of the present invention,
More than, unless otherwise clearly specifically defined.
In the present invention unless specifically defined or limited otherwise, term " installation ", " connected ", " connection ", " Gu
It is fixed " etc. terms shall be understood in a broad sense, for example, it may be being fixedly connected, may be a detachable connection, or integral;It can be
Mechanical connection, is also possible to be electrically connected;It can be directly connected, two can also be can be indirectly connected through an intermediary
The interaction relationship of connection or two elements inside element.It for the ordinary skill in the art, can basis
Concrete condition understands the concrete meaning of above-mentioned term in the present invention.
As shown in Fig. 1~2, a kind of three-dimensional imaging coated glass provided by the embodiment of the utility model, including glass substrate
10, transfer is set in the glass substrate 10 and has the UV glue-line 20 of space pattern 21 and is covered on UV glue-line 20 and makes
The functional film layer 30 of space pattern imaging effect is presented in the outer surface for obtaining glass substrate, and functional film layer 30 is the control plating of offline sunlight
Membrane system layer or offline low-emission coated membrane system layer.
It is transferred first in glass substrate 10 using UV roller mould, transfer glue, transfer printing process various with required
Transparent space pattern 21 UV glue-line 20, secondly on UV glue-line 20 covering setting functional film layer 30, utilize functional film layer
30 body color, reflection, the adjusting of transmission, so that the space pattern 21 that UV has been transferred is showed in the outer surface of glass substrate
Apparent space pattern imaging effect, while the color state of its pattern, bright-dark degree, depth degree can be by functional film layers 30
Function control.So it is achieved that the outer surface of coated glass can show apparent space pattern 21 according to demand and imitate
Fruit, while the true qualities and performance of plated film functional layer are not influenced, have good sunshade, translucency, both meeting does not influence plated film
Layer performance has both again meets 21 demand of space pattern, the not spies such as tempering demand, high transparency demand, sun-shading requirements, ecological requirements
It is different to require.And then replaces the pattern patch printed on previous coated glass using stickup or carry out ink, oil in glass surface
The imaging mode and product of the coating covering treatments such as paint, and improve the drawbacks of thus bringing.To promote the upgrading of coated glass,
Realize that large area has the mass production of coated glass of three-dimensional imaging effect.
Preferably, the present embodiment is made of glass substrate 10, UV glue-line 20 and functional film layer 30.
UV glue-line 20 is the upper surface that glass substrate 10 is arranged in using the transfer of UV transfer printing process, since UV technology is one
Kind environmentally friendly green technology, the UV glue-line 20 used is using UV radiation curing, and speed is fast and reaction is controllable, simultaneously
Material is solvent-free, green and pollution-free, and adhesives is extensive, and adhesive strength is high, is suitble to automated job.UV transfer technique can
Transfer out the various perspective views such as 10 surface of glass substrate and back side CD line, drawing pattern, atomized surface effect, irregular decorative pattern, male and fomale(M&F)
Case 21.In addition optical property is excellent, and glue is colorless and transparent, and light transmittance is high and ultra-thin after UV glue-line 20 solidifies, can permanent retention product
Space pattern 21 it is as bright as new, it is noble dazzling, to 10 ontology of glass substrate and 30 body color of functional film layer or performance without bright
Development is rung.
In the present embodiment, the glass substrate 10 is float flat glass substrate.Since float glass is that glass floats on tin
It is made on the surface of liquid, the Pingdu of this kind of glass is preferable, no water ripples and is not easy out of shape.Secondly as float glass process
For glass mostly using ore quartz sand as raw material, raw material are good, and the glass produced is relatively pure, transparency is higher, while
There is no glass malignant boil and the other defects of bubble.In addition, float glass also has matter weight, close structure and feel
Smoothly, every square metre of same thickness than great, good cutting and not than plate glass cracky.Therefore, the present embodiment has
The coated glass of three-dimensional imaging effect preferably uses float glass as glass substrate 10, can improve the performance of glass finished-product.
In the present embodiment, the UV glue-line 20 is the highly resistance scratch-type ultraviolet curing glue layer of clear, colorless.
In the present embodiment, the functional film layer 30 is made of one or more kinds of film layers, the material membrane
Layer is SiO2Layer, Si3N4Film layer, AZO film layer, TZO film layer, ito film layer, TCO film layer, Cu film layer, NiCr film layer, Ag film layer,
MgF2Film layer, Al2O3Film layer, ZnO film layer, TiO2Film layer, SnO2Film layer, ZrO2Film layer or ZnSnO3Film layer.Functional film layer 30
Material and structure can be designed according to the concrete condition such as color, sunshade, heat preservation etc. of glass product use environment, to protect
Card effect is sufficient for subject to every requirement.For example, above-mentioned functional film layer 30 can be offline solar control coated glass membrane system
Layer, material is by Si3N4/NiCr/Si3N4It constitutes, or is offline low-emission coated membrane system layer, material is by SnO2/ ZnO/Ag/
NiCr/SnO2/ZrO2It constitutes.
In the present embodiment, the functional film layer 30 is covered in the UV by offline vacuum magnetron sputtering coating film process deposits
On glue-line 20.Specifically, since offline vacuum magnetic control cathode sputtering deposition technique has sputter coating speed fast, sputtering formation
Film layer is fine and close, adhesion is good and good evenness and be suitable in high volume, expeditiously industrial production the advantages of, while the property of film layer
Energy, color, light transmittance, reflectivity can be adjusted according to demand, have different sunshades, heat insulating ability, low diathermaneity.Cause
This deposits functional film layer 30 not only using offline vacuum magnetic control cathodic spattering technique herein and can be improved and UV glue-line 20
Between bond strength, in addition can by the transparent stereo pattern 21 on UV glue-line 20 by the characteristic of functional film layer 30 make its
The outer surface of glass substrate 10 shows, and realizes the sunshade of coated glass, heat insulating ability, low diathermaneity, while also can be improved
Production efficiency, the time cost for saving production.
In this way, by the setting of above-mentioned film layer structure and technique, realize coated glass space pattern 21 be imaged it is decorative and
It is functional.UV transfer technique can transfer out surface and back side CD line, drawing pattern, the atomized surface effect, irregular grain of glass substrate 10
The various space patterns 21 such as decorations, male and fomale(M&F).In addition optical property is excellent, and glue is colorless and transparent, and light transmittance is high after UV glue-line 20 solidifies
And it is ultra-thin, can permanent retention product space pattern 21 it is as bright as new, it is noble dazzling, to 10 ontology of glass substrate and functional membrane
The color or performance of 30 ontology of layer have no significant effect.Offline vacuum magnetic control cathodic spattering technique deposits functional film layer 30 not
The bond strength between UV glue-line 20 only can be improved, in addition can pass through the transparent stereo pattern 21 on UV glue-line 20
The characteristics such as color, translucency, the reflectivity of functional film layer 30 show it in the outer surface of glass substrate 10, while realizing plating
Film glass sunshade, heat insulating ability, low diathermaneity.Above-mentioned technology and function complement each other so that this has the plating of three-dimensional imaging effect
Film glass shows excellent functionality, while lower production costs, has wide development potentiality and the market space.
The manufacturing method of the three-dimensional imaging coated glass of the present embodiment includes the following steps: to produce UV transfer glass, production
Coated glass.
Specifically, the cleaning for carrying out cleaning machine to glass substrate 10 dries up, 20 DEG C~40 DEG C of the water temperature range of cleaning, water
Resistance range 8M Ω~20M Ω, pressure limit 0.15MPa~0.35MPa of water.The die coating UV of good pattern is formulated equipment
Glass substrate 10 after cleaning is sent into mold, with UV transfer printing process to the mold and glass for covering UV glue layer by glue
Carry out roll-in transfer pressing, by mold and glass be put into UV photo solidification machine carry out illumination curing, solidify built-in temperature less than 50 DEG C,
UV intensity of light source 30mw/cm2More than, irradiation time is greater than 60 seconds, carries out appearance test to the UV glass of curing molding.
Specifically, cleaning machine cleaning drying, 20 DEG C~40 DEG C of the water temperature range of cleaning, the electricity of water are carried out to UV transfer glass
Range 8M Ω~20M Ω, pressure limit 0.15MPa~0.35MPa of water are hindered, by the offline vacuum of the glass substrate 10 after cleaning
Magnetic-controlled sputtering coating equipment deposit covering function film layer 30, wherein functional film layer 30 be offline solar control coated glass membrane system layer or
Offline low-emission coated membrane system layer, is made of, including SiO one or more kinds of film layers2、Si3N4、AZO、TZO、
ITO、TCO、Cu、NiCr、Ag、MgF2、 Al2O3、ZnO、TiO2、SnO2、ZrO2、ZnSnO3In multiple material.Equipment vacuum pressure
Power is range 0.1*10-6Mba~9.9*10-5Mba, sputter gas are argon gas or argon gas and oxygen or argon gas and nitrogen
Mixed gas sputters operating air pressure range 0.4*10-3Mba~9.0*10-3mba;The plated film of functional film layer 30 is covered to deposition
Glass carries out on-line performance detection, obtains the optical data etc. of coated glass.
Embodiment 1:
Prepare after the white glass cleaning of a piece of 6mm float glass process air-dries, it is three-dimensional with UV technique to transfer out transparent bubble in air surface
Pattern 21, using offline vacuum magnetron sputtering coating film technique in UV deposition on glass covering function film layer 30, wherein functional film layer
30 be offline solar control coated glass membrane system layer, material Si3N4, equipment vacuum pressure is range 2.5*10-6Mba, sputter gas
For the mixed gas of argon gas and nitrogen, operating air pressure range 3.5*10 is sputtered-3Mba, thicknesses of layers 150nm, in X -ray inspection X knot
Fruit and presentation effect are as follows:
Project | Pattern effect | Pattern color | Surface reflectivity | Product light transmittance | Shading coefficient |
As a result | Three-dimensional bubble | Sky blue | 10% | 85% | 0.93 |
Embodiment 2:
Prepare after the white glass cleaning of a piece of 6mm float glass process air-dries, it is three-dimensional with UV technique to transfer out transparent brick wall in air surface
Pattern 21, using offline vacuum magnetron sputtering coating film technique in UV deposition on glass covering function film layer 30, wherein functional film layer
30 be offline solar control coated glass membrane system layer, material TiO2/Si3N4, equipment vacuum pressure is range 2.5*10-6Mba, sputtering
Gas is the mixed gas of argon gas and oxygen, argon gas and nitrogen, sputters operating air pressure range 3.5*10-3Mba, thicknesses of layers are
80nm, 125nm, online inspection result and presentation effect are as follows:
Project | Pattern effect | Pattern color | Surface reflectivity | Product light transmittance | Shading coefficient |
As a result | Three-dimensional brick wall | It is golden yellow | 28% | 70% | 0.8 |
Embodiment 3:
Prepare to transfer out transparent metal network chain with UV technique in air surface after the white glass cleaning of a piece of 6mm float glass process air-dries
Space pattern 21, using offline vacuum magnetron sputtering coating film technique in UV deposition on glass covering function film layer 30, wherein function
Film layer 30 is offline low-emission coated membrane system layer, and material and structure are SnO2/ ZnO/Ag/NiCr/SnO2/ZrO2, equipment vacuum
Pressure is range 2.5*10-6Mba, sputter gas include argon gas, and the mixed gas of argon gas and oxygen sputters operating air pressure range
3.5*10-3Mba, film layer overall thickness 80nm, online inspection result and presentation effect are as follows:
Project | Pattern effect | Pattern color | Surface reflectivity | Product light transmittance | Shading coefficient |
As a result | Three-dimensional network chain | Silver gray | 25% | 45% | 0.55 |
The present embodiment design has the advantages that the coated glass of three-dimensional imaging effect is compared with the existing technology: more
UV roller mould, transfer glue are easily utilized by reasonable material, the optimization of technique, equipment in transparent glass substrate 10
Water, transfer printing process transfer various required transparent stereo patterns 21, are turned by offline vacuum magnetron sputtering coating film technique in UV
It is coated with covering function film layer 30 on print glass, using the body color of film plating layer, reflection, the adjusting of transmission, so that UV is transferred
Pattern show apparent stereoscopic effect, while the color state of its pattern, bright-dark degree, depth journey in the outer surface of glass
Degree can be controlled by the function of film plating layer.UV technique is a kind of environmental-friendly green technology, and UV glue is colorless and transparent to ring
Border is pollution-free, combines the coated product of production with offline vacuum magnetron sputtering coating film technology, realizes the appearance of plate glass
Face can show apparent 21 effect of space pattern according to demand, while not influence the true qualities and performance of plated film functional layer, tool
Standby good sunshade, translucency, not only having met not influences film plating layer performance but also has both to meet 21 demand of space pattern, not tempering need
It asks, the particular/special requirements such as high transparency demand, ecological requirements.And then replace the pattern printed on previous coated glass using stickup
Patch carries out the imaging mode and product of the coating covering treatments such as ink, paint in glass surface, and improves thus bring
Drawback.To promote the upgrading of coated glass, realize that large area has the mass production of coated glass of three-dimensional imaging effect.
The above is only the preferred embodiment of the utility model only, is not intended to limit the utility model, all at this
Made any modifications, equivalent replacements, and improvements etc., should be included in the utility model within the spirit and principle of utility model
Protection scope within.
Claims (8)
1. a kind of three-dimensional imaging coated glass, it is characterised in that: include:
Glass substrate;
UV glue-line, transfer are set in the glass substrate and have space pattern;
Functional film layer is covered on the UV glue-line and the outer surface of the glass substrate is made to show space pattern imaging effect
Fruit, the functional film layer are offline solar control coated glass membrane system layer or offline low-emission coated membrane system layer.
2. three-dimensional imaging coated glass according to claim 1, it is characterised in that: the glass substrate is float glass process plate glass
Glass substrate.
3. three-dimensional imaging coated glass according to claim 1, it is characterised in that: the UV glue-line is the height of clear, colorless
Anti-scratch type ultraviolet curing glue layer.
4. three-dimensional imaging coated glass according to claim 1, it is characterised in that: the functional film layer is by one kind or one
Kind or more film layer composition.
5. three-dimensional imaging coated glass according to claim 4, it is characterised in that: the film layer is SiO2Layer,
Si3N4Film layer, AZO film layer, TZO film layer, ito film layer, TCO film layer, Cu film layer, NiCr film layer, Ag film layer, MgF2Film layer, Al2O3
Film layer, ZnO film layer, TiO2Film layer, SnO2Film layer, ZrO2Film layer or ZnSnO3Film layer.
6. three-dimensional imaging coated glass according to claim 1, it is characterised in that: the functional film layer passes through offline vacuum
Magnetron sputtering membrane process deposition is covered on the UV glue-line.
7. described in any item three-dimensional imaging coated glasses according to claim 1~6, it is characterised in that: the space pattern is
CD line, drawing pattern, cloudy surface, irregular decorative pattern or male and fomale(M&F).
8. described in any item three-dimensional imaging coated glasses according to claim 1~6, it is characterised in that: the three-dimensional imaging plating
Film glass is made of the glass substrate, the UV glue-line and the functional film layer.