CN208827244U - A kind of modified form Low-E glass - Google Patents
A kind of modified form Low-E glass Download PDFInfo
- Publication number
- CN208827244U CN208827244U CN201821117587.4U CN201821117587U CN208827244U CN 208827244 U CN208827244 U CN 208827244U CN 201821117587 U CN201821117587 U CN 201821117587U CN 208827244 U CN208827244 U CN 208827244U
- Authority
- CN
- China
- Prior art keywords
- film layer
- glass
- low
- azo
- modified form
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to a kind of modified form Low-E glass, including glass-base, the upper surface of the glass-base is provided with Low-E combination film layer, and the lower surface of the glass-base is provided with tin oxide film layer;The Low-E combination film layer successively includes Si from bottom to up3N4Film layer A, AZO film layer A, TiO2Film layer A, Cu film layer, Ag film layer A, NiCr film layer A, AZO film layer B, Si3N4Film layer B, AZO film layer C, Ag film layer B, Ti film layer, ZnAlOx film layer, NiCr film layer B, TiO2Film layer B, SiNx.The utility model has the following beneficial effects: improving the refractive index of product, and there are low radiation functions by adjusting the structure of Low-E combination film layer.
Description
Technical field
The utility model relates to glass technology field more particularly to a kind of modified form Low-E glass.
Background technique
Glass is a kind of ancient construction material, with the horizontal rapid day crescent improved with application technology of modern science and technology
Different, the various unique glass of function come out one after another, prosperous glass family.In the development of glass, be used to do earliest vessel and
Ornament, with the industrialization and scale of glass production, the glass of various uses and various performances is come out one after another.Present glass
Have become the important materials of daily life, production and science and technology field.In the prior art, in response to different use scopes, such as
Why not break and promote the function of glass, is the direction that research staff constantly researches and develops, innovates.
Utility model content
Based on this, the purpose of this utility model is to provide a kind of modified form Low-E glass, by adjusting Low-E combination
The structure of film layer improves the refractive index of product, and has low radiation functions.
The utility model provides a kind of modified form Low-E glass, including glass-base, and the upper surface of the glass-base is set
It is equipped with Low-E combination film layer, the lower surface of the glass-base is provided with tin oxide film layer;The Low-E combination film layer is under
Supreme successively includes Si3N4Film layer A, AZO film layer A, TiO2Film layer A, Cu film layer, Ag film layer A, NiCr film layer A, AZO film layer B,
Si3N4Film layer B, AZO film layer C, Ag film layer B, Ti film layer, ZnAlOx film layer, NiCr film layer B, TiO2Film layer B, SiNx.
Preferably, the upper surface of the SiNx is provided with SiC film layer, reinforces the hard of Low-E combination film surface
Degree and wear resistance, to promote service life.
Preferably, the lower surface of the tin oxide film layer is provided with low iron glass layer, has a surface of glass
There is heat-insulating, fire-preventing function.
Preferably, the upper surface of the SiC film layer is provided with nano antifouling coating, has a surface of glass
Anti-pollution function.
Preferably, the Si3N4Film layer A, Si3N4The thickness of film layer B, SiNx is disposed as 15-25nm;It is described
The thickness of AZO film layer A, AZO film layer B, AZO film layer C is disposed as 8-15nm;The thickness of NiCr film layer A, the NiCr film layer B
It is disposed as 0.5-3nm.
Preferably, the thickness of the SiC film layer is set as 30-55nm.
The utility model has the following beneficial effects: Si3N4Film layer plays the role of basement membrane and middle film layer, improves the hard of membrane system
Degree, satisfactory mechanical property;TiO2Film layer characteristic with a high refractive index;NiCr film layer improves Ag film layer to protect Ag film layer
Oxidation resistent susceptibility;AZO film layer also has the function of good starvation, further protects Ag film layer;ZnAlOx can be by Ti
Film layer complete oxidation reduces the optical attenuation of film layer, so that membrane system has higher light transmittance, Cu film layer is arranged, to reduce Ag
The thickness of film layer A, generally speaking, rationally, refractive index is high for such film layer structure design;The lower surface setting of glass-base is aerobic
Change tin film layer, a surface of glass is made to have the function of Low emissivity.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of the utility model.
Fig. 2 is the structural schematic diagram of another embodiment of the utility model.
Appended drawing reference are as follows: glass-base 11, tin oxide film layer 10, Si3N4Film layer A12, AZO film layer A13, TiO2Film layer
A14, Cu film layer 15, Ag film layer A16, NiCr film layer A17, AZO film layer B18, Si3N4Film layer B19, AZO film layer C20, Ag film layer
B21, Ti film layer 22, ZnAlOx film layer 23, NiCr film layer B24, TiO2Film layer B25, SiNx26, SiC film layer 27, low iron glass layer
28, nano antifouling coating 29.
Specific embodiment
For the feature, technological means and specific purposes achieved, function that can further appreciate that the utility model, below
The utility model is described in further detail in conjunction with attached drawing and specific embodiment.
It please refers to shown in Fig. 1: a kind of modified form Low-E glass, including glass-base 11, the upper table of the glass-base 11
Face is provided with Low-E combination film layer, and the lower surface of the glass-base 11 is provided with tin oxide film layer 10;The Low-E combination
Film layer successively includes Si from bottom to up3N4Film layer A12, AZO film layer A13, TiO2Film layer A14, Cu film layer 15, Ag film layer A16,
NiCr film layer A17, AZO film layer B18, Si3N4Film layer B19, AZO film layer C20, Ag film layer B21, Ti film layer 22, ZnAlOx film layer
23, NiCr film layer B24, TiO2Film layer B25, SiNx26, wherein Si3N4Film layer plays the role of basement membrane and middle film layer, improves
The hardness of membrane system, satisfactory mechanical property;TiO2Film layer characteristic with a high refractive index;NiCr film layer is mentioned to protect AG film layer
The oxidation resistent susceptibility of high AG film layer;AZO film layer also has the function of good starvation, further protects AG film layer;
Ti film layer complete oxidation can be reduced the optical attenuation of film layer by ZnAlOx, so that membrane system has higher light transmittance, Cu film is arranged
Layer, to reduce the thickness of Ag film layer A, generally speaking, rationally, refractive index is high for such film layer structure design;Glass-base
Lower surface is provided with tin oxide film layer, and a surface of glass is made to have the function of Low emissivity.
Please refer to shown in Fig. 2: as preferred embodiment, the upper surface of the SiNx26 is provided with SiC film layer 27, adds
The hardness and wear resistance of strong Low-E combination film surface, to promote service life.
Please refer to shown in Fig. 2: as preferred embodiment, the lower surface of the tin oxide film layer 10 is provided with low iron glass
Glass layer 28 makes a surface of glass have the function of heat-insulating, fire-preventing.
Please refer to shown in Fig. 2: as preferred embodiment, the upper surface of the SiC film layer 27 is provided with nano antifouling
Coating 29 makes a surface of glass have anti-pollution function.
As preferred embodiment, the Si3N4Film layer A12, Si3N4The thickness of film layer B19, SiNx26 is disposed as
15-25nm;The thickness of AZO film layer A13, AZO film layer B18, the AZO film layer C20 is disposed as 8-15nm;The NiCr film layer
The thickness of A17, NiCr film layer B24 are disposed as 0.5-3nm.
As preferred embodiment, the thickness of the SiC film layer 27 is set as 30-55nm.
Above-described embodiments merely represent several embodiments of the utility model, the description thereof is more specific and detailed,
But it should not be understood as limiting the scope of the patent of the utility model.It should be pointed out that for the common of this field
For technical staff, without departing from the concept of the premise utility, various modifications and improvements can be made, these all belong to
In the protection scope of the utility model.Therefore, the scope of protection shall be subject to the appended claims for the utility model patent.
Claims (6)
1. a kind of modified form Low-E glass, including glass-base (11), it is characterised in that: the upper table of the glass-base (11)
Face is provided with Low-E combination film layer, and the lower surface of the glass-base (11) is provided with tin oxide film layer (10);The Low-E
Combine film layer successively includes Si from bottom to up3N4Film layer A (12), AZO film layer A (13), TiO2Film layer A (14), Cu film layer (15),
Ag film layer A (16), NiCr film layer A (17), AZO film layer B (18), Si3N4Film layer B (19), AZO film layer C (20), Ag film layer B
(21), Ti film layer (22), ZnAlOx film layer (23), NiCr film layer B (24), TiO2Film layer B (25), SiNx (26).
2. a kind of modified form Low-E glass according to claim 1, it is characterised in that: the upper surface of the SiNx (26)
It is provided with SiC film layer (27).
3. a kind of modified form Low-E glass according to claim 1, it is characterised in that: the tin oxide film layer (10)
Lower surface is provided with low iron glass layer (28).
4. a kind of modified form Low-E glass according to claim 2, it is characterised in that: the upper table of the SiC film layer (27)
Face is provided with nano antifouling coating (29).
5. a kind of modified form Low-E glass according to claim 1, it is characterised in that: the Si3N4Film layer A (12),
Si3N4Film layer B (19), SiNx (26) thickness be disposed as 15-25nm;The AZO film layer A (13), AZO film layer B (18), AZO
The thickness of film layer C (20) is disposed as 8-15nm;The NiCr film layer A (17), NiCr film layer B (24) thickness be disposed as
0.5-3nm。
6. a kind of modified form Low-E glass according to claim 2, it is characterised in that: the thickness of the SiC film layer (27)
It is set as 30-55nm.