CN207391332U - Adhesive film - Google Patents

Adhesive film Download PDF

Info

Publication number
CN207391332U
CN207391332U CN201721318854.XU CN201721318854U CN207391332U CN 207391332 U CN207391332 U CN 207391332U CN 201721318854 U CN201721318854 U CN 201721318854U CN 207391332 U CN207391332 U CN 207391332U
Authority
CN
China
Prior art keywords
adhesive film
film
layer
resin
adhering agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201721318854.XU
Other languages
Chinese (zh)
Inventor
荒添铁也
安斋刚史
仓田雄
仓田雄一
高田耕辅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lintec Corp
Original Assignee
Lintec Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lintec Corp filed Critical Lintec Corp
Application granted granted Critical
Publication of CN207391332U publication Critical patent/CN207391332U/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The utility model provides a kind of adhesive film, and suitability is excellent, and design is also excellent for batching when being processed by roll-to-roll mode to slim adhesive film.The adhesive film is the adhesive film of protection graphite flake.The adhesive film possesses stripping film, adhering agent layer, resin film and roughened layer.Above-mentioned adhering agent layer is arranged on the surface of above-mentioned stripping film.Above-mentioned resin film is arranged on the surface of side opposite with above-mentioned stripping film of above-mentioned adhering agent layer.Above-mentioned roughened layer is arranged on the surface of side opposite with above-mentioned adhering agent layer of above-mentioned resin film.The average height (Rc) of the roughness curve element of the structural plane of above-mentioned roughened layer is 0.5 μm or more.The dynamic friction factor compared with above-mentioned stripping film in said structure face is less than 2.

Description

Adhesive film
Technical field
The utility model is related to a kind of adhesive films.
Background technology
In order to promote to be arranged at the heat dissipation of internal electronic unit, in the small-sized electronic products such as mobile phone, laptop Use the graphite flake for having heat transmission.For the slimming of electronic product and raising thermal diffusivity, these small-sized electronic products are used in Graphite flake be extremely thinned.Therefore, in graphite flake, its missing, stripping etc. in order to prevent uses coloring adhesive tape Protection sheet material surface (for example, referenced patent document 1,2).
In patent document 1, as protecting the adhesive tape of graphite flake, a kind of coloring adhesive tape is disclosed, There is adhering agent layer, the colored matrix materials have at least one surface of colored matrix materials:Thickness is less than 1 μm or more 6 μm The dyed layer that resin film layer, thickness are less than 1 μm or more 6 μm of adhering agent layer and thickness is less than 0.5 μm or more 2 μm, institute The light transmittance for stating colored matrix materials is less than more than 0.1% 10%, and the thickness of adhesive tape is less than 3 μm or more 10 μm.
In patent document 2, as protecting the adhesive tape of graphite flake, a kind of coloring adhesive tape is disclosed, There is adhering agent layer, the coloring film is provided with what is formed by coloring printing ink on support at least one surface of coloring film Dyed layer, and disclose the dyed layer by containing binder resin, coloured material and with specific average grain diameter two The coloring printing ink of silicon oxide particle is formed.
Coloring adhesive tape for example possesses adhering agent layer, the resin film being arranged on adhering agent layer and is arranged at resin film On dyed layer.Resin film is, for example, the base material of adhesive film.In addition, dyed layer is for example as the apparent unevenness for making graphite flake Even not eye-catching shielding layer and work.In the coloring adhesive tape, also requirement slimming, the thickness of adhesive tape is very thin 10 Below μm.Such coloring adhesive tape, such as formed together by roll-to-roll mode with stripping film.In roll-to-roll mode In, the coloring adhesive tape (following, which is denoted as adhesive film) with stripping film is taken up roller and rolls.
Then, by roll-to-roll mode, adhesive film is processed as defined width by severing, for use as the guarantor of protection graphite flake Retaining tape.When manufacturing very thin adhesive film by roll-to-roll mode like this, it some times happens that adhesion (film table when being batched Attaching between face and the film back side being contacted on it), air be mixed into (fold) etc. batch it is bad.In addition, in recent years, from U.S. The angle of sight is set out, and for the adhesive film, when being configured at the inside of electronic product, also requirement seems in integration Design.
Prior art literature
Patent document
Patent document 1:Japanese Unexamined Patent Publication 2013-203965 publications
Patent document 2:Japanese Unexamined Patent Publication 2013-112695 publications
Utility model content
The technical problems to be solved in the utility model
In view of the above circumstances, the purpose of this utility model is to provide a kind of adhesive film, roll-to-roll mode pair is being passed through Suitability is excellent, and design is also excellent for batching when slim adhesive film is processed.
Solve the technological means of technical problem
In order to achieve the above object, the adhesive film of a mode of the utility model is the adhesive film of protection graphite flake.It is viscous It film and possesses stripping film, adhering agent layer, resin film and roughened layer.Above-mentioned adhering agent layer is arranged at the surface of above-mentioned stripping film On.Above-mentioned resin film is arranged on the surface of side opposite with above-mentioned stripping film of above-mentioned adhering agent layer.Above-mentioned roughened layer quilt It is arranged on the surface of side opposite with above-mentioned adhering agent layer of above-mentioned resin film.The coarse of structural plane of above-mentioned roughened layer is write music The average height (Rc) of line feature is 0.5 μm or more, the dynamic friction factor compared with above-mentioned stripping film in said structure face for 2 with Under.
According to such adhesive film, even if adhesive film is taken up roller and rolls, adhesive film is not easy to that adhesion and air is caused to mix The generation entered, and suitability is excellent, and design is also excellent for batching when processing slim adhesive film by roll-to-roll mode.
In above-mentioned adhesive film, above-mentioned roughened layer can include particle and binder resin.
In addition, in above-mentioned adhesive film, 60 ° of mirror surface lusters on said structure face can be more than 0.5% Less than 50%.
In addition, in above-mentioned adhesive film, at least one in above-mentioned adhering agent layer, above-mentioned resin film and above-mentioned roughened layer Person can include colorant.
In addition, in above-mentioned adhesive film, the thickness of above-mentioned adhering agent layer can be less than 1 μm or more 5 μm.
In addition, in above-mentioned adhesive film, the thickness of above-mentioned resin film can be less than 1 μm or more 6 μm.
In addition, in above-mentioned adhesive film, the thickness of above-mentioned roughened layer can be less than 0.5 μm or more 10 μm.
In addition, in above-mentioned adhesive film, the dynamic friction factor compared with the stripping film of the structural plane can be 0.5 More than less than 1.5.
In addition, in above-mentioned adhesive film, the arithmetic mean roughness (Ra) in said structure face can be 0.1 μm or more 1.0 μ Below m.
In addition, in above-mentioned adhesive film, the average height (Rc) of the roughness curve element in said structure face can be 0.5 μm or more less than 5.0 μm.
In addition, in above-mentioned adhesive film, 10 mean roughness (Rzjis) in said structure face can be 1.0 μm or more Less than 9.0 μm.
In addition, in above-mentioned adhesive film, the average height of the roughness curve element of the lower surface of above-mentioned stripping film (Rc) it can be below 500nm.
In addition, in above-mentioned adhesive film, in above-mentioned roughened layer, compared with the binder resin of 100 mass parts, on The content for stating particle can be below mass part for more than 40 mass parts 150.
In addition, in above-mentioned adhesive film, above-mentioned roughened layer can include colorant.
In addition, above-mentioned adhesive film can be formed long sheet.
In addition, in above-mentioned adhesive film, above-mentioned adhering agent layer, above-mentioned resin film and above-mentioned roughened layer can be attached at electricity In subassembly inside on the surface of set graphite flake.
According to such adhesive film, adhesive film is difficult to happen adhesion and air is mixed into, and is further added by roll-to-roll mode Suitability is excellent, and design is also excellent for batching during work slim adhesive film.
Utility model effect
As described above, according to the utility model, be capable of providing a kind of adhesive film, by roll-to-roll mode to slim Suitability is excellent, and design is also excellent for batching when adhesive film is processed.
Description of the drawings
In Fig. 1, figure (a) is stereoscopic schematic diagram of the adhesive film of present embodiment in the state of being wound;(b) is schemed for this The diagrammatic cross-section of the adhesive film of embodiment;
Fig. 2 is the state that the graphite flake of the adhesive tape with present embodiment is attached at via double faced adhesive tape on housing Diagrammatic cross-section;
Fig. 3 is the schematic diagram illustrated to the manufacturing process of the adhesive film of present embodiment.
Reference sign
1:Adhesive tape;2:Adhesive film;11:Resin film;15:Roughened layer;15u:Upper surface;20:Adhering agent layer;30: Stripping film;30d:Lower surface;51:Stripping film with adhering agent layer;52:Adhesive film;100:Graphite flake;101:Double faced adhesive tape; 102:Housing;210:Work beam;211:Roll out roller;220:Coating mechanism;230:Hothouse;240:Attach mechanism;240a:It rolls out Roller;240b:Roller;240c:Roller;250a、250b、250c、250d:Deflector roll;310:Work beam;311:Roll out roller;320:Coating machine Structure;330:Hothouse;350a、350b、350c:Deflector roll.
Specific embodiment
Hereinafter, while with reference to Figure of description while being illustrated to the embodiment of the utility model.Sometimes each XYZ axial coordinates are imported in Figure of description.
[composition of adhesive film]
Fig. 1 (a) is stereoscopic schematic diagram of the adhesive film of present embodiment in the state of being wound.Fig. 1 (b) is this implementation The diagrammatic cross-section of the adhesive film of mode.
As shown in Fig. 1 (a), the adhesive film 2 of present embodiment is formed long sheet.Adhesive film 2 is can be along an axis To the soft resin tape being wound.For example, in the example of Fig. 1 (a), adhesive film 2 is rolled up along long side direction DL and rolled up It takes on roller (batching core) 310.The length (overall length) on long side direction DL for being rolled up the adhesive film 2 on work beam 310 is for example For more than 6000m below 10000m.The length of adhesive film 2 on the width DW (short side direction) vertical with long side direction DL Degree is, for example, more than 800mm below 1500mm.
It is for example formed by the adhesive film 2 rolled up on work beam 310 by roll-to-roll mode.It is rolled up on work beam 310 Adhesive film 2 defined width is processed by severing by roll-to-roll mode, be cut into defined shape, such as conduct afterwards It protects the Protection glue band of graphite flake set in electronic unit inside and is used.It is for example, viscous on work beam 310 by rolling up Film 2 on width DW, such as can be divided into multiple with the width of every 100mm by severing.Divided adhesive film 2 can also be batched by other work beams again.In addition, in the attached drawing of present embodiment, using width DW as X-axis side To using long side direction DL as Y direction.
The cross-section structure of adhesive film 2 is illustrated below.
As shown in Fig. 1 (b), adhesive film 2 possesses resin film 11, roughened layer 15, adhering agent layer 20 and stripping film 30.Scheming In the example of 1 (b), adhesive film 2 is laminated with the order of 30/ adhering agent layer of stripping film, 20/ resin film, 11/ roughened layer 15. In the present embodiment, sometimes using 30 one side of stripping film as downside, using roughened 15 one side of layer as upside.
In adhesive film 2, stripping film 30 can be removed from the interface of stripping film 30 and adhering agent layer 20.In this embodiment party In formula, the composition after stripping film 30 is removed from adhesive film 2 is as adhesive tape 1.Adhesive tape 1 possesses resin film 11, thick Face layer 15 and adhering agent layer 20.
Stripping film 30 be arranged at adhering agent layer 20 on the surface of 11 opposite side of resin film.In the example of Fig. 1 (b) In, stripping film 30 is lowest level.Adhering agent layer 20 is arranged on the surface of side opposite with lower surface 30d of stripping film 30.It is viscous Oxidant layer 20 to be arranged between stripping film 30 and resin film 11.Resin film 11 be arranged at adhering agent layer 20 with stripping film 30 On the surface of opposite side.Resin film 11 is arranged between roughened layer 15 and adhering agent layer 20.Resin film 11 is adhesive film 2 Base material.Roughened layer 15 be arranged at resin film 11 on the surface of 20 opposite side of adhering agent layer.
In the example of Fig. 1 (b), roughened layer 15 is top layer.It is roughened when adhesive film 2 is taken up roller 310 and rolls The upper surface 15u (structural plane) of layer 15 is contacted with stripping film 30 with the face (lower surface 30d) of 20 opposite side of adhering agent layer.
The arithmetic mean roughness Ra of the upper surface 15u (structural plane) of roughened layer 15, there is no particular limitation, but preferably For 0.1 μm or more, more preferably less than 0.1 μm or more 1.0 μm, further preferably less than 0.2 μm or more 0.5 μm.It is roughened The average height Rc of the roughness curve element of layer 15 is 0.5 μm or more, is preferably less than 0.5 μm or more 5.0 μm, more preferably Less than 0.8 μm or more 3.0 μm, further preferably less than 1.0 μm or more 2.0 μm.10 mean roughness of roughened layer 15 There is no particular limitation by Rzjis, but preferably 1.0 μm or more, more preferably less than 1.0 μm or more 9.0 μm, further preferably Less than 2.0 μm or more 7.0 μm, particularly preferably less than 2.5 μm or more 5.0 μm.
By making roughened layer 15 that there is the structural plane in above range, aftermentioned dynamic friction factor can be set to provide Scope.Even if adhesive film 2 is taken up roller 310 and rolls as a result, adhesive film 2 is not easy to cause adhesion and the mixed generation of air, And when processing slim adhesive film 2 by roll-to-roll mode to batch suitability excellent.In addition, by having roughened layer 15 There is the structural plane in above range, 60 ° of mirror surface lusters of the upper surface 15u of aftermentioned roughened layer 15 can be set to defined Scope.The design when graphite flake 100 for being pasted with adhesive film 2 to be arranged to the inside of electronic unit as a result, is excellent.
For example, the dynamic friction factor of the lower surface 30d compared with stripping film 30 of the upper surface 15u of roughened layer 15 is 2 Hereinafter, it is preferably less than 1.8, more preferably less than 1.5.There is no particular limitation for the lower limit of dynamic friction factor, but preferably 0.5 More than, more preferably more than 1.If dynamic friction factor is more than 2, when adhesive film 2 is taken up roller 310 and batches, it is viscous to there is generation Company or the mixed possibility of air.In addition, when dynamic friction factor is less than 0.5, adhesive film 2 is taken up roller 310 when rolling, it is possible to Batch dislocation.
In addition, 60 ° of mirror surface lusters of the upper surface 15u of the roughened layer 15 with such roughness, without special Restriction, but preferably less than more than 0.5% 50%, more preferably less than more than 1% 9%, further preferably more than 1% Less than 5%.As a result, since in the graphite flake 100 for being pasted with adhesive film 2, appearance is unglazed style, adhesive tape 1 is set When being placed in the inside of electronic unit, it is in integrated that adhesive tape 1, which seems with electronic unit, therefore its design is excellent.
In adhesive film 2, in the Z-axis direction between adjacent layer, it can contact directly, it also can mediate contact.It is connecing indirectly When touching, in the Z-axis direction between adjacent layer, the interlayer (not shown) for improving adherence etc. may be present.In addition, adhesive film Each layer in 2 can be individual layer, can also be made of multiple layers.In addition, in adhesive film 2, it can be in roughened layer 15 and tree Dyed layer (not shown) is set between adipose membrane 11.
In adhesive film 2, there is no particular limitation for the thickness of stripping film 30, but preferably less than 20 μm or more 80 μm, more Preferably less than 20 μm or more 30 μm.Here, the thickness of present embodiment refers to, it is aftermentioned thick as obtained from measuring multiple points The average value of degree.
There is no particular limitation for the thickness of adhering agent layer 20, but preferably less than 1 μm or more 5 μm, more preferably 1 μm or more Less than 3 μm.If the thickness of adhering agent layer 20 is less than 1 μm, adhering agent layer 20 is low with the adherence of graphite flake, is difficult to sometimes fully Protect graphite flake.If the thickness of adhering agent layer 20 is more than 5 μm, adhesive film 2 is thickening, is unsatisfactory for the requirement of slimming.
The thickness of resin film 11 is, for example, less than 1 μm or more 6 μm, is preferably less than 1 μm or more 3 μm.If resin film 11 Thickness is less than 1 μm, then the intensity of resin film 11 is lower, it is difficult to be transported by roll-to-roll mode.If the thickness of resin film 11 More than 6 μm, then adhesive film 2 is thickening, is unsatisfactory for the requirement of slimming.
The thickness of roughened layer 15 is, for example, less than 0.5 μm or more 10 μm, is preferably less than 0.6 μm or more 3.0 μm, more excellent Elect less than 0.8 μm or more 2.0 μm as.If the thickness of roughened layer 15 is less than 0.5 μm, it cannot get required structural plane, if slightly The thickness of face layer 15 is more than 10 μm, then adhesive film 2 is thickening, is unsatisfactory for the requirement of slimming.
By the way that the thickness of each layer is set to above-mentioned scope, the thickness of adhesive tape 1 after stripping film 30 is stripped is 10 μ M or so, adhesive tape 1 are formed very thin.
Fig. 2 is the state that the graphite flake of the adhesive tape with present embodiment is attached at via double faced adhesive tape on housing Diagrammatic cross-section.
As shown in Fig. 2, the adhesive tape 1 that stripping film 30 has been stripped, such as be attached on graphite flake 100.It is for example, viscous The exposed surface for the adhering agent layer 20 of adhesive tape 1 is adhered on the surface of graphite flake 100.In addition, graphite flake 100 is via double faced adhesive tape Band 101 is attached on housing 102 (for example, electronic unit).As a result, in graphite flake 100, heat is along Z-direction, also along X Direction of principal axis and Y direction diffusion.It is effectively radiated by the heat that electronic unit distributes as a result,.
Further, since adhesive tape 1 is very thin, therefore can be in the situation for the inner space for not interfering small-sized electronic product Under, it is configured in electronic product.Further, it is unglazed style due to being provided with roughened layer 15 in adhesive tape 1 Appearance.As a result, since adhesive tape 1 seems with electronic unit in integrated (seeming to combine together), glue of adhering Band 1 is not eye-catching, and design is also improved.
In addition, in order not to make the apparent uneven eye-catching of graphite flake 100, to assign the purpose of shielding, adhering In adhesive tape 1, at least one of adhering agent layer 20, resin film 11 and roughened layer 15 can include colorant, also can in addition set It is different from the dyed layer of adhering agent layer 20, resin film 11 and roughened layer 15.There is no particular limitation for colorant, but can include Such as carbon black, titanium oxide, calcium carbonate, barium sulfate, yellow ferric oxide, red ferric oxide, cyanine blue, aluminium powder, mica titanium valve etc..As a result, Graphite flake 100 it is apparent it is uneven become not eye-catching, 100 apparent aesthetics of graphite flake is further enhanced.That is, will Being pasted with the design when graphite flake 100 of adhesive film 2 is arranged inside electronic unit becomes more excellent.
Material, the assay method of physics value of each layer of adhesive film 2 are as described below.
[resin film]
The resin types of resin film are used in, there is no particular limitation, but can for example include by poly terephthalic acid second The polyester that the polyester such as diol ester (PET), polybutylene terephthalate (PBT) (PBT), polyethylene naphthalate (PEN) are formed Film;The cellulose membranes such as polyurethane film, polyethylene film, polypropylene screen, Triafol T;Polychloroethylene film, polyvinylidene chloride Film, polyvinyl alcohol film, ethylene-vinyl acetate copolymer film, polystyrene film, polycarbonate membrane, acrylic resin film, drop ice The resin films such as piece vinyl resin film, cycloolefin resin film;Laminated body of these two or more resin films etc..Resin film can also It is stretched uniaxially or biaxially.Wherein, the precision of the thickness that is required, surface smoothness, obtained from filming Difficulty is angularly set out, preferably polyester film.As polyester film, particularly preferred PET film.In addition, from dimensional stability and intensity Angle set out, polyester film is preferably through biaxial stretch-formed film.Wherein, preferably through biaxial stretch-formed PET film.
[dyed layer]
For dyed layer, as long as cooperation colours the color for the electronic unit that adhesive tape is attached or with reconciliation Color is coloured, then there is no particular limitation, but never makes the apparent uneven angle that is eye-catching, assigning design etc. of ink sheet Degree sets out, and is preferably black.
Dyed layer preferably comprises coloured material and binder resin.As binder resin, such as amino first can be included Acid ester resin, epoxy resin, polyester resin, polyester urethane resin etc..These binder resins can be used alone, and also may be used Simultaneously using two or more.Wherein, from flexibility is excellent, angle with the adherence of roughened layer, binder resin is more Preferably at least one of polyester resin, polyester urethane resin, more preferably polyester urethane resin.From with The angle of the adherence of roughened layer is set out, and the glass transition temperature (Tg) of above-mentioned binder resin is preferably -30 DEG C or more Less than 10 DEG C.
Dyed layer is preferably cured by curing agent.There is no particular limitation for curing agent, binder resin can be coordinated and Appropriate selection.When binder resin is polyester urethane resin, as curing agent, such as cured with isocyanates can be included Agent etc..In addition, there are when hydroxyl or isocyanate group, can use amine hardener as curing in polyester urethane resin Agent.These curing agent can be used alone, and also can be used simultaneously two or more.
As coloured material, known usual pigment or dyestuff can be used.When dyed layer is black, such as carbon can be included It is black;For white when, titanium oxide, calcium carbonate, barium sulfate can be included;For yellow when, yellow ferric oxide can be included;For red when, Red ferric oxide can be included;For blueness when, cyanine blue can be included;For silver color when, aluminium powder can be included;For pearl when, can Include mica titanium valve etc..Wherein, since the concealment of carbon black is excellent, preferably.The content of coloured material in dyed layer, There is no particular limitation, can be appropriately configured according to concealment as a purpose etc..For example, dyed layer preferably comprises binding agent Resin and be more than 10 mass parts 70 coloured materials below mass part compared with the binder resin of 100 parts by weight.If it The content of color material is more than 70 mass parts, then there is a possibility that reduce with the adherence of roughened layer, therefore not preferably.It is above-mentioned Commercial goods can also be used in coloured material, the commercial goods of the coloured material as black, such as can include UTCO-Black (Dainichiseika Color & Chemicals Mfg.Co., Lt d. manufactures) etc..
According to required, dyed layer can also further contain transparent resin (medium), antioxidant, ultra-violet absorber, light The additives such as stabilizer.The thickness of dyed layer is, for example, less than 0.5 μm or more 10 μm, is preferably less than 0.8 μm or more 3 μm.
[adhering agent layer]
As the sticker for forming adhering agent layer, there is no particular limitation, such as can be from acrylic compounds sticker, rubber Sticker, silicone sticker, carbamates sticker, polyesters sticker, Styrene-diene block copolymer analog glue Suitably selection use in sticker well known to agent etc..Sticker may be used alone or in combination using two or more.
As sticker, particularly acrylic compounds sticker, can be it is preferable to use since its bonding reliability is high. Acrylic compounds sticker using acrylic polymer as adherence ingredient or host agent, on this basis needed for, includes friendship Join the appropriate additives such as agent, tackifier, softening agent, plasticizer, filler, age resister, colorant.Acrylic polymer For the polymer using (methyl) alkyl acrylate as monomer main component, according to required, by using can be with (methyl) Monomer (co-polymerized monomer) that alkyl acrylate is copolymerized and prepare.As (methyl) alkyl acrylate, such as can arrange Enumerate (methyl) methyl acrylate, (methyl) ethyl acrylate, (methyl) propyl acrylate, (methyl) isopropyl acrylate, (first Base) butyl acrylate, (methyl) isobutyl acrylate, (methyl) sec-butyl acrylate, (methyl) tert-butyl acrylate, (methyl) Amyl acrylate, (methyl) Hexyl 2-propenoate, (methyl) heptylacrylate, (methyl) 2-ethyl hexyl acrylate, (methyl) acrylic acid -2- Ethylhexyl, (methyl) Isooctyl acrylate monomer, (methyl) acrylic acid nonyl ester, the different nonyl ester of (methyl) acrylic acid, (methyl) acrylic acid Last of the ten Heavenly stems ester, (methyl) isodecyl acrylate, (methyl) acrylic acid hendecane base ester, (methyl) dodecylacrylate, (methyl) Tridecyl acrylate, (methyl) acrylic acid tetradecane base ester, (methyl) acrylic acid pentadecane base ester, (methyl) acrylic acid ten Six Arrcostabs, (methyl) acrylic acid heptadecane base ester, (methyl) octadecyl acrylate, (methyl) acrylic acid nonadecyl (methyl) acrylic acid C1-20 Arrcostabs such as ester, (methyl) acrylic acid eicosane base ester [are preferably (methyl) acrylic acid C4-18 alkane Base (alkyl of straight-chain or branched) ester] etc..(methyl) alkyl acrylate can be fitted according to adherence as a purpose etc. Work as selection.
In addition, as the co-polymerized monomer that can be copolymerized with (methyl) alkyl acrylate, such as can enumerate Go out the carboxyl group-containing monomers such as (methyl) acrylic acid, itaconic acid, maleic acid, fumaric acid, crotonic acid, iso-crotonic acid or its acid anhydrides;Ethylene The monomers containing sulfonic group such as base sodium sulfonate;The aromatic ethenyl compounds such as styrene, substituted phenylethylene;The cyano-containings list such as acrylonitrile Body;The olefines such as ethylene, propylene, butadiene;The vinyl esters such as vinylacetate;Vinyl chloride;Acrylamide, methacryl The amide-containings monomer such as amine, n-vinyl pyrrolidone, N, N- dimethyl (methyl) acrylamide;(methyl) dihydroxypropyl alkane The hydroxyls monomer such as base ester, glycerol dimethacrylate;(methyl) acrylate, (methyl) acryloyl morpholine etc. contain Amino monomers;The monomers containing imide such as N-cyclohexylmaleimide, isopropylmaleimide;(methyl) acrylic acid shrinks sweet Grease, (methyl) acrylic acid methylglycidyl esters etc. contain epoxy based monomers;Except 2- methacryloxyethyl isocyanic acids Beyond the monomers containing isocyanate group such as ester, triethylene glycol two (methyl) acrylate, diethylene glycol two (methyl) can be also included Acrylate, ethylene glycol two (methyl) acrylate, tetraethylene glycol two (methyl) acrylate, neopentyl glycol two (methyl) propylene Acid esters, 1,6-HD two (methyl) acrylate, trimethylolpropane tris (methyl) acrylate, pentaerythrite three (methyl) Co-polymerized monomer (the multifunctional list of the polyfunctionalities such as acrylate, dipentaerythritol six (methyl) acrylate, divinylbenzene Body) etc..Co-polymerized monomer may be used alone or in combination using two or more.As co-polymerized monomer, preferably using with hydroxyl The modification monomer of the functional groups such as base or carboxyl.
(methyl) alkyl acrylate copolymer, the modification with functional group for preferably comprising 0.1~20 mass % are single Body, particularly preferably the modification monomer with functional group containing 1~10 mass %.
The weight average molecular weight of (methyl) alkyl acrylate copolymer is preferably 200,000~2,000,000, and particularly preferably 500,000 ~150 ten thousand.In addition, the weight average molecular weight in this specification is to be scaled polyphenyl by what gel permeation chromatography (GPC) method measured The value of ethylene.
As crosslinking agent, as long as being the friendship reacted with functional group possessed by (methyl) alkyl acrylate copolymer Join agent, such as isocyanates crosslinking agent, epoxies crosslinking agent, amine cross-linking agent, melamine class crosslinking can be included Agent, aziridines crosslinking agent, hydrazine crosslinking agent, aldehyde crosslinking agent, oxazoline classes crosslinking agent, metal alkoxide class crosslinking agent, metal Chelates crosslinking agent, metallic salt crosslinking agent, ammonium salt class crosslinking agent etc., wherein it is preferred that excellent with the reactivity of hydroxyl and carboxyl Isocyanates crosslinking agent.Crosslinking agent, which can be used alone, one kind or to be applied in combination two or more.
Isocyanates crosslinking agent includes at least polyisocyanate compounds.As polyisocyanate compounds, such as can Include the aromatic series polyisocyanate such as toluene di-isocyanate(TDI), '-diphenylmethane diisocyanate, benzene dimethylene diisocyanate Ester;The aliphatic polymeric isocyanates such as hexamethylene diisocyanate;Isophorone diisocyanate, two isocyanide of hydrogenated methylene diphenyld Ester ring types polyisocyanate such as acid esters etc.;And biuret body, the isocyanuric acid ester body of these compounds, further, can also it arrange Enumerate as with the low molecules active hydrogen-contg compound such as ethylene glycol, propylene glycol, neopentyl glycol, trimethylolpropane, castor oil Adduct of reactant etc., wherein, from the angle of the reactivity of the reactive group with (methyl) acrylate polymers It sets out, the aromatic poly-isocyanate that preferably trimethylolpropane is modified, particularly preferred trimethylolpropane is modified two methylene of benzene Group diisocyanate and trimethylolpropane modified toluene diisocyanate.
Compared with (methyl) alkyl acrylate copolymer of 100 mass parts, the blended amount of crosslinking agent is preferably 0.1~20 Mass parts, particularly preferably 1~10 mass parts.If the blended amount of crosslinking agent is in above-mentioned scope, easily by aftermentioned adhesion The gel fraction of agent is controlled in preferred scope.
In addition, in order to improve the adhesion strength of adhering agent layer, tackifying resin is further preferably added.Further, since by adding this A little tackifying resins, can improve tensile strength or tensile break strength, therefore by according to used acrylic copolymer, Tackifying resin is suitably added, tensile strength or tensile break strength can be adjusted.As the adhesion for making an addition to the utility model Tackifying resin in the adhering agent layer of adhesive tape, such as the rosin resinoid such as ester compounds that can include rosin or rosin;Diterpene The terpene resins such as polymer or australene-phenol copolymer;The Petropols such as aliphatic category (C5 classes) or the fragrant same clan (C9);Separately Styrene resin, phenolic resin, xylene resin etc. can be included outside.Wherein, using with (methyl) acrylic acid just In adhesion agent composition of the butyl ester as the acrylic copolymer of main monomer component, take into account slim, adhesion strength with it is heat-resisting During property, rosin resinoid and styrene resin are preferably used in mixed way.
In addition, according to required, adhering agent layer can contain silane coupling agent, antistatic agent, antioxidant, ultraviolet radiation absorption Agent, light stabilizer, softening agent, filler, adjustable refractive index agent, dyestuff, pigment, antirust agent etc..
[stripping film]
The peeling agent layer that stripping film preferably has film base material and is arranged on the film base material.As film base material, can include It is formed by polyester such as polyethylene terephthalate, polybutylene terephthalate (PBT), polyethylene naphthalate poly- Ester film, polyolefin film, polycarbonate membrane, the polyvinyl acetate formed by polyolefin such as polyethylene, polypropylene, polymethylpentenes Any one or laminated body for being made of these two or more films in the plastic foils such as film etc..
Peeling agent layer is for example formed by the peeling agent layer comprising remover and formed with the solidfied material of composition.As remover Layer formation composition, as long as peeling agent layer can be assigned so that the arbitrary layer being laminated on peeling agent layer to be shelled from stripping film From function, there is no particular limitation.As remover, such as silicone resin, chain alkyl resin and alcohol can be included Acid resin etc..
As silicone remover, addition reaction-type silicone, condensation reaction type silicone, energy ray-curable silicon can be included Ketone.In addition, in order to adjust peeling force, can also by the dimethyl silicone polymer of non-functional, phenyl modified silicone, silicone resin, Silica, cellulose compound are used as additive.
Adhesive film 2 is taken up roller 310 when rolling, the upper surface 15u (structural plane) of roughened layer 15 and stripping film 30 with Face (lower surface 30d) contact of 20 opposite side of adhering agent layer.Therefore, the arithmetic mean roughness of the lower surface 30d of stripping film 30 Ra is preferably below 50nm, more preferable below 40nm.There is no particular limitation for the lower limit of the Ra of lower surface 30d, but is preferably 10nm.There is no particular limitation by the average height Rc of the roughness curve element of lower surface 30d, but preferably below 500nm, more Preferably below 450nm.There is no particular limitation for the lower limit of the Rc of lower surface 30d, but preferably 100nm.The 10 of lower surface 30d There is no particular limitation by point mean roughness Rzjis, but preferably below 800nm, more preferably below 700nm.Lower surface 30d The lower limit of Rzjis there is no particular limitation, but preferably 100nm.
It, can will be with roughened layer by the way that Ra, Rc and Rzjis of the lower surface 30d of stripping film 30 are set to above range 15 dynamic friction factor is set to required scope.When adhesive film 2 is taken up roller 310 and rolls as a result, even if roughened layer 15 is upper Surface 15u is contacted with the lower surface 30d of stripping film 30, since Ra, Rc and Rzjis of the lower surface 30d of stripping film 30 are set as Above range, therefore adhesive film 2 is not easy to cause adhesion and the mixed generation of air, and slim glue is processed by roll-to-roll mode When film 2 to batch suitability excellent.
[roughened layer]
On roughened layer, as long as the arithmetic mean roughness Ra of upper surface (structural plane), roughness curve element is flat Height Rc and 10 mean roughness Rzjis is required scope, then to its material, there is no particular limitation.As in adjusting Roughened layer by carrying out the method for roughening treatment or can also be set to include by the method for Ra, Rc and Rzjis of surface 15u Method of layer of at least one of inorganic particle and organic granular etc. adjusts above-mentioned roughness etc..As the roughened place of progress The method of reason can include the method for carrying out Corona discharge Treatment, blasting treatment, coarse roller surface is crimped on upper surface Surface is so as to transferring method of the roughness of roller surface etc..In addition, by the way that roughened layer is made to contain particle, can adjust above-mentioned thick Rugosity etc..
Wherein, roughened layer preferably comprises particle and binder resin, more preferably comprising in inorganic particle and organic granular At least any one, further preferably include inorganic particle and binder resin.By adjusting inorganic particle and/or organic Average grain diameter, blended amount of grain etc., can also easily adjust above-mentioned roughness etc..Inorganic particle and/or organic granular it is flat Equal grain size can be more than the thickness of roughened layer.
As binder resin, there is no particular limitation, can include thermoplastic resin, thermosetting resin, light-cured resin Deng, such as carbamate resins, epoxy resin, polyester resin, polyester urethane resin etc. can be included.These are bonded Agent resin can be used alone, and also can be used simultaneously two or more.Wherein, since flexibility is excellent, preferred thermoplastic resin, preferably Carbamate resins, polyester resin, polyester urethane resin.When roughened layer includes particle, from the angle of compatibility It sets out, binder resin is more preferably at least one of polyester resin, polyester urethane resin.
Roughened layer can be cured by curing agent.There is no particular limitation for curing agent, binder resin can be coordinated and Suitably selected.When binder resin is polyester urethane resin, as curing agent, such as isocyanates can be included Curing agent etc..In addition, amine hardener can be used as curing there are when hydroxyl or isocyanate group in polyester urethane resin Agent.These curing agent can be used alone, and also can be used simultaneously two or more.In addition, it can contain according to required, in roughened layer same Sample is contained in the additives such as antioxidant, ultra-violet absorber, the light stabilizer in dyed layer.
[particle]
There is no particular limitation for organic granular, such as can include the acrylic resins such as poly methyl methacrylate particle Grain, granules of polystyrene, polycarbonate pellets, carbamate resins pearl, epoxy bead, polyester resin pearl, Amino-Polyester Formate resin pearl etc..These particles can be used alone, and also can be used simultaneously two or more.
As inorganic particle, there is no particular limitation, such as can include silica (SiO2), barium sulfate (BaSO4), oxygen Change in titanium, the particles such as calcium carbonate at least any one.These inorganic particles can be used alone, also can be used simultaneously two kinds with On.Wherein, the difficulty and the angle of the difficulty of acquisition adjusted from granularity, preferably silica, barium sulfate (BaSO4) or silica and barium sulfate (BaSO4) mixture.
The volume ratio of silica and barium sulfate ([volume of silica]:[volume of barium sulfate]) it is preferably controlled in 100:50~100:In the range of 500.In addition, there is no particular limitation for the content of above-mentioned particle, but compared with 100 mass parts More than binder resin, preferably 40 mass parts 150 is below mass part, and more than more preferably 50 mass parts 140 is below mass part, More than further preferably 60 mass parts 130 is below mass part, and more than particularly preferably 80 mass parts 125 is below mass part.If It is less than 40 mass parts compared with binder resin, particle the content of 100 mass parts, then there are the upper surfaces of roughened layer 15 The dynamic friction factor of the lower surface 30d compared with stripping film 30 of 15u is more than 2,60 ° of mirror surface lusters of roughened layer 15 and is more than 50% possibility.
Inorganic particle and organic granular can be mixed in roughened layer 15.It can be in the upper surface of roughened layer 15 Expose inorganic particle or organic granular on 15u.
There is no particular limitation for the average grain diameter of above-mentioned particle, but preferably less than 0.5 μm or more 10 μm, more preferably 1 μ Below 5 μm of more than m, further preferably less than 1.5 μm or more 3.0 μm.When above-mentioned average grain diameter beyond above range when, become It must be difficult to adjust the average height (Rc) of roughness curve element to the average height (Rc) of required roughness curve element In the range of, therefore not preferably.
In addition, in adhesive film 2, when at least one of silica, barium sulfate particle are dispersed in roughened layer 15 When interior, by changing the blend ratio of silica dioxide granule and barium sulfate particle in roughened layer 15, roughened layer can be expanded The selecting range of 15 color.For example, the content by relatively increasing barium sulfate particle, the indigo plant in the color of roughened layer 15 Discoloration obtains stronger.In addition, the content by relatively reducing barium sulfate particle, 60 ° of specular lights of roughened layer 15 can be reduced Damp degree.That is, by changing the blend ratio of silica dioxide granule and barium sulfate particle, 100 appearance of graphite flake can further be expanded On color selecting range.Furthermore it is possible to further expand the selection of the aesthetics for the graphite flake 100 for being pasted with adhesive film 2 Amplitude.
In addition, when particle is dispersed in roughened layer 15, adhesive film 2 is taken up when roller 310 batches or in adhesive film 2 when being transferred, and scratch equivalent damage is not likely to produce on the upper surface 15u of roughened layer 15.The productivity of adhesive film 2 obtains as a result, It is improved to further.
[average grain diameter measure]
The average grain diameter of particle can be measured by coulter counter method.For example, it will be measured by coulter counter method Peak value is as average grain diameter.
[measure of thickness]
For the thickness measurement of each layer of adhesive film 2, there is no particular limitation, and well known thickness gauge can be used, such as make With film thickness gauge (the film thickness gauge DIGIMICR O MH-15M that Nikon Corporation are manufactured).
[manufacturing method of adhesive film]
Hereinafter, the manufacturing process of the adhesive film of present embodiment is illustrated, but it's not limited to that.Fig. 3 (a) and figure 3 (b) is the schematic diagram illustrated to the manufacturing process of the adhesive film of present embodiment.In the present embodiment, volume pair is passed through Volume mode manufactures adhesive film 2.Such as adhesive film 2 is manufactured in an atmosphere.Arrow DR in figure represents the traffic direction of film.Operation side Correspond to long side direction DL to DR.
As shown in Fig. 3 (a), stripping film 30 by roll out roller 211 from then by continuously release from rolling out roller 211, pass through Coating mechanism 220 is directed to by deflector roll 250a.The surface that peeling agent layer is formed at stripping film 30 (forms the table of adhering agent layer 20 Face) on.
By coating mechanism 220, the coating fluid of adhering agent layer 20 is being coated with from the stripping film 30 for rolling out the releasing of roller 211. Stripping film 30 with adhering agent layer 20 is directed to hothouse 230 via deflector roll 250b, at an established temperature, for example (,) it is dry Less than 5 minutes 10 seconds or more.Stripping film with stripping film 30 and adhering agent layer 20, with adhering agent layer is formed as a result, 51.Stripping film 51 with adhering agent layer is directed to via deflector roll 250c attaches mechanism 240.
By attaching mechanism 240, resin film 11 be attached at be directed to attach mechanism 240, it is with adhering agent layer On the adhering agent layer 20 of stripping film 51.For example, the stripping film 51 with adhering agent layer is clamped between roller 240b and roller 240c, Resin film 11 rolling out roller 240a between roller 240b and roller 240c by releasing.
Resin film 11 is fitted on adhering agent layer 20 as a result, and being formed has stripping film 30, adhering agent layer 20 and resin film 11 adhesive film 52.Afterwards, adhesive film 52 is taken up roller 210 and continuously batches via deflector roll 250d.
Then, as shown in Fig. 3 (b), the adhesive film 52 on roller 311 is rolled out is taken up by rolling out transferring certainly for roller 311 It is continuously released, coating mechanism 320 is directed to via deflector roll 350a.By coating mechanism 320, it is coated on resin film 11 The coating fluid of roughened layer 15.
The adhesive film 52 for being coated with the coating fluid of roughened layer 15 is directed to hothouse 330 via deflector roll 350b, is advising It is dried at a temperature of fixed.The adhesive film 2 that roughened layer 15 is provided on the resin film 11 of adhesive film 52 is formed in as a result,. Then, adhesive film 2 is taken up roller 310 and continuously batches via deflector roll 350c.In addition, in adhesive film 2, when roughened layer 15 When being provided with dyed layer between resin film 11, the process for forming dyed layer can be set between Fig. 3 (a) and Fig. 3 (b).
In addition, for the coating method of coating mechanism 220 and coating mechanism 320, for example, can be suitably used scraper rubbing method, Scraper for coating method (knife coat method), roller coating method, scraping blade rubbing method (blade coat method), die coating Any one method in method (die coating method), gravure coating method etc..
Embodiment
Hereinafter, the utility model is described in further detail by embodiment etc., but the scope of the utility model And from the restriction of these embodiments etc..
[embodiment 1]
The preparation > of < adherence compositions
By by the butyl acrylate of 95.5 mass parts, the vinylacetate of 3 mass parts, 1 mass parts acrylic acid -2- hydroxyls The acrylic acid copolymer of base ethyl ester and 0.5 mass parts prepares the acrylate copolymer that weight average molecular weight is 1,000,000.Then, pass through (solid constituent is scaled compared with 100 mass parts;It is same as below) the acrylate copolymer, add 25 mass parts hydrogenation Rosin ester (Araka wa Chemical Industries, Ltd. manufactures, PINECRYSTAL KE-100, softening point:100 DEG C), (Arakawa Chemical Industries, Ltd. manufactures, Pensel D-135 are soft for the newtrex esters of 4 mass parts Change point:135 DEG C) and 24 mass parts petroleum resinoid (Mitsui Che micals, Inc. manufacture, FTR6100, softening point: 95 DEG C), it further mixes, forms adhesion ingredient.Adhesion ingredient is dissolved in toluene, prepares solid component concentration as 13 mass % Adhesion agent solution.
The preparation > of < roughened layers coating solution A
Roughened layer coating solution A is prepared by following manner, i.e.,:Compared with 100 mass parts (be scaled solid into Point) as binder resin polyester resin (TOYOBO CO., L TD. manufacture:Vylon 20SS), 22 mass parts of addition Silicon dioxide microparticle (Tosoh Silica C orporation are manufactured, NIPSIL SS50B, 2.1 μm of average grain diameter), 100 matter Measure barium sulfate particles (Sakai Chemical Industry Co., the Ltd. manufactures of part:BMH, 2.5 μm of average grain diameter), it uses Toluene/methyl ethyl ketone (MEK) mixed solvent (toluene:MEK (mass ratio)=50:50) solid component concentration is adjusted to 20 matter Measure %.
The manufacture > of < adhesive films
Silicone remover will be used to have carried out the stripping of lift-off processing to the single side of polyethylene terephthalate film Film (LINTEC Corporation manufacture SP-PET251130, and the Ra of the lower surface 30d of stripping film is 34nm, Rc 400nm, Rzjis is 672nm, and thickness is 25 μm) it releases, in a manner that dried thickness becomes 2 μm, using knife type coater, at it After being coated with the coating solution of adherence composition on lift-off processing face, obtained film is carried out at 90 DEG C to add within 1 minute Heat treatment forms the adhering agent layer that thickness is 2 μm on stripping film.Then, it is bonded and makees in the exposed surface one side of above-mentioned coating layer For the polyethylene terephthalate film (Tor ay Industries, Inc., ET2F51L, 2 μm of thickness) of resin film, by institute Obtained adhesive film coils into web-like.
Then, cured 7 days, made by removing under conditions of 23 DEG C, 50%RH by the way that the adhesive film of web-like will be coiled into Film/adhering agent layer (thickness:2 μm)/resin film (thickness:2 μm) form adhesive film.
Then, release and be rolled into the adhesive film of web-like, by gravure coater by black ink (Dai nichiseika Color&Chemicals Mfg.Co., Ltd. manufactures, " UTCO-591Black (N X) ") it is coated in resin film surface, further Heated, the dyed layer that thickness is 1 μm is formed on adhesive film.Then, obtained coloring adhesive film is batched in rolls Shape.
Then, the coloring adhesive film for being rolled into web-like is released, in a manner that dried thickness becomes 1 μm, uses notch board After coating machine is coated with roughened layer coating solution A in its coloring level, obtained film is carried out 1 minute at 90 DEG C Heat, form the roughened layer that thickness is 1 μm.Then, obtained coloring adhesive film is coiled into web-like.
[embodiment 2]
In addition to being not provided with dyed layer, adhesive film has been obtained in the same manner as example 1.
[embodiment 3]
Except being added into roughened layer coating solution compared with the total of the solid constituent of binder resin and colorant Measure it is for 25wt%, as the carbon black of colorant beyond, obtained adhesive film in the same way as in example 2.
[embodiment 4]
In addition to using roughened layer coating solution B, adhesive film has been obtained in the same manner as example 1.
The preparation > of < roughened layers coating solution B
Roughened layer coating solution B, is prepared, i.e., by following manner:Compared with 100 mass parts (be scaled solid into Point) as binder resin polyester resin (TOYOBO CO., L TD. manufacture:Vylon 20SS), add 117 mass parts Silicon dioxide microparticle (Tosoh Silica Corporation are manufactured, NIPSIL SS50B, 2.1 μm of average grain diameter), use Toluene/methyl ethyl ketone (MEK) mixed solvent (toluene:MEK (mass ratio)=50:50) solid component concentration is adjusted to 20 matter Measure %.
[embodiment 5]
Except silicone remover will be used to have carried out lift-off processing to the single side of polyethylene terephthalate film (Ra of the SP-PET381130 of LINTEC Corporation manufactures, the lower surface 30d of stripping film are 29nm to stripping film, and Rc is 320nm, Rzjis 666nm, thickness are 38 μm) it is used as beyond stripping film, it is adhered in the same manner as example 1 Film.
[comparative example 1]
In addition to not forming roughened layer, adhesive film has been obtained in the same manner as example 1.
[surface roughness measurement]
Using contact surface roughometer (Mitutoyo Corporation manufacture, trade name " S V3000S4 "), According to JIS B 0601-2001, the side opposite with adhering agent layer of the surface of roughened layer, the surface of dyed layer and stripping film is measured Surface (lower surface 30d) roughness curve element average height Rc, arithmetic mean roughness Ra and 10 average roughness Spend Rzjis.
[60 ° of mirror surface lusters]
Use NIPPON DENSHOKU INDUSTRIES Co., the glossometer " VG7000 " of Ltd manufactures, according to JIS K 7105, measure 60 ° of mirror surface lusters on the surface of roughened layer or the surface of dyed layer.
[dynamic friction factor measure]
According to JIS K 7125, the table of roughened layer surface side opposite with adhering agent layer with stripping film of adhesive film is measured The surface (lower surface 30d) of the dynamic friction factor or dyed layer in face (lower surface 30d) side opposite with adhering agent layer with stripping film Dynamic friction factor.It is 200g by load setting, uses precision universal testing machine Autograph AG-IS in the assay (Shimadzu Corporation manufactures).
[measure of the thickness of each layer]
The thickness of resin film, stripping film and each layer passes through simple type number length measurement system (Nikon Corporation systems Make, trade name " DIGIMICRO MH-15M ") it is measured.
Table 1 show Examples 1 to 5, comparative example 1 adhesive film composition, table 2 shows Examples 1 to 5, comparative example 1 The surface roughness of roughened layer of adhesive film, the surface roughness of dyed layer, the surface roughness of stripping film, roughened layer Or dyed layer is batched compared with the dynamic friction factor of stripping film, 60 ° of mirror surface lusters of the structural plane of adhesive film, adhesive film The design of suitability and adhesive film is evaluated.
[batching suitability evaluation]
In each process, visual observations, which whether there is adhesion, when coiling into web-like, whether there is air is mixed into (fold), according to following bases Suitability is batched in quasi- evaluation.Herein, suitability is batched in table 2, A, B have following meanings:
A:It does not stick together completely and air is mixed into, suitability is batched for stable.
B:It sticks together or air is mixed into, to there is the scope of the possibility generated in practical.
[design evaluation]
The adhesive film for having removed stripping film is fitted on the graphite flake " SGS-025-APH " of Selen.Inc. manufactures, cut The size of 50mm × 50mm is cut into, makes evaluation sample.Under fluorescent light by the adhesion film surface of the visual observations sample, with Following benchmark are evaluated.The visual observations are carried out by object of 5 subjects, and have carried out comprehensive descision.Herein, in table 2 Design evaluation in, A, B have following meanings:
A:The gloss for confirming adhesion film surface is not almost estimated or dazzle, design are good.
B:Range estimation confirms the gloss of adhesion film surface or dazzle, design are damaged.
[table 1]
The composition of adhesive film
Embodiment 1 Stripping film/adhering agent layer/resin film/dyed layer/roughened layer
Embodiment 2 Stripping film/adhering agent layer/resin film/roughened layer
Embodiment 3 Stripping film/adhering agent layer/resin film/roughened layer (contains colorant)
Embodiment 4 Stripping film/adhering agent layer/resin film/dyed layer/roughened layer
Embodiment 5 Stripping film/adhering agent layer/resin film/dyed layer/roughened layer
Comparative example 1 Stripping film/adhering agent layer/resin film/dyed layer
[table 2]
As shown in table 2, in Examples 1 to 5, the Rc of the roughened layer as top layer is 0.5 μm or more, roughened The dynamic friction factor compared with stripping film of layer is less than 2.At this point, suitability is batched as " A ".On the other hand, in comparative example 1 In, the Rc of the dyed layer as top layer is 0.33 μm, less than 0.5 μm, the dynamic friction factor compared with stripping film of dyed layer It is 2.4 more than 2.At this point, suitability is batched as " B ".
In addition, in Examples 1 to 5,60 ° of mirror surface lusters are less than more than 0.5% 50%.At this point, design is commented Valency is " A ".On the other hand, in comparative example 1,60 ° of mirror surface lusters are 63.9%, more than 50%.At this point, design is evaluated as “B”。
More than, the embodiment of the utility model is illustrated, but the utility model can be subject to various changes completely More, it is not limited in above-mentioned embodiment.

Claims (16)

1. a kind of adhesive film, for the adhesive film of protection graphite flake, which possesses:
Stripping film;
Adhering agent layer is arranged on the surface of the stripping film;
Resin film is arranged on the surface of side opposite with the stripping film of the adhering agent layer;And
Roughened layer is arranged on the surface of side opposite with the adhering agent layer of the resin film, and with roughness The average height Rc of curve element is 0.5 μm or more, the structural plane for being less than 2 compared with the dynamic friction factor of the stripping film.
2. adhesive film according to claim 1, wherein, the roughened layer includes particle and binder resin.
3. adhesive film according to claim 1 or 2, wherein, the structural plane has 60 ° of less than more than 0.5% 50% Mirror surface luster.
4. adhesive film according to claim 1, wherein, in the adhering agent layer, the resin film and the roughened layer At least one contain colorant.
5. adhesive film according to claim 1, wherein, the thickness of the adhering agent layer is less than 1 μm or more 5 μm.
6. adhesive film according to claim 1, wherein, the thickness of the resin film is less than 1 μm or more 6 μm.
7. adhesive film according to claim 1, wherein, the thickness of the roughened layer is less than 0.5 μm or more 10 μm.
8. adhesive film according to claim 1, wherein, the dynamic friction factor compared with the stripping film of the structural plane For less than more than 0.5 1.5.
9. adhesive film according to claim 1, wherein, the arithmetic mean roughness Ra of the structural plane is 0.1 μm or more Less than 1.0 μm.
10. adhesive film according to claim 1, wherein, the average height Rc of the roughness curve element of the structural plane For less than 0.5 μm or more 5.0 μm.
11. adhesive film according to claim 1, wherein, 10 mean roughness Rzjis of the structural plane are 1.0 μm More than less than 9.0 μm.
12. adhesive film according to claim 1, wherein, the roughness curve element of the lower surface of the stripping film is put down Height Rc is below 500nm.
13. adhesive film according to claim 2, wherein, in the roughened layer, compared with the bonding of 100 mass parts Agent resin, the content of the particle are below mass part for more than 40 mass parts 150.
14. adhesive film according to claim 1, wherein, the roughened layer includes colorant.
15. adhesive film according to claim 1, wherein, above-mentioned adhesive film is formed long sheet.
16. adhesive film according to claim 1, wherein, the adhering agent layer, the resin film and the roughened layer quilt It is attached on the surface of graphite flake set in electronic unit inside.
CN201721318854.XU 2016-12-28 2017-10-13 Adhesive film Active CN207391332U (en)