CN207296293U - A kind of fire-retardant digital coloured drawing floor modelled after an antique of no aldehyde - Google Patents
A kind of fire-retardant digital coloured drawing floor modelled after an antique of no aldehyde Download PDFInfo
- Publication number
- CN207296293U CN207296293U CN201720908908.1U CN201720908908U CN207296293U CN 207296293 U CN207296293 U CN 207296293U CN 201720908908 U CN201720908908 U CN 201720908908U CN 207296293 U CN207296293 U CN 207296293U
- Authority
- CN
- China
- Prior art keywords
- fire
- antique
- aldehyde
- retardant
- coloured drawing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of fire-retardant digital coloured drawing floor modelled after an antique of no aldehyde, it is described including substrate, be disposed on the substrate the panel on surface, be arranged on the bottom plate of base lower surface, the substrate includes some veneers, stack by the crisscross mode of wood grain between two adjacent veneer, be adhesively fixed between the adjacent veneer, panel, bottom plate by the fire-retardant glue of no aldehyde.The utility model is disclosed without the fire-retardant digital coloured drawing floor modelled after an antique of aldehyde, by being added to base material without aldehyde, fire protection flame retarding is modified, and greatly promotes the environmental protection on floor, fire resistance, along with the utilization of digital coloured drawing technology, not only the space that uses on floor, but also beautifying household environment had been expanded.
Description
Technical field
The present invention relates to a kind of fire-retardant digital coloured drawing floor modelled after an antique of no aldehyde, specifically a kind of zero aldehyde addition, fire prevention
There is the digital coloured drawing floor of antique effect on fire-retardant surface.
Background technology
With the continuous improvement of China's per capita income and Living consumption, the finishing in house is increasingly particular about, it is special
It is not constantly sound and people's security against fire consciousness the enhancing with state's laws regulation, the requirement to the floor of finishing is got over
Come it is stringenter, to have preferable fire resistance, without noxious material release, beautiful and generous, durable floor demand it is higher and higher, because
This, developing floor that is a kind of while meeting a variety of demands of consumer becomes very necessary.
The content of the invention
There is preferable fire resistance it is an object of the invention to provide one kind, discharged without noxious material, is beautiful and generous, durable
Floor the modelled after an antique digital coloured drawing floor fire-retardant without aldehyde.
The object of the present invention is achieved like this：
A kind of fire-retardant digital coloured drawing floor modelled after an antique of no aldehyde, including substrate, be disposed on the substrate the panel on surface, be arranged on
The bottom plate of base lower surface, the substrate include some veneers 2, the crisscross mode of wood grain are pressed between two adjacent veneer 2
Stack, be adhesively fixed between the adjacent veneer 2, panel 1, bottom plate 3 by the fire-retardant glue of no aldehyde.
The glue is formaldehydeless addition and has the MDI glue of fire retardant performance.
The upper surface of the panel successively covered with white or clear primer layer, the digital coloured drawing figure layer for decoration, can
The top coat layer of adsorption-decomposition function formaldehyde.
The paint effect can be closed or open and semi open model.
2 thickness of veneer is 1.3-3.6mm.
1 thickness of panel is 1.2-3mm.
The panel 1 is entire body plates of solid wood, by birch, hard maple wood plus maple, oak, elm, black walnut, teak, sub- flower
One kind in pears, sour branch, Acacia is fabricated.
The veneer 2 is fabricated by poplar or Eucalyptus.
The preparation method on the modelled after an antique digital coloured drawing floor fire-retardant without aldehyde, comprises the technical steps that：
(1) log veneer (2) rotary-cut, selects log of the diameter grade in more than 80mm to carry out boiling, after wooden softening, carries out
Rotary-cut, is then dried with infrared drier, and the moisture control of veneer (2) is in 8%-10%；
(2) impregnation, carries out impregnation by veneer (2), allows glue fully penetrated to be filled into the pore of veneer (2)；
(3) embryo is organized, a group embryo is carried out to the veneer (2) after impregnation, the grain direction per adjacent two veneers (2) mutually hangs down
Directly, three veneers (2) form Zhang San's clamping plate；
(4) it is cold-pressed, to group embryo, good three-ply board is cold-pressed, time 30-40min, pressure 11-13kg/cm2；
(5) hot pressing, hot pressing, time 15min, 120~125 DEG C of temperature, pressure 12- are carried out to the three-ply board after cold pressing
14kg/cm2；(6) cool down health, and the three-ply board after hot pressing is stood, and Temperature fall, is placed more than 3 days, discharges stress；
(7) embryo is organized again, and two-sided roller coat glue above and below the three-ply board good to health, the coating weight of single side is 220~235g/
m2, then carry out group embryo and form nine clamping plates；
(8) it is cold-pressed, nine clamping plates good to group embryo are cold-pressed, time 35-45min, pressure 13-15kg/cm2；
(9) nine clamping plates after cold pressing are carried out hot pressing, time 20min, 120-125 DEG C of temperature, pressure 14-16kg/ by hot pressing
cm2；(10) health, nine clamping plates after hot pressing stand health, 5-6 days summer, 4-5 days winter；
(11) fixed thick cutting edge：Nine clamping plates good to health carry out cutting edge, fixed thick polishing；
(12) double applying：Thick good plate fixed to cutting edge is rule, two-sided roller glue, and then bottom surface is carried out at the same time fitting；
(13) it is cold-pressed：The sheetpile pile good to double applying, is then cold-pressed, and is cold-pressed time 25-30 minute, pressure 11-13kg/
cm2
(14) hot pressing：Hot pressing, time 6min, 105-110 DEG C of temperature, pressure 13-15kg/ are carried out to the double applying plate being cold-pressed
cm2；
(15) health determines thickness and opens bar：The plain plate good to hot pressing carries out the health of 3-5 days, and the fixed thickness of sanding, deburring, opens bar, obtains
To lath, open the smooth heap of plain plate after bar and stamp, place more than 2 days it is spare；
(16) tongue and groove：Tongue and groove is carried out to lath, flat button or lock can be opened up as requested；
(17) it is modelled after an antique：Processing modelled after an antique is directly carried out to plate face, plate face effect includes lifts, blunt knife, random knife；
(18) priming paint：Priming paint roller coat is carried out to the plate after processing modelled after an antique, specific steps, which are followed successively by, adjusts aqueous priming paint, coating attached
Priming paint, putty mends soil, hardening primer, sanding priming paint, offline；
(19) numerial code spray drawing：Sanding is first carried out to priming paint plate, is then destaticed to carrying out dedusting, then carry out digital pattern spray
Paint；
(20) finishing coat：Plate after numerial code spray drawing is first dried, and makes top layer ink fully dry, then carries out finishing coat roller
Apply, specific steps be followed successively by coating adhesion primer, coating wear-resistant primer, sanding priming paint, hardening primer, coating except aldehyde finishing coat, under
Line；
(21) sealing wax：Sealing wax processing is carried out to the surrounding tongue and groove of lath, plays waterproof and dampproof effect.
Beneficial effects of the present invention are as follows：
The fire-retardant digital coloured drawing floor modelled after an antique of above-mentioned no aldehyde, by being added to base material without aldehyde, fire protection flame retarding is modified, and makes ground
The environmental protection of plate, fire resistance greatly promote, and along with the utilization of digital coloured drawing technology, have not only expanded the space that uses on floor, but also
Beautifying household environment.
Brief description of the drawings
Fig. 1 is the structure diagram of one embodiment of the invention.
Embodiment
The invention will be further described with reference to the accompanying drawings and embodiments.
Referring to Fig. 1, this without the fire-retardant digital coloured drawing floor modelled after an antique of aldehyde, it is described including substrate, be disposed on the substrate surface
Panel 1, the bottom plate 3 for being arranged on base lower surface, the substrate include some veneers 2, wood grain are pressed between two adjacent veneer 2
Crisscross mode stacks, and is adhesively fixed between the adjacent veneer 2, panel 1, bottom plate 3 by the fire-retardant glue of no aldehyde.
The formaldehydeless addition and the MDI glue with fire retardant performance.
The upper surface of the panel 1 successively covered with white or clear primer layer, the digital coloured drawing figure layer for decoration, can
The top coat layer of adsorption-decomposition function formaldehyde.
The pattern of the digital coloured drawing figure layer is a variety of to sample, there is stone pattern, wood grain, woven design, landscape figure picture etc..
The paint effect can be closed or open and semi open model.
2 thickness of veneer is 1.3-3.6mm.
1 thickness of panel is 1.2-3mm.
The panel 1 is entire body plates of solid wood 2, by birch, hard maple wood plus maple, oak, elm, black walnut, teak, Asia
One kind in Hua Li, sour branch, Acacia is fabricated.
The veneer 2 is fabricated by poplar or Eucalyptus.
The preparation method on the modelled after an antique digital coloured drawing floor fire-retardant without aldehyde, comprises the technical steps that：
(1) log veneer (2) rotary-cut, selects log of the diameter grade in more than 80mm to carry out boiling, after wooden softening, carries out
Rotary-cut, is then dried with infrared drier, and the moisture control of veneer (2) is in 8%-10%；
(2) impregnation, carries out impregnation by veneer (2), allows glue fully penetrated to be filled into the pore of veneer (2)；
(3) embryo is organized, a group embryo is carried out to the veneer (2) after impregnation, the grain direction per adjacent two veneers (2) mutually hangs down
Directly, three veneers (2) form Zhang San's clamping plate；
(4) it is cold-pressed, to group embryo, good three-ply board is cold-pressed, time 30-40min, pressure 11-13kg/cm2；
(5) hot pressing, hot pressing, time 15min, 120~125 DEG C of temperature, pressure 12- are carried out to the three-ply board after cold pressing
14kg/cm2；(6) cool down health, and the three-ply board after hot pressing is stood, and Temperature fall, is placed more than 3 days, discharges stress；
(7) embryo is organized again, and two-sided roller coat glue above and below the three-ply board good to health, the coating weight of single side is 220~235g/
m2, then carry out group embryo and form nine clamping plates；
(8) it is cold-pressed, nine clamping plates good to group embryo are cold-pressed, time 35-45min, pressure 13-15kg/cm2；
(9) nine clamping plates after cold pressing are carried out hot pressing, time 20min, 120-125 DEG C of temperature, pressure 14-16kg/ by hot pressing
cm2；
(10) health, nine clamping plates after hot pressing stand health, 5-6 days summer, 4-5 days winter；
(11) fixed thick cutting edge：Nine clamping plates good to health carry out cutting edge, fixed thick polishing；
(12) double applying：Thick good plate fixed to cutting edge is rule, two-sided roller glue, and then bottom surface is carried out at the same time fitting；
(13) it is cold-pressed：The sheetpile pile good to double applying, is then cold-pressed, and is cold-pressed time 25-30 minute, pressure 11-13kg/
cm2
(14) hot pressing：Hot pressing, time 6min, 105-110 DEG C of temperature, pressure 13-15kg/ are carried out to the double applying plate being cold-pressed
cm2；
(15) health determines thickness and opens bar：The plain plate good to hot pressing carries out the health of 3-5 days, and the fixed thickness of sanding, deburring, opens bar, obtains
To lath, open the smooth heap of plain plate after bar and stamp, place more than 2 days it is spare；
(16) tongue and groove：Tongue and groove is carried out to lath, flat button or lock can be opened up as requested；
(17) it is modelled after an antique：Processing modelled after an antique is directly carried out to plate face, plate face effect includes lifts, blunt knife, random knife；
(18) priming paint：Priming paint roller coat is carried out to the plate after processing modelled after an antique, specific steps, which are followed successively by, adjusts aqueous priming paint, coating attached
Priming paint, putty mends soil, hardening primer, sanding priming paint, offline；
(19) numerial code spray drawing：Sanding is first carried out to priming paint plate, is then destaticed to carrying out dedusting, then carry out digital pattern spray
Paint；
(20) finishing coat：Plate after numerial code spray drawing is first dried, and makes top layer ink fully dry, then carries out finishing coat roller
Apply, specific steps be followed successively by coating adhesion primer, coating wear-resistant primer, sanding priming paint, hardening primer, coating except aldehyde finishing coat, under
Line；
(21) sealing wax：Sealing wax processing is carried out to the surrounding tongue and groove of lath, plays waterproof and dampproof effect.
The digital coloured drawing floor burst size of methanal≤0.1mg/L manufactured by above-mentioned technique, fire retardant performance reach B1
Level.
Above-described embodiment is the preferred solution of the present invention, and the present invention can also have other embodiments.The technology of this area
Personnel can also make equivalent variations or replacement on the premise of without prejudice to spirit of the invention, these equivalent modifications or replacement are wrapped
It is contained in the scope set by the application claim.
Claims (6)
1. the fire-retardant digital coloured drawing floor modelled after an antique of a kind of no aldehyde, it is characterised in that including substrate, be disposed on the substrate the face on surface
Plate (1), the bottom plate (3) for being arranged on base lower surface, the substrate include some veneers (2), between two adjacent veneer (2)
Stacked by the crisscross mode of wood grain, pass through the fire-retardant glue of no aldehyde between the adjacent veneer (2), panel (1), bottom plate (3)
Water is adhesively fixed, and the glue is formaldehydeless addition and has the MDI glue of fire retardant performance, the upper table of the panel (1)
Face the digital coloured drawing figure layer covered with prime coat, for decoration, the top coat layer of adsorbable decomposing formaldehyde successively.
2. the fire-retardant digital coloured drawing floor modelled after an antique of no aldehyde according to claim 1, it is characterised in that the veneer (2) is thick
Spend for 1.3-3.6mm.
3. the fire-retardant digital coloured drawing floor modelled after an antique of no aldehyde according to claim 1, it is characterised in that the panel (1) is thick
Spend for 1.2-3mm.
4. the fire-retardant digital coloured drawing floor modelled after an antique of no aldehyde according to claim 1, it is characterised in that the panel (1) is
Entire body plates of solid wood, by birch, hard maple wood plus maple, oak, elm, black walnut, teak, sub- flower pears, sour branch, Acacia
One kind is fabricated.
5. the fire-retardant digital coloured drawing floor modelled after an antique of no aldehyde according to claim 1, it is characterised in that the bottom plate (3) by
One kind in poplar, Eucalyptus, beech is fabricated.
6. the fire-retardant digital coloured drawing floor modelled after an antique of no aldehyde according to claim 1, it is characterised in that the veneer (2) by
Poplar or Eucalyptus are fabricated.