CN207044850U - A kind of compound vehicle seat leather - Google Patents
A kind of compound vehicle seat leather Download PDFInfo
- Publication number
- CN207044850U CN207044850U CN201720283969.3U CN201720283969U CN207044850U CN 207044850 U CN207044850 U CN 207044850U CN 201720283969 U CN201720283969 U CN 201720283969U CN 207044850 U CN207044850 U CN 207044850U
- Authority
- CN
- China
- Prior art keywords
- layer
- vehicle seat
- tpu
- compound vehicle
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model provides a kind of compound vehicle seat leather, including base cloth layer, spongy layer and TPUE rubber TPU layer；The base cloth layer is combined into first structure with the spongy layer, and the TPU layer is bonded with the base fabric aspect of the first structure.The utility model provides a kind of compound vehicle seat leather, by first by base cloth layer with spongy layer is compound is allowed to be firmly bonded, the base fabric aspect of the structure after bonding is bonded with TPU layer, skin effect phenomenon occurs to avoid the TPU layer after being bonded from pressing.Spongy layer provides elasticity, pliability simultaneously so that relaxation sense of the compound vehicle seat leather with corium, voluptuousness.
Description
Technical field
It the utility model is related to technical field of synthetic leather, and in particular to a kind of compound vehicle seat leather.
Background technology
Improved with the living standard of people, quality that people remove from offices to compound vehicle seat, susceptibility and to environment guarantor
The attention of shield.At present, TPU synthetic leather is increasingly liked by people, but TPU synthetic leather Boardy Feeling, surface are felt without relaxation
Limit its application in automotive seat leather field.
Utility model content
The purpose of this utility model is to be directed to above-mentioned the deficiencies in the prior art, there is provided a kind of compound vehicle seat
Leather, avoid the pressing of the TPU layer after fitting from skin effect phenomenon occur, while there is the relaxation sense of corium, voluptuousness.
To achieve the above object, the utility model employs following technical scheme：The utility model provides a kind of compound
Type automotive seat is removed from office：The compound vehicle seat leather includes base cloth layer, spongy layer and TPUE rubber TPU
Layer；The base cloth layer is combined into first structure with the spongy layer, and the base fabric aspect of the TPU layer and the first structure is pasted
Close.
Preferably, the base cloth layer is bonded by polyurethane PU R PURs and the spongy layer.
Preferably, compound vehicle seat leather also includes：PE polyurethane layer；The PU layers paste with the TPU layer
Close.
Preferably, compound vehicle seat leather also includes：Layer at table, layer is bonded with the PU layers at the table.
Preferably, layer is provided with lines at the table.
Using above-mentioned technical proposal, the utility model passes through provided with base cloth layer, spongy layer and TPUE
Rubber TPU layer；The base cloth layer is combined into first structure, the base fabric of the TPU layer and the first structure with the spongy layer
Aspect is bonded.The utility model provides a kind of compound vehicle seat leather, by first by base cloth layer with spongy layer is compound is allowed to
It is firmly bonded, base fabric elder generation and the first compound elder generation that is allowed to of sponge are integral, and the base fabric aspect of the structure after bonding and TPU layer are pasted
Close, sponge provides elasticity, pliability, presses after protection fitting TPU layer and does not flake, that is, avoids the TPU layer pressing after fitting
There is skin effect phenomenon.Spongy layer provides elasticity, pliability simultaneously so that relaxation sense of the compound vehicle seat leather with corium,
Voluptuousness.
Brief description of the drawings
Fig. 1 is the structural representation of compound vehicle seat provided by the utility model leather.
Embodiment
In order that the purpose of this utility model, technical scheme and advantage are more clearly understood, below in conjunction with the accompanying drawings and implement
Example, the utility model is further elaborated.It should be appreciated that specific embodiment described herein is only explaining this
Utility model, it is not used to limit the utility model.
Fig. 1 is the structural representation of compound vehicle seat of the present utility model leather.As shown in figure 1, compound vehicle seat
Chair leather includes base cloth layer 4, spongy layer 5 and TPUE rubber TPU layer 3；Base cloth layer 4 is combined into spongy layer 5
First structure, TPU layer 3 are bonded with the surface of the base cloth layer 4 of first structure.After tested, it is provided by the utility model compound
Automotive seat is removed from office, by first by base cloth layer with spongy layer is compound is allowed to be firmly bonded, by the base fabric aspect of the structure after bonding and
TPU layer is bonded, to avoid the TPU layer pressing after fitting from skin effect phenomenon occur.Spongy layer provides elasticity, pliability simultaneously so that
Relaxation sense of the compound vehicle seat leather with corium, voluptuousness.
Base cloth layer 4 provided by the utility model is bonded by polyurethane PU R PURs and spongy layer 5, be implemented as by
Polyurethane PU R PURs after 80 DEG C of baking oven preheating 3h, base cloth layer 4 and spongy layer 5 are carried out it is compound, after compound post curing 24h
Form first structure.Preferably, compound vehicle seat leather also includes：TPU layer 3, it is implemented as drying polyether-type TPU layer
80 DEG C of case is extruded after drying 2h at 190-200 DEG C, and extrusion TPU layer is thick 0.3 millimeter, is bonded on the base cloth layer after compounded with sponge layer,
Speed 8m/s.Preferably, compound vehicle seat leather also includes：Layer 1, polyurethane at PE polyurethane layer 2 and table
Ester PU layers 2 are bonded with TPU layer 3, and layer 1 is bonded with PU layers 2 at table, and layer 1 is provided with lines at table.Roller coat is implemented as, is used
Environment-friendly type aqueous material, 30C rollers, rotating ratio 3:1st, 130 DEG C of oven temperature, speed 10m/s, layer is in 195-205 DEG C of fluorescent tube at table
Heat 30s, inhale line 30s, speed 8m/s.Preferably, 120 mesh roller feedings of above-mentioned environment-friendly type aqueous material, 130 DEG C of oven temperature,
Speed 10m/s.Finally, the rejecting abnormalities product in caused finished product.
Embodiment 1
A kind of preparation method of compound vehicle seat leather, carries out following step successively：
Step 1, sponge are compound, and by polyurethane PU R PURs after 80 DEG C of preheating 3h of baking oven, base cloth layer and spongy layer are entered
Row is compound, and first structure is formed after compound post curing 24h；
Step 2, extrusion fitting, polyether-type TPU is extruded at 190-200 DEG C after 80 DEG C of baking oven dries 2h, extrudes TPU layer
The shiny surface of thick 0.3 millimeter of fitting base cloth layer；
Step 3, roller coat, use environment-friendly type aqueous material, 30C rollers, rotating ratio 3:1st, 130 DEG C of oven temperature, speed 10m/
s；
Step 4, line is inhaled, layer is in 195-205 DEG C of fluorescent tube heating 30s, suction line 30s, speed 8m/s at table；
Step 5, printing, environment-friendly type aqueous material 120 mesh roller feedings, 130 DEG C of oven temperature, speed 10m/s；
Step 6, Cheng Jian, the rejecting abnormalities product in caused finished product.
Resulting compound vehicle seat leather performance indications are shown in Table 1：
The compound vehicle seat of table 1 removes from office performance indications
Embodiment described above only expresses embodiment of the present utility model, and its description is more specific and detailed, but simultaneously
Therefore the limitation to the utility model patent scope can not be interpreted as.It should be pointed out that the ordinary skill for this area
For personnel, without departing from the concept of the premise utility, various modifications and improvements can be made, these belong to this
The protection domain of utility model.Therefore, the protection domain of the utility model patent should be determined by the appended claims.
Claims (4)
- A kind of 1. compound vehicle seat leather, it is characterised in that including：Base cloth layer, spongy layer, TPUE rubber Glue TPU layer and PE polyurethane layer；The base cloth layer is combined into first structure, the TPU layer and institute with the spongy layer The base fabric aspect fitting of first structure is stated, the PU layers are bonded with the TPU layer.
- 2. compound vehicle seat leather according to claim 1, it is characterised in that the base cloth layer passes through polyurethane PU R PUR bonds with the spongy layer.
- 3. compound vehicle seat leather according to claim 2, it is characterised in that also include：Layer at table, layer at the table It is bonded with the PU layers.
- 4. compound vehicle seat leather according to claim 3, it is characterised in that layer is provided with lines at the table.