CN205291848U - Automatic former of preparation stereoplasm carbon graphite felt section of thick bamboo material - Google Patents
Automatic former of preparation stereoplasm carbon graphite felt section of thick bamboo material Download PDFInfo
- Publication number
- CN205291848U CN205291848U CN201521089012.2U CN201521089012U CN205291848U CN 205291848 U CN205291848 U CN 205291848U CN 201521089012 U CN201521089012 U CN 201521089012U CN 205291848 U CN205291848 U CN 205291848U
- Authority
- CN
- China
- Prior art keywords
- graphite felt
- cylinder material
- forming equipment
- hard carbon
- automatic forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides an automatic former of preparation stereoplasm carbon graphite felt section of thick bamboo material, belongs to carbon graphite felt preparation technical field. This automation former includes the saturating device connect squeeze device, and the wind is connected to the extrusion device. Saturating device includes that the splendid attire has the dip tank of adhesive, and the bottom of dip tank sets up agitating unit, and the extrusion device includes at least a set of extrusion wheel, and the extrusion wheel is the wheel that a set of structure from top to bottom set up, and the wind includes motor connecting cylinder material centre form. The utility model discloses an automatic mode compared with the compound carbon graphite felt material of traditional manual parcel, glues closelyr between layer and the layer, be difficult for the layering, and the accuracy is high, and intensity is high, and the ash content is few, and thermal insulation performance improves, improvement life, adopt the automated production mode, only need be at initial stage 2 -3 name operative employee material loading to and monitor in manufacturing process and to accomplish, practice thrift 70% operating time, improved production efficiency greatly, reduce work and material cost.
Description
Technical field
This utility model belongs to carbon graphite felt preparing technical field, particularly to a kind of automatic forming equipment making hard carbon/graphite felt cylinder material.
Background technology
Traditional carbon graphite felt cylinder material manufacture method is the mode making to be wound around by hand, on cylinder material internal mold, first wrap up one layer of graphite paper, after on graphite paper use binding agent attach carbon cloth, after on carbon cloth, wrap up soft carbon felt, finally attach one layer of carbon cloth and one layer of graphite paper more successively, namely manual adhesive means parcel is adopted between layers, it is very not tight that the firmly inequality of artificial manual parcel is easily caused each ply adhesion, in use it is easily generated delamination splitting phenomenon, heat-insulating property affects adversely, and this process is it is generally required to 5-6 people operates simultaneously, production operation overlong time, production efficiency is low, human cost is high.
Utility model content
The purpose of this utility model is to overcome above the deficiencies in the prior art, it is provided that the automatic forming equipment of a kind of making hard carbon/graphite felt cylinder material adopting automated production mode. This utility model is the technical scheme is that a kind of automatic forming equipment making hard carbon/graphite felt cylinder material for achieving the above object, it is characterised in that: including immersion system and connect pressurizing unit, pressurizing unit connects wind.
Further, immersion system includes the maceration tank being loaded with binding agent, and the bottom of maceration tank arranges agitating device.
Further, the bottom of immersion system connects iron wire filter screen, and iron wire filter screen is positioned at the top of agitating device.
Further, pressurizing unit includes least one set squeegee roller, and squeegee roller is connected to one end of maceration tank.
Further, squeegee roller is the wheel that up-down structure is arranged, and turning to of upper lower whorl is identical.
Further, the lower end of squeegee roller connects deflector.
Further, wind includes motor connecting cylinder material internal mold.
Further, motor is can rate controlling threephase asynchronous.
This utility model adopts automatic mode, compared with traditional craft parcel composite carbon/graphite felt materials, viscous more tight between layers, is not easily layered, and degree of accuracy is high, and intensity is high, and ash is few, and heat-insulating property improves, and improves service life; Adopt automated production mode, it is only necessary to operate employee's feeding in initial period 2-3 name, and monitor in manufacturing process and can complete, saved for 70% operating time, substantially increase production efficiency, reduce and work into and material basis.
Accompanying drawing explanation
Fig. 1 is the structural representation of a kind of automatic forming equipment making hard carbon/graphite felt cylinder material.
In figure: 1, immersion system, 2, pressurizing unit, 3, wind, 4, binding agent, 5, maceration tank, 6, agitating device, 7, squeegee roller, 8, motor, 9, cylinder material inner membrance, 10, deflector, 11, iron wire filter screen, 12, soft carbon felt.
Detailed description of the invention
Below in conjunction with accompanying drawing, this utility model is described further, but utility model is not limited to specific embodiment.
Embodiment 1
A kind of automatic forming equipment making hard carbon/graphite felt cylinder material as shown in Figure 1, connects pressurizing unit 2 including immersion system 1, and pressurizing unit 2 connects wind 3.
Immersion system 1 includes the maceration tank 5 being loaded with binding agent 4, and the bottom of maceration tank 5 arranges agitating device 6, and the bottom of immersion system 1 connects iron wire filter screen 11, and iron wire filter screen 11 is positioned at the top of agitating device 6. Agitating device 6 arrange in order that immerse in binding agent 4 process in maceration tank 5 in soft carbon felt 12, the graphite powder ensured in binding agent 4 does not precipitate, so that the graphite powder of the binding agent 4 immersed in soft carbon felt 12 has stable component ratio, and then the bond property of binding agent 4 is enable to be fully played.
Pressurizing unit 2 includes one group of squeegee roller 7, and squeegee roller 7 is the wheel that one group of up-down structure is arranged, and turning to of upper lower whorl is identical, and squeegee roller 7 is connected to one end of maceration tank 5, and the lower end of squeegee roller 7 connects deflector 10. Owing to binding agent 4 contained in the soft carbon felt 12 that spreads out of from maceration tank 5 is more, therefore pressurizing unit 2 is used to be squeezed out by binding agent 4 unnecessary in soft carbon felt 12, deflector 10 is utilized to flow back in maceration tank 5, the pickup of binding agent 4 in soft carbon felt 12 can be controlled on the one hand, the effect economized in raw materials can also be played on the other hand.
Wind 3 includes motor 8 connecting cylinder material internal mold 9, and motor 8 is can rate controlling threephase asynchronous. The slewing rate of motor 8 application cylinder material internal mold 9, coordinates pressurizing unit 2 that a material can be made uniformly fully tight Wrapping formed.
Embodiment 2
The work process of a kind of automatic forming equipment making hard carbon/graphite felt cylinder material described in embodiment 1 is: wrap up one layer of template on cylinder material internal mold 9, graphite paper in attaching, use binding agent to attach last layer carbon cloth again on graphite paper surface, the automatic forming equipment of the described hard carbon of rear unlatching/graphite felt cylinder material, the rotating speed (see table 1) of motor 8 is adjusted according to target cylinder material diameter, soft carbon felt 12 is first dipped in the binding agent 4 in maceration tank 5, extrusion process is rotated backward afterwards by the upper lower whorl of squeegee roller 7, unnecessary binding agent 4 is extruded, it is back in maceration tank 5 by deflector 10, soft carbon felt 12 through extruding is wound to the automatic forming namely completing a material on a material inner membrance 9 uniformly tightly.
The adjustment of rotational speed synopsis of 1 material diameter of table and motor
| Cylinder material diameter (mm) | Motor speed (min/ circle) | Cylinder material diameter (mm) | Motor speed (min/ circle) |
| Less than 400 | 3 | 400��800 | 5 |
| 800��1500 | 9 | More than 1500 | 15 |
Attach last layer carbon cloth, one layer of graphite paper, template after reaching product thickness requirement more successively, adopt external mold parcel, make to be tightened by bolts, enter air dry oven and slough interior outer mold after 180 DEG C dry 10 hours.Finally, at 1800 DEG C, obtain hard carbon felt cylinder material through high-temperature heat treatment, at 2300 DEG C, obtain hard graphite felt cylinder material.
This utility model adopts automatic mode, compared with traditional craft parcel composite carbon/graphite felt materials, viscous tightr between layers, not easily being layered, degree of accuracy is high, and intensity is high, ash is few, heat-insulating property improves, and improves service life, uses the product of this utility model production and uses conventionally produced product quality contrast as shown in table 2.
Table 2 uses the product that this utility model produces to contrast with using conventionally produced product quality
| Intensity (MP) | Density (g/cm3) | Ash (ppm) | Thermal conductivity (w/mk) | |
| Traditional handicraft | 1.5-2.1 | 0.30-0.35 | 345 | 0.25-0.35 |
| This utility model | 2.5-3.5 | 0.25-0.31 | 262 | 0.15-0.20 |
Of the present utility model ultimate principle and principal character have more than been shown and described; skilled person will appreciate that this utility model is not restricted to the described embodiments; what the above embodiments and description described simply illustrates principle of the present utility model; under the premise without departing from this utility model spirit and scope; this utility model has various changes and modifications; these changes and improvements both fall within the scope that this utility model claims, and this utility model claims scope and defined by appending claims and equivalent.
Claims (8)
1. the automatic forming equipment making hard carbon/graphite felt cylinder material, it is characterised in that: including immersion system (1) and connect pressurizing unit (2), pressurizing unit (2) connects wind (3).
2. a kind of automatic forming equipment making hard carbon/graphite felt cylinder material according to claim 1, it is characterized in that: described immersion system (1) includes being loaded with the maceration tank (5) of binding agent (4), and the bottom of maceration tank (5) arranges agitating device (6).
3. a kind of automatic forming equipment making hard carbon/graphite felt cylinder material according to claim 1 and 2, it is characterized in that: the bottom of described immersion system (1) connects iron wire filter screen (11), and iron wire filter screen (11) is positioned at the top of agitating device (6).
4. a kind of automatic forming equipment making hard carbon/graphite felt cylinder material according to claim 1, it is characterized in that: described pressurizing unit (2) includes least one set squeegee roller (7), and squeegee roller (7) is connected to one end of maceration tank (5).
5. a kind of automatic forming equipment making hard carbon/graphite felt cylinder material according to claim 4, it is characterised in that: the wheel that described squeegee roller (7) is arranged for up-down structure, turning to of upper lower whorl is identical.
6. a kind of automatic forming equipment making hard carbon/graphite felt cylinder material according to claim 4 or 5, it is characterised in that: the lower end of described squeegee roller (7) connects deflector (10).
7. a kind of automatic forming equipment making hard carbon/graphite felt cylinder material according to claim 1, it is characterised in that: described wind (3) includes motor (8) connecting cylinder material internal mold (9).
8. a kind of automatic forming equipment making hard carbon/graphite felt cylinder material according to claim 7, it is characterised in that: described motor (8) is can rate controlling threephase asynchronous.