CN206749303U - Delustring increases the gold stamping paper tinsel that rubs - Google Patents
Delustring increases the gold stamping paper tinsel that rubs Download PDFInfo
- Publication number
- CN206749303U CN206749303U CN201720214214.8U CN201720214214U CN206749303U CN 206749303 U CN206749303 U CN 206749303U CN 201720214214 U CN201720214214 U CN 201720214214U CN 206749303 U CN206749303 U CN 206749303U
- Authority
- CN
- China
- Prior art keywords
- delustring
- layer
- gold stamping
- paper tinsel
- rubs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model belongs to technical field of composite materials, is related to gold stamping paper tinsel, and more particularly to a kind of delustring increases the gold stamping paper tinsel that rubs.Following functional layer is comprised at least from configuration aspects：In base material film（1）On coat release layer successively（2）, grittiness layer（3）, extinction layer（4）, separation layer（5）, tack coat（6）.Wherein grittiness layer（3）It is delustring, increases the key that the hot stamping foil that rubs is raising thermoprint product coefficient of friction, extinction layer（4）It is the key for realizing gold stamping product surface delustring.Delustring disclosed in the utility model increases the gold stamping paper tinsel that rubs, delustring or raising coefficient of friction suitable for some specialities surfaces, such as the delustring etc. that classroom blackboard face, city high rise building glass outer wall need, also or climbing gear, sports apparatus surface need to improve coefficient of friction etc..It is made because delustring increases the gold stamping paper tinsel that rubs of anti-abrasive material, it is durable in use；It is simultaneously similar with common gold stamping paper tinsel, can repeatedly thermoprint to ensure the delustring of physical surface, increase performance of rubbing.
Description
Technical field
The utility model belongs to technical field of composite materials, is related to gold stamping paper tinsel, and more particularly to a kind of delustring increases the gold stamping paper tinsel that rubs.
Background technology
Gold stamping paper tinsel since the advent of the world was after in 1 hundred 50 wind and rain, from the thermoprint for being initially only applicable to clothing, pencil surface
Paper finally, wood surface thermoprint, it is attempted to assign gold stamping paper tinsel and more puts space to good use.For example,
ZL2015210767541, a kind of software surface gilding anodized aluminium, disclosing one kind can be in the soft material such as sponge, rubber
Expect the anodized aluminium of surface thermoprint.
At the same time, with the aesthetic continuous improvement of people and the high speed development of modern science and technology, more outward appearances are novel, figure
The exquisite gold stamping paper tinsel of case is come out one after another.It is common laser gold blocking anodized aluminium to improve obtain earliest, its preparation technology with it is traditional
Hot stamping foil is similar, and mold pressing procedure is simply set up after chromatograph is coated and causes chromatograph to produce the effect of radium-shine illusion-colour.After again
Come, hot stamping foil is introduced into field of anti-counterfeit technology, and the scientists of German KURZ company take the lead in a series of anti-fake holographics
Pattern invests chromatograph surface, is manufactured that first laser holography anti-counterfeit internal hot stamping foil.
Researchers can always bring unexpected effect to updating for gold stamping paper tinsel.At present, suitable for not
Same domain, the gold stamping paper tinsel prepared using different process have formed numerous and jumbled group.For example, ZL2016205577024, Yi Zhongkang
Gold stamping paper tinsel is aoxidized, anti-corrosion, antioxidant effect can be reached in one layer of special electrochemical aluminum foil of body surface thermoprint by disclosing；Example
Such as, ZL2016204933464, a kind of heat resistant composite film-stuck disclose the composite film-stuck of thermal resistance excellent performance, and production cost is low
It is honest and clean, also using, tear off simplicity；For another example ZL201620046297X, a kind of electrochemical aluminium gold-stamped paper tinsel of high glaze, disclose a kind of table
The higher hot stamping foil of face glossiness, it is widely used in traffic road because it is low to light absorption, reflecting effect is strong
Board, special direction board make, and less process make it that finished product rate is high, production cost is low.
With above-mentioned application field on the contrary, exactly needing glossiness relatively low or the gold stamping paper tinsel ability of delustring in some special dimensions
Meet consumption demand.For example, front-seat both sides student dysopia is usually caused in teacher's blackboard surface because of light mirror-reflection,
For this, people make blackboard surface usually using frosted glass, and not only cost is higher, and easily produce rupture in handling, make for a long time
With serious wear, change cumbersome etc.；For another example city high rise building uses disjunctor glass to improve room light brightness more, but again simultaneously
Cause the light pollution of building body exterior space；In addition, on some special tool(s) surfaces, people pass through polishing or special chemical material
Then occur that abrasion, surface increase phenomena such as material that rubs peels off to improve its coefficient of friction, but after long-time use.
If gold stamping paper tinsel is improved, assign its delustring, increase the characteristic rubbed, can solve the above problems well.
The content of the invention
The purpose of this utility model, it is disclosed in order to solve to need in some cases to rub to body surface delustring, increasing
A kind of delustring increases the gold stamping paper tinsel that rubs.
A kind of delustring increases the gold stamping paper tinsel that rubs, and following functional layer is comprised at least from configuration aspects：In base material film（1）On successively
Coat release layer（2）, grittiness layer（3）, extinction layer（4）, separation layer（5）, tack coat（6）.Wherein grittiness layer（3）It is delustring, increases
The hot stamping foil that rubs be improve thermoprint product coefficient of friction key, extinction layer（4）It is the pass for realizing gold stamping product surface delustring
Key.
The base material film（1）Thickness is between 10~100 μm.
The release layer（2）Coating dry measure is in 0.1~5.0 g/m2, coating layer thickness is between 0.01~2.0 μm.
The grittiness layer（3）Coating dry measure is in 10.0~50.0 g/m2, coating layer thickness control 10.0~50.0 μm it
Between.
The extinction layer（4）Coating dry measure is in 0.5~1.5 g/m2, coating layer thickness control between 0.3~1.2 μm.
The separation layer（5）Thickness is between 0.01~0.05 μm.
The tack coat（6）Coating dry measure is in 0.5~5.0 g/m2, coating layer thickness control between 1.0~5.0 μm.
Delustring disclosed in the utility model increases rub gold stamping paper tinsel, wherein base material film（1）Carrying is depended on as each coating afterwards
Thing, it is desirable to possess higher tensile resistance, preferable surface wettability, biaxially oriented polyester film, two-way can be selected
Stretch polyvinyl chloride film, polypropylene fibre film.Release layer（2）Base material film during as thermoprint（1）With holding boiling hot thing sur-face peeling
It is crucial, it is desirable to which that it can be melted when being heated, the characteristic of low-temperature setting, organic silicon resin, such as siloxanes can be selected to gather
Resin, silicones metlyl branching silicone oil or wax class material, such as synthesis paraffin, microcrystalline wax, Tissuemat E.Sand
Property layer（3）It is delustring, increases the key that the hot stamping foil that rubs is raising thermoprint product coefficient of friction, it is desirable to class can be produced when being coated with
The coating effect of frosted texture is similar to, choice requirement wearability is good, while the anti-deformation nature that is heated during thermoprint is higher, can select
High temperature resistant polyketone resin, high temperature resistant acrylic resin, thermostable phenolic resin, high-temperature-resistant epoxy resin etc..Extinction layer（4）It is real
The key of existing gold stamping product surface delustring, it is desirable to the characteristics such as it is high to light absorption, light transmittance is low, so as in thermoprint carrier
Surface produces extinction effect, can select organic delustring wax liquor, 3M solid ceramic microballoons hybrid resin, TF-W series delustrings
Wax breast etc..Separation layer（5）Between extinction layer（4）With tack coat（6）Between, it is difficult to permeate and breaks its role is to tack coat material
Bad grittiness layer（3）With extinction layer（4）, especially grittiness layer（3）Possess certain space stereochemical structure, prevent oozing for tack coat material
It is crucial thoroughly；Separation layer（5）It can select the coat of metal, such as nickel, chromium, aluminium, zinc etc. or the higher height of sealing property
Molecule resin.Tack coat（6）As delustring, increase and rub gold stamping paper tinsel outermost layer, directly contacted with holding boiling hot thing surface during thermoprint, when being heated
Melt and produce stickiness and be attached to and hold boiling hot thing surface, cooling solidify afterwards ultimately form thermoprint finished product, tack coat（6）Thermoplastic resin
Can be polymethyl methacrylate, polyamide, polyphenylene oxide, polymethyl methacrylate etc..
As further preferred, base material film（1）It is optimal using biaxially oriented polyester film, thickness is optimal with 50 μm.
As further preferred, release layer（2）It is optimal using silicones metlyl branching silicone oil, with the g/ of coating dry measure 4.0
m2, 1.0 μm of coating layer thickness be optimal.
As further preferred, grittiness layer（3）It is optimal using high temperature resistant acrylic resin, with the g/m of coating dry measure 40.02、
35.5 μm of coating layer thickness is optimal.
As further preferred, extinction layer（4）With TF-W series delustrings wax breast to be optimal etc., with the g/ of coating dry measure 1.2
m2, 0.8 μm of coating layer thickness be optimal.TF-W series delustring wax breasts are produced by Zhejiang Province Chuanhua Co., Ltd.
As further preferred, separation layer（5）It is optimal using aluminium, is realized by vacuum aluminum-plating machine, 0.02 μm is with thickness
Most preferably.
As further preferred, tack coat（6）It is optimal using polymethyl methacrylate, with the g/m of coating dry measure 2.02、
1.2 μm of coating layer thickness is optimal.
Beneficial effect
Delustring disclosed in the utility model increases the gold stamping paper tinsel that rubs, and delustring or raising suitable for some specialities surfaces rub
Coefficient, such as the delustring etc. that classroom blackboard face, city high rise building glass outer wall need are wiped, also or climbing gear, sports apparatus table
Face needs to improve coefficient of friction etc..It is made because delustring increases the gold stamping paper tinsel that rubs of anti-abrasive material, it is durable in use.Simultaneously with it is common
Gold stamping paper tinsel is similar, can repeatedly thermoprint to ensure that the delustring of physical surface, increasing rub performance.
Brief description of the drawings
Fig. 1, delustring increase gold stamping paper tinsel deployed configuration schematic diagram of rubbing；
Fig. 2, delustring increase the structural representation for the gold stamping paper tinsel that rubs.
Wherein, 1, base material film, 2, release layer, 3, grittiness layer, 4, extinction layer, 5, separation layer, 6, tack coat.
Embodiment
The utility model is described in detail with reference to specific embodiment, following examples will be helpful to this area
Technical staff further understands the utility model, but does not limit the utility model in any form.It should be pointed out that to ability
For the technical staff in domain, without departing from the concept of the premise utility, various modifications and improvements can be made, these
Belong to the scope of protection of the utility model.
A kind of delustring increases the gold stamping paper tinsel that rubs, functional layer structure as shown in Figure 1, 2, in base material film（1）On coat release layer successively
（2）, grittiness layer（3）, extinction layer（4）, separation layer（5）, tack coat（6）.Wherein grittiness layer（3）It is delustring, increases gold stamping electrification of rubbing
Aluminium be improve thermoprint product coefficient of friction key, extinction layer（4）It is the key for realizing gold stamping product surface delustring.
Base material film（1）Carrier is depended on as each coating afterwards, it is desirable to possesses higher tensile resistance, preferable table
Face wettability.Base material film（1）Biaxially oriented polyester film, biaxial tension polyvinyl chloride film, polypropylene fibre can be selected
Film.Thickness is between 10~100 μm.
Release layer（2）Base material film during as thermoprint（1）Key with holding boiling hot thing sur-face peeling, it is desirable to which it can be when heated
Melting, the characteristic of low-temperature setting.Release layer（2）Organic silicon resin, such as siloxane polymerization resin, silicones first can be selected
Base branched chain silicone or wax class material, such as synthesis paraffin, microcrystalline wax, Tissuemat E.Coating dry measure is 0.1~5.0
g/m2, coating layer thickness is between 0.01~2.0 μm.
Grittiness layer（3）It is the key that delustring increases that the hot stamping foil that rubs is raising thermoprint product coefficient of friction, it is desirable to when being coated with
The coating effect similar to frosted texture can be produced, choice requirement wearability is good, while be heated during thermoprint anti-deformation nature compared with
It is high.Grittiness layer（3）High temperature resistant polyketone resin, high temperature resistant acrylic resin, thermostable phenolic resin, fire resistant epoxy can be selected
Resin etc..Coating dry measure is in 10.0~50.0 g/m2, coating layer thickness control between 10.0~50.0 μm.
Extinction layer（4）It is the key for realizing gold stamping product surface delustring, it is desirable to which it is high to light absorption, light transmittance is low etc.
Characteristic, to produce extinction effect on thermoprint carrier surface.Extinction layer（4）Organic delustring wax liquor, 3M can be selected solid
Ceramic microsphere hybrid resin, TF-W series delustring wax breasts etc..Coating dry measure is in 0.5~1.5 g/m2, coating layer thickness control exist
Between 0.3~1.2 μm.
Separation layer（5）Between extinction layer（4）With tack coat（6）Between, its role is to tack coat material to be difficult to infiltration simultaneously
Destroy grittiness layer（3）With extinction layer（4）, especially grittiness layer（3）It must be stereoeffect to possess, and prevent tack coat material
Infiltration will be crucial.Separation layer（5）Can select the coat of metal, for example, nickel, chromium, aluminium, zinc etc. or sealing property compared with
High macromolecule resin.Thickness is between 0.01~0.05 μm.
Tack coat（6）Increase as delustring and rub gold stamping paper tinsel outermost layer, directly contact with holding boiling hot thing surface during thermoprint, melted when heated
Melt and produce stickiness and be attached to and hold boiling hot thing surface, cooling solidify afterwards ultimately form thermoprint finished product.Tack coat（6）Thermoplastic resin can
To be polymethyl methacrylate, polyamide, polyphenylene oxide, polymethyl methacrylate etc..Coating dry measure is in 0.5~5.0 g/
m2, coating layer thickness control between 1.0~5.0 μm.
Technological means disclosed in the utility model is not limited only to the technological means disclosed in above-mentioned embodiment, also
Including being combined formed technical scheme by above technical characteristic.It should be pointed out that the ordinary skill for the art
For personnel, on the premise of the utility model principle is not departed from, some improvements and modifications can also be made, these are improved and profit
Decorations are also considered as the scope of protection of the utility model.
Claims (10)
1. a kind of delustring increases the gold stamping paper tinsel that rubs, it is characterised in that：In base material film（1）On at least coat release layer successively（2）, grittiness layer
（3）, extinction layer（4）, separation layer（5）And tack coat（6）.
2. delustring according to claim 1 increases the gold stamping paper tinsel that rubs, it is characterised in that：The base material film（1）Thickness is 10~100
Between μm.
3. delustring according to claim 1 increases the gold stamping paper tinsel that rubs, it is characterised in that：The release layer（2）Coating dry measure exists
0.1~5.0 g/m2, coating layer thickness is between 0.01~2.0 μm.
4. delustring according to claim 1 increases the gold stamping paper tinsel that rubs, it is characterised in that：The grittiness layer（3）Coating dry measure exists
10.0~50.0 g/m2, coating layer thickness control between 10.0~50.0 μm.
5. delustring according to claim 1 increases the gold stamping paper tinsel that rubs, it is characterised in that：The extinction layer（4）Coating dry measure exists
0.5~1.5 g/m2, coating layer thickness control between 0.3~1.2 μm.
6. delustring according to claim 1 increases the gold stamping paper tinsel that rubs, it is characterised in that：The separation layer（5）Thickness 0.01~
Between 0.05 μm.
7. delustring according to claim 1 increases the gold stamping paper tinsel that rubs, it is characterised in that：The tack coat（6）Coating dry measure exists
0.5~5.0 g/m2, coating layer thickness control between 1.0~5.0 μm.
8. delustring according to claim 2 increases the gold stamping paper tinsel that rubs, it is characterised in that：The base material film（1）50 μm of thickness.
9. delustring according to claim 3 increases the gold stamping paper tinsel that rubs, it is characterised in that：The release layer（2）Coating dry measure 4.0
g/m2, 1.0 μm of coating layer thickness；The grittiness layer（3）Coating dry measure is in 40 g/m2, 35.5 μm of coating layer thickness；The extinction layer（4）
The g/m of coating dry measure 1.22, 0.8 μm of coating layer thickness.
10. delustring according to claim 6 increases the gold stamping paper tinsel that rubs, it is characterised in that：The separation layer（5）0.02 μm of thickness；
The tack coat（6）The g/m of coating dry measure 2.02, 1.2 μm of coating layer thickness.