CN102896927B - Novel alumite suitable for rotary gold stamping on ultraviolet (UV) glazing oil paper - Google Patents
Novel alumite suitable for rotary gold stamping on ultraviolet (UV) glazing oil paper Download PDFInfo
- Publication number
- CN102896927B CN102896927B CN201210398942.0A CN201210398942A CN102896927B CN 102896927 B CN102896927 B CN 102896927B CN 201210398942 A CN201210398942 A CN 201210398942A CN 102896927 B CN102896927 B CN 102896927B
- Authority
- CN
- China
- Prior art keywords
- alumite
- percent
- gold stamping
- rotary
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to novel alumite suitable for rotary gold stamping on ultraviolet (UV) glazing oil paper. The alumite comprises a basic film layer, a film release layer, an information layer, an aluminized layer and a bonding layer, wherein the information layer comprises the following material components in percentage by mass: 85 to 90 percent of epoxy modified acrylic resin and 10 to 15 percent of metal complex dye toner; and the bonding layer comprises the following material components in percentage by mass: 10 to 20 percent of thermoplastic polyurethane hot melt adhesive, 1 to 2 percent of nano silica, 30 to 40 percent of toluene, 30 to 50 percent of butanone and 5 to 15 percent of isopropanol. The alumite has the characteristics of high gold stamping efficiency, transfer efficiency and adhesion, clear image-text edge and the like, coating thickness is reduced by 40 to 50 percent compared with that of the common alumite, and heat-conducting property is higher; and compared with the common UV flat gold stamping alumite, the alumite has the advantages that effective gold stamping speed can be improved from 40 to 60m/min to 90 to 120m/min when the alumite is applied to rotary UV gold stamping, and an optimization effect is obvious.
Description
Technical field
The present invention relates to printing technology, specifically a kind of novel electrochemical aluminium being applicable to rotary-cutting hot stamping on UV oil polish paper.
Background technology
Electrochemical aluminium gold-stamped is one very important post-press finishing technique in packages printing, and mainly gold stamping pattern, word, lines are with the ranking of outstanding product, trade mark, drop, beautify product, thus improve the class of packaging product.With the hot stamping foil of anti-counterfeiting information layer, due to complex manufacturing technology, forge difficulty greatly, more can play effective anti-fake effect.The Lacquer finish that UV oil polish is usually used in plastics or carton external packing bands, and plays even false proof effect attractive in appearance.Hot stamping foil and UV oil polish combine and will greatly improve class and the antifalse effect of product.
Electrochemical aluminium gold-stamped is the anodized aluminium coating with anti-counterfeiting information in medium film strips, transfers to the technique above stock under the action of heat and pressure.Time gold stamping, the tack coat of anodized aluminium film surface melts, and with stock surface travel adhesive force, the silicones flowing in the releasing agent of anodized aluminium internal layer simultaneously, be separated with carrier thin film, the graph text information on carrier thin film is just transferred to stock surface.During transfer; only have PUR to be heated to produce cohesive force and be greater than the adhesive force that releasing agent provides; just can reach global transfer effect; but the binding agent that current most of anodized aluminium uses does not mate with UV glazing oil reservoir, often can cause gold stamping loosely, picture and text shift and thoroughly or are not easily scratched.
And circle pressure circle high speed gilding technology, due to rollers roll speed, the pressure mode of action is contacted by face and changes linear contact lay into, and especially the speed of a motor vehicle is close to after 100 ms/min, and thermoprint is shorter for time of contact.Therefore, under same actuating pressure, require high to the heat-conductive characteristic of bronzing material and thermo-sensitive property.Conventional electrochemical aluminium is generally difficult to reach the effect of carrying out high speed rotary-cutting hot stamping on UV oil polish surface.
Chinese patent CN101284968B take amino acrylic resin as the oil polish system of prepolymer, can the timeliness of gold stamping property for UV oil polish, and prepared by reflection can round-the-clock gold stamping UV oil polish; Chinese patent CN102120908A has prepared UV oil polish that can be directly gold stamping on surface with acrylic resin, dilution property monomer composition, acrylamide and free radical initiation type initator, but it remains gold stamping mainly for platen, speed needs during rotary-cutting hot stamping cannot be met.
Summary of the invention
The technical problem to be solved in the present invention is: be difficult to realize high speed rotary-cutting hot stamping for various common UV oil polish paper, even be difficult to gold stamping problem, by optimal imaging resin and PUR, a kind of anodized aluminium product of optimization is provided, not only possesses holographic laser laser anti-counterfeiting effect, and can at UV oil polish paper surface, gold stamping speed is entered and can be reached 90 ~ 120m/min.
For solving the problems of the technologies described above, present invention employs following technical scheme:
A kind of novel electrochemical aluminium being applicable to rotary-cutting hot stamping on UV oil polish paper, comprise base membrane layer, release layer, Information Level, aluminium coated and tack coat successively from the bottom to top, the material composition of described Information Level and mass percent thereof are: epoxy modified acrylic resin 85 ~ 90%, premetallized dye toner 10 ~ 15%; The material composition of described tack coat and mass percent thereof are: hot retrospective polyurethane hot melt 10 ~ 20%, nano silicon 1 ~ 2%, toluene 30 ~ 40%, butanone 30 ~ 50%, isopropyl alcohol 5 ~ 15%.
Be applicable to the novel electrochemical aluminium of rotary-cutting hot stamping on UV oil polish paper as above, described base membrane layer is made up of polyethylene terephthalate film.
Be applicable to the novel electrochemical aluminium of rotary-cutting hot stamping on UV oil polish paper as above, described release layer is positioned on base membrane layer, and the fluorine-containing aqueous wax material standby by emulsified wax legal system is made.
Be applicable to the novel electrochemical aluminium of rotary-cutting hot stamping on UV oil polish paper as above, on described Information Level, positioning module is pressed with holographic laser anti-counterfeiting information, described holographic laser anti-counterfeiting information is at 85 ~ 100 DEG C, utilize soft moulding press, with the compacting of the pressure of 20 ~ 30kg on this information layer.
The present invention utilizes the imaging resin of optimization and PUR to make electrochemical aluminium gold-stamped material at a lower temperature, there is gold stamping efficiency high, there is the features such as high transfer efficiency, picture and text edge clear, strong adhesion, its properties is excellent, coating layer thickness comparatively conventional electrochemical aluminium reduces by 40 ~ 50%, and heat conductivility is better; More common UV platen hot stamping foil, be applied to circle pressure circle UV gold stamping time, effective gold stamping speed is from 40 ~ 60m/min, and bring up to 90 ~ 120m/min, effect of optimization is remarkable.
Accompanying drawing explanation
Fig. 1 is the structural representation that the embodiment of the present invention is applicable to the novel electrochemical aluminium of rotary-cutting hot stamping on UV oil polish paper.
Detailed description of the invention
Below by specific embodiment, the invention will be further described, but the present invention is not limited in these embodiments.
As shown in Figure 1, the embodiment of the present invention provides a kind of novel electrochemical aluminium being applicable to rotary-cutting hot stamping on UV oil polish paper, comprises base membrane layer 1, release layer 2, Information Level 3, aluminium coated 4 and tack coat 5 from the bottom to top successively.
Base membrane layer 1 is 12-18 μm of thick polyethylene terephthalate (PET) film, as each layer (release layer 2, Information Level 3, aluminium coated 4 and tack coat 5) depend on and complete coating and the carrier substrate of mold pressing, it not only has, and intensity is large, the performance of stretch-proof, can guarantee can not affect hologram size because of change in size in coating process; Also possess the feature of high heat-resisting, high tenacity in addition, can ensure coating continuously and final gold stamping time can not breakage be out of shape.
Release layer 2 is positioned on base membrane layer 1, the fluorine-containing aqueous wax material standby primarily of emulsified wax legal system is made, its thermal sensitivity feature can make it after gold stamping (heating pressurization), with Information Level 3, aluminium coated 4 and tack coat 5, hightail base membrane layer 1, and be transferred and be attached to stock surface.Described release layer 2 selects fluorine ion modified water-borne wax material as releasing agent, and it is made mainly through emulsified wax method, fluorine ion modified when not affecting releasing agent film forming and viscosity, adds temperature-sensitive effect.When meeting HTHP and being gold stamping, fluorine ion plays and reduces the effect of surface free energy, and the adhesion between itself and imaging layer, base membrane layer is declined, and play the effect of the demoulding, than the mould release that conventional electrochemical aluminium is used, gold stamping stripping result is better.
Information Level 3 is positioned on release layer 2, and its material composition and mass percent thereof are: epoxy modified acrylic resin 85 ~ 90%, premetallized dye toner 10 ~ 15%, change than regular meeting according to color depth.Epoxy modified acrylic resin described in the present embodiment coordinates the common acrylic resin for anodized aluminium imaging layer to form by the E-44 epoxy resin of 10 ~ 15%.Premetallized dye toner mixes into red, blue, yellow, the shades of colour such as green by different proportion, on product, a kind of visual holographic laser anti-counterfeiting information is produced again by laser holographic plate-making technology and moulding replication technology, its principle utilizes soft moulding press at 85 ~ 100 DEG C, hologram is suppressed in information layer surface with the pressure of 20 ~ 30kg, this hologram, by the optical principle of interference and diffraction, presents and has anti-fraud functional special visual effect.
The epoxy modified acrylic resin that the collocation of premetallized dye toner is better with its compatibility, when showing identical form and aspect, this dyestuff is common dye few 20 ~ 30% comparatively, and the use amount of the epoxy modified acrylic resin coordinating it to adopt when producing also is only 20 ~ 30% of primary resin.Therefore, the coating weight of product imaging layer semi-manufactured coated paper is from 1.0 ~ 1.2g/m of mill run
2drop to 0.7 ~ 0.8g/m
2, thickness decline directly reduces the effect of heat insulation of system.
Further, premetallized dye toner of the present invention, enhances the heat conductivility of product, and the content accounting for dry coating after its coating is reduced within 20% from original 25 ~ 30%.
Aluminium coated 4 is positioned on Information Level, and described aluminium coated 4 is plated under vacuum by gaseous aluminum, and its effect is by reflection ray, changes Information Level color property, increases gloss.Tack coat 5 is positioned on aluminium coated 4, and its effect is that anodized aluminium is bonded in stock surface.
Wherein, material composition and the mass percent thereof of described tack coat 5 are: hot retrospective polyurethane hot melt 10 ~ 20%, nano silicon 1 ~ 2%, toluene 30 ~ 40%, butanone 30 ~ 50%, isopropyl alcohol 5 ~ 15%, main body glue is the hot retrospective polyurethane hot melt of Continuous maching excellent performance, and molecular weight ranges is within 6 ~ 100,000.This fills a prescription original coating weight from 1.4 ~ 2.0g/m
2be reduced to 0.7 ~ 0.9g/m
2, the nano silicon that heat-insulating capability is stronger also reduces thereupon in a large number, and therefore the heat conductivility of anodized aluminium significantly promotes thereupon.
Below in conjunction with specific embodiment, the present invention will be described:
Embodiment 1
In the PET film of 12um thickness scribbling the fluorine ion modified water-borne wax releasing agent of one deck, be coated with that one deck is epoxide modified again and according to the acrylic resin paint (epoxy modified acrylic resin accounting 90%) of the subsidiary 10% premetallized dye toner of color requirements, coating dry measure is 0.7g/m
2, wherein toner content is 0.07g/m
2, mold pressing and after aluminizing, then press polyurethane hot melt 10%, nano silicon 1%, toluene 30%, butanone 50%, the ratio of isopropyl alcohol 9% is coated with one deck tack coat, and its dry-coated amount is 0.7g/m
2.By the anodized aluminium film strips of this explained hereafter, through printing house's circle pressure circle process test, effective gold stamping speed can be stabilized in 90m/min continuous operation.
Embodiment 2
In the PET film of 14um thickness scribbling the fluorine ion modified water-borne wax releasing agent of one deck, be coated with that one deck is epoxide modified again and according to the acrylic resin paint (epoxy modified acrylic resin accounting 88%) of the subsidiary 12% premetallized dye toner of color requirements, coating dry measure is 0.7g/m
2, wherein toner content is 0.084g/m
2, mold pressing and after aluminizing, then press polyurethane hot melt 20%, nano silicon 2%, toluene 40%, butanone 30%, the ratio of isopropyl alcohol 8% is coated with one deck tack coat, and its dry-coated amount is 0.9g/m
2.By the anodized aluminium film strips of this explained hereafter, through printing house's circle pressure circle process test, effective gold stamping speed can be stabilized in 110m/min continuous operation.
Embodiment 3
In the PET film of 18um thickness scribbling the fluorine ion modified water-borne wax releasing agent of one deck, be coated with that one deck is epoxide modified again and according to the acrylic resin paint (epoxy modified acrylic resin accounting 85%) of the subsidiary 15% premetallized dye toner of color requirements, coating dry measure is 0.8g/m
2, wherein toner content is 0.12g/m
2, mold pressing and after aluminizing, then press polyurethane hot melt 14.4%, nano silicon 1.6%, toluene 35%, butanone 44%, the ratio of isopropyl alcohol 5% is coated with one deck tack coat, and its dry-coated amount is 0.8g/m
2.By the anodized aluminium film strips of this explained hereafter, through printing house's circle pressure circle process test, effective gold stamping speed can be stabilized in 120m/min continuous operation.
The above; be only the specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, anyly belongs to those skilled in the art in the technical scope that the present invention discloses; the change that can expect easily or replacement, all should be encompassed within protection scope of the present invention.
Claims (4)
1. one kind is applicable to the novel electrochemical aluminium of rotary-cutting hot stamping on UV oil polish paper, comprise base membrane layer (1), release layer (2), Information Level (3), aluminium coated (4) and tack coat (5) from the bottom to top successively, it is characterized in that: material composition and the mass percent thereof of described Information Level (3) are: epoxy modified acrylic resin 88 ~ 90%, premetallized dye toner 10 ~ 12%; Material composition and the mass percent thereof of described tack coat (5) are: hot retrospective polyurethane hot melt 10 ~ 20%, nano silicon 1 ~ 2%, toluene 30 ~ 40%, butanone 30 ~ 50%, isopropyl alcohol 5 ~ 15%, and the coating weight of described tack coat (5) is 0.7 ~ 0.9g/m
2.
2. be applicable to the novel electrochemical aluminium of rotary-cutting hot stamping on UV oil polish paper as claimed in claim 1, it is characterized in that: described base membrane layer (1) is made up of polyethylene terephthalate film.
3. be applicable to the novel electrochemical aluminium of rotary-cutting hot stamping on UV oil polish paper as claimed in claim 1, it is characterized in that: described release layer (2) is positioned on base membrane layer (1), and the fluorine-containing aqueous wax material standby by emulsified wax legal system is made.
4. be applicable to the novel electrochemical aluminium of rotary-cutting hot stamping on UV oil polish paper as claimed in claim 1, it is characterized in that: described Information Level (3) is pressed with holographic laser anti-counterfeiting information by positioning module, described holographic laser anti-counterfeiting information is at 85 ~ 100 DEG C, utilize soft moulding press, be compressed on described Information Level (3) with the pressure of 20 ~ 30kg.