CN206722118U - A kind of fire-retardant abatvoix one-shot forming automatic production line of polyester fiber - Google Patents
A kind of fire-retardant abatvoix one-shot forming automatic production line of polyester fiber Download PDFInfo
- Publication number
- CN206722118U CN206722118U CN201720295444.1U CN201720295444U CN206722118U CN 206722118 U CN206722118 U CN 206722118U CN 201720295444 U CN201720295444 U CN 201720295444U CN 206722118 U CN206722118 U CN 206722118U
- Authority
- CN
- China
- Prior art keywords
- sheet material
- fire
- retardant
- liquid case
- immersion liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of fire-retardant abatvoix one-shot forming automatic production line of polyester fiber, including the opening mechanism being sequentially connected, carding mechanism, net laying mechanism and acupuncture mechanism, the opening mechanism sets chopped fiber charging aperture, acupuncture mechanism sets sheet material discharging opening, the sheet material discharging opening is connected with the spraying mechanism for applying fire retardant to sheet material, the output end of the spraying mechanism is connected with the prebake mechanism for being solidificated in fire retardant on the fiber of sheet material in turn, by the heating arrangements of plate forming, press polish mechanism and cold wind mechanism, sheet material through the output of cold wind mechanism enters laser cutting mechanism.By the way of disposal molding, the loss of intermediate link noenergy, sheet material processing serialization, while production efficiency greatly improves, production cost is reduced, also ensure that the Forming Quality of sheet material and fire-retardant, sound absorption qualities.
Description
Technical field
It the utility model is related to fire-retardant abatvoix production equipment technology, more particularly to a kind of fire-retardant sound-absorbing of polyester fiber
Plate one-shot forming automatic production line.
Background technology
Fire is to seriously endanger people's lives and properties, directly affect the most common disaster of economic development and social stability.Closely
Nian Lai, with new energy, new material, the extensive utilization of new equipment and urban construction scale constantly expansion and people's material and culture
Growth in the living standard, personal injury and property loss are also increasing caused by fire.Therefore, the fire protecting performance of sound-absorbing material
It is vital, fire prevention idea has been the most important safety requirements in each field.The appearance of flame retardant fibre board, solves tradition
The problem of indoor decorating and refurnishing materials are inflammable, flame-retardant board of the flame retardant fibre board using timber as main material production, due to its structure
Reasonability and production process in retrofit, can generally overcome the physics for substantially improving and improving timber the defects of timber
Mechanical property, while fire retardant glued board also overcomes the incendive shortcoming of normal plywood, effectively increases glued board anti-flammability
Energy.A kind of composite flame-retardant agent and its method, CN for preparing flame retardant fibre board such as disclosed in the A of CN 105131627
Fire retardant, flame retardant fibre board and its manufacture method disclosed in 101892057 A.Above-mentioned flame retardant fibre board is due to using timber as original
Material, not only needs a large amount of wood raw materials, and cost is higher, expensive, and production process route is complicated, and the high weight of density is big,
Installation process worker's intensity is larger, and higher in the fixed requirement of metope installation, and its fire resistance that absorbs sound still meets will
Ask, but still have deficiency.
Therefore there is the more superior polyester fibre acoustic panel of performance, polyester fibre acoustic panel full name is polyester fiber
Decoration acoustic panel, be it is a kind of using polyester fiber be raw material through the hot-forming manufactured ornament materials for having sound absorption function concurrently.Polyester
Fiber abatvoix has sound-absorption and heat-insulation heat preservation property, and plate is uniform in material solid, high resilience, toughness, wear-resisting, anti-impact
Hit, be tear-resistant, being not easy to scratch, plate width it is big.Because its have decoration, insulation, fire-retardant, environmentally friendly, light body, easy processing, stably, anti-impact
Hit, easy maintenance the features such as, turn into the preferred decoration sound-absorbing material of interior decoration, be widely used in family, market, wine
The playground that the public such as shop, KTV, cinema, dancing hall, auditorium, multifunctional hall, gymnasium gather.Polyester fiber is inhaled at present
The production process of soundboard typically passes through：--- --- --- baking oven is hot pressed into mixed cotton for lapping --- acupuncture --- for combing for shredding
Type --- air-cooled processing --- process such as trimming.Will be to causing polyester fibre acoustic panel that there is fire resistance, it is necessary to addition resistance
Fire agent.Adding method mainly has plate face cladding process and additive process.Additive process, i.e., into the flame retardant treatment carried out before plate, be by
Fire retardant carries out simple mechanical agitation physical blending with fiber or fire retardant is sprayed on fiber, is then pressed into plate.
For the method though so that whole sheet material all has flame retardant effect, amount of flame-retardant agent is big, and with the addition of fire retardant, the interior knot of sheet material
Intensity decreases are closed, and then influence the mechanical property of sheet material, limit the use of sheet material；Because the fire-retardant abatvoix of current polyester fiber is
It is made by the mixing of polyester fiber, low melting point core-skin fibre and three-dimensional hollow fiber, combing and then lapping, therefore additive process does not apply to
In the production of the fire-retardant abatvoix of polyester fiber.Cladding process, i.e., uniformly coated in fibreboard surface fire-retardant into after plate in fiber
Agent or anti-flaming dope, prepare flame retardant fibre board.Though the method outer layer protection, directly fire-retardant effect is played, dosage is few, also deposits
In poor durability, the problem of uneven and adhesive glueability and retardant load level relation etc. is sprayed, and is once hindered
Combustion top layer is destroyed, and there is no flame retardant effect for whole sheet material.
CN1335218A discloses a kind of nonwoven fibrous plate and its manufacture method, and sheet material is by a variety of different short
Fiber mixes, the sheet material through acupuncture shaping and heat-shaping, is characterized in that it is than 50%~60% by weight to mix chopped fiber
Polyester fiber, 20%~30% polyacrylonitrile fibre, 15%~25% polypropylene fibre mixing form.Manufacture method is characterized in
By mixing chopped fiber shredding, point comb, web is made, web is knitted on needing machine through close acupuncture, base fabric is disposably made,
Base fabric is heated into polypropylene fibre to melt, compacting makes scrim surfaces smooth and makes the amendment of base fabric thickness to product thickness, sizing
Just it is finished product afterwards.The A of CN 102896684 disclose a kind of preparation system of polyester fiber insulation acoustic board, its when being produced,
Raw material enters preparation system from raw material feeding unit, enters back into thick opener and is mixed and realize thick shredding；Then essence is utilized
Opener carries out smart shredding to raw material, then raw material is exported to baking oven；Baking oven heats to raw material so that the eutectic in raw material
After the skin fusing of point core-skin fibre, bonding is mixed with other raw materials, forms space network；Cold water roller is to from baking oven discharging opening
The raw material of outflow carries out cooling rolling, raw material is shaped；Cutting machine to cooling roll after raw material sheared and deburring after, it is defeated
Go out final products.
Although above-mentioned two art solutions are disclosed using nonwoven method, non-woven fabrics is prepared using chemical fibre
Technique productions fiberboard, but utilize the two methods production fibrous plate and do not have anti-flammability.
CN1635211A discloses a kind of retardant coating process of heavily fabric, and it is used carries out machine to low viscous fire retardant glue
Tool, which foams, reaches the purpose of thickening, make it have can coating processability, after scraper coating, the foam in extrusion process is scratched
It is broken, become low viscous fire retardant glue again, penetrate into coated base material, then dry, reach the overall flame performance of fabric
To requiring.
The A of CN 106113214 disclose a kind of preparation method of compound flame retardant fibre board, can effectively solve fire retardant into
This height, the problem of the mechanical property and poor durability of fiberboard, method is to crush the waste paper pulp fiber of collection, adds matter
Measure in the NaOH alkali lye of concentration 2% and impregnate 24h, then cleaned with water, dissociate, alkali is removed completely, sampling drying, calculate sample and contain
Water rate；By the borax for accounting for fiber gross dry weight 3%-6%, account for fiber gross dry weight 3%-5% Firebrake ZB, account for fiber gross dry weight 20%-40%
Montmorillonite mixed with fiber, under mechanical stirring, be well mixed, into blank；Blank is put into fiber plate forming die
Tool middle berth dresses up type, then is prepared into fiberboard through cold, hot pressure two-step method；The surface of fiberboard is coated into expanding fire retardant, room temperature
Dry, flame retardant fibre board.Above-mentioned two art solutions coat fire retardant glue using cladding process in fabric face so that thick
Weight fabric face possesses fire resistance, but fire retardant glue only forms flame retardant coating on surface, and fire retardant glue can not be complete
Thick and heavy fabric is penetrated into entirely, can not accomplish overall fire-retardant, and fire resistance is relatively poor.
The A of CN 105506979 disclose a kind of handling process of Fire-retarded carpet, concretely comprise the following steps：1）By fire resistant fluid with 1:
1 volume ratio is diluted with water, and is separately added under normal temperature in pond A and pond B；2）Acidizer is added toward pond A, is made
PH values are below 3；3）Carpet yarn is put into the A of pond, soak at room temperature 15-20 minutes, takes out, pad, in 80-
Dried at a temperature of 90 DEG C；4）Alkaline agent is added toward pond B, makes pH values more than 9；5）Again by the carpet yarn after drying
It is put into the B of pond, soak at room temperature 15-20 minutes, takes out, pad, dried at a temperature of 80-90 DEG C；6）Finally press carpet
Process processes.The A of CN 102851879 are related to a kind of manufacturing process of flame-retardant non-woven carpet.Its purpose is to make use
The nonwoven carpet of the technique productions has good anti-flammability and wearability.The manufacture work of the utility model flame-retardant non-woven carpet
Skill, using the short silk of chemical fibre as raw material, the short silk of chemical fibre include mass percent be 90%~96% polypropylene chopped fiber and 4%~
10% terylene short fiber, comprises the following steps：（1）The short silk shredding of chemical fibre, mixing, combing, lapping are first formed into uniform fibre web,
Then consolidated using acupuncture；（2）Fibre web is immersed in through conveying roller conveying and is formed and is passed through by acrylate glue, phosphorus flame retardant and water
In flame-retardant emulsion after foaming, the flame-retardant emulsion includes the acrylate glue that mass percent is 22.5%~25%, 4.5%~5%
Phosphorus flame retardant, surplus be water, the coefficient of foaming of flame-retardant emulsion is 10~15, and the speed of travel that fibre web immerses flame-retardant emulsion is
4~6m/min；（3）Obtained fibre web is impregnated with roll pressed；（4）Drying and shaping.
Common carpet is processed into Fire-retarded carpet by above-mentioned two patents by the way of fire retardant is impregnated, although can have
Standby excellent fire resistance, and environmental protection, cost are low, but by the way of using dipping, drying, the product finally given easily becomes
Shape, and out-of-flatness, it is difficult to ensure the quality of carpet.
It follows that common wood fibre board discloses the fire-retardant technique of gluing, but it is not to use fiber non-woven system
, also without sound absorption qualities, although prior art discloses at present for the production of polyester fiber board, in polyester fiber board
Upper applying fire retardant, fire retardant can not be infiltrated into all inside plate body, its entirety is possessed good fire resistance, it is ensured that
Certain service life and flatness, the mouldability of the sheet material that gets both, it may have certain difficulty.And use the side of dipping fire retardant
Formula, hardness, shape and the surface forming of polyester fiber board are difficult to ensure that again, that is to say, that at present to the resistance of polyester fiber board
Fire except applying fire retardant, have no other effective ways, and the production of the fire-retardant abatvoix of polyester fiber is also that substep produces, from
The shaping currently available technology of raw material to final sheet material can not accomplish, not only hinder the technology hair of this area significantly, and
And the quality of production of sheet material and production efficiency is caused to substantially reduce.Also, disposal molding is there is no at present and possesses fire resistance
Board production equipment, this constrains the development of this area significantly.
The content of the invention
In view of the deficienciess of the prior art, technical problem to be solved in the utility model is to provide a kind of production effect
Rate is high, while such that sheet material has excellent anti-flammability from inside to outside, and and can effectively ensures the good mouldability of product, hardness
And surface quality, and production efficiency is high, saves the fire-retardant abatvoix one-shot forming automatic production line of polyester fiber of the energy.
In order to solve the above technical problems, technical solution adopted in the utility model is：A kind of fire-retardant sound-absorbing of polyester fiber
Plate one-shot forming automatic production line, including opening mechanism, carding mechanism, net laying mechanism and the acupuncture mechanism being sequentially connected, institute
State opening mechanism set chopped fiber charging aperture, acupuncture mechanism set sheet material discharging opening, the sheet material discharging opening be connected with for
Sheet material applies the spraying mechanism of fire retardant, and spraying mechanism includes an immersion liquid case for being used to impregnating sheet material into fire retardant, the immersion liquid
The side of case is arranged to upstream end, and opposite side is arranged to output end, is provided with the top of immersion liquid case multiple when sheet material is through entering
End is reached for the spray head that fire retardant is uniformly sprayed to the surface of sheet material when in immersion liquid case, and each spray head is all connected with being used to convey
The delivery pipe of fire retardant, sprayed tank from fire retardant to spray head and driving fire retardant height for providing are connected with delivery pipe
The compression pump sprayed is pressed, also includes one and is used to control sheet material to enter immersion liquid case and the pickup control machine immersed in fire retardant
Structure, the pickup controlling organization include the lifting support for driving sheet material to immerse fire retardant, and driving institute is provided with immersion liquid case
The servomotor of lifting support lifting is stated, is provided with the immersion liquid case for detecting sheet material apart from the position of fire retardant liquid level size
Sensor is put, the position sensor is sent to servomotor, servomotor receiving position after detecting the position signalling of sheet material
Lifting support is driven to rise or land after signal, the output end of the spraying mechanism is connected with turn for fire retardant to be solidificated in
Prebake mechanism on the fiber of sheet material, by the heating arrangements of plate forming, press polish mechanism and cold wind mechanism, through cold wind mechanism
The sheet material of output enters laser cutting mechanism.
The fire-retardant abatvoix one-shot forming automatic production line of above-mentioned polyester fiber, from the upstream end of immersion liquid case to output end
The roll assembly for conveying and supporting sheet material is disposed with, the roll assembly includes the input roller for being arranged on upstream end
Wheel, the first support disk roller on immersion liquid case, the first shaping roller, the second shaping roller in immersion liquid case, are arranged on
On the immersion liquid case of output end second support disk roller, and output roller, it is described input disk roller, first support disk roller, the first one-tenth
Type roller, the second shaping roller, the second support disk roller and output roller are fixedly connected with lifting support.
The fire-retardant abatvoix one-shot forming automatic production line of above-mentioned polyester fiber, the upstream end of the immersion liquid case and output
End is respectively arranged with first support bar, the second support bar that can be moved up and down along the tank wall of immersion liquid case, the first support disk roller and the
Two support disk rollers are connected with first support bar, second support bar respectively, and the first support bar and second support bar pass through silk
Thick stick is connected with servomotor.
The fire-retardant abatvoix one-shot forming automatic production line of above-mentioned polyester fiber, width side of the spray head along sheet material
To setting gradually.
The fire-retardant abatvoix one-shot forming automatic production line of above-mentioned polyester fiber, the fire retardant is by following weight percent
The composition composition of ratio：
Water-based Virgin's milk modified emulsion 15%~25%；
Water soluble polymer thickener 2%~5%；
Foaming agent 1.5%~5%；
Foam stabilizer 1%~3%；
Firebrake ZB 5%~10%；
Bittern-free phosphorous-nitrogen ammonia system fireproof powder 20%~30%；
Soften water surplus.
The fire-retardant abatvoix one-shot forming automatic production line of above-mentioned polyester fiber, the fire retardant is by following weight percent
The composition composition of ratio：Water-based Virgin's milk modified emulsion 20%, water soluble polymer thickener 3.5%, foaming agent 3%, foam stabilizer 1.5%,
Firebrake ZB 7%, bittern-free phosphorous-nitrogen ammonia system fireproof powder 28.5%, softened water, surplus.
The fire-retardant abatvoix one-shot forming automatic production line of above-mentioned polyester fiber, the water-based Virgin's milk modified emulsion are to change
Property acrylic emulsion or aqueous polyurethane emulsion, water soluble polymer thickener is acrylic acid amides, coconut oleamide, quaternary ammonium salt
One or more in modified starch, foaming agent are one kind in SAS, lauryl sodium sulfate, sodium alcohol ether carboxylate
Or it is several, foam stabilizer is the one or more in polyethylene glycol, amine oxide, and bittern-free phosphorous-nitrogen ammonia system fireproof powder is pentaerythrite, phosphorus
One or more in acid esters, phosphite ester, melamine.
The advantages of the utility model polyester fiber fire-retardant abatvoix one-shot forming automatic production line is：The utility model profit
The method acted on simultaneously with spray, immersion liquid, impregnated under the upper spray of fire retardant, is not only able to rationally control treating for abatvoix
Liquid rate, prepare for follow-up baking operation, and the addition of rational fire retardant, can be that abatvoix is effectively ensured be good
While flame retardant effect, additionally it is possible to ensure that abatvoix has a good mouldability after the drying, hardness reaches standard, will not go out
Existing traditional formation that the uneven three-dimensional netted form for influenceing fiber of fibrous inside fusing is excessively caused because of fire retardant addition,
And fire retardant is evenly distributed in the fiber of abatvoix, flame retardant effect will not reduce because of normal use, it is ensured that sound-absorbing
The optimal overall flame effect of plate.According to the flame retardant fibre board provided by the utility model for including fire retardant, can not change
It is made under conditions of the production technology and equipment of fiberboard, thus its manufacturing cost is relatively low.According to fire-retardant fibre of the present utility model
Dimension plate can not only significantly improve the mechanical property of flame retardant fibre board, and its combustibility meet GB8624 B levels or
The regulation of C levels, and formaldehydeless burst size, thus be a kind of high-strength environment-friendly flame-retarding fiberboard of high quality and at a reasonable price, it can answer extensively
For building interior decoration, fire-retardant Furniture manufacturing, antiflaming floor production, ship and vehicle interior decoration etc., there is good warp
Ji and social benefit.Bond to form physics adhesive structure by raw material fuse itself in process of production, without any glue etc.
Sticker, thoroughly solve the problems, such as to contain a large amount of glue, the product generated by the utility model preparation system in traditional product
Environmental protection, formaldehydeless, free from extraneous odour.And by the way of disposal molding, the loss of intermediate link noenergy, sheet material processing is continuously
Change, while production efficiency greatly improves, reduce production cost, also ensure that the Forming Quality of sheet material and fire-retardant, sound absorption properties
Energy.
Brief description of the drawings
Fig. 1 is overall structure diagram of the present utility model；
Fig. 2 is the schematic enlarged-scale view of the utility model spraying mechanism.
Embodiment
The utility model is described in further details with reference to specific embodiment；
As shown in Figure 1, 2, the fire-retardant abatvoix one-shot forming automatic production line of a kind of polyester fiber, including be sequentially connected
Opening mechanism 22, carding mechanism 23, net laying mechanism 24 and acupuncture mechanism 25, the opening mechanism 22 set chopped fiber charging aperture
26, acupuncture mechanism 25 sets sheet material discharging opening 27, and the sheet material discharging opening 27 is connected with the spray for applying fire retardant to sheet material 1
Mechanism 28 is drenched, spraying mechanism 28 includes an immersion liquid case 3 for being used to impregnating sheet material 1 into fire retardant 2, and the side of the immersion liquid case 3 is set
Upstream end 4 is set to, opposite side is arranged to output end 5, is provided with the top of immersion liquid case 3 multiple when abatvoix 1 arrives through upstream end 4
When in up to immersion liquid case 3, for uniformly spraying the spray head 6 of fire retardant 2, width of the spray head 6 along sheet material 1 to the surface of sheet material 1
Direction sets gradually into a row, and according to the production needs of reality, spray head 6 can set multiple row along the conveying direction of sheet material 1.Spray
The output end of leaching mechanism 28 be connected with turn for fire retardant is solidificated on the fiber of sheet material 1 prebake mechanism 29, by plate
Heating arrangements 30, press polish mechanism 31 and the cold wind mechanism 32 that material 1 is molded, the sheet material 1 exported through cold wind mechanism 32 enter laser
Cutting mechanism 33.Each spray head 6 is all connected with the delivery pipe 7 for conveying fire retardant 2, is connected with and is used for spray in delivery pipe 7
The sprayed tank 20 that head provides fire retardant is drenched, and the compression pump 21 that driving fire retardant high pressure sprays, compression pump 21 are connected to conveying
On pipe 7.In the spray process of reality, it can be imitated according to the actual size and thickness of sheet material 1 by the work for adjusting hydraulic pump
Rate, to control the fountain height of spray head 6, obtain sheet material 1 it is optimal treat liquid rate, and finally obtain optimum resistance combustion effect.
Also include one to be used to control sheet material 1 to enter immersion liquid case 3 and immerse the pickup control machine of the depth size of fire retardant 2
Structure, the pickup controlling organization include the lifting support 8 for driving sheet material 1 to immerse fire retardant 2, drive are provided with immersion liquid case 3
The servomotor 9 that the lifting support 8 lifts is moved, is provided with the immersion liquid case 3 for detecting sheet material 1 apart from the liquid of fire retardant 2
The position sensor 10 of face size, the position sensor 10 are sent to servomotor 9 after detecting the position signalling of sheet material 1,
Lifting support 8 is driven to rise or land after the receiving position signal of servomotor 9.From the upstream end 4 of immersion liquid case 3 to output end 5 according to
The secondary roll assembly being provided with for conveying and supporting sheet material 1, the roll assembly include the input disk roller for being arranged on upstream end 4
11st, the first support disk roller 12 on immersion liquid case 3, the first shaping roller 13, the second shaping roller in immersion liquid case 3
14, the second support disk roller 15 being arranged on the immersion liquid case 3 of output end 5, and output roller 16, the input disk roller 11, the
One support disk roller 12, the first shaping roller 13, the second shaping roller 14, second support disk roller 15 and output roller 16 with liter
Descending branch frame 8 is fixedly connected.The upstream end 4 and output end 5 of the immersion liquid case 3 are respectively arranged with can be along above and below the tank wall of immersion liquid case 3
Mobile first support bar 17, second support bar 18, the first support support roller 15 of disk roller 12 and second take turns respectively with the first support
Bar 17, second support bar 18 connect, and first support bar 17, second support bar 18 serve the support disk roller 12 and second of support first
The effect of support roller 15, the first support support roller 15 of disk roller 12 and second can be respectively in first support bar 17, second support bar
18 top rotates motion.The first support bar 17 and second support bar 18 are connected by leading screw 19 with servomotor 9.
Purpose is accurately controlled in order to play, servomotor 9 can set two, be separately positioned on the both sides of immersion liquid case 3.
Fire retardant used in the utility model is made up of the composition of following percentage by weight：
Water-based Virgin's milk modified emulsion 15%~25%；
Water soluble polymer thickener 2%~5%；
Foaming agent 1.5%~5%；
Foam stabilizer 1%~3%；
Firebrake ZB 5%~10%；
Bittern-free phosphorous-nitrogen ammonia system fireproof powder 20%~30%；
Soften water surplus.
Water-based Virgin's milk modified emulsion is modified acrylic acid emulsion or aqueous polyurethane emulsion, and water soluble polymer thickener is
One or more in acrylic acid amides, coconut oleamide, quaternary ammonium salt-modified starch, foaming agent are SAS, 12
One or more in sodium alkyl sulfate, sodium alcohol ether carboxylate, foam stabilizer is polyethylene glycol, the one or more in amine oxide, nothing
Halogen phosphorus nitrogen ammonia system fireproof powder is the one or more in pentaerythrite, phosphate, phosphite ester, melamine.
Embodiment 1：
The fire retardant is made up of the composition of following percentage by weight：
Modified acrylic acid emulsion 15%；
Acrylic acid amides 2%；
SAS 1.5%；
Polyethylene glycol 1%；
Firebrake ZB 5%；
Pentaerythrite 20%；
Soften water surplus.
Embodiment 2：
The fire retardant is made up of the composition of following percentage by weight：
Aqueous polyurethane emulsion 20%；
Coconut oleamide 3.5%；
Lauryl sodium sulfate 3%；
Amine oxide 1.5%；
Firebrake ZB 7%；
Phosphate 28.5%；
Soften water surplus.
Embodiment 3：
The fire retardant is made up of the composition of following percentage by weight：
Modified acrylic acid emulsion 25%；
Quaternary ammonium salt-modified starch 5%；
Sodium alcohol ether carboxylate 5%；
Polyethylene glycol 3%；
Firebrake ZB 10%；
Melamine 30%；
Soften water surplus.
The method that the utility model prepares fire retardant, comprises the following steps：
（1）, according to above-mentioned percentage by weight, quantitative softened water, water-based Virgin's milk modified adhesive are weighed in agitator tank；The two
It is sufficiently stirred 8~15 minutes, mixing speed 1000r/min~1500r/min；
（2）And then foaming agent is sequentially added, foam stabilizer, reduce mixing speed, mixing speed 600r/min~800r/
Min, stir 3~8 minutes；
（3）, weigh Firebrake ZB, bittern-free phosphorous-nitrogen ammonia system fireproof powder is slowly homogeneously added into mixture, stirred while adding,
Mixing speed 500r/min~800r/min, whole process 40 minutes；
（4）, add water soluble polymer thickener, be sufficiently stirred 20~40 minutes, mixing speed 600r/min~
1000r/min, filtering and discharging obtain the fire retardant.
Certainly, it is to limitation of the present utility model that described above, which is not, and the utility model is also not limited to the example above, this
The those of ordinary skill of technical field, in essential scope of the present utility model, the variations, modifications, additions or substitutions made, all
The scope of protection of the utility model should be belonged to.
Claims (4)
1. a kind of fire-retardant abatvoix one-shot forming automatic production line of polyester fiber, including be sequentially connected opening mechanism, comb
Mechanism, net laying mechanism and acupuncture mechanism, the opening mechanism set chopped fiber charging aperture, and acupuncture mechanism sets sheet material discharging opening,
It is characterized in that：The sheet material discharging opening is connected with the spraying mechanism for applying fire retardant to sheet material, and spraying mechanism includes one
For sheet material to be impregnated to the immersion liquid case of fire retardant, the side of the immersion liquid case is arranged to upstream end, and opposite side is arranged to output end,
Be provided with the top of immersion liquid case it is multiple when sheet material through upstream end reach immersion liquid case in when for uniformly being sprayed to the surface of sheet material
The spray head of fire retardant, each spray head are all connected with the delivery pipe for conveying fire retardant, are connected with and are used for spray in delivery pipe
The compression pump that head provides the sprayed tank of fire retardant and driving fire retardant high pressure sprays is drenched, also includes one and is used to control sheet material to enter
Enter immersion liquid case and the pickup controlling organization immersed in fire retardant, the pickup controlling organization includes driving sheet material immersion fire-retardant
The lifting support of agent, the servomotor for driving the lifting support lifting is provided with immersion liquid case, is set in the immersion liquid case
There is the position sensor apart from fire retardant liquid level size for detection plate material, the position sensor detects the position letter of sheet material
Sent after number to servomotor, drive lifting support to rise or landing after servomotor receiving position signal, the spraying mechanism
Output end be connected with turn for fire retardant to be solidificated in the prebake mechanism on the fiber of sheet material, the heating by plate forming
Mechanism, press polish mechanism and cold wind mechanism, the sheet material through the output of cold wind mechanism enter laser cutting mechanism.
2. the fire-retardant abatvoix one-shot forming automatic production line of polyester fiber according to claim 1, it is characterized in that：From leaching
The upstream end of liquid case is disposed with the roll assembly for conveying and supporting sheet material to output end, and the roll assembly includes setting
Put in the input disk roller of upstream end, the first support disk roller on immersion liquid case, the first shaping roller in immersion liquid case, the
Two shaping rollers, the second support disk roller being arranged on the immersion liquid case of output end, and output roller, the input disk roller, the
One support disk roller, the first shaping roller, the second shaping roller, the second support disk roller and output roller are fixed with lifting support
Connection.
3. the fire-retardant abatvoix one-shot forming automatic production line of polyester fiber according to claim 2, it is characterized in that：It is described
The upstream end and output end of immersion liquid case are respectively arranged with the first support bar that can be moved up and down along the tank wall of immersion liquid case, the second support
Bar, first support disk roller and second support disk roller be connected respectively with first support bar, second support bar, the first support bar and
Second support bar is connected by leading screw with servomotor.
4. the fire-retardant abatvoix one-shot forming automatic production line of polyester fiber according to claim 3, it is characterized in that：It is described
Spray head is set gradually along the width of sheet material.