CN101554551A - Process for preparing flame-retarding washable filtering material - Google Patents
Process for preparing flame-retarding washable filtering material Download PDFInfo
- Publication number
- CN101554551A CN101554551A CNA2009100647097A CN200910064709A CN101554551A CN 101554551 A CN101554551 A CN 101554551A CN A2009100647097 A CNA2009100647097 A CN A2009100647097A CN 200910064709 A CN200910064709 A CN 200910064709A CN 101554551 A CN101554551 A CN 101554551A
- Authority
- CN
- China
- Prior art keywords
- water
- fiber
- filtering material
- retarding
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a process for preparing a flame-retarding washable filtering material. The flame-retarding washable filtering material is prepared by the following steps of: needling various terylene or polypropylene staple fiber and three-dimensional crimp polyester staple fiber by a certain proportion to prepare a basic material; subsequently soaking the basic material in a flame-retarding adhesive solution prepared by mixing an acrylate polymer and a cyclic phosphate flame retardant with a certain proportion; subsequently rolling by dual rollers, drying and spraying the flame-retarding adhesive; and subsequently drying and ironing out the solution, thus forming the filtering material with the fiber crossing fixed by adhesive point and fiber surface covered by a smooth adhesive layer. The process is flame-retarding and washable.
Description
Technical field:
The present invention relates to a kind of anti-flaming washable filter material and preparation technology thereof, relate to the filtering material of systems such as a kind of concentrated ventilation, central air-conditioning and fluid purification specifically.
Background technology:
China is the maximum developing country of world population, since phase late 1970s, along with China's economic development continuously and healthily, the environmental problem that occurs stage by stage in the century-old course of industrialization in the developed country is concentrated in China and is occurred, and the contradiction order benefit of environment and development is outstanding.The resource relative shortage, ecological environment frailty, the environmental carrying capacity deficiency becomes the significant problem in the Chinese development gradually.
The Eleventh Five-Year Plan of China is had higher requirement to environmental protection, and aspects such as water, gas, sound, slag all arrive filtering material, filtering material industry market promise well with more applications.Along with the pay attention to day by day of people to atmospheric environment and IAQ, the issuing and implementation of a series of environmental regulations make air filting material take on the role who becomes more and more important in environmental improvement, and have obtained significant progress.Air filting material has occupied the 3rd in six big markets of international filtering material, become fastest-rising part in the international filtering material market.Air environmental pollution is the emphasis of China's environmental pollution control, air filting material is the important technical that atmospheric environment is administered, along with country's perfect day by day to the increasing of environmental protection investment and environmental regulation, the application prospect of air filting material in atmospheric environment is administered will be more wide.
At present, our used fire-retardant filtering material is because water-fast washing not, promptly needs after saturated more to renew when dust containing capacity reaches, and this had both increased the spending of enterprise, again environment had been caused pollution simultaneously.And the anti-flaming washable filter material of my company's development removes water to rinse well and can reuse after dust containing capacity reaches capacity, and this greatly reduces the cost of enterprise, has reduced the pollution to environment simultaneously again.
Summary of the invention:
The technical issues that need to address of the present invention are the preparation methods that disclose a kind of anti-flaming washable filter material, to satisfy the problem of contemporary society to the resource energy-conserving and environment-protective, the said anti-flaming washable filter material of the present invention is to form basic material by several different terylene or the acupuncture by a certain percentage of polypropylene chopped fiber peacekeeping three-dimensional crimp polyester staple, and then be soaked in acrylate polymer, in the fire retardant glue solution that the cyclic phosphate fire retardant is made into by a certain percentage, yet roll through two roll-ins again, oven dry, spray fire retardant glue solution again, oven dry is plated again, form fiber intersection points and fix and the filtering material of fiber surface, promptly obtain the present invention by smooth glue-line covering by glue point.
The preparation method of anti-flaming washable filter material of the present invention comprises the steps:
(1) preparation of needling material:
It is by terylene or polypropylene short fiber, and fibre fineness is 2-20dtex, and length is 50-80mm; Three-dimensional crimp polyester staple, fibre fineness are 5-18dtex, and length is 40-60mm; Above weight ratio is 85: 15, evenly mixes, and forms by shredding, combing, lapping, acupuncture, and needing machine speed is 1000-1500 time/minute, and bestock is 2000-4000 piece/meter, makes that several terylene or polypropylene fiber are well-proportioned to be connected as a single entity.
(2) preparation of fire retardant glue:
Acrylate polymer, cyclic phosphate fire retardant are evenly mixed weight ratio by weight the ratio of 40-60: 40-60.
(3) needling material is soaked in the mixture of (2) and water, with 0.5-10 rice/minute the speed operation, roll through two roll-ins, moisture content is removed, under 90 ℃-240 ℃ temperature, dry.
(4) again with the two-sided uniform sprinkling (2) of the material made in (3) and the mixture of water, under 90 ℃-200 ℃ temperature, dry, the press that enters 130 ℃-200 ℃ flattens, the rolling of cutting edge then, form fiber intersection points and fix and the filtering material of fiber surface, promptly obtain the present invention by smooth glue-line covering by glue point.
Because this filtering material is not only fire-retardant but also water-fast to be washed, so can be widely used in relevant use field both at home and abroad, reduced use cost, reduce the discharging of pollutant, thereby reached the effect of protection environment and energy-saving and emission-reduction.
The specific embodiment:
Embodiment 1
(1) preparation of needling material:
It is by terylene or polypropylene short fiber, and fibre fineness is 2dtex, and length is 50mm; Three-dimensional crimp polyester staple, fibre fineness are 5dtex, and length is 40mm; Above weight ratio is 85: 15, evenly mixes, and forms by shredding, combing, lapping, acupuncture, and needing machine speed is 1000 times/minute, and bestock is 2000 pieces/meter, makes that several terylene or polypropylene fiber are well-proportioned to be connected as a single entity.
(2) preparation of fire retardant glue:
With acrylate polymer or melmac or aqueous polyurethane: cyclic phosphate or phosphate or ammonium polyphosphate flame retardant were in 40: 60 the even proportioning of ratio, and weight ratio mixes.
(3) needling material is soaked in the mixture of (2) and water,, rolls, moisture content is removed, under 240 ℃ temperature, dry through two roll-ins with 0.5 meter/minute speed operation.
(4) again with the two-sided uniform sprinkling (2) of the material made in (3) and the mixture of water, under 90 ℃ temperature, dry, the press that enters 130 ℃ flattens, the rolling of cutting edge then, form fiber intersection points and fix and the filtering material of fiber surface, promptly obtain the present invention by smooth glue-line covering by glue point.Material of the present invention adopts TB/T 3138-2006 " rolling stock fire proofing technical conditions "; GB/T5454-1997 " textile combustion performance test oxygen index method "; GB/T 8323-1987 " plastics combustibility test method smoke density method "; GB 8624-2006 standards such as " construction material and the classifications of goods combustibility " detects, and the result is as follows:
Thickness: 1.0mm
Wind speed: 0.2m/s
Resistance: 15pa
Dust containing capacity 〉=50g/m
2
Face proportion: 100g/m
2
Numeration efficient: 40 (〉=5 μ m)
Oxygen index (OI): 27.4
Miter angle burning: difficult combustion
Smoke density D4:320
Resistance to water: wash 6 times, its flame retarding efficiency still can reach the E level
Embodiment 2
(1) preparation of needling material:
It is by terylene or polypropylene short fiber, and fibre fineness is 16dtex, and length is 75mm; Three-dimensional crimp polyester staple, fibre fineness are 12dtex, and length is 50mm; Above weight ratio is 85: 15, evenly mixes, and forms by shredding, combing, lapping, acupuncture, and needing machine speed is 1200 times/minute, and bestock is 3000 pieces/meter, makes that several terylene or polypropylene fiber are well-proportioned to be connected as a single entity.
(2) preparation of fire retardant glue:
With acrylate polymer or melmac or aqueous polyurethane: cyclic phosphate or phosphate or ammonium polyphosphate flame retardant were in 50: 50 the even proportioning of ratio, and weight ratio mixes.
(3) needling material is soaked in the mixture of (2) and water,, rolls, moisture content is removed, under 150 ℃ temperature, dry through two roll-ins with 5 meters/minute speed operation.
(4) again with the two-sided uniform sprinkling (2) of the material made in (3) and the mixture of water, under 150 ℃ temperature, dry, the press that enters 160 ℃ flattens, the rolling of cutting edge then, form fiber intersection points and fix and the filtering material of fiber surface, promptly obtain the present invention by smooth glue-line covering by glue point.Material of the present invention adopts TB/T 3138-2006 " rolling stock fire proofing technical conditions "; GB/T5454-1997 " textile combustion performance test oxygen index method " GB/T 8323-1987 " plastics combustibility test method smoke density method "; GB 8624-2006 standards such as " construction material and the classifications of goods combustibility " detects, and the result is as follows:
Thickness: 6.0mm
Wind speed: 1.60m/s
Resistance: 32pa
Dust containing capacity 〉=130g/m
2
Face proportion: 300g/m
2
Numeration efficient: 65 (〉=5 μ m)
Oxygen index (OI): 27.4
Miter angle burning: difficult combustion
Smoke density D4:320
Resistance to water: wash 6 times, its flame retarding efficiency still can reach the E level
Embodiment 3
(1) preparation of needling material:
It is by terylene or polypropylene short fiber, and fibre fineness is 20dtex, and length is 80mm; Three-dimensional crimp polyester staple, fibre fineness are 18dtex, and length is 60mm; Above weight ratio is 85: 15, evenly mixes, and forms by shredding, combing, lapping, acupuncture, and needing machine speed is 1500 times/minute, and bestock is 4000 pieces/meter, makes that several terylene or polypropylene fiber are well-proportioned to be connected as a single entity.
(2) preparation of fire retardant glue:
With acrylate polymer or melmac or aqueous polyurethane: cyclic phosphate or phosphate or ammonium polyphosphate flame retardant were in 60: 40 the even proportioning of ratio, and weight ratio mixes.
(3) needling material is soaked in the mixture of (2) and water,, rolls, moisture content is removed, under 90 ℃ temperature, dry through two roll-ins with 10 meters/minute speed operation.
(4) again with the two-sided uniform sprinkling (2) of the material made in (3) and the mixture of water, under 200 ℃ temperature, dry, the press that enters 200 ℃ flattens, the rolling of cutting edge then, form fiber intersection points and fix and the filtering material of fiber surface, promptly obtain the present invention by smooth glue-line covering by glue point.Material of the present invention adopts TB/T 3138-2006 " rolling stock fire proofing technical conditions "; GB/T5454-1997 " textile combustion performance test oxygen index method "; GB/T 8323-1987 " plastics combustibility test method smoke density method "; GB 8624-2006 standards such as " construction material and the classifications of goods combustibility " detects, and the result is as follows:
Thickness: 10.0mm
Wind speed: 3.0m/s
Resistance: 50pa
Dust containing capacity 〉=200g/m
2
Face proportion: 500g/m
2
Numeration efficient: 90 (〉=5 μ m)
Oxygen index (OI): 27.4
Miter angle burning: difficult combustion
Smoke density D4:320
Resistance to water: wash 6 times, its flame retarding efficiency still can reach the E level.
Claims (3)
1, the preparation technology of anti-flaming washable filter material, it is characterized in that, this filtering material is not only fire-retardant but also water-fast to be washed, it is by several terylene or polypropylene fiber, acupuncture by a certain percentage forms, be soaked in the fire retardant glue solution of proportioning by a certain percentage again, oven dry, again surface sprinkling by a certain percentage the fire retardant glue solution of proportioning then dry and form, comprise the steps: step 1: the preparation of needling material, it is by terylene or polypropylene short fiber, fibre fineness is 2-20dtex, and length is 50-80mm; Three-dimensional crimp polyester staple, fibre fineness are 5-18dtex, and length is 40-60mm; Above weight ratio is 85: 15, evenly mixes, and forms by shredding, combing, lapping, acupuncture, and needing machine speed is 1000-1500 time/minute, and bestock is 2000-4000 piece/meter, makes that several terylene or polypropylene fiber are well-proportioned to be connected as a single entity; Step 2: the preparation of fire retardant glue evenly mixes acrylate polymer, cyclic phosphate fire retardant by weight the ratio of 40-60: 40-60; Step 3: step 1 is soaked in the mixed solution of step 2 and water, with 0.5-6 rice/minute the speed operation, roll through two roll-ins, moisture content is removed, under 90 ℃-240 ℃ temperature, dry; Step 4: with the fire retardant glue of the two-sided uniform sprinkling step 2 of the material made in the step 3 and the mixed solution of water, under 90 ℃-200 ℃ temperature, dry, the press that enters 130 ℃-200 ℃ flattens, and the rolling of cutting edge then promptly obtains filtering material of the present invention.
2, the preparation technology of anti-flaming washable filter material according to claim 1 is characterized in that: anti-flaming washable filter material has fiber intersection points and is covered by smooth glue-line with fiber surface by glue point is fixing.
3, the preparation technology of anti-flaming washable filter material according to claim 1, it is characterized in that: this material is not only fire-retardant but also water-fast to be washed, and water cleans more than 6 times, and its flame retardant effect still can reach more than the E level, the initial resistance of this filtering material :≤15-50pa, dust containing capacity: 〉=50-200g/m
2, face proportion: 100-500g/m
2, thickness: 1-10mm, rated wind speed: 0.2-3m/s, numeration efficient: 40-90% (〉=5 μ m), the water-fast number of times 6 of washing washed back filter effect E level with last time.