CN206574722U - A kind of UV barrier packaging adhesive films used for solar batteries and the solar cell module using the packaging adhesive film - Google Patents
A kind of UV barrier packaging adhesive films used for solar batteries and the solar cell module using the packaging adhesive film Download PDFInfo
- Publication number
- CN206574722U CN206574722U CN201720241161.9U CN201720241161U CN206574722U CN 206574722 U CN206574722 U CN 206574722U CN 201720241161 U CN201720241161 U CN 201720241161U CN 206574722 U CN206574722 U CN 206574722U
- Authority
- CN
- China
- Prior art keywords
- packaging adhesive
- adhesive film
- layers
- barrier
- high permeable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model is specifically related to a kind of UV barrier packaging adhesive films used for solar batteries and the solar cell module using the packaging adhesive film, one of which UV barriers packaging adhesive film used for solar batteries, it includes at least one layer of UV barrier layers of high permeable layers and formation in the high permeable layers any surface.By forming at least one layer of UV barrier layers in any surface of high permeable layers, the UV auxiliary agents in UV barrier layers can be so avoided to diffuse out, avoid the reduction of solar cell power generation efficiency, and can avoid solder resist or cell piece and UV absorbents it is incompatible caused by xanthochromia;And high permeable layers will not be produced with upper strata packaging adhesive film and influenced each other, cell piece surface is spilt over even if it also will not influence generating efficiency as conventional glued membrane.
Description
Technical field
The utility model belongs to area of solar cell, is related to a kind of packaging adhesive film, and in particular to a kind of solar cell
Packaging adhesive film and the solar cell module using the packaging adhesive film are obstructed with UV.
Background technology
The usual structure of solar cell is:Glass/height thoroughly seal by packaging film (upper strata packaging adhesive film)/cell piece/UV barriers
Film (lower floor's packaging adhesive film)/backboard is filled, what can be used as the encapsulating material of solar cell module includes EVA, POE, gathers
Vinyl butyral (PVB), ionomer, polyurethane, silica gel, epoxy resin etc..Upper strata packaging adhesive film uses high-transparency thinner package
Film can cause UV luminous energy to reach cell piece surface, improve generated output.And lower floor's packaging adhesive film is encapsulated using UV isolation-types
Glued membrane can cause UV light not reach back plate surface, so as to protect backboard, improve service life (the upper strata encapsulation of component
Glued membrane and lower floor's packaging adhesive film a generally only Rotating fields).
But, in actual lamination process, lower floor UV barrier packaging adhesive films are possible to that cell piece surface can be spilt over, so that shadow
Generating efficiency is rung;And, the UV auxiliary agents of lower floor's packaging adhesive film can diffuse to upper strata packaging plastic in component in actual use
In film, so as to greatly reduce the generating efficiency of component.In addition, some solar cells employ special solder resist or electricity
Pond piece, they are bad with UV absorbent compatibility so that UV absorbents can be separated out and shape at cell piece, busbar, the welding back side
Yellowly color spot, so as to cause component facade bad.
The content of the invention
The utility model purpose is to provide a kind of UV barriers envelope used for solar batteries to overcome the deficiencies in the prior art
Fill glued membrane.
To reach above-mentioned purpose, the technical solution adopted in the utility model is:A kind of UV barriers encapsulation used for solar batteries
Glued membrane, it includes at least one layer of UV barrier layers of high permeable layers and formation in the high permeable layers any surface.
Optimally, it is made up of high permeable layers and the UV barrier layers formed in the high permeable layers any surface.
Optimally, the thickness of the high permeable layers is 50~400 μm.
Optimally, the thickness of the UV barrier layers is 100~600 μm.
Optimally, it is that the high permeable layers and the UV barrier layers coextrusion mold or film layer are suppressed.
A further object of the present invention is to provide a kind of solar cell module using above-mentioned packaging adhesive film, it include by
Backsheet layer, lower floor's packaging adhesive film, cell piece, upper strata packaging adhesive film and the glassy layer being cascading upwards down, the lower floor
Packaging adhesive film is above-mentioned UV used for solar batteries barrier packaging adhesive films, and the high permeable layers are in contact with the cell piece.
Because above-mentioned technical proposal is used, the utility model has following advantages compared with prior art:The utility model
UV used for solar batteries obstructs packaging adhesive film, by forming at least one layer of UV barrier layers in any surface of high permeable layers, so may be used
To avoid the UV auxiliary agents in UV barrier layers from diffusing out, it is to avoid the reduction of solar cell power generation efficiency, and it can avoid
Solder resist or cell piece and UV absorbents it is incompatible caused by xanthochromia;And high permeable layers will not be produced with upper strata packaging adhesive film
Life influences each other, and cell piece surface is spilt over even if it also will not influence generating efficiency as conventional glued membrane.
Brief description of the drawings
Fig. 1 is the structural representation that the utility model UV used for solar batteries obstructs packaging adhesive film.
Embodiment
The utility model is further described below in conjunction with embodiment.
UV used for solar batteries barrier packaging adhesive films as shown in Figure 1, it includes high permeable layers 1 and at least one layer UV barrier layers
2。
Wherein, the matrix resin of high permeable layers 1 can be EVA, POE, polyvinyl butyral resin (PVB), ionomer, poly- ammonia
Ester, silica gel or epoxy resin, and (addition of above-mentioned auxiliary agent is containing the auxiliary agent such as appropriate crosslinking agent, crosslinking coagent, coupling agent
Conventional mass content), its thickness is usually 50~400 μm.And at least one layer of UV barrier layers 2, they are formed in height
On any surface of permeable layers 1 (on i.e. a certain surface).In the present embodiment, packaging adhesive film is by high permeable layers 1 and is formed for UV barriers
Constituted in the UV barrier layers 2 of the high any surface of permeable layers 1, so can be with cost-effective and simplified manufacture craft.The base of UV barrier layers 2
Body resin can be EVA, POE, polyvinyl butyral resin (PVB), ionomer, polyurethane, silica gel or epoxy resin, and thickness is usual
For 100~600 μm;It can also containing the auxiliary agent such as appropriate crosslinking agent, crosslinking coagent, coupling agent, its matrix resin preferably with
The matrix resin of high permeable layers 1 is consistent;Unlike, UV barrier layers 2 contain UV absorbers, the purple that high permeable layers 1 do not have
The UV such as outer light stabilizer auxiliary agents (addition of above-mentioned auxiliary agent is conventional mass content), to ensure that UV light can not pass through,
So as to avoid influence of the UV light to solar cell module back veneer, so as to improve the life-span of battery component.In the present embodiment,
UV barriers packaging adhesive film can be made using existing coextrusion forming process or film laminating technology.
By above-mentioned UV barrier packaging adhesive films according to saturating packaging film (upper strata the packaging adhesive film)/battery of existing glass/height
Piece/UV barrier packaging film (lower floor's packaging adhesive film)/backboards are assembled into solar cell, and wherein UV barrier packaging films are this
UV used for solar batteries barrier packaging adhesive films in embodiment, and high permeable layers 1 are in contact with cell piece.
The UV barrier packaging adhesive films that the high permeable layers 1 and UV barrier layers 2 of different-thickness shown in table 1 are formed into same thickness are carried out
Test, it the results are shown in Table 2
The difference of table 1 UV obstructs the list of packaging adhesive film
Wherein, high permeable layers 1 and UV barrier layers 2 can directly buy commercially available, and homemade routine is employed in the application and is matched somebody with somebody
Fang Jinhang coextrusion molds.Wherein, the matrix resin EVA of high permeable layers 1:It is commercially available, 98wt%;Crosslinking agent:Commercially available TBEC
(0.5wt%), TAIC (0.5wt%);Coupling agent:Commercially available KH570,1wt%;And the matrix resin EVA of UV barrier layers 2:It is commercially available,
97.5wt%;Crosslinking agent:Commercially available TBEC (0.5wt%), TAIC (0.5wt%);Coupling agent:Commercially available KH570,1wt%;Ultraviolet light
Stabilizer (0.2wt%), it is commercially available;UV absorbers (0.3wt%):It is commercially available.
The difference of table 2 UV obstructs the performance table of packaging adhesive film
By above-mentioned UV barrier packaging adhesive films and conventional material formation solar cell module (as shown in table 3).According to
Above comparative result, it can be seen that compared with commercially available UV isolation-type EVA packaging adhesive films, packaging adhesive film of the invention is same
UV barriering effects.But but there is long-term efficient photoelectricity treater efficiency with the component prepared by the packaging adhesive film of the present invention.
The solar cell module performance table that the difference of table 3 UV barrier packaging adhesive films are assembled into
Above-described embodiment is only to illustrate technical concepts and features of the present utility model, and its object is to allow be familiar with technique
Personage can understand content of the present utility model and implement according to this, protection domain of the present utility model can not be limited with this.
All equivalent change or modifications made according to the utility model Spirit Essence, should all cover protection domain of the present utility model it
It is interior.
Claims (6)
1. a kind of UV barriers packaging adhesive film used for solar batteries, it is characterised in that:It includes high permeable layers and formed in the height
At least one layer of UV barrier layers of permeable layers any surface.
2. UV barriers packaging adhesive film used for solar batteries according to claim 1, it is characterised in that:It by high permeable layers and
The UV barrier layers formed in the high permeable layers any surface are constituted.
3. UV barriers packaging adhesive film used for solar batteries according to claim 1, it is characterised in that:The thickness of the high permeable layers
Spend for 50 ~ 400 μm.
4. UV barriers packaging adhesive film used for solar batteries according to claim 1, it is characterised in that:The UV barrier layers
Thickness is 100 ~ 600 μm.
5. UV barriers packaging adhesive film used for solar batteries according to claim 1, it is characterised in that:It is the high permeable layers
Suppressed with the UV barrier layers coextrusion mold or film layer.
6. a kind of solar cell module using the packaging adhesive film, backsheet layer that it includes being cascading from bottom to top,
Lower floor's packaging adhesive film, cell piece, upper strata packaging adhesive film and glassy layer, it is characterised in that:Lower floor's packaging adhesive film will for right
Any described UV used for solar batteries barrier packaging adhesive films in 1 to 5 are sought, the high permeable layers are in contact with the cell piece.