CN206510514U - A kind of automotive trim fiber reinforcement sheet material - Google Patents
A kind of automotive trim fiber reinforcement sheet material Download PDFInfo
- Publication number
- CN206510514U CN206510514U CN201621325112.5U CN201621325112U CN206510514U CN 206510514 U CN206510514 U CN 206510514U CN 201621325112 U CN201621325112 U CN 201621325112U CN 206510514 U CN206510514 U CN 206510514U
- Authority
- CN
- China
- Prior art keywords
- layer
- automotive trim
- fiber reinforcement
- sheet material
- reinforcement sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of automotive trim fiber reinforcement sheet material, including layer wrapped in cloth, outer layer, la m and central core, the arrangement of each layer from inside to outside is followed successively by central core, la m, outer layer, layer wrapped in cloth, the la m material is glass fiber reinforced polypropylene material, and the central core material is bamboo fibre base material.Automotive trim of the present utility model fiber reinforcement sheet material, compact conformation is reasonable in design, lightweight compared with existing automotive trim plate, bulk strength is strengthened, sandwich construction makes it have shock resistance, the premium properties of wear-resisting, high load-bearing, with longer service life.
Description
Technical field
The utility model belongs to Material Field, especially a kind of automotive trim fiber reinforcement sheet material.
Background technology
Automobile has increasingly becomed the product of people's popular consumer, automotive trim as technical and artistry combination,
Account for the major part of automobile overall design workload, it is seen that the significance level and fine degree of interior trim.Interior trim is also people's choosing simultaneously
Purchase a significant consideration of automobile.
Automotive trim has different requirements in different parts, therefore is also impossible to all interior trims all from same material
Material.In many occasions of current automotive trim, such as dormer window sunshading board, standby chamber interior wall, tyre-well lid all use fiber and plastics
（It is many times PP plastics）Composite material hot pressing or punching shaping.But this structure has not wear-resisting, not load-bearing, not durable
The shortcomings of, it is impossible to the demand of people is met well.
Utility model content
The characteristics such as weight capacity, wearability in order to strengthen automotive trim plate, and with excellent combination property and compared with
The wide scope of application, the utility model provides a kind of automotive trim fiber reinforcement sheet material, to solve above-mentioned problem.
A kind of automotive trim fiber reinforcement sheet material, including layer wrapped in cloth, outer layer, la m and central core, each layer by
Interior and outer arrangement is followed successively by central core, la m, outer layer, layer wrapped in cloth, and the la m material is glass fiber reinforcement
Polypropylene material, the central core material is bamboo fibre base material.
Preferably, the fiber reinforcement sheet material is 7 Rotating fields, and centered on central core, one layer of inner side of respectively arranging up and down
Layer, outer layer, layer wrapped in cloth.Symmetry arrangement structure play further enhance effect while, also by the bamboo fibre of central core
Wrap up, the effect that it can be made to play its bending strength and buffering as a complete layer.
Preferably, the material of the outer layer is nylon 6 or polyurethane.Nylon 6 and polyurethane material are respectively provided with outstanding
Wearability and the life-span, nylon 6 is preferable in anti-flammability and weight capacity performance, and polyurethane has sound-deadening properties and shock resistance,
Two kinds of materials are well suited for as outer layer, can be selected according to different interior trim application regions.
Further, the la m includes the first enhancement layer and the second enhancement layer, and first enhancement layer and second increase
The glass fibre of strong layer is ordered into unidirectional array, and the glass fibre orientation of the first enhancement layer and the second enhancement layer is mutual
Vertically.The intensity enhancing that glass fiber reinforced polypropylene has la m intensity, and the fiber of two enhancement layers is arranged vertically, more
It is that further enhancing the overall intensity of the utility model.
Preferably, the layer wrapped in cloth is one kind in non-woven fabrics, looped fabric, artificial leather, leather.Non-woven fabrics, knitting
Cloth, artificial leather, leather are the conventional outer shell fabrics in automotive trim, can be occurred at the different application position of automotive trim, according to
Different demands are selected.
The beneficial effects of the utility model are：Automotive trim of the present utility model fiber reinforcement sheet material, compact conformation,
It is reasonable in design, excellent combination property.Lightweight compared with existing automotive trim plate, bulk strength is strengthened, multilayer
Structure makes it have shock resistance, the premium properties of wear-resisting, high load-bearing, and with longer service life.
Brief description of the drawings
Fig. 1 is the cross-sectional view of the utility model embodiment.
1- layers wrapped in cloth, 2- outer layers, 3- la ms, the enhancement layers of 31- first, the enhancement layers of 32- second, 4- central cores.
Embodiment
A kind of automotive trim fiber reinforcement sheet material, including layer wrapped in cloth 1, outer layer 2, la m 3 and central core 4, respectively
The arrangement of layer from inside to outside is followed successively by central core 4, la m 3, outer layer 2, layer wrapped in cloth 1, and the material of la m 3 is glass
TRPP material, the material of central core 4 is bamboo fibre base material.
Preferably, the fiber reinforcement sheet material is 7 Rotating fields, and centered on central core 4, one layer of inner side of respectively arranging up and down
Layer 3, outer layer 2, layer wrapped in cloth 1.
Preferably, the material of the outer layer 2 is nylon 6 or polyurethane.
Further, the la m 3 includes the first enhancement layer 31 and the second enhancement layer 32, the He of the first enhancement layer 31
The glass fibre of second enhancement layer 32 is ordered into unidirectional array, and the glass fibre of the first enhancement layer 31 and the second enhancement layer 32
Orientation is mutually perpendicular to.
Preferably, the layer wrapped in cloth 1 is one kind in non-woven fabrics, looped fabric, artificial leather, leather.
The automotive trim of the utility model embodiment is as follows with the preparation method of fiber reinforcement sheet material：
（1）, central core 4 bamboo fibre spray appropriate adhesive and fire retardant, then dry, make its aqueous less than 10%；
（2）, the mechanical spreading machine of bamboo fibre mated formation into slab, it is rear to be suppressed with roller machine with 0.2-0.5 MPa pressure
Into bamboo fibre base material；
（3）, in the levels drawout layer glass TRPP plate of central core 4, layer glass fiber reinforcement gathers
Add appropriate adhesive between acrylic panel, the thickness of bamboo fibre base material is not less than 6mm, every layer of glass fiber reinforced polypropylene plate
Thickness is in 0.5-1.5mm；
（4）, the material of outer layer 2 is uniformly spread over to the upper and lower surface of la m, with mould heating make material melts or
Foaming, is then suppressed with mould, such as uses polyurethane, upper mould temperature control is at 120-125 DEG C, and lower mould temperature control is in 130-135
DEG C, such as use nylon 6, upper 180-185 DEG C of mould temperature, lower 190-195 DEG C of mould temperature, the compressing pressure 7-8MPa of mould, pressurize
Time 1.5-2min, shaping is taken out, and is cut out.
（5）, with adhesive or packaging line surround sheet material overall package layer wrapped in cloth, produce.
With fiber reinforcement sheet material compared to the prior art, lightweight, bulk strength is obtained automotive trim made from the method
Enhancing, sandwich construction makes it have impact, the premium properties of wear-resisting, high load-bearing and long life.
Above example is only to illustrate optimal technical scheme of the present utility model, it is noted that for the art
Those of ordinary skill for, some improvement made on the premise of the utility model principle is not departed from or equivalent substitution,
Protection domain of the present utility model is accordingly to be regarded as, should be covered in right of the present utility model.
Claims (5)
1. a kind of automotive trim fiber reinforcement sheet material, it is characterised in that including layer wrapped in cloth, outer layer, la m and center
Layer, the arrangement of each layer from inside to outside is followed successively by central core, la m, outer layer, layer wrapped in cloth, and the la m material is glass
TRPP material, the central core material is bamboo fibre base material.
2. a kind of automotive trim fiber reinforcement sheet material according to claim 1, it is characterised in that the fibre reinforcement plate
Material is 7 Rotating fields, centered on central core, up and down one layer of la m, outer layer, layer wrapped in cloth of each arrangement.
3. a kind of automotive trim fiber reinforcement sheet material according to claim 1, it is characterised in that the material of the outer layer
Matter is nylon 6 or polyurethane.
4. a kind of automotive trim fiber reinforcement sheet material according to claim 1, it is characterised in that the la m includes
First enhancement layer and the second enhancement layer, the glass fibre of first enhancement layer and the second enhancement layer are ordered into unidirectional array,
And first the glass fibre orientation of enhancement layer and the second enhancement layer be mutually perpendicular to.
5. a kind of automotive trim fiber reinforcement sheet material according to claim 1, it is characterised in that the layer wrapped in cloth is
One kind in non-woven fabrics, looped fabric, artificial leather, leather.