CN206048926U - A kind of uvioresistant, heat-resisting BOPET films - Google Patents
A kind of uvioresistant, heat-resisting BOPET films Download PDFInfo
- Publication number
- CN206048926U CN206048926U CN201620983100.5U CN201620983100U CN206048926U CN 206048926 U CN206048926 U CN 206048926U CN 201620983100 U CN201620983100 U CN 201620983100U CN 206048926 U CN206048926 U CN 206048926U
- Authority
- CN
- China
- Prior art keywords
- bopet
- heat
- uvioresistant
- resisting
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
This utility model discloses a kind of uvioresistant, heat-resisting BOPET films, and it is followed successively by basement membrane, graphene layer, ultraviolet resistant layer and organic silica refractory coating with BOPET film as basement membrane, from the bottom to top.Compared with existing BOPET films, BOPET films of the present utility model have good being heated evenly property, can prevent hot-spot, can absorb shielding ultraviolet rays, and do not reduce film clarity.
Description
Technical field
This utility model belongs to film applications, and in particular to a kind of uvioresistant, heat-resisting BOPET films.
Background technology
BOPET film(That is biaxially oriented polyester film)With intensity it is high, rigidity is good, transparent, glossiness is high the features such as;
Particularly odorless, tasteless, colourless, nontoxic, prominent obdurability, and be widely used in automobile, household, electronic product
In protecting film.But find in actual applications in common BOPET film heat shrink fire-retardant fireproof and uvioresistant performance and bad.
Patent 203305606U discloses a kind of heat resistant fire-proof plate BOPET protecting film, and its BOPET films surface has one layer
Organic silica refractory coating, with good flame-proof heat-resistant performance, but does not have anti-ultraviolet function.
Utility model content
This utility model is intended to be improved above-mentioned heat resistant fire-proof plate BOPET protecting film, improves the resistance to of BOPET film
Hot and anti-ultraviolet property.
This utility model realizes that the technical scheme adopted by above-mentioned purpose is as follows:
A kind of uvioresistant, heat-resisting BOPET films, it is followed successively by basement membrane, Graphene with BOPET film as basement membrane, from the bottom to top
Layer, ultraviolet resistant layer and organic silica refractory coating.
Further, the BOPET film thickness is 25~150 μm.
Further, the graphene layer is with 1~10 layer of Graphene.
Further, the ultraviolet resistant layer thickness is 10~20 μm.
Further, organic silica refractory coating thickness is 2~5 μm.
Beneficial effect:This utility model increases graphene layer between organic silica refractory coating and basement membrane, can improve
Being heated evenly property of thin film, prevents hot-spot, so as to improve the heat resistance of thin film.Ultraviolet resistant layer adopts the anti-purple of light absorbs type
Outside line agent, the alternative ultraviolet that absorbs are converted into harmless low-energy radiation, and graphene layer can play auxiliary shield ultraviolet
Effect, reach, and do not reduce the effect of film clarity.
Description of the drawings
Fig. 1 be uvioresistant, the schematic diagram of heat-resisting BOPET films, wherein, 1-BOPET thin film, 2- graphene layers, 3- UV resistance
Line layer, the organic silica refractory coatings of 4-.
Specific embodiment
This utility model is described in further details with accompanying drawing with reference to embodiments.
Embodiment 1
Organic silica coating is constituted by weight:
60 parts of ethanol
10 parts of tetraethoxysilane
20 parts of dimethyldiethoxysilane
3 parts of silicon dioxide
8 parts of hydrochloric acid
80 parts of water.
Anti-ultraviolet paint is constituted by weight:
40 parts of polyurethane resin
20 parts of benzotriazole
40 parts of ethanol.
(1)By sided corona treatment mistake(48 dynes of corona value)Thickness is that 135 μm of BOPET film surface carries out ethanol cleaning,
Except degreasing and impurity, hot-air seasoning, then one layer of adhesive is coated with surface, then with the Graphene being grown on copper(By normal
Rule CVD growth)Stick together, the pressing of Jing volume to volume removes copper using etch, obtains BOPET film/Graphene;
(2)Above-mentioned anti-ultraviolet paint is coated into graphenic surface, 15 microns of coating thickness is heating and curing, solidified
Time 20s, 100 DEG C of solidification temperature obtain BOPET film/Graphene/anti-ultraviolet;
(3)Finally, heat with above-mentioned organic silica coatings in anti-ultraviolet layer surface, 3 microns of coating thickness
Solidification, hardening time 20s, 80 DEG C of solidification temperature, be obtained uvioresistant, heat-resisting BOPET films.
Embodiment 2
Organic silica coating is constituted by weight:
50 parts of ethanol
15 parts of MTES
25 parts of aminomethyl phenyl diethoxy silane
2 parts of silicon dioxide
6 parts of hydrochloric acid
70 parts of water.
Anti-ultraviolet paint is constituted by weight:
50 parts of polyurethane resin
15 parts of benzotriazole
15 parts of ESCALOL 567
20 parts of ethanol.
(1)By sided corona treatment mistake(50 dynes of corona value)Thickness is that 135 μm of BOPET film surface carries out ethanol cleaning,
Except degreasing and impurity, hot-air seasoning, then one layer of adhesive is coated with surface, then with the Graphene being grown on copper(By normal
Rule CVD growth)Stick together, the pressing of Jing volume to volume removes copper using etch, and 10 layer graphene of repetitive displacement is obtained
BOPET film/graphene layer;
(2)Above-mentioned anti-ultraviolet paint is coated into graphenic surface, 15 microns of coating thickness is heating and curing, solidified
Time 20s, 100 DEG C of solidification temperature obtain BOPET film/graphene layer/ultraviolet resistant layer;
(3)Finally, heat with above-mentioned organic silica coatings in anti-ultraviolet layer surface, 3 microns of coating thickness
Solidification, hardening time 20s, 80 DEG C of solidification temperature, be obtained uvioresistant, heat-resisting BOPET films.
Claims (5)
1. a kind of uvioresistant, heat-resisting BOPET films, it be followed successively by with BOPET film as basement membrane, from the bottom to top basement membrane, graphene layer,
Ultraviolet resistant layer and organic silica refractory coating.
2. uvioresistant, heat-resisting BOPET films according to claim 1, it is characterised in that:The BOPET film thickness be 25~
150μm。
3. uvioresistant, heat-resisting BOPET films according to claim 1, it is characterised in that:The ultraviolet resistant layer thickness be 10~
20μm。
4. uvioresistant, heat-resisting BOPET films according to claim 1, it is characterised in that:The graphene layer has 1~10 layer
Graphene.
5. uvioresistant, heat-resisting BOPET films according to claim 1, it is characterised in that:Organic silica refractory coating thickness
For 2~5 μm.