CN106166865A - A kind of flame-retardant and anti-static BOPET composite membrane - Google Patents
A kind of flame-retardant and anti-static BOPET composite membrane Download PDFInfo
- Publication number
- CN106166865A CN106166865A CN201610760018.0A CN201610760018A CN106166865A CN 106166865 A CN106166865 A CN 106166865A CN 201610760018 A CN201610760018 A CN 201610760018A CN 106166865 A CN106166865 A CN 106166865A
- Authority
- CN
- China
- Prior art keywords
- bopet
- flame
- retardant
- static
- composite membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The open a kind of flame-retardant and anti-static BOPET composite membrane of the present invention, it is with BOPET film as basement membrane, has one layer of organic silica refractory coating in membrane surface, and its feature is: have graphene layer between organic silica refractory coating and basement membrane.This composite membrane has good antistatic effect, and being heated evenly property, can prevent hot-spot, can be used for household building materials, the PLASTIC LAMINATED protecting film of electronic product.
Description
Technical field
The invention belongs to film applications, be specifically related to a kind of flame-retardant and anti-static BOPET composite membrane.
Background technology
BOPET film (i.e. biaxially oriented polyester film) has intensity height, good rigidly, transparent, glossiness high;
The most odorless, tasteless, colourless, nontoxic, prominent obdurability, and be widely used in automobile, household, electronic product
In protecting film.But find in actual applications in common BOPET film heat shrink fire-retardant fireproof performance bad.
Patent 203305606U discloses a kind of heat resistant fire-proof plate BOPET protecting film, and its BOPET film surface has one layer
Organic silica refractory coating, has good flame-proof heat-resistant performance, but does not have anlistatig effect.
Summary of the invention
It is contemplated that above-mentioned heat resistant fire-proof plate BOPET protecting film is improved, improve being heated all of BOPET film
Even property and antistatic effect.
It is as follows that the present invention realizes the technical scheme that above-mentioned purpose used:
A kind of flame-retardant and anti-static BOPET composite membrane, it is with BOPET film as basement membrane, has one layer of organic silica in membrane surface
Refractory coating, its feature is: have graphene layer between organic silica refractory coating and basement membrane.
Further, described BOPET film thickness is 25~150 μm.
Further, described organic silica refractory coating thickness is 2~5 μm.
Further, described graphene layer has the Graphene of 1-10 layer.
Beneficial effect: the present invention while retaining the good flame-proof heat-resistant performance of organic silica refractory coating, by
Increase graphene layer between organic silica refractory coating and basement membrane, thus improve the being heated evenly property of thin film, prevent hot-spot,
And there is good antistatic effect, can be used for household building materials, the PLASTIC LAMINATED protecting film of electronic product.
Accompanying drawing explanation
Fig. 1 is the schematic diagram of flame-retardant and anti-static BOPET composite membrane, and wherein, 1-BOPET thin film, 2-graphene layer, 3-is organic
Silica refractory coating.
Detailed description of the invention
Below in conjunction with embodiment and accompanying drawing, the present invention is described in further details.
Embodiment 1
Organic silica coating forms by weight:
Ethanol 60 weight portion
Tetraethoxysilane 10 weight portion
Dimethyldiethoxysilane 20 weight portion
Silicon dioxide 3 weight portion
Hydrochloric acid 8 weight portion
Water 80 weight portion
By 60 parts by weight of ethanol, 10 weight portion hydrochloric acid (concentration of hydrochloric acid solution is 10.54wt%) and 80 weight parts waters uniformly mix,
Obtain mixed solution, take 10 weight portion tetraethoxysilanes (Shanghai to prosperous Chemical Co., Ltd., purity: 99%), 20 weight portion diformazans
Base diethoxy silane (Shanghai ethyl Chemical Co., Ltd., purity > 97%), 3 parts by weight of silica (Wa Ke company of Germany,
Model: V15), add mixed solution, continuous stirring is uniform, obtains coating fluid.
Sided corona treatment is crossed the BOPET film surface that (corona value 48 dyne) thickness is 135 μm and carries out ethanol cleaning, remove
Greasy dirt and impurity, hot-air seasoning, then it is coated with one layer of adhesive on surface, then with the Graphene (CVD routinely being grown on copper
Method grows) stick together, through volume to volume pressing, use etch to remove copper, finally by the coating solution for preparing above in stone
Ink alkene surface, coating thickness 3 microns, be heating and curing, hardening time 20s, solidification temperature 80 DEG C, rolling prepares BOPET composite membrane.
Embodiment 2
Organic silica coating forms by weight:
Ethanol 50 weight portion
MTES 15 weight portion
Aminomethyl phenyl diethoxy silane 25 weight portion
Silicon dioxide 2 weight portion
Hydrochloric acid 6 weight portion
Water 70 weight portion
By 50 parts by weight of ethanol, 6 weight portion hydrochloric acid (concentration of hydrochloric acid solution is 10.54wt%) and 70 weight parts waters uniformly mix,
Mixed solution, takes 15 weight portion MTESs (Nanjing Chemical Co., Ltd. forward, content >=99%), 25 weight portions
Aminomethyl phenyl diethoxy silane (Hangzhou Ka Wei Chemical Industry Science Co., Ltd, content >=98%), 2 parts by weight of silica (Germany
Wa Ke company, model: V15) add mixed solution, continuous stirring is uniform, obtains coating fluid.
Sided corona treatment is crossed the BOPET film surface that (corona value 48 dyne) thickness is 135 μm and carries out ethanol cleaning, remove
Greasy dirt and impurity, hot-air seasoning, then one layer of adhesive it is coated with on surface, then stick together with the Graphene being grown on copper,
Through volume to volume pressing, use etch to remove copper, repetitive displacement 8 layer graphene, finally by the coating solution for preparing above in
Graphenic surface, coating thickness 3 microns, be heating and curing, hardening time 20s, solidification temperature 80 DEG C, rolling prepare BOPET be combined
Film.
Claims (4)
1. a flame-retardant and anti-static BOPET composite membrane, it is with BOPET film as basement membrane, has one layer of organosilicon in membrane surface
Oxygen refractory coating, it is characterised in that: between organic silica refractory coating and basement membrane, there is graphene layer.
Flame-retardant and anti-static BOPET composite membrane the most according to claim 1, it is characterised in that: described BOPET film thickness is
25~150 μm.
Flame-retardant and anti-static BOPET composite membrane the most according to claim 1, it is characterised in that: the described heat-resisting painting of organic silica
Layer thickness is 2~5 μm.
Flame-retardant and anti-static BOPET composite membrane the most according to claim 1, it is characterised in that: described graphene layer has 1-
The Graphene of 10 layers.