CN206030704U - High pressure decorative board - Google Patents
High pressure decorative board Download PDFInfo
- Publication number
- CN206030704U CN206030704U CN201620980257.2U CN201620980257U CN206030704U CN 206030704 U CN206030704 U CN 206030704U CN 201620980257 U CN201620980257 U CN 201620980257U CN 206030704 U CN206030704 U CN 206030704U
- Authority
- CN
- China
- Prior art keywords
- layer
- sandwich layer
- decorative pattern
- top layer
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model belongs to the technical field of ornamental material, especially, relate to a high pressure decorative board and production technology. It has solved the unreasonable scheduling problem of prior art design. This high pressure decorative board includes top layer and bottom, is equipped with the core board by at least two -layer sandwich layer stratification between top layer and bottom, and the one side of keeping away from the core board on the top layer is equipped with surperficial decorative pattern, and the one side of keeping away from the bottom at every layer of sandwich layer is equipped with sandwich layer decorative pattern respectively, and the surperficial decorative pattern who sets up on the top layer aligns or dislocation set with the sandwich layer decorative pattern who sets up on the sandwich layer, sets up sandwich layer decorative pattern on the sandwich layer aligns or dislocation set, top layer, bottom and core board form through hot pressing high pressure decorative board. The utility model has the advantages of: it is more reasonable to design, can reduce use cost and improve the practicality.
Description
Technical field
This utility model belongs to decorative materials technology, more particularly to a kind of high-pressure decorating plate.
Background technology
Decorative panel is a kind of conventional ornament materials.
Which is applied in desktop and kitchen cabinet etc. life furniture.
Existing ornament materials its at least there is following technical problem：The size that the decorative panel for dispatching from the factory generally sets, when
After in actual decoration process cut off decorative panel, the circumferential surface of decorative panel is planless structure or is a face
The structure of color, comparison are stiff, dull, in order to be able to further improve aesthetic property, in addition it is also necessary to be configured in the circumferential surface of decorative panel
Decorative pattern, decorative pattern are typically realized using transfer or by the way of coating, although can improve decorative effect, but, on
The mode stated not only increases use cost, and decorative pattern also easily comes off, and service life is short and practicality is poor.
For example, Chinese patent literature discloses a kind of thermal compound dalle for internal decoration component [application number：CN98236172.6]：By setting
Sesame felt, non-metal board glue successively it is hot-forming, during use according to different inside gadgets require thermo-compression bonding on adnexa.Thus
See, saved time using the material, material-saving, labor intensity it is little, pollution-free.
Although above-mentioned scheme has many advantages, such as the above, the program does not simultaneously solve above-mentioned technical problem, also
It is the presence of the technological deficiencies such as relatively costly and poor practicability.
Utility model content
The purpose of this utility model is for the problems referred to above, there is provided a kind of design more rationally, can reduce use cost and
Improve the high-pressure decorating plate of practicality.
Another purpose of the present utility model is for the problems referred to above, there is provided a kind of process is simple, can reduce using
The high pressure decorative board production technology of cost and raising practicality.
For reaching above-mentioned purpose, this utility model employs following technical proposal：This high-pressure decorating plate includes top layer and bottom
Layer, be provided between top layer and bottom by the core plate of at least two-layer sandwich layer stratification, top layer away from core plate one side
Incrustation pattern is provided with, and sandwich layer decorative pattern is respectively equipped with every layer of sandwich layer away from the one side of bottom, is arranged on top layer
Incrustation pattern and the sandwich layer decorative pattern alignment being arranged on sandwich layer are shifted to install, the core being arranged on the sandwich layer
The alignment of layer decorative pattern is shifted to install, and described top layer, bottom and core plate form described high pressure decorative by hot pressing
Plate.The circumferential surface or high-pressure decorating plate of the high-pressure decorating plate formed on face in cutting for high-pressure decorating plate after arbitrarily being cut
There is decorating structure.
In above-mentioned high-pressure decorating plate, the figure of the incrustation pattern it is identical with the figure of sandwich layer decorative pattern or
It is different.
In above-mentioned high-pressure decorating plate, described bottom is provided with bottom decorative pattern near the one side of core plate, described
Bottom decorative pattern and the sandwich layer decorative pattern alignment being arranged on sandwich layer or shift to install, described top layer, bottom and
Core plate forms described high-pressure decorating plate and any in the circumferential surface or high-pressure decorating plate of high-pressure decorating plate by hot pressing
Decorating structure be formed with face in being cut for high-pressure decorating plate after cutting.
In above-mentioned high-pressure decorating plate, the figure of the bottom decorative pattern is identical with the figure of sandwich layer decorative pattern
Or it is different.
In above-mentioned high-pressure decorating plate, described core plate thickness is more than the thickness on top layer.
In above-mentioned high-pressure decorating plate, described core plate thickness is more than the thickness of bottom.
In order to reach another purpose, this utility model employs following technical proposal：
This high pressure decorative board production technology comprises the steps：
A, dipping：By top layer and bottom dipping modified melamine-formaldehyde resin, modified melamine-formaldehyde resin consumption
For 100-140g/m2, the top layer and bottom after dipping after drying volatile quantity control between 5-9%；
Sandwich layer is impregnated into modified resin, modified resin consumption is 60-80g/m2, the sandwich layer after dipping volatilizees after drying
Amount control is between 5-9%；
B, assembly：By the top layer for having impregnated, bottom and sandwich layer according to the decorative pattern being arranged on top layer, bottom and sandwich layer
Position is alignd or is shifted to install, and then carries out assembly, that is, slab is obtained；
C, hot pressing：Slab feeding press is carried out into hot pressing, hot pressing temperature is 110-160 DEG C, and hot pressing time is 35-60 point
Clock, pressure are 6-10Mpa, i.e. high pressure decorative board finished product is obtained, and the circumferential surface of the high pressure decorative board finished product has decorating structure
Or high pressure decorative board finished product arbitrarily cut after cutting on face have decorating structure.The hot pressing under above-mentioned technological parameter
Decorative panel its there is preferable performance.
In above-mentioned step A, described modified resin is by melamine resin 60-70% and acrylic resin
30-40% is blended.
This high pressure decorative board production technology comprises the steps：
A, dipping：By top layer and bottom dipping modified melamine-formaldehyde resin, modified melamine-formaldehyde resin consumption
For 110-130g/m2, the top layer and bottom after dipping after drying volatile quantity control between 5-9%；
Sandwich layer is impregnated into modified resin, modified resin consumption is 65-75g/m2, the sandwich layer after dipping volatilizees after drying
Amount control is between 5-9%；Described modified resin is by melamine resin 60-70% and acrylic resin 30-
40% is blended；
B, assembly：By the top layer for having impregnated, bottom and sandwich layer according to the decorative pattern being arranged on top layer, bottom and sandwich layer
Position is alignd or is shifted to install, and then carries out assembly, that is, slab is obtained；
C, hot pressing：Slab feeding press is carried out into hot pressing, hot pressing temperature is 120-160 DEG C, and hot pressing time is 40-60 point
Clock, pressure are 6-10Mpa, i.e. high pressure decorative board finished product is obtained, and the circumferential surface of the high pressure decorative board finished product has decorating structure
Or high pressure decorative board finished product arbitrarily cut after cutting on face have decorating structure.
In above-mentioned step A, described top layer is modified melamine-formaldehyde resin pickup stain paper；Described sandwich layer is to change
Property Tetefol.Bottom is the paper of melamine impregnated paper or other materials.
Compared with prior art, the advantage of this high-pressure decorating plate and its production technology is：1st, design is more reasonable, subsequently
Using packaging efficiency that is more convenient and improve follow-up assembling, practicality more before, i.e. need not be transferred or be coated periphery
Decorative pattern.2nd, virtually reduce use cost.3rd, its long service life of the decorating structure of periphery.4th, substantially reduce and add
Between man-hour, difficulty of processing is reduced.5th, process is simple.
Description of the drawings
Fig. 1 is the structural representation that this utility model is provided.
Fig. 2 is the surface structure schematic diagram that this utility model is provided.
Fig. 3 is the core structure schematic diagram that this utility model is provided.
Fig. 4 is two structural representation of embodiment that this utility model is provided.
Fig. 5 is the fabric schematic diagram that this utility model is provided.
Fig. 6 is the process flow diagram that this utility model is provided.
In figure, top layer 1, incrustation pattern 11, bottom 2, bottom decorative pattern 21, core plate 3, sandwich layer 31, sandwich layer dress
Decorations pattern 311, high-pressure decorating plate a, decorating structure b.
Specific embodiment
The following is the specific embodiment of utility model and combine accompanying drawing, further is made to the technical solution of the utility model
Description, but this utility model is not limited to these embodiments.
Embodiment one
As Figure 1-3, this high-pressure decorating plate includes top layer 1 and bottom 2, is provided with by least between top layer 1 and bottom 2
The core plate 3 of 31 stratification of two-layer sandwich layer, top layer 1, bottom 2 and sandwich layer 31 are made by resin material.By top layer 1, bottom 2
Immerse into glue with sandwich layer 31,31 hot pressing of sandwich layer is formed as one into core plate 3, then just top layer 1, bottom 2 and core
3 hot pressing of plate is integrated.Top layer 1, bottom 2 and sandwich layer 31 are resin paper.
Secondly, thickness of 3 thickness of core plate more than top layer 1.Thickness of 3 thickness of core plate more than bottom 2.
Incrustation pattern 11 is provided with top layer 1 away from the one side of core plate 3, in every layer of sandwich layer 31 away from the one of bottom 2
Face is respectively equipped with sandwich layer decorative pattern 311, the incrustation pattern that is arranged on top layer 1 11 and the sandwich layer being arranged on sandwich layer 31
Decorative pattern 311 aligns or shifts to install, and the sandwich layer decorative pattern 311 being arranged on the sandwich layer 31 aligns or misplaces and sets
Put, described top layer 1, bottom 2 and core plate 3 form described high-pressure decorating plate a by hot pressing.The thickness of high-pressure decorating plate a
For 3-40mm.
In addition, the figure of the figure and sandwich layer decorative pattern 311 of the incrustation pattern 11 of the present embodiment is identical or different.
In the present embodiment, due to being all provided with decorative pattern, in the circumferential surface or high-pressure decorating plate of high-pressure decorating plate a
A be formed with face decorating structure b in cutting for high-pressure decorating plate a after arbitrarily being cut.That is, the present embodiment can leave to cut simultaneously
And still there is decorating structure b in its circumferential surface, it is to avoid transfer coats etc. showing for long the production cycle that technique is produced
As.
Further, the decorative pattern of the present embodiment and decorating structure copper stricture of vagina be in the same manner.Decorative pattern passes through 3D printing or coating
Up.
As shown in Fig. 1-3 and Fig. 6
The high-pressure decorating plate employing of the present embodiment is produced by below technique and processes, and specifically, the height of the present embodiment press-fits
The production technology of plaque comprises the steps：
A, dipping：Top layer 1 and bottom 2 are impregnated into modified melamine-formaldehyde resin, modified melamine-formaldehyde resin is used
Measure as 100-140g/m2, the top layer 1 and bottom 2 after dipping after drying volatile quantity control between 5-9%；
Sandwich layer 31 is impregnated into modified resin, modified resin consumption is 60-80g/m2, the sandwich layer 31 after dipping is after drying
Volatile quantity is controlled between 5-9%；
B, assembly：By the top layer 1 for having impregnated, bottom 2 and sandwich layer 31 according to being arranged on top layer 1, on bottom 2 and sandwich layer 31
Decorative pattern position is alignd or is shifted to install, and then carries out assembly, that is, slab is obtained；
C, hot pressing：Slab feeding press is carried out into hot pressing, hot pressing temperature is 110-160 DEG C, and hot pressing time is 35-60 point
Clock, pressure are 6-10Mpa, i.e. high pressure decorative board finished product is obtained, and the circumferential surface of the high pressure decorative board finished product has decorating structure
B or high pressure decorative board finished product are being cut on face with decorating structure b after arbitrarily being cut.
Prioritization scheme, in above-mentioned step A, described modified resin is by melamine resin 60-70% and third
Olefin(e) acid resinoid 30-40% is blended.This resin pliability and permeability are very good.Secondly, in above-mentioned step A, institute
The top layer 1 stated is modified melamine-formaldehyde resin pickup stain paper；Described sandwich layer 31 is that modified resin impregnates paper.
Further, this technique comprises the steps：
A, dipping：Top layer 1 and bottom 2 are impregnated into modified melamine-formaldehyde resin, modified melamine-formaldehyde resin is used
Measure as 110-130g/m2, the top layer 1 and bottom 2 after dipping after drying volatile quantity control between 5-9%；
Sandwich layer 31 is impregnated into modified resin, modified resin consumption is 65-75g/m2, the sandwich layer 31 after dipping is after drying
Volatile quantity is controlled between 5-9%；Described modified resin is by melamine resin 60-70% and acrylic resin
30-40% is blended；
B, assembly：By the top layer 1 for having impregnated, bottom 2 and sandwich layer 31 according to being arranged on top layer 1, on bottom 2 and sandwich layer 31
Decorative pattern position is alignd or is shifted to install, and then carries out assembly, that is, slab is obtained；
C, hot pressing：Slab feeding press is carried out into hot pressing, hot pressing temperature is 120-160 DEG C, and hot pressing time is 40-60 point
Clock, pressure are 6-10Mpa, i.e. high pressure decorative board finished product is obtained, and the circumferential surface of the high pressure decorative board finished product has decorating structure
B or high pressure decorative board finished product are being cut on face with decorating structure b after arbitrarily being cut.
Used as the prioritization scheme of the present embodiment, this technique comprises the steps：
A, dipping：Top layer 1 and bottom 2 are impregnated into modified melamine-formaldehyde resin, modified melamine-formaldehyde resin is used
Measure as 120g/m2, the top layer 1 and bottom 2 after dipping after drying volatile quantity control 7%；Described modified resin is by three
Melamine-formaldehyde resin 65% and acrylic resin 35% are blended；
Sandwich layer 31 is impregnated into modified resin, modified resin consumption is 70g/m2, the sandwich layer 31 after dipping waved after drying
Amount control is sent out 7%；
B, assembly：By the top layer 1 for having impregnated, bottom 2 and sandwich layer 31 according to being arranged on top layer 1, on bottom 2 and sandwich layer 31
Decorative pattern position is alignd or is shifted to install, and then carries out assembly, that is, slab is obtained；
C, hot pressing：Slab feeding press is carried out into hot pressing, hot pressing temperature is 135 DEG C, and hot pressing time is 50 minutes, and pressure is
8Mpa, i.e. high pressure decorative board finished product is obtained, there is the circumferential surface of the high pressure decorative board finished product decorating structure b or height to press-fit
Plaque finished product is being cut on face with decorating structure b after arbitrarily being cut.
Embodiment two
The present embodiment is essentially identical with the structure and principle of embodiment one, though therefore not to repeat here, different place
It is：The figure of incrustation pattern 11 is different with the figure of sandwich layer decorative pattern 311.But, both are close figure.
Embodiment three
As illustrated in figures 4-5, the present embodiment is essentially identical with the structure and principle of embodiment one, Gu therefore not to repeat here, and
Different place is：Bottom decorative pattern 21, described bottom decoration figure is provided with bottom 2 near the one side of core plate 3
Case 21 and the sandwich layer decorative pattern 311 being arranged on sandwich layer 31 align or shift to install, described top layer 1, bottom 2 and core
Plate 3 forms described high-pressure decorating plate a and any in the circumferential surface or high-pressure decorating plate a of high-pressure decorating plate a by hot pressing
Decorating structure b be formed with face in being cut for high-pressure decorating plate a after cutting.
The figure of the figure and sandwich layer decorative pattern 311 of bottom decorative pattern 21 is identical or different.
Example IV
The present embodiment is essentially identical with the structure and principle of embodiment one, though therefore not to repeat here, different place
It is：This technique comprises the steps：
A, dipping：Top layer 1 and bottom 2 are impregnated into modified melamine-formaldehyde resin, modified melamine-formaldehyde resin is used
Measure as 100g/m2, the top layer 1 and bottom 2 after dipping after drying volatile quantity control 5%；
Sandwich layer 31 is impregnated into modified resin, modified resin consumption is 60g/m2, the sandwich layer 31 after dipping waved after drying
Amount control is sent out 5%；Described modified resin is blended by melamine resin 60% and acrylic resin 30%；
B, assembly：By the top layer 1 for having impregnated, bottom 2 and sandwich layer 31 according to being arranged on top layer 1, on bottom 2 and sandwich layer 31
Decorative pattern position is alignd or is shifted to install, and then carries out assembly, that is, slab is obtained；
C, hot pressing：Slab feeding press is carried out into hot pressing, hot pressing temperature is 110 DEG C, and hot pressing time is 35 minutes, and pressure is
6Mpa, i.e. high pressure decorative board finished product is obtained, there is the circumferential surface of the high pressure decorative board finished product decorating structure b or height to press-fit
Plaque finished product is being cut on face with decorating structure b after arbitrarily being cut.
Embodiment five
The present embodiment is essentially identical with the structure and principle of embodiment one, though therefore not to repeat here, different place
It is：This technique comprises the steps：
A, dipping：Top layer 1 and bottom 2 are impregnated into modified melamine-formaldehyde resin, modified melamine-formaldehyde resin is used
Measure as 140g/m2, the top layer 1 and bottom 2 after dipping after drying volatile quantity control 9%；
Sandwich layer 31 is impregnated into modified resin, modified resin consumption is 80g/m2, the sandwich layer 31 after dipping waved after drying
Amount control is sent out 9%；
B, assembly：By the top layer 1 for having impregnated, bottom 2 and sandwich layer 31 according to being arranged on top layer 1, on bottom 2 and sandwich layer 31
Decorative pattern position is alignd or is shifted to install, and then carries out assembly, that is, slab is obtained；
C, hot pressing：Slab feeding press is carried out into hot pressing, hot pressing temperature is 160 DEG C, and hot pressing time is 60 minutes, and pressure is
10Mpa, i.e. high pressure decorative board finished product is obtained, there is the circumferential surface of the high pressure decorative board finished product decorating structure b or height to press-fit
Plaque finished product is being cut on face with decorating structure b after arbitrarily being cut.
Prioritization scheme, in above-mentioned step A, described modified resin is by melamine resin 70% and acrylic acid
Resinoid 40% is blended.This resin pliability and permeability are very good.Secondly, in above-mentioned step A, described top layer
1 is modified melamine-formaldehyde resin pickup stain paper；Described sandwich layer 31 is that modified resin impregnates paper.
Specific embodiment described herein is only explanation for example to this utility model spirit.This utility model institute
Category those skilled in the art can make various modifications or supplement or using similar to described specific embodiment
Mode substitute, but without departing from it is of the present utility model spirit or surmount scope defined in appended claims.
Although more having used top layer 1, incrustation pattern 11, bottom 2, bottom decorative pattern 21, core plate herein
3rd, the term such as sandwich layer 31, sandwich layer decorative pattern 311, high-pressure decorating plate a, decorating structure b, but be not precluded from using other terms
Probability.It is used for the purpose of more easily describing and explaining essence of the present utility model using these terms；It is construed as
Any additional restriction is all contrary with this utility model spirit.
Claims (6)
1. a kind of high-pressure decorating plate, including top layer (1) and bottom (2), is provided with by least two between top layer (1) and bottom (2)
The core plate (3) of layer sandwich layer (31) stratification, it is characterised in that described top layer (1) is provided with away from the one side of core plate (3)
Incrustation pattern (11), is respectively equipped with sandwich layer decorative pattern (311) in every layer of sandwich layer (31) away from the one side of bottom (2), if
Put the incrustation pattern (11) on top layer (1) and be arranged on sandwich layer (31) sandwich layer decorative pattern (311) alignment or
Shift to install, the sandwich layer decorative pattern (311) being arranged on the sandwich layer (31) aligns or shifts to install, described top layer
(1), bottom (2) and core plate (3) by hot pressing formed described high-pressure decorating plate (a) and high-pressure decorating plate circumferential surface or
Person's high-pressure decorating plate be formed with face decorating structure in cutting for high-pressure decorating plate after arbitrarily being cut.
2. high-pressure decorating plate according to claim 1, it is characterised in that the figure and core of incrustation pattern (11)
The figure of layer decorative pattern (311) is identical or different.
3. high-pressure decorating plate according to claim 1, it is characterised in that described bottom (2) near core plate (3)
Face is provided with bottom decorative pattern (21), described bottom decorative pattern (21) and the sandwich layer decorative pattern being arranged on sandwich layer (31)
(311) align or shift to install, described top layer (1), bottom (2) and core plate (3) formed by hot pressing described in high pressure
Decorative panel (a) and after the circumferential surface or high-pressure decorating plate (a) of high-pressure decorating plate (a) are arbitrarily cut in high-pressure decorating plate
A cutting for () be formed with face decorating structure (b).
4. high-pressure decorating plate according to claim 3, it is characterised in that the figure and core of bottom decorative pattern (21)
The figure of layer decorative pattern (311) is identical or different.
5. high-pressure decorating plate according to claim 1, it is characterised in that described core plate (3) thickness is more than top layer (1)
Thickness.
6. high-pressure decorating plate according to claim 1, it is characterised in that described core plate (3) thickness is more than bottom (2)
Thickness.