CN205498170U - Glass is decorated to safe dysmorphism - Google Patents
Glass is decorated to safe dysmorphism Download PDFInfo
- Publication number
- CN205498170U CN205498170U CN201620081373.0U CN201620081373U CN205498170U CN 205498170 U CN205498170 U CN 205498170U CN 201620081373 U CN201620081373 U CN 201620081373U CN 205498170 U CN205498170 U CN 205498170U
- Authority
- CN
- China
- Prior art keywords
- glass
- eva glue
- line
- ambetti
- bunting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to a glass is decorated to safe dysmorphism and manufacture craft belong to and decorate glass preparation technical field, and glass is decorated to safe dysmorphism only needs one deck glass by unsmooth special -shaped glass, EVA glue film, upholstery fabrics or decorative brick are first, this glass is decorated to safe dysmorphism is constituteed to the PET aluminizer, can not fade, and pleasing to the eye effect is changeable lasting, and light in weight is shock -resistant, and easy to assemble.
Description
Technical field
This utility model relates to a kind of safety abnormity ambetti and processing technology thereof, belongs to ambetti preparing technical field.
Background technology
In building decoration engineering, glass is the class ornament materials being most widely used.Along with the development of building industry, glass is being built
Build to use more and more extensive.Glass, from the most single daylighting function decoration functions till now, the most gradually develops non-line generation
The main flow of building.And architectural decorative glass is to take as the leading factor with design concept and function, use glass material and artistry, with quilt
The building of decoration becomes unified harmonious entirety, has both enriched art of architecture image, it is possible to improve utilitarian function, economic worth
And social value.
The most general ambetti, is by two glass laminatings, i.e. glass+glue+glass, clamps decorations and manufacture in the middle of two glass
Forming, some is in glass surface spraying decoration or engraving spraying decoration.
The effect that ambetti is played as a kind of novel building and ornament materials is increasing.Answering of architectural environment and function thereof
Polygamy and the personalization of people's esthetic sentiment, all make glass constantly to weed out the old and bring forth the new, to meet the requirement of people.
CN200310110141.0 discloses the production technology of a kind of fabricating color decorative glass sheet, with quartz sand, flux, coloring agent, Borax
For primary raw material, after mixing, it is smelt fluidised form glass through high temperature melting, uses by pedal gas-filled switching tube (1), to support trachea (2), valve total
Fluidised form glass blowing is become glass big by the blowing device manufacturing spherical decorative glass becoming (3), blowpipe (4), blowpipe pernetti (5) to constitute
Ball, after cooling, broken ball draws into fabricating color decorative glass sheet；CN201310049147.5 discloses a kind of plated film dress with crackle coating
The preparation method of decorations glass, screen printed pattern on glass, pattern cracks or void pattern, use Physical the most again
It is coated with metal or high reflecting inorganic oxide filling crackle or space, its silk-screen ink printed patterns and thing at crackle or gap
Reason method plated film combines, and makes the color of the existing ink of glass of printed decoration, has again and be embedded in the pattern that metal in ink is glittering
Or the high peculiar pattern of reflecting inorganic oxidation film；The open a kind of touch screen glass cover-plate of CN201310026158.1, its overall knot
Structure includes cover-plate glass and prints the ink layer on its frame, it is characterised in that: described ink layer is Muscovitum ink layer；This practicality
Novel with ultra-thin glass as base material, through precisely cutting, CNC refine edging, chemical tempering, and add in ink, paint
Colorful, insulated type natural mica, artificial mica synthesis, form more esthetical touch by Muscovitum ink printing on cover-plate glass
Screen cover plate decorating glass.
Although about the technology development of ambetti, but being all not fee from is by two glass laminatings, such aesthetic is simple,
And all plate glass, if there being different form glass, two blocks of glass cannot be realized at all and carry out plastic clip, also existing easily to fall simultaneously
Color, aesthetic is difficult to lasting shortcoming.Further, since traditional ambetti is made up of two blocks of glass, weight is big, volume
Weight, it is not easy to install, frangible.
Summary of the invention
The problem that this utility model exists for prior art, it is provided that a kind of safety abnormity ambetti, it has only to one layer of glass,
Will not fade, aesthetic is changeable persistently, lightweight, impact resistance, and convenient installation.
In order to solve the problems referred to above, this utility model be the technical scheme is that
A kind of safety abnormity ambetti, is made up of concavo-convex special-shaped glass, EVA glue-line and PET aluminizer.
Described safety abnormity ambetti, its structure is to be respectively concavo-convex special-shaped glass, EVA glue-line, decoration from top to bottom
Cloth or decorative brick, EVA glue-line, PET aluminizer.
Described concavo-convex special-shaped glass and EVA glue-line, bunting or decorative brick, EVA glue-line, the thickness of PET aluminizer
Degree ratio is: 10:0.5:1:0.5:1.
Another one purpose of the present utility model is to provide the processing technology of a kind of safety abnormity ambetti, comprises the following steps:
Choosing the glass mold of style, put the glass of flat board, then heat, temperature is 700～1000 DEG C, within 1.5～2 hours, dissolves into
Type, then low temperature is moulding, after 18～22 hours, forms the special-shaped glass of concaveconvex shape, is pasted into+one layer of bunting of one layer of EVA glue
Or+one layer of EVA glue of decorative brick+last layer of PET aluminizer, then to heat, temperature is 130～180 DEG C, in heating
Meanwhile, heating, evacuation on one side, form safety abnormity ambetti.
The beneficial effects of the utility model are:
A kind of safety abnormity ambetti that this utility model provides, is different from traditional glass+glue+glass technology, and it has only to
One layer of glass, can be applicable to special-shaped glass, and will not fade, and aesthetic is changeable persistently, the most lightweight, impact resistance, its
Thickness proportion can realize penetrating attractive in appearance, overall convenient installation.And processing technology is simple, with low cost, it is easy to accomplish industry metaplasia
Produce.
Accompanying drawing explanation
Fig. 1 safety abnormity ambetti structural representation；
Fig. 2 product shaping figure；
Wherein: 1 is concavo-convex special-shaped glass, 2 is EVA glue, and 3 is bunting or decorative brick, and 4 is PET aluminizer.
Detailed description of the invention
Being described in further details this utility model below by embodiment, these embodiments are only used for this utility model is described,
It is not limiting as scope of the present utility model.
Embodiment 1
A kind of safety abnormity ambetti, is aluminized by concavo-convex special-shaped glass, EVA glue-line, bunting or decorative brick, PET
Film forms；
Described safety abnormity ambetti, its structure be from top to bottom respectively concavo-convex special-shaped glass, EVA glue-line,
Bunting or decorative brick, EVA glue-line, PET aluminizer.
Described concavo-convex special-shaped glass and EVA glue-line, bunting or decorative brick, EVA glue-line, the thickness of PET aluminizer
Degree ratio is: 10:0.5:1:0.5:1.
Its processing technology, comprises the following steps:
Choosing the glass mold of style, put the glass of flat board, then heat, temperature is 700 DEG C, within 1.5 hours, dissolves molding,
Low temperature is moulding again, after 18 hours, forms the special-shaped glass of concaveconvex shape, is pasted into+one layer of bunting of one layer of EVA glue or decorative brick
+ one layer of EVA glue+last layer of PET aluminizer, then heats, and temperature is 130 DEG C, while heating, adds
Heat, evacuation, form safety abnormity ambetti.
Embodiment 2
A kind of safety abnormity ambetti, by concavo-convex special-shaped glass, EVA glue-line, bunting or decoration brick, PET plating
Aluminum film forms；
Described safety abnormity ambetti, its structure be from top to bottom respectively concavo-convex special-shaped glass, EVA glue-line,
Bunting or decorative brick, EVA glue-line, PET aluminizer.
Described concavo-convex special-shaped glass and EVA glue-line, bunting or decorative brick, EVA glue-line, the thickness of PET aluminizer
Degree ratio is: 10:0.5:1:0.5:1.
Its processing technology, comprises the following steps:
Choosing the glass mold of style, put the glass of flat board, then heat, temperature is 1000 DEG C, within 2 hours, dissolves molding,
Low temperature is moulding again, after 22 hours, forms the special-shaped glass of concaveconvex shape, is pasted into+one layer of bunting of one layer of EVA glue or decorative brick
+ one layer of EVA glue+last layer of PET aluminizer, then heats, and temperature is 180 DEG C, while heating, adds
Heat, evacuation, form safety abnormity ambetti.
Embodiment 3
A kind of safety abnormity ambetti, by concavo-convex special-shaped glass, EVA glue-line, bunting or decoration brick, PET plating
Aluminum film forms；
Described safety abnormity ambetti, its structure be from top to bottom respectively concavo-convex special-shaped glass, EVA glue-line,
Bunting or decorative brick, EVA glue-line, PET aluminizer.
Described concavo-convex special-shaped glass and EVA glue-line, bunting or decorative brick, EVA glue-line, the thickness of PET aluminizer
Degree ratio is: 10:0.5:1:0.5:1.
Its processing technology, comprises the following steps:
Choosing the glass mold of style, put the glass of flat board, then heat, temperature is 800 DEG C, within 1.8 hours, dissolves molding,
Low temperature is moulding again, after 20 hours, forms the special-shaped glass of concaveconvex shape, is pasted into+one layer of bunting of one layer of EVA glue or decorative brick
+ one layer of EVA glue+last layer of PET aluminizer, then heats, and temperature is 150 DEG C, while heating, adds
Heat, evacuation, form safety abnormity ambetti.
Embodiment 4
A kind of safety abnormity ambetti, by concavo-convex special-shaped glass, EVA glue-line, bunting or decoration brick, PET plating
Aluminum film forms；
Described safety abnormity ambetti, its structure be from top to bottom respectively concavo-convex special-shaped glass, EVA glue-line,
Bunting or decorative brick, EVA glue-line, PET aluminizer.
Described concavo-convex special-shaped glass and EVA glue-line, bunting or decorative brick, EVA glue-line, the thickness of PET aluminizer
Degree ratio is: 10:0.5:1:0.5:1.
Its processing technology, comprises the following steps:
Choosing the glass mold of style, put the glass of flat board, then heat, temperature is 750 DEG C, within 1.6 hours, dissolves molding,
Low temperature is moulding again, after 19 hours, forms the special-shaped glass of concaveconvex shape, is pasted into+one layer of bunting of one layer of EVA glue or decorative brick
+ one layer of EVA glue+last layer of PET aluminizer, then heats, and temperature is 135 DEG C, while heating, adds
Heat, evacuation, form safety abnormity ambetti.
Embodiment 5
A kind of safety abnormity ambetti, by concavo-convex special-shaped glass, EVA glue-line, bunting or decoration brick, PET plating
Aluminum film forms；
Described safety abnormity ambetti, its structure be from top to bottom respectively concavo-convex special-shaped glass, EVA glue-line,
Bunting or decorative brick, EVA glue-line, PET aluminizer.
Described concavo-convex special-shaped glass and EVA glue-line, bunting or decorative brick, EVA glue-line, the thickness of PET aluminizer
Degree ratio is: 10:0.5:1:0.5:1.
Its processing technology, comprises the following steps:
Choosing the glass mold of style, put the glass of flat board, then heat, temperature is 950 DEG C, within 1.9 hours, dissolves molding,
Low temperature is moulding again, after 21 hours, forms the special-shaped glass of concaveconvex shape, is pasted into+one layer of bunting of one layer of EVA glue or decorative brick
+ one layer of EVA glue+last layer of PET aluminizer, then heats, and temperature is 170 DEG C, while heating, adds
Heat, evacuation, form safety abnormity ambetti.
Claims (2)
1. a safety abnormity ambetti, it is characterized in that: this ambetti is by concavo-convex special-shaped glass, EVA glue-line, bunting or decorative brick, EVA glue-line, PET aluminizer, and its structure is to be respectively concavo-convex special-shaped glass, EVA glue-line, bunting or decorative brick, EVA glue-line, PET aluminizer from top to bottom.
A kind of safety abnormity ambetti the most according to claim 1, it is characterised in that: described concavo-convex special-shaped glass with EVA glue-line, bunting or decorative brick, EVA glue-line, the thickness proportion of PET aluminizer is: 10:0.5:1:0.5:1.