CN205443067U - A glass for furniture desktop - Google Patents
A glass for furniture desktop Download PDFInfo
- Publication number
- CN205443067U CN205443067U CN201620238276.8U CN201620238276U CN205443067U CN 205443067 U CN205443067 U CN 205443067U CN 201620238276 U CN201620238276 U CN 201620238276U CN 205443067 U CN205443067 U CN 205443067U
- Authority
- CN
- China
- Prior art keywords
- layer
- glass
- thicknesses
- layers
- furniture table
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a glass for furniture desktop, include from the last low who sets gradually extremely down the low energy -conserving glass layer of radiation of E, it has the photochromy to become PVB glued membrane layer, picture film layer, half steel glass no. 1, cavity aluminum strip layer, half steel glass no. 2 and the fireproof composite membrane layer of material to mix, low the energy -conserving glass layer from the bottom up of the low radiation of E has set gradually glass basic unit, a siNx layer, the 2nd tiO2 layer, the 3rd niCr layer, fourth ag layer, the 5th niCr layer, the 6th siNx layer, the 7th protective layer and the 8th superhard layer. The beneficial effects of the utility model are that: at outmost the 7th protective layer and the 8th superhard layer of setting up, the no fish tail in surface, the roughness is good, the bottommost sets up the fireproof composite membrane layer, makes the utility model discloses have good fire behavior, the security performance is strong.
Description
Technical field
This utility model relates to glass art, is specifically related to a kind of glass for furniture table.
Background technology
Glass plays key player in the production and life in the present age, its application very extensive, such as windowpane, glass decorative accessory, glassmaking ware, vehicle-mounted glass, glass curtain wall etc..Along with the continuous expansion of glass applications scope, market demand is also constantly increasing, and the exploitation about New Glasses Materials has become development trend in the industry.
Summary of the invention
The purpose of this utility model is to provide a kind of glass for furniture table, ornamental strong, and safe and practical.
The technical solution adopted in the utility model is: a kind of glass for furniture table, including the Low-E Low emissivity energy-saving glass layer set gradually from top to bottom, PVB adhesive film doped with photochromic material, picture films layer, semi-tempered glass one, hollow aluminum strip layer, semi-tempered glass two and fire prevention composite film；Described Low-E Low emissivity energy-saving glass layer is disposed with glass-base, a SiN from top to bottomxLayer, the 2nd TiO2Layer, the 3rd NiCr layer, the 4th Ag layer, the 5th NiCr layer, the 6th SiNxLayer, the 7th protective layer and the 8th superabrasive layer.
Further, described 7th protective layer is the combination of one or more in silicon oxide layer, titanium oxide layer, titanium nitride film；The thicknesses of layers of described 7th protective layer is 5-40nm.
Further, the combination of one or more during described 8th superabrasive layer is zirconium oxide film layer, yittrium oxide film layer, titanium nitride aluminum membranous layer；The thicknesses of layers of described 8th superabrasive layer is 5-40nm.
Further, described fire prevention composite film includes that dielectric layer and barrier layer, described dielectric layer are Si3N4Layer, described Si3N4The thickness of layer is 0.01-0.09mm；Described barrier layer is NiCr layer, and thickness is 0.01-0.09mm.
Further, the described PVB adhesive film doped with photochromic material is the PVB film containing spiropyran class organic photochromic material.
Further, a described SiNxThe thicknesses of layers of layer is 15-25nm；Described 6th SiNxThe thicknesses of layers of layer is 20-30nm.
Further, described 2nd TiO2The thicknesses of layers of layer is 10-25nm.
Further, the thicknesses of layers of described 3rd NiCr layer is 2-5nm；The thicknesses of layers of described 5th NiCr layer is 2-5nm.
Further, in the described PVB film layer containing spiropyran class organic photochromic material, the content of spiropyran class organic photochromic material is 0.4-0.8%.
Further, it is filled with fluid sealant at the interval between semi-tempered glass one and the semi-tempered glass two outside described hollow aluminum strip layer.
The beneficial effects of the utility model are: arrange the 7th protective layer and the 8th superabrasive layer at outermost layer, and surface is without scratching, and flatness is good；Bottommost arranges fire prevention composite film, makes this utility model have good fire protecting performance, and security performance is strong.
Accompanying drawing explanation
Fig. 1 is structural representation of the present utility model.
Fig. 2 is the structural representation of Low-E Low emissivity energy-saving glass layer.
In figure: Low-E Low emissivity energy-saving glass layer 1, the PVB adhesive film 2 doped with photochromic material, picture films layer 3, semi-tempered glass 1, hollow aluminum strip layer 5, semi-tempered glass 26, fire prevention composite film 7, glass-base the 10, the oneth SiNxLayer the 11, the 2nd TiO2Layer the 12, the 3rd NiCr layer the 13, the 4th Ag layer the 14, the 5th NiCr layer the 15, the 6th SiNxLayer the 16, the 7th protective layer the 17, the 8th superabrasive layer 18.
Detailed description of the invention
With embodiment, the technical solution of the utility model is illustrated below in conjunction with the accompanying drawings.
Shown in seeing figures.1.and.2, a kind of glass for furniture table, including the Low-E Low emissivity energy-saving glass layer 1 set gradually from top to bottom, PVB adhesive film 2 doped with photochromic material, picture films layer 3, semi-tempered glass 1, hollow aluminum strip layer 5, semi-tempered glass 26 and fire prevention composite film 7.By arranging fire prevention composite film 7 at bottommost, making this utility model have good fire protecting performance, security performance is strong.Described fire prevention composite film 7 includes that dielectric layer and barrier layer, described dielectric layer are Si3N4Layer, described Si3N4The thickness of layer is 0.01-0.09mm；Described barrier layer is NiCr layer, and thickness is 0.01-0.09mm.The described PVB adhesive film 2 doped with photochromic material is the PVB film containing spiropyran class organic photochromic material.In the described PVB film layer 2 containing spiropyran class organic photochromic material, the content of spiropyran class organic photochromic material is 0.4-0.8%.It is filled with fluid sealant at the interval between semi-tempered glass 1 and semi-tempered glass 26 outside described hollow aluminum strip layer 5.
Described Low-E Low emissivity energy-saving glass layer 1 is disposed with glass-base the 10, the oneth SiN from top to bottomxLayer the 11, the 2nd TiO2Layer the 12, the 3rd NiCr layer the 13, the 4th Ag layer the 14, the 5th NiCr layer the 15, the 6th SiNxLayer the 16, the 7th protective layer 17 and the 8th superabrasive layer 18.By arranging the 7th protective layer 17 and the 8th superabrasive layer 18 at outermost layer, surface is without scratching, and flatness is good.Described 7th protective layer 17 is the combination of one or more in silicon oxide layer, titanium oxide layer, titanium nitride film；The thicknesses of layers of described 7th protective layer 17 is 5-40nm.Described 8th superabrasive layer 18 is the combination of one or more in zirconium oxide film layer, yittrium oxide film layer, titanium nitride aluminum membranous layer；The thicknesses of layers of described 8th superabrasive layer 18 is 5-40nm.A described SiNxThe thicknesses of layers of layer 11 is 15-25nm；Described 6th SiNxThe thicknesses of layers of layer 16 is 20-30nm.Described 2nd TiO2The thicknesses of layers of layer 12 is 10-25nm.The thicknesses of layers of described 3rd NiCr layer 13 is 2-5nm；The thicknesses of layers of described 5th NiCr layer 15 is 2-5nm.
Above-described embodiment is only that of the present utility model ultimate principle, principal character and advantage have been shown and described.Skilled person will appreciate that of the industry; this utility model is not restricted to the described embodiments; described in above-described embodiment and description, principle of the present utility model is simply described; on the premise of without departing from this utility model spirit and scope; this utility model also has various changes and modifications, in the range of these changes and improvements both fall within claimed this utility model.
Claims (10)
1. the glass for furniture table, it is characterised in that: include the Low-E Low emissivity energy-saving glass layer set gradually from top to bottom, PVB adhesive film, picture films layer, semi-tempered glass one, hollow aluminum strip layer, semi-tempered glass two and fire prevention composite film doped with photochromic material；Described Low-E Low emissivity energy-saving glass layer is disposed with glass-base, a SiN from top to bottomxLayer, the 2nd TiO2Layer, the 3rd NiCr layer, the 4th Ag layer, the 5th NiCr layer, the 6th SiNxLayer, the 7th protective layer and the 8th superabrasive layer.
A kind of glass for furniture table the most according to claim 1, it is characterised in that: described 7th protective layer is the combination of one or more in silicon oxide layer, titanium oxide layer, titanium nitride film；The thicknesses of layers of described 7th protective layer is 5-40nm.
A kind of glass for furniture table the most according to claim 1, it is characterised in that: described 8th superabrasive layer is the combination of one or more in zirconium oxide film layer, yittrium oxide film layer, titanium nitride aluminum membranous layer；The thicknesses of layers of described 8th superabrasive layer is 5-40nm.
A kind of glass for furniture table the most according to claim 1, it is characterised in that: described fire prevention composite film includes that dielectric layer and barrier layer, described dielectric layer are Si3N4Layer, described Si3N4The thickness of layer is 0.01-0.09mm；Described barrier layer is NiCr layer, and thickness is 0.01-0.09mm.
A kind of glass for furniture table the most according to claim 1, it is characterised in that: the described PVB adhesive film doped with photochromic material is the PVB film containing spiropyran class organic photochromic material.
A kind of glass for furniture table the most according to claim 1, it is characterised in that: a described SiNxThe thicknesses of layers of layer is 15-25nm；Described 6th SiNxThe thicknesses of layers of layer is 20-30nm.
A kind of glass for furniture table the most according to claim 1, it is characterised in that: described 2nd TiO2The thicknesses of layers of layer is 10-25nm.
A kind of glass for furniture table the most according to claim 1, it is characterised in that: the thicknesses of layers of described 3rd NiCr layer is 2-5nm；The thicknesses of layers of described 5th NiCr layer is 2-5nm.
A kind of glass for furniture table the most according to claim 5, it is characterised in that: in the described PVB film layer containing spiropyran class organic photochromic material, the content of spiropyran class organic photochromic material is 0.4-0.8%.
A kind of glass for furniture table the most according to claim 1, it is characterised in that: it is filled with fluid sealant at the interval between semi-tempered glass one and semi-tempered glass two outside described hollow aluminum strip layer.