CN205498240U - A decorate glass for shower room - Google Patents
A decorate glass for shower room Download PDFInfo
- Publication number
- CN205498240U CN205498240U CN201620238277.2U CN201620238277U CN205498240U CN 205498240 U CN205498240 U CN 205498240U CN 201620238277 U CN201620238277 U CN 201620238277U CN 205498240 U CN205498240 U CN 205498240U
- Authority
- CN
- China
- Prior art keywords
- layer
- glass
- layers
- thicknesses
- ambetti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a decorate glass for shower room, do it have the photochromy to become PVB glued membrane layer, picture film layer, toughened glass no. 2, cavity aluminum strip layer, the low of material to include from the toughened glass that sets gradually of the right side a to left side no. 1, night light film layer, mix the low energy -conserving glass layer of radiation of E, low the low energy -conserving glass layer of radiation of E has set gradually glass basic unit, a siNx layer, the 2nd tiO2 layer, the 3rd niCr layer, fourth ag layer, the 5th niCr layer, the 6th siNx layer, the 7th protective layer and the 8th superhard layer from the right side to a left side. The beneficial effects of the utility model are that: the setting contains the organic photochromic material's of spiral pyran class PVB rete, and it is quick to discolour, and the optical property is sensitive, in addition night light film layer luminous illumination and can show the picture film layer of picture, decorative effect is good.
Description
Technical field
This utility model relates to glass art, is specifically related to a kind of ambetti for shower house.
Background technology
Glass plays key player in the production and life in the present age, its application very extensive, such as windowpane, glass system
Ornament, glassmaking ware, vehicle-mounted glass, glass curtain wall etc..Along with the continuous expansion of glass applications scope, market demand
Also constantly increasing, the exploitation about New Glasses Materials has become development trend in the industry.
Summary of the invention
The purpose of this utility model is to provide a kind of ambetti for shower house, this kind of ambetti band colour change function,
Appearance looks elegant is changeable, ornamental strong, and safe and practical.
The technical solution adopted in the utility model is: a kind of ambetti for shower house, including setting gradually from right to left
Safety glass one, noctilucence film layers, PVB adhesive film doped with photochromic material, picture films layer, safety glass two,
Hollow aluminum strip layer, Low-E Low emissivity energy-saving glass layer, described Low-E Low emissivity energy-saving glass layer is disposed with from right to left
Glass-base, a SiNxLayer, the 2nd TiO2Layer, the 3rd NiCr layer, the 4th Ag layer, the 5th NiCr layer, the 6th SiNx
Layer, the 7th protective layer and the 8th superabrasive layer.
Further, described 7th protective layer is the group of one or more in silicon oxide layer, titanium oxide layer, titanium nitride film
Close；The thicknesses of layers of described 7th protective layer is 5-40nm.
Further, one or more during described 8th superabrasive layer is zirconium oxide film layer, yittrium oxide film layer, titanium nitride aluminum membranous layer
Combination；The thicknesses of layers of described 8th superabrasive layer is 5-40nm.
Further, described hollow aluminum strip layer is tight with safety glass two, Low-E Low emissivity energy-saving glass layer respectively by butyl rubber
Close bonding.
Further, the described PVB adhesive film doped with photochromic material is containing spiropyran class organic photochromic material
PVB film.
Further, a described SiNxThe thicknesses of layers of layer is 15-25nm；Described 6th SiNxThe thicknesses of layers of layer is
20-30nm。
Further, described 2nd TiO2The thicknesses of layers of layer is 10-25nm.
Further, the thicknesses of layers of described 3rd NiCr layer is 2-5nm；The thicknesses of layers of described 5th NiCr layer is 2-5nm.
Further, the organic light-induced variable of spiropyran class in the described PVB film layer containing spiropyran class organic photochromic material
The content of color material is 0.4-0.8%.
Further, the thickness of described noctilucence film layers is 0.3-1.5mm, and the thickness of described picture films layer is 0.3-1.5mm.
The beneficial effects of the utility model are: arrange the PVB film layer containing spiropyran class organic photochromic material, variable color
Quickly, optical property is sensitive, adds the luminous lighting of noctilucence film layers and can show the picture films layer of picture, decoration
Respond well.
Accompanying drawing explanation
Fig. 1 is structural representation of the present utility model.
Fig. 2 is the structural representation of Low-E Low emissivity energy-saving glass layer.
In figure: safety glass 1, noctilucence film layers 2, the PVB adhesive film 3 doped with photochromic material, picture glue
Lamella 4, safety glass 27, hollow aluminum strip layer 5, Low-E Low emissivity energy-saving glass layer 6, glass-base the 10, the oneth SiNx
Layer the 11, the 2nd TiO2Layer the 12, the 3rd NiCr layer the 13, the 4th Ag layer the 14, the 5th NiCr layer the 15, the 6th SiNxLayer 16,
7th protective layer the 17, the 8th superabrasive layer 18.
Detailed description of the invention
With embodiment, the technical solution of the utility model is illustrated below in conjunction with the accompanying drawings.
Shown in seeing figures.1.and.2, a kind of ambetti for shower house, including the tempering glass set gradually from right to left
Glass 1, noctilucence film layers 2, PVB adhesive film 3 doped with photochromic material, picture films layer 4, safety glass 27,
Hollow aluminum strip layer 5, Low-E Low emissivity energy-saving glass layer 6.Described hollow aluminum strip layer 5 by butyl rubber respectively with safety glass two
7, Low-E Low emissivity energy-saving glass layer 6 tight bond.The described PVB adhesive film 3 doped with photochromic material is for containing
The PVB film of spiropyran class organic photochromic material, the PVB film layer 3 containing spiropyran class organic photochromic material,
Variable color is quick, and optical property is sensitive.Spiropyran in the described PVB film layer 3 containing spiropyran class organic photochromic material
The content of class organic photochromic material is 0.4-0.8%.The thickness of described noctilucence film layers 2 is 0.3-1.5mm, described picture glue
The thickness of lamella 4 is 0.3-1.5mm.
Described Low-E Low emissivity energy-saving glass layer 6 is disposed with glass-base the 10, the oneth SiN from right to leftxLayer 11,
2nd TiO2Layer the 12, the 3rd NiCr layer the 13, the 4th Ag layer the 14, the 5th NiCr layer the 15, the 6th SiNxLayer the 16, the 7th is protected
Sheath 17 and the 8th superabrasive layer 18.Described 7th protective layer 17 is in silicon oxide layer, titanium oxide layer, titanium nitride film
Kind or several combinations；The thicknesses of layers of described 7th protective layer 17 is 5-40nm.Described 8th superabrasive layer 18 is zirconium oxide film
The combination of one or more in layer, yittrium oxide film layer, titanium nitride aluminum membranous layer；The thicknesses of layers of described 8th superabrasive layer 18 is
5-40nm.A described SiNxThe thicknesses of layers of layer 11 is 15-25nm；Described 6th SiNxThe thicknesses of layers of layer 16 is
20-30nm.Described 2nd TiO2The thicknesses of layers of layer 12 is 10-25nm.The thicknesses of layers of described 3rd NiCr layer 13 is
2-5nm；The thicknesses of layers of described 5th NiCr layer 15 is 2-5nm.
Above-described embodiment is only that of the present utility model ultimate principle, principal character and advantage have been shown and described.The skill of the industry
Art personnel are it should be appreciated that this utility model is not restricted to the described embodiments, and described in above-described embodiment and description is to say
Bright principle of the present utility model, on the premise of without departing from this utility model spirit and scope, this utility model also has various change
Change and improve, in the range of these changes and improvements both fall within claimed this utility model.
Claims (8)
1. the ambetti for shower house, it is characterized in that: include the safety glass one set gradually from right to left, noctilucence film layers, the PVB adhesive film doped with photochromic material, picture films layer, safety glass two, hollow aluminum strip layer, Low-E Low emissivity energy-saving glass layer, described Low-E Low emissivity energy-saving glass layer is disposed with glass-base, a SiN from right to leftxLayer, the 2nd TiO2Layer, the 3rd NiCr layer, the 4th Ag layer, the 5th NiCr layer, the 6th SiNxLayer, the 7th protective layer and the 8th superabrasive layer.
A kind of ambetti for shower house the most according to claim 1, it is characterised in that: described 7th protective layer is the combination of one or more in silicon oxide layer, titanium oxide layer, titanium nitride film；The thicknesses of layers of described 7th protective layer is 5-40nm.
A kind of ambetti for shower house the most according to claim 1, it is characterised in that: described 8th superabrasive layer is the combination of one or more in zirconium oxide film layer, yittrium oxide film layer, titanium nitride aluminum membranous layer；The thicknesses of layers of described 8th superabrasive layer is 5-40nm.
A kind of ambetti for shower house the most according to claim 1, it is characterised in that: described hollow aluminum strip layer by butyl rubber respectively with safety glass two, Low-E Low emissivity energy-saving glass layer tight bond.
A kind of ambetti for shower house the most according to claim 1, it is characterised in that: a described SiNxThe thicknesses of layers of layer is 15-25nm；Described 6th SiNxThe thicknesses of layers of layer is 20-30nm.
A kind of ambetti for shower house the most according to claim 1, it is characterised in that: described 2nd TiO2The thicknesses of layers of layer is 10-25nm.
A kind of ambetti for shower house the most according to claim 1, it is characterised in that: the thicknesses of layers of described 3rd NiCr layer is 2-5nm；The thicknesses of layers of described 5th NiCr layer is 2-5nm.
A kind of ambetti for shower house the most according to claim 1, it is characterised in that: the thickness of described noctilucence film layers is 0.3-1.5mm, and the thickness of described picture films layer is 0.3-1.5mm.