CN205428952U - 一种光伏焊带 - Google Patents

一种光伏焊带 Download PDF

Info

Publication number
CN205428952U
CN205428952U CN201520346176.2U CN201520346176U CN205428952U CN 205428952 U CN205428952 U CN 205428952U CN 201520346176 U CN201520346176 U CN 201520346176U CN 205428952 U CN205428952 U CN 205428952U
Authority
CN
China
Prior art keywords
coat
base material
alloy
welding belt
photovoltaic welding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201520346176.2U
Other languages
English (en)
Inventor
印冰
朱永兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201520346176.2U priority Critical patent/CN205428952U/zh
Application granted granted Critical
Publication of CN205428952U publication Critical patent/CN205428952U/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本实用新型公开了一种光伏焊带。所述基材表面电镀或热浸镀有涂覆层；所述基材为异形结构；所述异形结构面积为0.01mm2～0.15mm2，高度为0.10mm～0.35mm。涂覆层的厚度为5μm-30μm。基材选用纯铜、铜银合金、铜铝合金、铜镍、高铜合金中的一种。涂覆层选用锡铅合金、纯锡、纯银、锡铋合金、锡银合金、锡镍合金中的一种。本实用新型基材采用异形结构可以满足客户对于光伏焊带不同形状的需求，使得本产品适用范围更广，提高了生产企业的效益。

Description

一种光伏焊带
技术领域：
本实用新型属于太阳能电池板组件，特别涉及一种光伏焊带。
背景技术：
光伏焊带是太阳能电池板的原材料之一，起着连接电池片的作用。随着行业对电池板功率增加的要求日益提高，也对太阳能辅材提出了高要求。现有的光伏焊带形状结构单一，无法满足需要各类不同形状结构光伏焊带的客户要求。
公开于该背景技术部分的信息仅仅旨在增加对本实用新型的总体背景的理解，而不应当被视为承认或以任何形式暗示该信息构成已为本领域一般技术人员所公知的现有技术。
实用新型内容：
本实用新型的目的在于提供一种光伏焊带，从而克服上述现有技术中的缺陷。
为实现上述目的，本实用新型提供了
一种光伏焊带，包括：基材、涂覆层；所述基材表面镀有涂覆层；所述基材为截面为等腰三角形、等腰梯形、矩形中的一种的结构；所述基材的截面面积为0.01mm2～0.15mm2，高度为0.10mm～0.35mm。
优选地，技术方案中，基材的截面为等腰三角形时，等腰三角形的顶角为90°～140°。
优选地，技术方案中，基材的截面为等腰梯形时，等腰梯形的顶角为95°～168°。
优选地，技术方案中，基材选用纯铜、铜银合金、铜铝合金、铜镍合金、铜合金中的一种。
优选地，技术方案中，涂覆层的厚度为5μm-30μm。
优选地，技术方案中，涂覆层选用锡铅合金、纯锡、纯银、锡铋合金、锡银合金、锡镍合金中的一种。
优选地，技术方案中，涂覆层电镀或热浸镀在基材表面。
与现有技术相比，本实用新型具有如下有益效果：
基材采用异形结构可以满足客户对于光伏焊带不同形状的需求，使得本产品适用范围更广，提高了生产企业的效益。
附图说明：
图1为本实用新型一种光伏焊带的基材截面为等腰三角形的结构示意图；
图2为本实用新型一种光伏焊带的基材截面为等腰梯形的结构示意图；
图3为本实用新型一种光伏焊带的基材截面为矩形的结构示意图；
图4为本实用新型一种光伏焊带的基材截面为圆形的结构示意图；
主要附图标记说明：
1-基材、2-涂覆层。
具体实施方式：
下面对本实用新型的具体实施方式进行详细描述，但应当理解本实用新型的保护范围并不受具体实施方式的限制。
除非另有其它明确表示，否则在整个说明书和权利要求书中，术语“包括”或其变换如“包含”或“包括有”等等将被理解为包括所陈述的元件或组成部分，而并未排除其它元件或其它组成部分。
如图1所示，一种光伏焊带，包括：基材1、涂覆层2；所述基材1表面电镀或热浸镀有涂覆层2；所述基材1截面为等腰三角形，其顶角为90°～140°，所述等腰三角形面积为0.01mm2～0.15mm2，高度为0.10mm～0.35mm。涂覆层2的厚度为5μm-30μm。基材1选用铜银合金。涂覆层2选用锡铅合金。
如图2所示，一种光伏焊带，包括：基材1、涂覆层2；所述基材1表面电镀或热浸镀有涂覆层2；所述基材1截面为等腰梯形，其顶角为95°～168°，所述等腰梯形面积为0.01mm2～0.15mm2，高度为0.10mm～0.35mm。涂覆层2的厚度为5μm-30μm。基材1选用铜铝合金。涂覆层2选用锡铋合金。
如图3所示，一种光伏焊带，包括：基材1、涂覆层2；所述基材1表面电镀或热浸镀有涂覆层2；所述基材1截面为矩形，所述矩形面积为0.01mm2～0.15mm2，高度为0.10mm～0.35mm。涂覆层2的厚度为5μm-30μm。基材1选用铜镍合金。涂覆层2选用锡镍合金。
如图4所示，一种光伏焊带，包括：基材1、涂覆层2；所述基材1表面电镀或热浸镀有涂覆层2；所述基材1截面为圆形，所述圆形面积为0.01mm2～0.15mm2，高度为0.10mm～0.35mm。涂覆层2的厚度为5μm-30μm。基材1选用纯铜。涂覆层2选用纯锡。
前述对本实用新型的具体示例性实施方案的描述是为了说明和例证的目的。这些描述并非想将本实用新型限定为所公开的精确形式，并且很显然，根据上述教导，可以进行很多改变和变化。对示例性实施例进行选择和描述的目的在于解释本实用新型的特定原理及其实际应用，从而使得本领域的技术人员能够实现并利用本实用新型的各种不同的示例性实施方案以及各种不同的选择和改变。本实用新型的范围意在由权利要求书及其等同形式所限定。

Claims (7)

1.一种光伏焊带，包括：基材、涂覆层；所述基材表面镀有涂覆层；其特征在于：所述基材为截面为等腰三角形、等腰梯形、矩形中的一种的结构；所述基材的截面面积为0.01mm2～0.15mm2，高度为0.10mm～0.35mm。
2.根据权利要求1所述的光伏焊带，其特征在于：所述基材的截面为等腰三角形时，等腰三角形的顶角为90°～140°。
3.根据权利要求1所述的光伏焊带，其特征在于：所述基材的截面为等腰梯形时，等腰梯形的顶角为95°～168°。
4.根据权利要求1所述的光伏焊带，其特征在于：所述基材选用纯铜、铜银合金、铜铝合金、铜镍合金、铜合金中的一种。
5.根据权利要求1所述的光伏焊带，其特征在于：所述涂覆层的厚度为5μm-30μm。
6.根据权利要求1所述的光伏焊带，其特征在于：所述涂覆层选用锡铅合金、纯锡、纯银、锡铋合金、锡银合金、锡镍合金中的一种。
7.根据权利要求1所述的光伏焊带，其特征在于：所述涂覆层电镀或热浸镀在基材表面。
CN201520346176.2U 2015-05-25 2015-05-25 一种光伏焊带 Expired - Fee Related CN205428952U (zh)