CN204939286U - Minute surface chromatography colored glazed glass prepares structure - Google Patents
Minute surface chromatography colored glazed glass prepares structure Download PDFInfo
- Publication number
- CN204939286U CN204939286U CN201520553158.1U CN201520553158U CN204939286U CN 204939286 U CN204939286 U CN 204939286U CN 201520553158 U CN201520553158 U CN 201520553158U CN 204939286 U CN204939286 U CN 204939286U
- Authority
- CN
- China
- Prior art keywords
- glass
- screen
- minute surface
- chromatography
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to the technical field of colored glazed glass preparation method, disclose minute surface chromatography colored glazed glass and prepare structure, for silk-screen colored glaze face on the face of aluminizing of aluminized mirror surface glass and the aluminium coated dealuminzation that will do not covered by colored glaze face, comprise screen printer, aluminized mirror surface glass good for silk-screen carried out the dryer of drying and processing and be used for the dealumination agent of the aluminium coated dealuminzation do not covered by colored glaze face, screen printer has table top, and screen printer is provided with the half tone of silk-screen on the aluminium coated at aluminized mirror surface glass and the scraper for silk-screen.The minute surface chromatography colored glazed glass that the utility model provides prepares structure, minute surface chromatography colored glazed glass product can be prepared, one side can be prepared for high reflective mirror face effect pattern according to the pattern of web plate, one side is other color pattern chromatography products, chromatography is even, there will not be chromatography misplace or leak heterochromatic phenomenon; Utilize this structure to prepare colored glazed glass, expense is lower, and efficiency is also high.
Description
Technical field
The utility model relates to the technical field that colored glazed glass prepares structure, particularly relates to minute surface chromatography colored glazed glass and prepares structure.
Background technology
Colored glazed glass is by inorganic glaze (also known as ink), adopt certain technique bat printing to glass surface, the process of low-temperature glaze drying, high temperature glaze obtains a kind of decorative glasses product through high temperature sintering in glass surface, high temperature glaze colored glazed glass can use by monolithic, also the composite prod such as sandwiched product or double glazing product can be made, and low-temperature glaze colored glazed glass can not use by monolithic, the composite prod such as sandwiched product or double glazing product can only be made, because colored glazed glass has well ornamental, especially high reflective mirror surface cover colored glaze product, therefore, application can be more and more extensive.
In prior art, chromatography on the minute surface of glass, forms minute surface chromatography colored glazed glass, and like this, then can form one side is mirror effect, and another side is the pattern effect of other colors.At present, general adopt inkjet technology shaping minute surface chromatography colored glazed glass, although also can the uniform product of shaping chromatography, there is the problem that processing charges is too high and working (machining) efficiency is low.
Utility model content
The purpose of this utility model is to provide minute surface chromatography colored glazed glass to prepare structure, is intended to solve in prior art, adopts inkjet technology to prepare minute surface chromatography colored glazed glass, there is the problem that processing charges is high and working (machining) efficiency is low.
The utility model realizes like this, minute surface chromatography colored glazed glass prepares structure, for silk-screen colored glaze face on the face of aluminizing of aluminized mirror surface glass and by not by aluminium coated dealuminzation that described colored glaze face covers, comprise screen printer, aluminized mirror surface glass good for silk-screen carried out the dryer of drying and processing and be used for the dealumination agent of the aluminium coated dealuminzation do not covered by described colored glaze face, described screen printer has the table top for placing the aluminized mirror surface glass treating silk-screen colored glaze face, described screen printer be provided with silk-screen on the aluminium coated at described aluminized mirror surface glass half tone and for glaze silk-screen is being placed with the scraper of aluminizing on face of described half tone.
Further, described minute surface chromatography colored glazed glass is prepared structure and is also comprised stirrer for stirring glaze.
Further, the angular range of described scraper and aluminized mirror surface glass is between 70 ° to 80 °.
Further, the length at described scraper two ends exceeds between the pattern 50mm to 60mm on described half tone.
Further, the table top of described screen printer is provided with and prints point for locating rising of described aluminized mirror surface glass position.
Further, the bake out temperature of described dryer is between 150 °-180 °.
Further, the transmission speed of described aluminized mirror surface glass in described dryer is not more than 1.5cm/min.
Further, the delivery roll for transmitting aluminized mirror surface glass is provided with in described dryer.
Further, described minute surface chromatography colored glazed glass is prepared structure and is also comprised cleaning machine for cleaning the aluminized mirror surface glass after dealuminzation.
Compared with prior art, the minute surface chromatography colored glazed glass that the utility model provides prepares structure, minute surface chromatography colored glazed glass product can be prepared, this product can prepare one side for high reflective mirror face effect pattern according to the pattern of backboard, one side is other color pattern chromatography products, and chromatography is even, there will not be chromatography misplace or leak heterochromatic phenomenon, meet the pursuit that Designers is more and more higher to colored glaze product; Utilize this structure to prepare colored glazed glass, expense is lower, and efficiency is also high.
Accompanying drawing explanation
Fig. 1 is that the minute surface chromatography colored glazed glass that the utility model embodiment provides prepares the schematic flow sheet of structure in preparation process;
Fig. 2 is the simple and easy schematic diagram that minute surface chromatography colored glazed glass that the utility model embodiment provides prepares structure.
Embodiment
In order to make the purpose of this utility model, technical scheme and advantage clearly understand, below in conjunction with drawings and Examples, the utility model is further elaborated.Should be appreciated that specific embodiment described herein only in order to explain the utility model, and be not used in restriction the utility model.
Below in conjunction with specific embodiment, realization of the present utility model is described in detail.
With reference to shown in Fig. 1 and Fig. 2, it is the preferred embodiment that the utility model provides.
The preparation structure that the present embodiment provides, for the preparation of minute surface chromatography colored glazed glass, for silk-screen colored glaze face on the face of aluminizing of aluminized mirror surface glass and the aluminium coated dealuminzation that will do not covered by colored glaze face, it comprises screen printer 11, dryer 12 and dealumination agent, wherein, dryer 12 is for carrying out drying and processing by aluminized mirror surface glass good for silk-screen, and dealumination agent is used for the aluminium coated dealuminzation that will do not covered by colored glaze face; Screen printer 11 has the table top 111 for placing the aluminized mirror surface glass treating silk-screen colored glaze face, and screen printer 11 is provided with half tone on the aluminium coated for being laid on aluminized mirror surface glass and for glaze silk-screen is being placed with the scraper of aluminizing on face of half tone.
The above-mentioned minute surface chromatography colored glazed glass provided prepares structure, and its preparation manipulation step is as follows:
1), half tone, glaze, dealumination agent and aluminized mirror surface glass is prepared, wherein, aluminized mirror surface glass must be fresh aluminized products, namely the face of aluminizing of aluminized mirror surface glass can not be formed with back of the body paint, further, need to check whether the glass surface of aluminized mirror surface glass and face of aluminizing exist macroscopic irregularity;
2), by aluminized mirror surface glass be placed in screen printer 11, the layout that faces up of aluminizing of aluminized mirror surface glass, by setting according to position location of aluminized mirror surface glass, and upper blade and half tone, what half tone was placed in described aluminized mirror surface glass aluminizes on face;
3), by glaze be poured on uniformly on half tone, utilize scraper to aluminize on face by glaze silk-screen at aluminized mirror surface glass, the face of aluminizing is formed colored glaze face;
4), drying and processing is carried out by aluminized mirror surface glass good for silk-screen feeding dryer 12;
5), utilize dealumination agent to remove aluminium coated that the face of aluminizing does not cover the region of glaze;
6), by aluminized mirror surface glass good for dealuminzation first rinse with clear water, then put into cleaning machine cleaning.
The above-mentioned minute surface chromatography colored glazed glass provided prepares structure, minute surface chromatography colored glazed glass product can be prepared, this product can prepare one side for high reflective mirror face effect pattern according to the pattern of backboard, one side is other color pattern chromatography products, and chromatography is even, there will not be chromatography misplace or leak heterochromatic phenomenon, meet the pursuit that Designers is more and more higher to colored glaze product; Utilize this structure to prepare colored glazed glass, expense is lower, and efficiency is also high.
The minute surface chromatography colored glazed glass product of above-mentioned formation cannot use by monolithic, and the colored glaze face both formed cannot be outside exposed, and need to prepare composite prod and use, as being prepared into sandwiched product or hollow product, colored glaze face all will towards middle layer.
In the present embodiment, minute surface chromatography colored glazed glass is prepared structure and is comprised whipped-up structure, the step 1 above-mentioned) in, utilizing stirrer to stir glaze, when stirring, having prevented bubble from producing; For half tone, the pattern covers rate in half tone does not exceed 40%, and, before use half tone, need cleaning machine to clean half tone, after cleaning up, reexamine the quality of half tone.
In above-mentioned steps 2) in, when upper blade, the angle of scraper and glass is the scope of 70 ° to 80 °, further, the length at scraper two ends needs the pattern 50mm to 60mm exceeded on half tone, like this, after ensureing silk-screen, what glaze evenly can be formed in aluminized mirror surface glass aluminizes on face, and the pattern of formation is even, there will not be phenomenons such as leaking look.
Aluminized mirror surface glass is placed on the table top 111 of screen printer 11, keeps aluminizing the layout that faces up, and the table top 111 of screen printer 11 is provided with and prints point for locating rising of aluminized mirror surface glass position, according to playing the requirement of print point, the position of location aluminized mirror surface glass; When glaze is poured on after on half tone, glaze is formed in the front end of scraper, directly utilizes scraper silk-screen one cutter.
In step 3) in, after utilizing scraper silk-screen complete, check silk-screen quality, with or without defect such as leakage mirrored colour, scraper print etc.
In step 4) in, the aluminized mirror surface glass that silk-screen is good is sent in dryer 12, and bake out temperature controls 150 ° of-180 ° of scopes, and the transmission speed of aluminized mirror surface glass delivery roll 121 in dryer 12 is not more than 1.5cm/min.When the later aluminized mirror surface glass of oven dry is unloaded down, to be cooled to room temperature, then enter in subsequent processing.
In above-mentioned steps 5) in, the aluminized mirror surface glass of having dried is placed on table top, and, the colored glaze of aluminized mirror surface glass faces up layout, be formed in ventilation, dealumination agent be directly poured on the colored glaze face of aluminized mirror surface glass, and uniform application, after treating 2min-3min, directly rinse the face of aluminizing of aluminized mirror surface glass with water, check dealuminzation effect, wherein, the aluminium coated of colored glaze covering place on face of aluminizing can not come off, and the aluminium coated at the place of covering then comes off under the effect of dealumination agent.
When the aluminium coated face of aluminizing not covering colored glaze does not come off clean, then can repeat above-mentioned steps 5) and step 6) operation, until dealuminzation clean position.
Minute surface chromatography colored glazed glass is prepared structure and is also comprised cleaning machine for cleaning the aluminized mirror surface glass after dealuminzation.
The foregoing is only preferred embodiment of the present utility model; not in order to limit the utility model; all do within spirit of the present utility model and principle any amendment, equivalent to replace and improvement etc., all should be included within protection domain of the present utility model.
Claims (9)
1. minute surface chromatography colored glazed glass prepares structure, it is characterized in that, for silk-screen colored glaze face on the face of aluminizing of aluminized mirror surface glass and by not by aluminium coated dealuminzation that described colored glaze face covers, comprise screen printer, aluminized mirror surface glass good for silk-screen carried out the dryer of drying and processing and be used for the dealumination agent of the aluminium coated dealuminzation do not covered by described colored glaze face, described screen printer has the table top for placing the aluminized mirror surface glass treating silk-screen colored glaze face, described screen printer be provided with silk-screen on the aluminium coated at described aluminized mirror surface glass half tone and for glaze silk-screen is being placed with the scraper of aluminizing on face of described half tone.
2. minute surface chromatography colored glazed glass as claimed in claim 1 prepares structure, it is characterized in that, described minute surface chromatography colored glazed glass is prepared structure and also comprised stirrer for stirring glaze.
3. minute surface chromatography colored glazed glass as claimed in claim 1 prepares structure, and it is characterized in that, the angular range of described scraper and aluminized mirror surface glass is between 70 ° to 80 °.
4. minute surface chromatography colored glazed glass as claimed in claim 1 prepares structure, and it is characterized in that, the length at described scraper two ends exceeds between the pattern 50mm to 60mm on described half tone.
5. the minute surface chromatography colored glazed glass as described in any one of Claims 1-4 prepares structure, it is characterized in that, the table top of described screen printer is provided with and prints point for locating rising of described aluminized mirror surface glass position.
6. the minute surface chromatography colored glazed glass as described in any one of Claims 1-4 prepares structure, it is characterized in that, the bake out temperature of described dryer is between 150 °-180 °.
7. the minute surface chromatography colored glazed glass as described in any one of Claims 1-4 prepares structure, it is characterized in that, the transmission speed of described aluminized mirror surface glass in described dryer is not more than 1.5cm/min.
8. minute surface chromatography colored glazed glass as claimed in claim 7 prepares structure, it is characterized in that, being provided with the delivery roll for transmitting aluminized mirror surface glass in described dryer.
9. the minute surface chromatography colored glazed glass as described in any one of Claims 1-4 prepares structure, it is characterized in that, described minute surface chromatography colored glazed glass is prepared structure and also comprised cleaning machine for cleaning the aluminized mirror surface glass after dealuminzation.