CN204029562U - The silicon steel sheet that low iron loss, low noise, high magnetic flux, closed assembly are fast - Google Patents

The silicon steel sheet that low iron loss, low noise, high magnetic flux, closed assembly are fast Download PDF

Info

Publication number
CN204029562U
CN204029562U CN201420504182.1U CN201420504182U CN204029562U CN 204029562 U CN204029562 U CN 204029562U CN 201420504182 U CN201420504182 U CN 201420504182U CN 204029562 U CN204029562 U CN 204029562U
Authority
CN
China
Prior art keywords
steel sheet
silicon steel
transformer
magnetic flux
flat hole
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201420504182.1U
Other languages
Chinese (zh)
Inventor
党小丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANYANG LIJU SOFT-MAGNETIC MATERIAL SCIENCE & TECHNOLOGY Co Ltd
Original Assignee
NANYANG LIJU SOFT-MAGNETIC MATERIAL SCIENCE & TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANYANG LIJU SOFT-MAGNETIC MATERIAL SCIENCE & TECHNOLOGY Co Ltd filed Critical NANYANG LIJU SOFT-MAGNETIC MATERIAL SCIENCE & TECHNOLOGY Co Ltd
Priority to CN201420504182.1U priority Critical patent/CN204029562U/en
Application granted granted Critical
Publication of CN204029562U publication Critical patent/CN204029562U/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The utility model discloses a kind of low iron loss, low noise, high magnetic flux, the silicon steel sheet that closed assembly is fast, comprise silicon steel sheet, described silicon steel sheet is provided with at least 1 flat hole, described silicon steel sheet side is provided with groove, this groove is square structure, the corresponding source of described silicon steel sheet groove opposite side arranges the projection mated with recess, silicon steel sheet formula of the present utility model and manufacture method play synergy, the eddy current that transformer work is produced is minimum, heat dissipation capacity is 0.2 of traditional transformer heat dissipation capacity, the transformer of equal model, the appendiron core transformer load capacity of foregoing invention is used greatly to improve, load capacity is 1.6 times of traditional transformer, and transformer is stable, the transformer of equal model carries out paired observation December, transformer zero failure of the present utility model, and the number of stoppages of traditional transformer is 7 times.

Description

The silicon steel sheet that low iron loss, low noise, high magnetic flux, closed assembly are fast
Technical field
The utility model belongs to power industry power transmission and distribution transformer core silicon-steel technical field, the silicon steel sheet that particularly a kind of low iron loss, low noise, high magnetic flux, closed assembly are fast.
Background technology
Transformer core is formed by several silicon steel sheet juxtapositions, and several silicon steel sheets are manually fixed together by steel plate and bolt by assembler, and closed assembly speed is slow, and time-consuming efficiency of taking a lot of work is low.In order to improve packaging efficiency, utility model people arranges at least two through holes on silicon steel sheet, and through hole plays guiding and fixing effect.Five-grade laminated transformer core disclosed in CN201120314442.5, be made up of stacked the amassing of at least one stack, stack layer is made up of stacked the amassing of some iron cores, adjacent stack layer adopts the stack that oppositely misplaces, described iron core layer includes upper and lower yoke sheet and core column sheet, described core column sheet two ends are connected with upper and lower yoke sheet respectively, junction forms seam, described stack layer includes five layers of iron core layer, the transversion malposition stepping in the same direction of each iron core layer, and adjacent iron cores layer transversion malposition stepping at least 3mm.And for example disclosed in CN201020160123.9, it includes iron core, iron core connects to form by after multilayer electrical sheet stack, electrical sheet two ends after stack are provided with seam region, electrical sheet in seam region adopts 45 ° of complete oblique seven stepping step arrangements in length and breadth, described seven step step arrangements are in length and breadth one group by every seven electrical sheets, a slice one is folded, seven steppings in length and breadth.After iron core of the present utility model adopts 45 ° of complete oblique seven stepping step-lap laminated modes in length and breadth, reduce air gap adjacent electrical sheet magnetic close, reduce the number of times that the magnetic line of force crosses more air gap, compared with tradition laterally three stepping iron core dry-type transformers, no-load loss on average reduces about 10%, noise on average reduces by 2 ~ 3dB, improve the magnetic property of conventional seams iron core at seam crossing, alleviate noise circumstance pollute and increase stock utilization, reduce the magnetic saturation of staggered place, thus decrease no-load loss and the noise of transformer, play energy savings, improve power supply quality.1) during the equal Shortcomings of technical characteristic disclosed in above-mentioned two patents, although silicon steel sheet is arranged at least two through holes to some extent solve the slow-footed problem of closed assembly, large to the flux effects of iron core, and then affect the performance of transformer.2) the silicon steel sheet thickness used in above-mentioned two patents is large, and is the conventional silicon steel sheet used, and iron loss amount is large, and noise is large.
CN201110305042.2 is disclosed a kind of from riveted type silicon sheet core transformer, comprise the iron core of riveting from riveting silicon steel sheet overlap by some, from riveting silicon steel sheet, there is first surface and second surface, its upper punch has riveted joint button, riveted joint button comprise to be formed on first surface and indent in the first riveted joint face of first surface, to be formed on second surface and evagination in the second riveted joint face of second surface, first riveted joint face surrounds indent in the groove of first surface, second riveted joint face surrounds evagination in the projection of second surface, the shape that face is riveted in first riveted joint face and second is identical, during riveted joint, first snaps in second in the groove of riveting silicon steel sheet from the projection of riveting silicon steel sheet, and first is adjacent to mutually from the first riveted joint face of riveting silicon steel sheet and second the second riveted joint face from riveting silicon steel sheet.Its weak point is: although technique scheme solves the problem that magnetic flux reduces, but in an assembling process, insulating barrier on silicon steel sheet is easily fallen by scratch, between silicon steel sheet, communicated magnetic circuit easily produces eddy current, eddy current can produce hundreds of degree Celsius makes transformer in operation blast, and causes immeasurable loss to electric power enterprise and the people.
Silicon steel sheet, it is a kind of silicon-iron soft magnetic alloy low containing carbon electrode, and general silicon content is 0.5 ~ 4.5%, adds resistivity and maximum permeability that silicon can improve iron, reduces coercive force, core loss (iron loss) and magnetic aging.Silicon steel mainly smelts (also can use electric arc furnace smelting) with oxygen coverter, coordinates molten steel vacuum treatment and AOD technology (see external refining, to adopt die casting or continuous metal cast process.According to different purposes, during smelting, change silicon (0.5 ~ 4.5%) and aluminium (0.2 ~ 0.5%) content are with the requirement of satisfied different magnetic.
Siliceous steel taken from by existing silicon steel sheet, and adopt hot rolling technology to produce, its shortcoming mainly existed is: 1, first heat, and consume mass energy, cost is high; 2, in course of hot rolling, first make steel billet, then beat after heating, the silicon steel sheet maximum specification of often opening of beating is 1.2 × 2.5m, and actual use specification is 1 × 2m, so slitter edge accounts for 1/4 ~ 1/3, wastes very large; 3, beat that to add man-hour noise very large, contaminated environment; 4, forge product became uneven even, properties of product are poor; 5, can not Continuous maching efficiency low.
Utility model content
In order to solve the problem, the utility model object is to develop the iron core silicon-steel sheet being applied to power transmission and distribution transformer in power industry, while realizing reducing silicon steel sheet thickness, improve magnetic strength B8, reduce iron loss and noise level, improve the closed assembly efficiency of assembler simultaneously.
For solving the problems of the technologies described above, the technical solution of the utility model is: the silicon steel sheet that a kind of low iron loss, low noise, high magnetic flux, closed assembly are fast, comprises silicon steel sheet, and described silicon steel sheet is provided with at least 1 flat hole.
Further, the quantity in preferred described flat hole is preferably 1.
Further, preferred described flat hole is slotted eye or diamond hole or square opening.
Further, preferred described flat hole is slotted eye.
Further, described silicon steel sheet also comprises positioning support, and described bearing comprises square base plate, described base plate is arranged four guide posts matched with flat hole size.
Further, described silicon steel sheet side is provided with groove, and this groove is square structure, and the corresponding source of described silicon steel sheet groove opposite side arranges the projection mated with recess.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 5 ~ 10mm.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 7 ~ 9mm.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 8mm.
Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.18mm.
Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.15mm.
Further, the thickness of preferred described silicon steel sheet is 0.14mm.
Further, the silicon steel sheet constituent that the utility model provides is: C: 0.001 ~ 0.002wt%, Si: 4.7 ~ 6.2wt%, Mn: 0.05 ~ 0.5wt%, Al: 0.1 ~ 0.25wt%, Sn: 0.01 ~ 1wt%, Mo: 0.05 ~ 0.1wt%, N: 0.003 ~ 0.02wt%, P: 0.002 ~ 0.06wt%, Sb:0.003 ~ 0.02wt%, surplus are by iron and other inevitable impurity.
More preferred, silicon steel sheet constituent is: C: 0.001 ~ 0.0015wt%, Si: 4.8 ~ 5.2wt%, Mn: 0.05 ~ 0.3wt%, Al: 0.1 ~ 0.25wt%, Sn: 0.01 ~ 1wt%, Mo: 0.05 ~ 0.08wt%, N: 0.009 ~ 0.02wt%, P: 0.002 ~ 0.06wt%, Sb:0.008 ~ 0.02wt%, surplus are by iron and other inevitable impurity.
The preparation method of above-mentioned silicon steel sheet, comprises following steps:
Through hot rolling: temperature is controlled at 1260 ~ 1300 DEG C, first roughing 2 passage after insulation 2 ~ 3h, then finish rolling 3 passage, final drafts is 91 ~ 94%, and sheet metal thickness≤0.25mm can form MnS inhibitor in the hot rolling;
Curling: to be heated to 610 ~ 650 DEG C;
Normalizing: anneal rapidly at 1120 ~ 1170 DEG C, the time is 6 ~ 8min, controls the precipitation of particle, size, distribution, and then controls the uniformity of tissue, and makes sheet material generation primary recrystallization;
Cold rolling: drafts is 91 ~ 94%, thickness≤0.18mm;
Decarburization-nitriding: pass into steam during decarburization, controls final C content at 30 ~ 200ppm, passes into NH3, carry out at 800 DEG C during nitriding, and coated glass film; High annealing, purification.
Preferably, described high annealing, under pure nitrogen gas protection, is raised to 400 ~ 500 DEG C of insulation 2 ~ 4h, removes steam and air-isolation.
Preferably, when passing into nitrogen: hydrogen is under 1: 1 ~ 3 conditions, heating rate is 31 DEG C/h ~ 43 DEG C/h under furnace temperature is risen to 1120 ~ 1200 DEG C after, environment is changed to pure hydrogen, insulation 8 ~ 10h.
Silicon steel sheet of the present utility model arranges flat hole, the sizes of flat hole and circular hole etc. simultaneously, flat hole almost can neglect to fall to disregarding on the impact of silicon steel sheet magnetic flux, and flat hole only needs one just can play guiding fixation, substantially reduce the impact of flat hole on silicon steel sheet magnetic flux, substantially can not affect the performance of transformer; More preferred flat hole adopts elliptical aperture, same to homalographic, and elliptical aperture is long, highly low, less to silicon steel sheet flux effects, can not affect the performance of transformer; Further, on the central horizontal line that preferred described flat hole is positioned at silicon steel sheet and distance silicon steel sheet central point 5 ~ 10mm, silicon steel sheet is by after positive and negative superposition successively, the silicon steel sheet Gong matched in the gap formed between silicon steel sheet inserts, silicon steel sheet can be made to be closely linked, fixation, noise is 50% of existing noise; Further, on the central horizontal line that preferred described flat hole is positioned at silicon steel sheet and distance silicon steel sheet central point 7 ~ 9mm, silicon steel sheet is by after positive and negative superposition successively, the silicon steel sheet Gong matched in the gap formed between silicon steel sheet inserts, silicon steel sheet can be made to be closely linked, fixing more firm, noise is 30% of existing noise; Further, on the central horizontal line that preferred described flat hole is positioned at silicon steel sheet and distance silicon steel sheet central point 8mm, silicon steel sheet is by after positive and negative superposition successively, the silicon steel sheet Gong matched in the gap formed between silicon steel sheet inserts, silicon steel sheet can be made to be closely linked, fixing more firm, noise is 10% of existing noise, reduce further the impact of transformer on resident living.Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.18mm, thin slice and lamination insulation process, greatly can reduce the eddy-current heating in magnetic field, reduce iron loss, but silicon steel sheet is too low is not easy to closed assembly, and closed assembly efficiency is extremely low, is not easy to large-scale production; Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.15mm, greatly can reduce the eddy-current heating in magnetic field, reduce iron loss, further, the thickness of preferred described silicon steel sheet is 0.14mm, make iron loss drop to best value and be convenient to closed assembly, both serve complementary synergy; The silicon steel sheet constituent more preferably adopting the utility model to provide is: C: 0.001 ~ 0.002wt%, Si: 4.7 ~ 6.2wt%, Mn: 0.05 ~ 0.5wt%, Al: 0.1 ~ 0.25wt%, Sn: 0.01 ~ 1wt%, Mo: 0.05 ~ 0.1wt%, N: 0.003 ~ 0.02wt%, P: 0.002 ~ 0.06wt%, Sb:0.003 ~ 0.02wt%, Ni:0.003 ~ 0.02wt%.Be added into antimony element first in composition, antimony element is surface active element, and face active component in silicon steel final annealing texture can be made to reduce for they and face component increases, thus reduce silicon steel iron loss, improve the magnetic permeability of silicon steel sheet, improve its magnetic flux density, improve high magentic induction oriented.Also have in composition simultaneously and time with the addition of nickel element, fining ferrite grains, promote hardening of steel performance; Hardening heat during heat treatment can be reduced, be therefore out of shape when heat treatment little; The plasticity and toughness of steel, particularly low-temperature flexibility can be improved; Can improve heat resistance and the corrosion resistance of steel, be one of main alloy element of refractory steel and austenitic stainless steel; What is more important can effectively raise the magnetic permeability of silicon steel sheet, improves the performance of transformer.More preferred, silicon steel sheet constituent is: C: 0.001 ~ 0.0015wt%, Si: 4.8 ~ 5.2wt%, Mn: 0.05 ~ 0.3wt%, Al: 0.1 ~ 0.25wt%, Sn: 0.01 ~ 1wt%, Mo: 0.05 ~ 0.08wt%, N: 0.009 ~ 0.02wt%, P: 0.002 ~ 0.06wt%, Sb:0.008 ~ 0.02wt%, surplus are by iron and other inevitable impurity.The magnetic permeability of silicon steel sheet reaches best, through utility model people investigation records data, it is 0.1 of traditional noise that transformer after assembling runs noise, what is more important silicon steel sheet formula of the present utility model and manufacture method play synergy, the eddy current that transformer work is produced is minimum, heat dissipation capacity is 0.2 of traditional transformer heat dissipation capacity, the transformer of equal model, the appendiron core transformer load capacity of above-mentioned utility model is used greatly to improve, load capacity is 1.6 times of traditional transformer, and transformer is stable, the transformer of equal model carries out paired observation December, transformer zero failure of the present utility model, and the number of stoppages of traditional transformer is 7 times.The silicon steel sheet preparation method of the application, through hot rolling: temperature is controlled at 1260 ~ 1300 DEG C, first roughing 2 passage after insulation 2 ~ 3h, finish rolling 3 passage again, final drafts is 91 ~ 94%, and sheet metal thickness≤0.25mm can form MnS inhibitor in the hot rolling; Curling: to be heated to 610 ~ 650 DEG C; Normalizing: anneal rapidly at 1120 ~ 1170 DEG C, the time is 6 ~ 8min, controls the precipitation of particle, size, distribution, and then controls the uniformity of tissue, and makes sheet material generation primary recrystallization; Cold rolling: drafts is 91 ~ 94%, thickness≤0.18mm; Decarburization-nitriding: pass into steam during decarburization, controls final C content at 30 ~ 200ppm, passes into NH3 during nitriding, carry out at 800 DEG C, and coated glass film; High annealing, purification.1. save material.The utility model adopts steel plate to form through modification of heating, consistent with the steel plate that reality uses, and does not produce slitter edge, saves material.2. manufacture simple.Traditional manufacture method needs first to make steel billet, then beats into steel plate after heating, and manufacturing process is complicated, and the utility model adopts existing steel plate modification, and operation is simple, and manufacturing speed is fast.3. thickness is even.Traditional manufacture method adopts the mode of beating to manufacture, and easily cause in uneven thickness, properties of product are poor, and the utility model adopts cold-reduced sheet modification to process, and thickness is even, and product qualified rate reaches more than 99%.
Accompanying drawing explanation
Below in conjunction with accompanying drawing, the utility model is described further:
Fig. 1 is silicon steel structure schematic diagram of the present utility model.
Embodiment
Embodiment 1: as shown in Figure 1, the silicon steel sheet that a kind of low iron loss, low noise, high magnetic flux, closed assembly are fast, comprises silicon steel sheet 1, and described silicon steel sheet is provided with at least 1 flat hole 3.
Further, the quantity in preferred described flat hole is preferably 1.
Further, preferred described flat hole is slotted eye or diamond hole or square opening.
Further, preferred described flat hole is slotted eye.
Further, described silicon steel sheet also comprises positioning support, and described bearing comprises square base plate, described base plate is arranged four guide posts matched with flat hole size.
Further, described silicon steel sheet side is provided with groove 2, and this groove 2 is square structure, the corresponding source of described silicon steel sheet groove opposite side is arranged and groove 2 the matches projection mated.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 5 ~ 10mm.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 7 ~ 9mm.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 8mm.
Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.18mm.
Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.15mm.
Further, the thickness of preferred described silicon steel sheet is 0.14mm.
Further, the silicon steel sheet constituent that the utility model provides is: C: 0.001wt%, Si: 4.7wt%, Mn: 0.05wt%, Al: 0.1wt%, Sn: 0.01wt%, Mo: 0.05wt%, N: 0.003wt%, P: 0.002wt%, Sb:0.003wt%, surplus is by iron and other inevitable impurity.
The preparation method of above-mentioned silicon steel sheet, comprises following steps:
Through hot rolling: temperature is controlled at 1260 DEG C, first roughing 2 passage after insulation 2h, then finish rolling 3 passage, final drafts is 91%, and sheet metal thickness≤0.25mm can form MnS inhibitor in the hot rolling;
Curling: to be heated to 610 DEG C;
Normalizing: anneal rapidly at 1120 DEG C, the time is 6min, controls the precipitation of particle, size, distribution, and then controls the uniformity of tissue, and makes sheet material generation primary recrystallization;
Cold rolling: drafts is 91%, thickness≤0.18mm;
Decarburization-nitriding: pass into steam during decarburization, controls final C content at 30ppm, passes into NH3 during nitriding, carry out at 850 DEG C, and coated glass film; High annealing, purification.
Preferably, described high annealing, under pure nitrogen gas protection, is raised to 400 DEG C of insulation 2h, removes steam and air-isolation.
Preferably, when passing into nitrogen: hydrogen is under 1: 1 condition, heating rate is that after furnace temperature being risen to 1120 DEG C under 31 DEG C/h, environment is changed to pure hydrogen, insulation 8h.
Embodiment 2: as shown in Figure 1, the silicon steel sheet that a kind of low iron loss, low noise, high magnetic flux, closed assembly are fast, comprises silicon steel sheet, and described silicon steel sheet is provided with at least 1 flat hole.
Further, the quantity in preferred described flat hole is preferably 1.
Further, preferred described flat hole is slotted eye or diamond hole or square opening.
Further, preferred described flat hole is slotted eye.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 5 ~ 10mm.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 7 ~ 9mm.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 8mm.
Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.18mm.
Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.15mm.
Further, the thickness of preferred described silicon steel sheet is 0.14mm.
Further, the silicon steel sheet constituent that the utility model provides is: C: 0.002wt%, Si: 6.2wt%, Mn: 0.5wt%, Al: 0.25wt%, Sn: 1wt%, Mo: 0.1wt%, N:0.02wt%, P: 0.06wt%, Sb:0.02wt%, surplus is by iron and other inevitable impurity.
The preparation method of above-mentioned silicon steel sheet, comprises following steps:
Through hot rolling: temperature is controlled at 1300 DEG C, first roughing 2 passage after insulation 3h, then finish rolling 3 passage, final drafts is 94%, and sheet metal thickness≤0.25mm can form MnS inhibitor in the hot rolling;
Curling: to be heated to 650 DEG C;
Normalizing: anneal rapidly at 1170 DEG C, the time is 8min, controls the precipitation of particle, size, distribution, and then controls the uniformity of tissue, and makes sheet material generation primary recrystallization;
Cold rolling: drafts is 94%, thickness≤0.18mm;
Decarburization-nitriding: pass into steam during decarburization, controls final C content at 200ppm, passes into NH3 during nitriding, carry out at 830 DEG C, and coated glass film; High annealing, purification.
Preferably, high annealing, under pure nitrogen gas protection, is raised to 500 DEG C of insulation 2 ~ 4h, removes steam and air-isolation.
Preferably, when passing into nitrogen: hydrogen is under 1: 3 condition, heating rate is that after furnace temperature being risen to 1200 DEG C under 43 DEG C/h, environment is changed to pure hydrogen, insulation 10h.
Embodiment 3: as shown in Figure 1, the silicon steel sheet that a kind of low iron loss, low noise, high magnetic flux, closed assembly are fast, comprises silicon steel sheet, and described silicon steel sheet is provided with at least 1 flat hole.
Further, the quantity in preferred described flat hole is preferably 1.
Further, preferred described flat hole is slotted eye or diamond hole or square opening.
Further, preferred described flat hole is slotted eye.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 5 ~ 10mm.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 7 ~ 9mm.
Further, preferred described flat hole be positioned at silicon steel sheet central horizontal line on and distance silicon steel sheet central point 8mm.
Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.18mm.
Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.15mm.
Further, the thickness of preferred described silicon steel sheet is 0.14mm.
Further, the silicon steel sheet constituent that the utility model provides is: C: 0.0015wt%, Si: 5.2wt%, Mn: 0.3wt%, Al: 0.18wt%, Sn: 0.05wt%, Mo: 0.075wt%, N: 0.01wt%, P: 0.03wt%, Sb:0.01wt%, surplus is by iron and other inevitable impurity.
The preparation method of above-mentioned silicon steel sheet, comprises following steps:
Through hot rolling: temperature is controlled at 1280 DEG C, first roughing 2 passage after insulation 2.5h, then finish rolling 3 passage, final drafts is 91 ~ 94%, and sheet metal thickness≤0.25mm can form MnS inhibitor in the hot rolling;
Curling: to be heated to 630 DEG C;
Normalizing: anneal rapidly at 1150 DEG C, the time is 7min, controls the precipitation of particle, size, distribution, and then controls the uniformity of tissue, and makes sheet material generation primary recrystallization;
Cold rolling: drafts is 93%, thickness≤0.18mm;
Decarburization-nitriding: pass into steam during decarburization, controls final C content at 110ppm, passes into NH3, carry out at 820 DEG C during nitriding, and coated glass film; High annealing, purification.
Preferably, described high annealing, under pure nitrogen gas protection, is raised to 450 DEG C of insulation 2 ~ 4h, removes steam and air-isolation.
Preferably, when passing into nitrogen: hydrogen is under 1: 1.8 condition, heating rate is that after furnace temperature being risen to 1160 DEG C under 35 DEG C/h, environment is changed to pure hydrogen, insulation 9h.
Silicon steel sheet of the present utility model arranges flat hole, the sizes of flat hole and circular hole etc. simultaneously, flat hole almost can neglect to fall to disregarding on the impact of silicon steel sheet magnetic flux, and flat hole only needs one just can play guiding fixation, substantially reduce the impact of flat hole on silicon steel sheet magnetic flux, substantially can not affect the performance of transformer; More preferred flat hole adopts elliptical aperture, same to homalographic, and elliptical aperture is long, highly low, less to silicon steel sheet flux effects, can not affect the performance of transformer; Described silicon steel sheet also comprises positioning support, described bearing comprises square base plate, described base plate is arranged four guide posts matched with flat hole size, the size of guide post is less than flat hole, silicon steel sheet suit can the rotation of smaller angle need operating personnel manually to carry out tunes together on the guide bar, guide post easily weares and teares in use for some time on the other hand, silicon steel sheet suit can the rotation of slightly wide-angle need operating personnel manually to carry out tunes together on the guide bar, waste time and energy and easily hurt arm, closed assembly efficiency is low; This groove is square structure, plays guide effect, prevents silicon steel sheet from superposing irregular.Further, described silicon steel sheet side is provided with groove, the corresponding source of this silicon steel sheet groove opposite side arranges the projection mated with recess, snapped together very soon by groove and projection between silicon steel sheet, guide post plays guide effect on the other hand, can carry out closed assembly fast, both combine, and closed assembly efficiency improves greatly.Further, on the central horizontal line that preferred described flat hole is positioned at silicon steel sheet and distance silicon steel sheet central point 5 ~ 10mm, silicon steel sheet is by after positive and negative superposition successively, the silicon steel sheet Gong matched in the gap formed between silicon steel sheet inserts, silicon steel sheet can be made to be closely linked, fixation, noise is 50% of existing noise; Further, on the central horizontal line that preferred described flat hole is positioned at silicon steel sheet and distance silicon steel sheet central point 7 ~ 9mm, silicon steel sheet is by after positive and negative superposition successively, the silicon steel sheet Gong matched in the gap formed between silicon steel sheet inserts, silicon steel sheet can be made to be closely linked, fixing more firm, noise is 30% of existing noise; Further, on the central horizontal line that preferred described flat hole is positioned at silicon steel sheet and distance silicon steel sheet central point 8mm, silicon steel sheet is by after positive and negative superposition successively, the silicon steel sheet Gong matched in the gap formed between silicon steel sheet inserts, silicon steel sheet can be made to be closely linked, fixing more firm, noise is 10% of existing noise, reduce further the impact of transformer on resident living.Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.18mm, thin slice and lamination insulation process, greatly can reduce the eddy-current heating in magnetic field, reduce iron loss, but silicon steel sheet is too low is not easy to closed assembly, and closed assembly efficiency is extremely low, is not easy to large-scale production; Further, the thickness of preferred described silicon steel sheet is 0.12 ~ 0.15mm, greatly can reduce the eddy-current heating in magnetic field, reduce iron loss, further, the thickness of preferred described silicon steel sheet is 0.14mm, make iron loss drop to best value and be convenient to closed assembly, both serve complementary synergy; The silicon steel sheet constituent more preferably adopting the utility model to provide is: C: 0.001 ~ 0.002wt%, Si: 4.7 ~ 6.2wt%, Mn: 0.05 ~ 0.5wt%, Al: 0.1 ~ 0.25wt%, Sn: 0.01 ~ 1wt%, Mo: 0.05 ~ 0.1wt%, N: 0.003 ~ 0.02wt%, P: 0.002 ~ 0.06wt%, Sb:0.003 ~ 0.02wt%, Ni:0.003 ~ 0.02wt%.Be added into antimony element first in composition, antimony element is surface active element, and face active component in silicon steel final annealing texture can be made to reduce for they and face component increases, thus reduce silicon steel iron loss, improve the magnetic permeability of silicon steel sheet, improve its magnetic flux density, improve high magentic induction oriented.Also have in composition simultaneously and time with the addition of nickel element, fining ferrite grains, promote hardening of steel performance; Hardening heat during heat treatment can be reduced, be therefore out of shape when heat treatment little; The plasticity and toughness of steel, particularly low-temperature flexibility can be improved; Can improve heat resistance and the corrosion resistance of steel, be one of main alloy element of refractory steel and austenitic stainless steel; What is more important can effectively raise the magnetic permeability of silicon steel sheet, improves the performance of transformer.More preferred, silicon steel sheet constituent is: C: 0.001 ~ 0.0015wt%, Si: 4.8 ~ 5.2wt%, Mn: 0.05 ~ 0.3wt%, Al: 0.1 ~ 0.25wt%, Sn: 0.01 ~ 1wt%, Mo: 0.05 ~ 0.08wt%, N: 0.009 ~ 0.02wt%, P: 0.002 ~ 0.06wt%, Sb:0.008 ~ 0.02wt%, surplus is by iron and other inevitable impurity, the magnetic permeability of silicon steel sheet reaches best, through the transformer that utility model people investigation records data use embodiment 3 to manufacture, it is 0.1 of traditional noise that transformer after assembling runs noise, what is more important silicon steel sheet formula of the present utility model and manufacture method play synergy, the eddy current that transformer work is produced is minimum, heat dissipation capacity is 0.2 of traditional transformer heat dissipation capacity, the transformer of equal model, the appendiron core transformer load capacity of above-mentioned utility model is used greatly to improve, load capacity is 1.6 times of traditional transformer, and transformer is stable, the transformer of equal model carries out paired observation December, transformer zero failure of the present utility model, and the number of stoppages of traditional transformer is 7 times.The silicon steel sheet preparation method of the application, through hot rolling: temperature is controlled at 1260 ~ 1300 DEG C, first roughing 2 passage after insulation 2 ~ 3h, finish rolling 3 passage again, final drafts is 91 ~ 94%, and sheet metal thickness≤0.25mm can form MnS inhibitor in the hot rolling; Curling: to be heated to 610 ~ 650 DEG C; Normalizing: anneal rapidly at 1120 ~ 1170 DEG C, the time is 6 ~ 8min, controls the precipitation of particle, size, distribution, and then controls the uniformity of tissue, and makes sheet material generation primary recrystallization; Cold rolling: drafts is 91 ~ 94%, thickness≤0.18mm; Decarburization-nitriding: pass into steam during decarburization, controls final C content at 30 ~ 200ppm, passes into NH3 during nitriding, carry out at 800 DEG C, and coated glass film; High annealing, purification.1. save material.The utility model adopts steel plate to form through modification of heating, consistent with the steel plate that reality uses, and does not produce slitter edge, saves material.2. manufacture simple.Traditional manufacture method needs first to make steel billet, then beats into steel plate after heating, and manufacturing process is complicated, and the utility model adopts existing steel plate modification, and operation is simple, and manufacturing speed is fast.3. thickness is even.Traditional manufacture method adopts the mode of beating to manufacture, and easily cause in uneven thickness, properties of product are poor, and the utility model adopts cold-reduced sheet modification to process, and thickness is even, and product qualified rate reaches more than 99%.

Claims (10)

1. the silicon steel sheet that low iron loss, low noise, high magnetic flux, closed assembly are fast, comprises silicon steel sheet, it is characterized in that: described silicon steel sheet is provided with at least 1 flat hole.
2. the silicon steel sheet that low iron loss as claimed in claim 1, low noise, high magnetic flux, closed assembly are fast, is characterized in that: the quantity in described flat hole is 1, and described flat hole is slotted eye or diamond hole or square opening.
3. the silicon steel sheet that low iron loss as claimed in claim 2, low noise, high magnetic flux, closed assembly are fast, is characterized in that: described flat hole is slotted eye.
4. the silicon steel sheet that low iron loss as claimed in claim 3, low noise, high magnetic flux, closed assembly are fast, is characterized in that: on the central horizontal line that described flat hole is positioned at silicon steel sheet and distance silicon steel sheet central point 5 ~ 10mm.
5. the silicon steel sheet that low iron loss as claimed in claim 4, low noise, high magnetic flux, closed assembly are fast, is characterized in that: on the central horizontal line that flat hole described in described flat hole is positioned at silicon steel sheet and distance silicon steel sheet central point 7 ~ 9mm.
6. the silicon steel sheet that low iron loss as claimed in claim 5, low noise, high magnetic flux, closed assembly are fast, is characterized in that: on the central horizontal line that described flat hole is positioned at silicon steel sheet and distance silicon steel sheet central point 8mm.
7. the silicon steel sheet that low iron loss as claimed in claim 1, low noise, high magnetic flux, closed assembly are fast, is characterized in that: the thickness of described silicon steel sheet is 0.12 ~ 0.18mm.
8. the silicon steel sheet that low iron loss as claimed in claim 7, low noise, high magnetic flux, closed assembly are fast, is characterized in that: the thickness of described silicon steel sheet is 0.12 ~ 0.15mm.
9. the silicon steel sheet that low iron loss as claimed in claim 8, low noise, high magnetic flux, closed assembly are fast, is characterized in that: the thickness of described silicon steel sheet is 0.14mm.
10. the silicon steel sheet that low iron loss as claimed in claim 9, low noise, high magnetic flux, closed assembly are fast, it is characterized in that: described silicon steel sheet also comprises positioning support, described bearing comprises square base plate, described base plate is arranged four guide posts matched with flat hole size.
CN201420504182.1U 2014-09-03 2014-09-03 The silicon steel sheet that low iron loss, low noise, high magnetic flux, closed assembly are fast Expired - Fee Related CN204029562U (en)