CN203267361U - 复合纤维针刺预制体 - Google Patents

复合纤维针刺预制体 Download PDF

Info

Publication number
CN203267361U
CN203267361U CN 201320259612 CN201320259612U CN203267361U CN 203267361 U CN203267361 U CN 203267361U CN 201320259612 CN201320259612 CN 201320259612 CN 201320259612 U CN201320259612 U CN 201320259612U CN 203267361 U CN203267361 U CN 203267361U
Authority
CN
China
Prior art keywords
carbon fiber
composite
coating
layer
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN 201320259612
Other languages
English (en)
Inventor
缪黎丽
缪黎燕
邵敏强
裴强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YIXING CITY FEIZHOU HI-TECH MATERIALS Co Ltd
Original Assignee
YIXING CITY FEIZHOU HI-TECH MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YIXING CITY FEIZHOU HI-TECH MATERIALS Co Ltd filed Critical YIXING CITY FEIZHOU HI-TECH MATERIALS Co Ltd
Priority to CN 201320259612 priority Critical patent/CN203267361U/zh
Application granted granted Critical
Publication of CN203267361U publication Critical patent/CN203267361U/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

本实用新型公开了一种复合纤维技术领域，特别是涉及一种复合纤维针刺预制体；本实用新型的复合纤维针刺预制体，结构强度较高，韧性较高；碳纤维层包括碳纤维长丝，碳纤维网胎包括碳纤维短丝，碳纤维长丝和碳纤维短丝的外侧面依次设置有热解碳涂层、碳化硅涂层和碳化钽涂层，碳纤维网胎的碳纤维短丝之间还设置有糠酮树脂基体层。

Description

复合纤维针刺预制体
技术领域
本实用新型涉及复合纤维技术领域，特别是涉及一种复合纤维针刺预制体。
背景技术
众所周知，复合纤维针刺预制体，通常是由碳纤维层与碳纤维网胎交替叠层针刺而成的复合纤维预制体，因其具有耐高温、耐摩擦和质地轻的特性，广泛应用于航空航天、能源、交通和轨道领域；现有的复合纤维针刺预制体，通常包括两层碳纤维层和一层碳纤维网胎，碳纤维网胎位于碳纤维层之间，这样的复合纤维针刺预制体，由于碳纤维的特性，存在结构强度较低，韧性较差的问题。
实用新型内容
为解决上述技术问题，本实用新型提供一种结构强度较高，韧性较高的复合纤维针刺预制体。
本实用新型的复合纤维针刺预制体，包括碳纤维层和碳纤维网胎，所述碳纤维层为两层，所述碳纤维网胎位于所述碳纤维层之间，所述碳纤维层包括碳纤维长丝，所述碳纤维网胎包括碳纤维短丝，所述碳纤维长丝和碳纤维短丝的外侧面依次设置有热解碳涂层、碳化硅涂层和碳化钽涂层，所述碳纤维网胎的碳纤维短丝之间还设置有糠酮树脂基体层。
进一步的，所述热解碳涂层的厚度大于0.5μm并小于1μm，所述碳化硅涂层的厚度大于1μm并小于2μm，所述碳化钽涂层的厚度大于1.5μm并小于3μm。
进一步的，所述碳化钽涂层的外侧还设置有热解碳基体层。
与现有技术相比本实用新型的有益效果为：碳纤维长丝和碳纤维短丝的外侧面依次设置有热解碳涂层(PyC)、碳化硅涂层(SiC)和碳化钽涂层(TaC)，碳纤维网胎的碳纤维短丝之间还设置有糠酮树脂基体层；碳纤维表面均匀致密的PyC、SiC和TaC多层结构，可有效提高碳纤维的强度和韧性；PyC涂层可以有效防止SiC涂层制备过程中对碳纤维的损伤，改变碳纤维的表面状态，减少或修复纤维表面的缺陷及编制损伤，有效提高碳纤维单丝的强度；SiC和TaC陶瓷具有较高的强度，即使TaC涂层断裂，SiC涂层仍然能够有效承载，这样碳纤维原丝的抗弯强度得到有效提高；而糠酮树脂基体层可以有效提高预制体的抗拉伸性和弯曲性能，层间抗剪切性能也较好。
附图说明
图1是本实用新型的结构示意图。
图2是本实用新型中碳纤维短丝剖向的结构示意图。
具体实施方式
下面结合附图和实施例，对本实用新型的具体实施方式作进一步详细描述。以下实施例用于说明本实用新型，但不用来限制本实用新型的范围。
如图1和图2所示，本实用新型的复合纤维针刺预制体，包括碳纤维层1和碳纤维网胎2，碳纤维层1为两层，碳纤维网胎2位于碳纤维层之间，碳纤维层1包括碳纤维长丝，碳纤维网胎2包括碳纤维短丝8，碳纤维长丝和碳纤维短丝8的外侧面依次设置有热解碳涂层7、碳化硅涂层6和碳化钽涂层3，碳纤维网胎的碳纤维短丝之间还设置有糠酮树脂基体层5；热解碳涂层、碳化硅涂层和碳化钽涂层的简称分别为PyC、SiC和TaC，这样，碳纤维表面均匀致密的PyC、SiC和TaC多层结构，可有效提高碳纤维的强度和韧性；PyC涂层可以有效防止SiC涂层制备过程中对碳纤维的损伤，改变碳纤维的表面状态，减少或修复纤维表面的缺陷及编制损伤，有效提高碳纤维单丝的强度；SiC和TaC陶瓷具有较高的强度，即使TaC涂层断裂，SiC涂层仍然能够有效承载，这样碳纤维原丝的抗弯强度得到有效提高；而糠酮树脂基体层可以有效提高预制体的抗拉伸性和弯曲性能，层间抗剪切性能也较好；PyC、SiC和TaC涂层可采用化学气相渗透法在碳纤维丝表面依次制备。
热解碳涂层的厚度大于0.5μm并小于1μm，碳化硅涂层的厚度大于1μm并小于2μm，碳化钽涂层的厚度大于1.5μm并小于3μm。
碳化钽涂层的外侧还设置有热解碳基体层4；这样可以有效地保护SiC和TaC涂层。
以上所述仅是本实用新型的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本实用新型技术原理的前提下，还可以做出若干改进和变型，这些改进和变型也应视为本实用新型的保护范围。

Claims (3)

1.一种复合纤维针刺预制体，包括碳纤维层和碳纤维网胎，所述碳纤维层为两层，所述碳纤维网胎位于所述碳纤维层之间，其特征在于，所述碳纤维层包括碳纤维长丝，所述碳纤维网胎包括碳纤维短丝，所述碳纤维长丝和碳纤维短丝的外侧面依次设置有热解碳涂层、碳化硅涂层和碳化钽涂层，所述碳纤维网胎的碳纤维短丝之间还设置有糠酮树脂基体层。
2.如权利要求1所述的复合纤维针刺预制体，其特征在于，所述热解碳涂层的厚度大于0.5μm并小于1μm，所述碳化硅涂层的厚度大于1μm并小于2μm，所述碳化钽涂层的厚度大于1.5μm并小于3μm。
3.如权利要求1所述的复合纤维针刺预制体，其特征在于，所述碳化钽涂层的外侧还设置有热解碳基体层。
CN 201320259612 2013-05-14 2013-05-14 复合纤维针刺预制体 Expired - Lifetime CN203267361U (zh)