CN202540431U - Bamboo mat veneered environment-friendly tobacco stem particle board for building decoration - Google Patents
Bamboo mat veneered environment-friendly tobacco stem particle board for building decoration Download PDFInfo
- Publication number
- CN202540431U CN202540431U CN2012201792767U CN201220179276U CN202540431U CN 202540431 U CN202540431 U CN 202540431U CN 2012201792767 U CN2012201792767 U CN 2012201792767U CN 201220179276 U CN201220179276 U CN 201220179276U CN 202540431 U CN202540431 U CN 202540431U
- Authority
- CN
- China
- Prior art keywords
- bamboo mat
- tobacco stem
- layer
- cigarette stalk
- bamboo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a bamboo mat veneered environment-friendly tobacco stem particle board for a building decoration, comprising a tobacco stem particle layer. The tobacco stem particle layer is a slab consisting of tobacco stem particles; an upper surface and a lower surface of the tobacco stem particle layer are respectively provided with one bamboo mat layer dipped with melamine resin glue; the bamboo mat layer is formed by weaving bamboo skins. Through the bamboo mat veneer dipped with the melamine resin glue, the physical intensity of tobacco stem glue-free particle board is obviously improved; the veering layer can decrease the contact area between the tobacco stem particle layer and air on a certain degree and reduce the absorbent thickness expansion rate therefore. Besides, the bamboo mat veneer also plays good decorating performance. Therefore, the additional value of the board is largely improved.
Description
Technical field
The utility model relates to a kind of novel artificial plate, is specially a kind of architectural decoration bamboo mat veneer environmental protection cigarette stalk chipboard.
Background technology
At present, China's cigarette stalk aboundresources.Cigarette stalk chemistry main component is similar with bamboo wood with timber, is cellulose, hemicellulose and lignin, the no glue flakeboard raw materials for production of suitable work.The no glue flakeboard of producing with cigarette stalk particle produce with use in the release of five formaldehyde, have the feature of environmental protection significantly.But the cigarette stalk does not have that glue flakeboard incrustation performance is poor, and intensity is low, and the absorber thickness expansion rate is bigger, and serviceability and applicable situation are restricted.Therefore, carry out have decoration functions, that the cigarette stalk of high strength, low thickness swelling rate does not have the glue flakeboard is very necessary.
The utility model content
The technical problem that the utility model solved is to provide a kind of architectural decoration bamboo mat veneer environmental protection cigarette stalk chipboard, to solve the shortcoming in the above-mentioned background technology.
The technical problem that the utility model solved adopts following technical scheme to realize:
A kind of architectural decoration bamboo mat veneer environmental protection cigarette stalk chipboard; Comprise cigarette stalk particle layer; The slab that said cigarette stalk particle layer is made up of cigarette stalk particle; The upper surface and the lower surface of said cigarette stalk particle layer are provided with the bamboo mat layer that one deck is impregnated with melamine resin adehsive respectively, and said bamboo mat layer is worked out by thin bamboo strips used for weaving.
Said thin bamboo strips used for weaving thickness is 0.6～1.0mm.
Said cigarette stalk particle is of a size of long 3 ~ 13mm, wide 1 ~ 6mm, thick 0.5 ~ 1.6mm.
Beneficial effect:
Significantly having improved the cigarette stalk behind the bamboo mat veneer of the utility model through impregnated melamine does not have glue flakeboard mechanical strength, and overlay coating can reduce the contact area of cigarette stalk particle layer and air to a certain extent, reduces its thickness swelling rate.In addition, the bamboo mat veneer has also played good decorate properties.Therefore, improved the added value of sheet material greatly.
Description of drawings
Fig. 1 is the utility model structural representation.
The specific embodiment
For technological means, creation characteristic that the utility model is realized, reach purpose and be easy to understand understanding with effect, below in conjunction with concrete diagram, further set forth the utility model.
Referring to Fig. 1; A kind of architectural decoration bamboo mat veneer environmental protection cigarette stalk chipboard; Comprise cigarette stalk particle layer 2; The slab that said cigarette stalk particle layer 2 is made up of cigarette stalk particle, the upper surface of said cigarette stalk particle layer 2 and lower surface are provided with the bamboo mat layer 1,3 that one deck is impregnated with melamine resin adehsive respectively, and said bamboo mat layer 1,3 is worked out by thin bamboo strips used for weaving.
Making of present embodiment according to following steps:
1, thin bamboo strips used for weaving processing
Choose the transversal one-tenth 1.3～2.5m of the bigger bamboo wood of diameter length, the tangential thin bamboo strips used for weaving of 0.8mm uniform thickness that tangential vertical profile becomes, its surface does not allow surf green or tabasheer.
2, bamboo mat processing
The tangential thin bamboo strips used for weaving of uniform thickness is woven into the bamboo mat of 1300 * 2500mm breadth with the bamboo mat braider, and the thin bamboo strips used for weaving thickness that requires same Zhang Zhuxi to select for use equates bamboo mat surfacing N/D as far as possible.
3, the drying of bamboo mat
In dry kiln, bamboo mat is carried out drying, making its moisture content is about 11%.
4, bamboo mat impregnation
Pile up neatly into the impregnation frame of packing into behind the certain thickness with bamboo mat is folded; Put the impregnation frame into the glue groove by the bamboo fiber direction again; Solids content is housed is 25% melamine resin adehsive in the glue groove, require the bamboo mat surface all evenly to flood glue, then the glue frame is hung out the glue groove; And the bamboo mat buttress is placed in vertical state, remove unnecessary glue so that drip.
5, the drying of impregnation bamboo mat
Respectively individual bamboo mat being sent into dry kiln, is to carry out drying under 70 ℃ of conditions in temperature, makes its moisture content about 12%.
6, cigarette stalk particle processing
With cigarette stalk the grow up cigarette stalk particle of 3 ~ 13mm, wide 1 ~ 6mm, thick 0.5 ~ 1.6mm of back processing of emedullating.
7, the drying of cigarette stalk particle
Respectively cigarette stalk particle being sent into the rotator type drying machine, is to carry out drying under 100 ℃ of conditions in temperature, makes its moisture content 30%.
8, mat formation and assembly
A good impregnation bamboo mat of drying is placed on the backing plate, through mechanical spreading machine sized cigarette stalk particle is mated formation equably on bamboo mat, again that another drying is good impregnation bamboo mat overlays on above the slab of mating formation, and forms the slab of three-decker at present.
9, hot-forming
It is hot-forming that the slab of three-decker is sent into hot press.Hot pressing temperature: 180 ℃; Unit pressure: 5Mpa; Hot pressing time: 70s/mm.
10, process behind the sheet material
Sheet material after hot-forming is sent into the sheet material that edging in length and breadth is sawn into 1220 * 2440mm.
More than show and described basic principle of the utility model and the advantage of principal character and the utility model.The technical staff of the industry should understand; The utility model is not restricted to the described embodiments; The principle of describing in the foregoing description and the specification that the utility model just is described; Under the prerequisite that does not break away from the utility model spirit and scope, the utility model also has various changes and modifications, and these variations and improvement all fall in the utility model scope that requires protection.The utility model protection defined by the appended claims and their equivalents defined
.
Claims (3)
1. architectural decoration bamboo mat veneer environmental protection cigarette stalk chipboard; Comprise cigarette stalk particle layer; It is characterized in that; The slab that said cigarette stalk particle layer is made up of cigarette stalk particle, the upper surface and the lower surface of said cigarette stalk particle layer are provided with the bamboo mat layer that one deck is impregnated with melamine resin adehsive respectively, and said bamboo mat layer is worked out by thin bamboo strips used for weaving.
2. architectural decoration bamboo mat veneer environmental protection cigarette stalk chipboard according to claim 1 is characterized in that said thin bamboo strips used for weaving thickness is 0.6～1.0mm.
3. architectural decoration bamboo mat veneer environmental protection cigarette stalk chipboard according to claim 1 is characterized in that, said cigarette stalk particle is of a size of long 3 ~ 13mm, wide 1 ~ 6mm, thick 0.5 ~ 1.6mm.