The utility model relates to a decorative thin bamboo sheet with stripes, which comprises thin steamed bamboo chips after being steamed, bleached and dried and thin carbonized chips. The decorative thin bamboo sheet with the stripes is characterized in that the decorative thin bamboo sheet with the stripes is formed by gluing the thin steamed bamboo chips and the thin carbonized bamboo chips at intervals. The decorative thin bamboo sheet with the stripes meets requirements of sustainable use, regeneration or cyclic utilization and environmental conservation, integrates various advantages of hard broad-leaved wood and inherits characteristics of excellent physical mechanics property and low contractibility rate of bamboos. Furthermore, the decorative thin bamboo sheet with the stripes has the advantages of large breadth, little deformation, stabilization in size, high strength, fine rigidity and wearing resistance.

Description

Speckle is decorated thin bamboo plate

Technical field

The utility model relates to furniture and interior art decorative materials technology, and especially a kind of speckle is decorated thin bamboo plate.

Background technology

Prior art generally is to use veneer as the furniture base material, because used raw material are timber, and timber resources is very in short supply in China, has therefore influenced the development of China's upholstery greatly.And China's bamboo timber resource is abundant, and afforest the once success and the time of becoming a useful person are short, only need 5-8.The exploitation bamboo wood replaces timber and makes the existing reduction furniture of furniture cost, can make full use of bamboo timber resource again, and can preserve the ecological environment, and promotes the well-being of mankind.

Summary of the invention

The purpose of this utility model is to provide a kind of speckle to decorate thin bamboo plate; this speckle is decorated thin bamboo plate and is solved the raw-material crisis of furniture decoration; help the further development of China's upholstery; can improve simultaneously the value of bamboo wood; promote outlying mountain area's expanding economy, good economy, society and ecological benefits are arranged.

Of the present utility model being characterised in that: a kind of speckle is decorated thin bamboo plate, comprise through boiling, bleaching and dried boiling thin bamboo plate and through the charing thin bamboo plate after the charing, it is characterized in that: described speckle is decorated thin bamboo plate and is formed by boiling thin bamboo plate and the interval splicing of charing thin bamboo plate, and the thickness that described speckle is decorated thin bamboo plate is: 0.1 ~ 2.0 ㎜.

In a preferred embodiment, described boiling thin bamboo plate and charing thin bamboo plate are cemented surface with the diametric plane, and the two becomes speckle to decorate thin bamboo plate by the lateral separation splicing.

In another preferred embodiment, described boiling thin bamboo plate and charing thin bamboo plate are cemented surface with the string face, and the two becomes speckle to decorate thin bamboo plate by the lateral spacing splicing.

Advantage of the present utility model: the one, speckle is decorated the requirement that thin bamboo meets regeneration or recycling and green environmental protection; The 2nd, have the excellent decoration effect; The 3rd, the exquisiteness sense that keeps the quality of bamboo wood, the added value of raising bamboo wood; The 4th, solve the raw-material crisis of furniture decoration, help the further development of China's upholstery; The 5th, can improve the value of bamboo wood, promote outlying mountain area's expanding economy,, good economy, society and ecological benefits are arranged.

Description of drawings

Fig. 1 is the structural representation of the utility model embodiment 1.

Fig. 2 is the structural representation of the utility model embodiment 2.

Among the figure: 1-boiling thin bamboo plate; 2-charing thin bamboo plate.

The specific embodiment

The speckle that the utility model is provided below in conjunction with accompanying drawing and specific embodiment is decorated thin bamboo plate and is done and specify.

Embodiment 1

A kind of speckle is decorated thin bamboo plate, comprise through boiling, bleaching and dried boiling thin bamboo plate and through the charing thin bamboo plate after the charing, it is characterized in that: described boiling thin bamboo plate and charing thin bamboo plate are cemented surface with the diametric plane, and the two becomes speckle to decorate thin bamboo plate by the lateral separation splicing.

Embodiment 2

A kind of speckle is decorated thin bamboo plate, comprise through boiling, bleaching and dried boiling thin bamboo plate and through the charing thin bamboo plate after the charing, it is characterized in that: described boiling thin bamboo plate and charing thin bamboo plate are cemented surface with the string face, and the two becomes speckle to decorate thin bamboo plate by the lateral spacing splicing.

Preparation method of the present utility model may further comprise the steps:

(1) select bamboo: select gross bamboo ages in 5 ~ 6 years, the mao bamboon stalk is straight;

(2) system bamboo chip: the bamboo chip thickness that the mao bamboon stalk is made is at 4 ~ 6 ㎜, uniformity, and scrape in the surface;

(3) bamboo chip boiling and drying: a part of bamboo chip is carried out the pressure cooking bleaching, and digestion time 5 ~ 7 hours, pressure are 0.5 ~ 0.9Mpa; Another part bamboo chip carries out charing, and the temperature of charing is 100 ~ 105 ℃, and pressure is 0.3 ~ 0.4Mpa, and the time is 3 ~ 4 hours;

(4) adjustable cast iron planes: clean to the surf green of the bamboo chip after boiling and bleaching or the charing and tabasheer planing, the precision of thickness remains on ± 0.2mm within;

(5) gluing: adopt urea-formaldehyde resin adhesive, resin added is at 190 ~ 200g/m ², bamboo chip ageing 15 ~ 20 minutes behind gluing;

(6) splicing: the bamboo chip of boiling and bleaching and the bamboo chip of charing are cemented surface with the diametric plane, become brindled horizontal single-board materials by horizontal alternate splicing, and described horizontal single-board materials is by the integrated square bar of the well-thought-out plan that superposes from level to level; Or the bamboo chip of the bamboo chip of boiling and bleaching and charing is cemented surface with the string face, becomes brindled side direction single-board materials by the alternate splicing of side direction, and described side direction single-board materials is by the integrated square bar of the well-thought-out plan that superposes from level to level;

(7) gummed: the integrated square bar of bamboo is carried out hot pressing, and temperature is 100 ~ 110 ℃, just pressure pressure is 1.5 ~ 1.8 MPa, and side pressure pressure is 1 ~ 1.5 MPa; Time is 8 ~ 12 minutes;

(8) softening: the integrated square bar of bamboo behind the gummed is softened in radio-frequency generator, and the energy is commercial power, and power supply is 380 V(50Hz), power output is 30 KW, grid current is 0.2 ~ 0.7 A, and anode current is 2.0 ~ 3.0 A, and the softening time is 70 ~ 90 minutes;

(9) slicing: the integrated square bar of bamboo after softening is carried out slicing, and the temperature of the integrated square bar of bamboo remains on 40 ~ 60 ℃;

(10) leveling: the thin bamboo of the speckle after the slicing is flattened nonwoven in the stickup;

(11) sanding: the thin bamboo of speckle of pasting nonwoven is used abrasive finishing machine abrasive finishing, make its any surface finish, thickness is even, makes described speckle and decorates thin bamboo.

In the described step (3) to the drying of carrying out after the boiling, to the moisture content of bamboo chip be 7% ~ 9%, dry temperature is 60 ~ 70 ℃.

The moisture content of the integrated square bar of bamboo in the described step (8) after softening the processing highly is 400 ~ 600 ㎜ 35% ~ 40%.

Described speckle is decorated Bao Zhushi and is made by described preparation method, and the thickness that described speckle is decorated thin bamboo is 0.1 ~ 2.0 ㎜.

The utility model does not limit to above-mentioned preferred forms, and anyone can draw other various forms of speckles and decorate thin bamboo plate under enlightenment of the present utility model.All equalizations of being done according to the utility model claim change and modify, and all should belong to covering scope of the present utility model.

Claims (4)

1. a speckle is decorated thin bamboo plate, comprises through boiling, bleaching and dried boiling thin bamboo plate and through the charing thin bamboo plate after the charing, it is characterized in that: described speckle is decorated thin bamboo plate and is formed by boiling thin bamboo plate and the interval splicing of charing thin bamboo plate.

2. speckle according to claim 1 is decorated thin bamboo plate, and it is characterized in that: described boiling thin bamboo plate and charing thin bamboo plate are cemented surface with the diametric plane, and the two becomes speckle to decorate thin bamboo plate by the lateral separation splicing.

3. speckle according to claim 1 is decorated thin bamboo plate, and it is characterized in that: described boiling thin bamboo plate and charing thin bamboo plate are cemented surface with the string face, and the two becomes speckle to decorate thin bamboo plate by the lateral spacing splicing.

4. decorate thin bamboo plate according to claim 1,2 or 3 described speckles, it is characterized in that: the thickness that described speckle is decorated thin bamboo plate is: 0.1 ~ 2.0 ㎜.