CN202047287U - Electric iron soleplate coated with temperature-resistant, abrasion-resistant, high-hardness and low-frictional coefficient paint - Google Patents

Electric iron soleplate coated with temperature-resistant, abrasion-resistant, high-hardness and low-frictional coefficient paint Download PDF

Info

Publication number
CN202047287U
CN202047287U CN2011200859233U CN201120085923U CN202047287U CN 202047287 U CN202047287 U CN 202047287U CN 2011200859233 U CN2011200859233 U CN 2011200859233U CN 201120085923 U CN201120085923 U CN 201120085923U CN 202047287 U CN202047287 U CN 202047287U
Authority
CN
China
Prior art keywords
resistant
low
coating
temperature
hardness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2011200859233U
Other languages
Chinese (zh)
Inventor
张蕾
李力锋
赵子龙
潘东强
王小群
王朝生
王华平
张玉梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI EXCILON NEW MATERIALS CO., LTD.
Original Assignee
SHANGHAI EXCILON NEW MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI EXCILON NEW MATERIAL TECHNOLOGY Co Ltd filed Critical SHANGHAI EXCILON NEW MATERIAL TECHNOLOGY Co Ltd
Priority to CN2011200859233U priority Critical patent/CN202047287U/en
Application granted granted Critical
Publication of CN202047287U publication Critical patent/CN202047287U/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The utility model relates to an electric iron soleplate coated with temperature-resistant, abrasion-resistant, high-hardness and low-frictional coefficient paint. A colored paint layer is arranged on the electric iron soleplate; a varnish layer is arranged on the colored paint layer; the thickness of the colored paint layer is 25 to 35um, preferably 30um; and the thickness of the varnish layer is 5 to 10um, preferably 8um. The electric iron soleplate coated with the temperature-resistant, abrasion-resistant, high-hardness and low-frictional coefficient paint has the advantages of excellent comprehensive performance of the coating, low sintering temperature, high hardness, high temperature resistance, high abrasion resistance and low frictional coefficient.

Description

A kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating
[technical field]
The utility model relates to technical field of coatings, specifically, is a kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating.
[background technology]
Paying close attention to more for iron plate coating people is ABRASION RESISTANCE and coefficient of friction under its high temperature.At present commercially available iron plate coating (market occupy volume data) usually adopts organosilicon coating.There is following problem in organosilicon coating: solidification temperature height has at first increased difficulty of construction and energy resource consumption; Its subsurface hardness especially case hardness under the high temperature is low, wears no resistance; The adhesion of organic silicon coating and aluminum ground is poor under the high-temperature vapor environment once more, and coating and ground are peeled off easily; And the organic silicon coating coefficient of friction is bigger, and general all greater than 0.30, smooth feeling is relatively poor during use.
For improving hardness, heatproof and the anti-wear performance of coating, reduce its coefficient of friction, the utility model provides a kind of coating of ceramic structure, and this coating and ground adhesion are good, but sintering under the low temperature, hardness height, heat-resistant, wear-resistant, coefficient of friction are low, excellent combination property.But heatproof is more than 400 ℃; The coating pencil hardness can reach more than the 7H under the normal temperature, and the coating pencil hardness can reach more than the 5H in the time of 200 ℃; ABRASION RESISTANCE is good; Coefficient of friction is low, less than 0.22.Effectively guarantee the service life and the smooth feeling of electric iron.
[utility model content]
The purpose of this utility model is to overcome the deficiencies in the prior art, and a kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating is provided.
The purpose of this utility model is achieved through the following technical solutions:
A kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating is provided with the colored paint layer on iron plate; Described colored paint layer also is provided with layer of varnish;
The thickness of described colored paint layer is 25um~35um, is preferably 30um;
The thickness of described layer of varnish is 5um~10um, is preferably 8um;
The base-material that constitutes coating has following component:
Colored paint has following component
Figure BDA0000052455060000022
Varnish has following component
Figure BDA0000052455060000023
Compared with prior art, good effect of the present utility model is:
The properties of coating excellence has sintering temperature and low concurrently, high rigidity, high-temperature resistant, high abrasion and low-friction coefficient.
[description of drawings]
The structural representation of Fig. 1 embodiment 1 of the present utility model;
The structural representation of Fig. 2 embodiment 2 of the present utility model;
Label in the accompanying drawing is respectively: 1, iron plate, 2, the colored paint layer, 3, layer of varnish.
[specific embodiment]
Below provide the utility model a kind of specific embodiment that scribbles the iron plate of heat-resistant, wear-resistant high rigidity low-friction coefficient coating.
Embodiment 1
Referring to accompanying drawing 1, a kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating is provided with the colored paint layer on iron plate clearly; Described colored paint layer also is provided with layer of varnish;
The thickness of described colored paint layer is 25um~35um, is preferably 30um;
The thickness of described layer of varnish is 5um~10um, is preferably 8um;
The base-material that constitutes coating has following component:
Figure BDA0000052455060000031
Colored paint has following component
Figure BDA0000052455060000041
Described auxiliary agent is as organosilicon modified polyorganosiloxane, phosphate modified acrylic acid etc.;
Described pigment is as titanium white, copper-chrome black, iron oxide red, phthalocyanine blue etc.;
Described filler is as kaolin, silicon whisker, aerosil;
Described catalyst is as zinc naphthenate, zirconium naphthenate, potassium acetate etc.;
Varnish has following component
Figure BDA0000052455060000042
Described auxiliary agent is as organosilicon modified polyorganosiloxane, phosphate modified acrylic acid etc.;
Described catalyst is as zinc naphthenate, zirconium naphthenate, potassium acetate etc.
With Ludox, ethyl orthosilicate, MTMS is raw material, adopts sol-gal process to synthesize base-material.Compounding aid, color stuffing and special catalyst can form the coating of ceramic structure at 200 ℃ of following sintering in this base-material.Owing to be rich in a large amount of silicon hydroxyls, coating and ground adhesion are very strong, efficiently solve organosilicon and are applied to the frequent foaming phenomenon (being that coating and ground are peeled off) that occurs on the iron plate.Coating is based on the inorganic constituents of silica silicon structure, so temperature tolerance is good, hardness is high, because coating surface is rich in methyl, so skin-friction coefficient is low, the smooth degree and the anti-wear performance of coating significantly are better than organic silicon coating simultaneously.
Embodiment 2
See also accompanying drawing 2, a kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating is provided with the colored paint layer on iron plate;
The thickness of described colored paint layer is 25um~35um;
The thickness of described layer of varnish is 5um~10um;
The base-material that constitutes coating has following component:
Figure BDA0000052455060000051
Colored paint has following component
Figure BDA0000052455060000052
Described auxiliary agent is as organosilicon modified polyorganosiloxane, phosphate modified acrylic acid etc.;
Described pigment is as titanium white, copper-chrome black, iron oxide red, phthalocyanine blue etc.;
Described filler is as kaolin, silicon whisker, aerosil;
Described catalyst is as zinc naphthenate, zirconium naphthenate, potassium acetate etc.
The above only is a preferred implementation of the present utility model; should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the utility model design; can also make some improvements and modifications, these improvements and modifications also should be considered as in the protection domain of the present utility model.

Claims (6)

1. an iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating is characterized in that, is provided with the colored paint layer on iron plate.
2. a kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating as claimed in claim 1 is characterized in that described colored paint layer also is provided with layer of varnish.
3. a kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating as claimed in claim 1 is characterized in that the thickness of described colored paint layer is 25um~35um.
4. a kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating as claimed in claim 3 is characterized in that the thickness of described colored paint layer is 30um.
5. a kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating as claimed in claim 1 is characterized in that the thickness of described layer of varnish is 5um~10um.
6. a kind of iron plate that scribbles heat-resistant, wear-resistant high rigidity low-friction coefficient coating as claimed in claim 5 is characterized in that the thickness of described layer of varnish is 8um.
CN2011200859233U 2011-03-28 2011-03-28 Electric iron soleplate coated with temperature-resistant, abrasion-resistant, high-hardness and low-frictional coefficient paint Expired - Fee Related CN202047287U (en)