CN201017736Y - 防止铁氧体磁心烧结变形的承烧垫片 - Google Patents

防止铁氧体磁心烧结变形的承烧垫片 Download PDF

Info

Publication number
CN201017736Y
CN201017736Y CNU2006201416759U CN200620141675U CN201017736Y CN 201017736 Y CN201017736 Y CN 201017736Y CN U2006201416759 U CNU2006201416759 U CN U2006201416759U CN 200620141675 U CN200620141675 U CN 200620141675U CN 201017736 Y CN201017736 Y CN 201017736Y
Authority
CN
China
Prior art keywords
ferrite core
ring sheet
firing ring
hold
model
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNU2006201416759U
Other languages
English (en)
Inventor
郭尚忠
王开旺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hengdian Group DMEGC Magnetics Co Ltd
Original Assignee
Hengdian Group DMEGC Magnetics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hengdian Group DMEGC Magnetics Co Ltd filed Critical Hengdian Group DMEGC Magnetics Co Ltd
Priority to CNU2006201416759U priority Critical patent/CN201017736Y/zh
Application granted granted Critical
Publication of CN201017736Y publication Critical patent/CN201017736Y/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本实用新型涉及一种防止粉末冶金产品在烧结过程中产生变形的垫片，尤其是涉及一种对永磁铁氧体磁心在烧结过程中变形程度的改善或免除变形的伴同烧结的承烧垫片。铁氧体磁心的正下方设置有一块承烧垫片。本实用新型具有能够有效防止铁氧体磁心在烧结过程中变形损坏、产品成品率高、生产成本相对较低、能够生产超细及超薄的不规则产品、设计合理、使用方便等特点。

Description

防止铁氧体磁心烧结变形的承烧垫片
技术领域
本实用新型涉及一种防止粉末冶金产品在烧结过程中产生变形的垫片，尤其是涉及一种对永磁铁氧体磁心在烧结过程中变形程度的改善或免除变形的伴同烧结的承烧垫片。
背景技术
随着家电和信息产业的不断发展，铁氧体磁心的用量越来越大，用于粉末冶金制作的各类产品也越来越多，大多数粉末冶金产品都要经过烧结过程包含铁氧体磁心。许多形状不规则或不对称的产品在烧结过程中都会发生变形，严重影响产品的成品率甚至有些形状的产品无法烧结成型导致电子元器件不能优化设计，烧结变形多年来一直困惑着各大制造业主和元器件设计工程师。磁心变形的举例见说明书附图1；类似该类产品在烧结过程中都会产生不同程度的变形，说明书附图1中E形铁氧体磁心4为非正品的变形铁氧体磁心。
发明内容
本实用新型主要是针对现有技术所存在的永磁铁氧体磁心在烧结过程中易变形损坏、产品成品率低、生产成本高等的技术问题，提供一种能够有效防止铁氧体磁心在烧结过程中变形损坏、产品成品率高、生产成本相对较低的防止铁氧体磁心烧结变形的承烧垫片。
本实用新型还针对现有技术所存在的无法生产超细、超薄的不规则产品而导致电子元器件设计受限制的技术问题，提供一种能够生产超细、超薄的不规则产品的防止铁氧体磁心烧结变形的承烧垫片。
本实用新型的上述技术问题主要是通过下述技术方案得以解决的：铁氧体磁心的正下方设置有一块承烧垫片。铁氧体磁心的正下方设置有一块承烧垫片，来取代产品直接摆放在氧化镐板上或刚玉推板烧结的方式；能够有效地防止铁氧体磁心在烧结过程中变形损坏。
作为优选，所述的承烧垫片厚度为2mm-5mm。产品重量大时可以采用厚度较大的承烧垫片；产品重量小时可以采用厚度较小的承烧垫片。
作为优选，所述的承烧垫片平面边缘处设置有倒角。倒角起到定位固定的作用，保证了承烧垫片与铁氧体磁心之间不会产生相对错位移动；其设计合理，使用方便。
作为优选，所述的承烧垫片呈矩形或圆形，其材料与铁氧体磁心的材料相同，承烧垫片面积覆盖铁氧体磁心垂直投影区域。可采用与被烧铁氧磁心相同的材料制成与该产品大平面外形尺寸相符的矩形承烧垫片，铁氧体磁心坯件不能超出承烧垫片的范围。
作为优选，所述的承烧垫片的密度与铁氧体磁心的坯件密度相差值小于等于5％。可采用与烧结产品坯件密度相同的材料压制成矩形承烧垫片。
因此，本实用新型具有能够有效防止铁氧体磁心在烧结过程中变形损坏、产品成品率高、生产成本相对较低、能够生产超细及超薄的不规则产品、设计合理、使用方便等特点；尤其是能够有效防止铁氧体磁心在烧结过程中变形损坏、产品成品率高、能够生产超细及超薄的不规则产品。
附图说明
附图1是本实用新型对比技术变形铁氧体磁心的一种立体结构图。
附图2是本实用新型承烧垫片的一种结构示意图。
附图3是本实用新型承烧垫片与铁氧体磁心一同烧结的一种结构立体示意图。
具体实施方式
下面通过实施例，并结合附图，对本实用新型的技术方案作进一步具体的说明。
实施例1：
采用与被烧铁氧磁心1相同的材料制成压制成与铁氧体磁心大平面外形尺寸相符的矩形承烧垫片2；承烧垫片面积覆盖铁氧体磁心垂直投影区域；承烧垫片厚度为2mm；承烧垫片平面边缘处设置有倒角3。承烧垫片设置在铁氧体磁心的正下方。
在烧结铁氧体磁心时将承烧垫片垫在氧化镐板或刚玉推板与铁氧体磁心的之间，一片承烧垫片上面也可叠装多层铁氧体磁心，承烧垫片与铁氧体磁心对正，多排铁氧体磁心之间不得有搭叠现象。承烧垫片与被烧结的铁氧体磁心在烧结过程中一同收缩，将被烧铁氧体磁心的收缩重心统一到一个收缩重心上，以承烧垫片重心为准一同收缩，从而克服了不规则铁氧体磁心有多个收缩重心所引起的变形。

Claims (5)

1.一种防止铁氧体磁心烧结变形的承烧垫片，其特征在于铁氧体磁心(1)的正下方设置有一块承烧垫片(2)。
2.根据权利要求1所述的防止铁氧体磁心烧结变形的承烧垫片，其特征在于所述的承烧垫片厚度为2mm-5mm。
3.根据权利要求1所述的防止铁氧体磁心烧结变形的承烧垫片，其特征在于所述的承烧垫片平面边缘处设置有倒角(3)。
4.根据权利要求1或2或3所述的防止铁氧体磁心烧结变形的承烧垫片，其特征在于所述的承烧垫片呈矩形或圆形，其材料与铁氧体磁心的材料相同，承烧垫片面积覆盖铁氧体磁心垂直投影区域。
5.根据权利要求1或2或3所述的防止铁氧体磁心烧结变形的承烧垫片，其特征在于所述的承烧垫片的密度与铁氧体磁心的坯件密度相差值小于等于5％。
CNU2006201416759U 2006-12-29 2006-12-29 防止铁氧体磁心烧结变形的承烧垫片 Expired - Fee Related CN201017736Y (zh)