CN1966176A - Forging method of high grade carbon steel hook, ring parts - Google Patents
Forging method of high grade carbon steel hook, ring parts Download PDFInfo
- Publication number
- CN1966176A CN1966176A CN 200610053359 CN200610053359A CN1966176A CN 1966176 A CN1966176 A CN 1966176A CN 200610053359 CN200610053359 CN 200610053359 CN 200610053359 A CN200610053359 A CN 200610053359A CN 1966176 A CN1966176 A CN 1966176A
- Authority
- CN
- China
- Prior art keywords
- forge
- rough
- finish
- spare
- forge spare
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method for forging catbon steel hook and ring, wherein it comprises that: (1), heating before rough forging; 92), removing the oxidized skin of hot blank; (3), roughly forging; (4), cutting edge of rough forged element; (5), grinding and furnishing; (6), heating before fine forging; (7), finish forging; (8), cutting edge of finished forged element; (9), furnishing. The invention has simple process and low cost.
Description
Technical field
The forging method of relate generally to machine components of the present invention specifically, the present invention relates to the forging method of a kind of high grade carbon steel hook, ring parts.
Background technology
Fine Steel Casting iron suspension ring, Fine Steel Casting iron suspension hook, Fine Steel Casting iron draw ring and Fine Steel Casting iron drag hook are crane gear and dilatory machinery machine components simple in structure commonly used.At present, domestic enterprise to produce this machine components be to finish by once forge cutting edge.Because the process equipment of domestic enterprise mostly is simple common apparatus, often can't reach intensity, the precision of designing requirement.Overseas enterprise adopts advanced forging equipment, can at high temperature once finish the forging of this machine components, but continuing the unnecessary edge of excision forging under the condition of high temperature behind the high temperature forging, cause the forging of removing unnecessary inside and outside periphery to have side cut interlayer and burr, produce very large deformation, forging precision reduces, and can't reach designing requirement.In addition, adopt advanced forging equipment, improved production cost greatly.
Summary of the invention
The present invention will solve the high grade carbon steel hook that the method that adopts existing forging high grade carbon steel hook, ring parts forges, the precision of ring parts can't reach designing requirement and the high problem of production cost, and a kind of new high grade carbon steel hook, the forging method of ring parts are provided.
The forging method of high grade carbon steel hook of the present invention, ring parts is characterized in that, order comprises the following steps:
1, heating before the rough forge, the blank that is about to the Fine Steel Casting iron material is put into firing equipment, is heated to 920 ℃ to 980 ℃;
2, remove the oxide skin of hot blank, be about to hot blank and put into the descale machine immediately and remove oxide skin;
3, rough forge will remove the hot blank of oxide skin and put into the moulding of stamping machine mould rough forge immediately, obtain the rough forge spare of heat;
4, rough forge spare is cut edge, even after the rough forge spare of heat naturally cools to normal temperature, dashes the unnecessary neighboring and the unnecessary inner rim of the rough forge spare body that removes rough forge spare with punch die in stamping machine, obtains rough forge spare body;
5, rough forge spare body polishing ball blast is about to rough forge spare body and puts into the polishing machine of removing slag and carry out the ball blast polishing;
6, heating before the finish forge, the rough forge spare body that is about to after ball blast is polished is put into firing equipment, is heated to 850 ℃ to 900 ℃;
7, finish forge, the rough forge spare body that is about to the heat after ball blast is polished is put into the moulding of stamping machine mould finish forge immediately, obtains the automobile draw ring finish forge spare of heat;
8, finish forge spare is cut edge, even after the ring finish forge spare of heat naturally cools to normal temperature, dashes the unnecessary neighboring and the unnecessary inner rim of the finish forge spare body that removes finish forge spare with punch die in stamping machine, obtains encircling finish forge spare body;
9, finish forge spare body sanding and polishing is about to finish forge spare body and puts into sanding and polishing machine and carry out the ball blast polishing.
The forging method of high grade carbon steel hook of the present invention, ring parts, owing to carry out hot finish forge behind hot rough forge, a deflection of forging is little, has improved the precision of forging; Owing to be cooled to normal temperature behind hot rough forge and hot finish forge, the shape and size of forging are stable, dash under this state and remove unnecessary inside and outside periphery, and resulting forging can not have side cut interlayer and burr, does not have distortion substantially, and precision improves greatly.Therefore, adopt the forging method of high grade carbon steel hook of the present invention, ring parts to compare with the forging method of existing high grade carbon steel hook, ring parts, just can forge high grade carbon steel hook, the ring parts of the precision that adheres to specification with simple forging machinery equipment, and reduce production cost.
Description of drawings
Fig. 1 is that the master that a kind of blank of automobile drag hook that expression will be implemented the forging method of high grade carbon steel hook of the present invention, ring parts carries out behind the rough forge looks schematic diagram;
Fig. 2 is the vertical profile schematic diagram of automobile drag hook shown in Figure 1;
Fig. 3 is that the master that automobile drag hook shown in Figure 1 carries out after rough forge is cut edge looks schematic diagram;
Fig. 4 is the vertical profile schematic diagram of automobile drag hook shown in Figure 3;
Fig. 5 is that the master that automobile drag hook shown in Figure 4 carries out behind the finish forge looks schematic diagram;
Fig. 6 is the vertical profile schematic diagram of automobile drag hook shown in Figure 5;
Fig. 7 is that the master that automobile drag hook shown in Figure 6 carries out after finish forge is cut edge looks schematic diagram;
Fig. 8 is the vertical profile schematic diagram of automobile drag hook shown in Figure 7.
The specific embodiment
Be further described below in conjunction with the forging method of the drawings and specific embodiments high grade carbon steel hook of the present invention, ring parts.
Referring to Fig. 1 to Fig. 8, a kind of forging process of automobile draw ring is as follows:
1, heating before the rough forge, the round steel or the square steel blank that are about to one section Fine Steel Casting iron material are put into the coal reverberatory furnace, are heated to 920 ℃ to 980 ℃, preferably are heated to 950 ℃;
2, remove the oxide skin of hot blank, be about to hot blank and put into the descale machine immediately and remove oxide skin;
3, rough forge, the hot blank that is about to remove oxide skin is put into the moulding of stamping machine mould rough forge immediately, obtains the automobile draw ring rough forge spare 1 of heat illustrated in figures 1 and 2;
4, rough forge spare is cut edge, after even the automobile draw ring rough forge spare 1 of heat naturally cools to normal temperature, in stamping machine, dash the unnecessary neighboring 111 and the unnecessary inner rim 112 of the automobile draw ring rough forge spare body 11 that removes automobile draw ring rough forge spare 1, obtain Fig. 3 and automobile draw ring rough forge spare body 11 shown in Figure 4 with punch die;
5, rough forge spare body polishing ball blast is about to automobile draw ring rough forge spare body 11 and puts into the polishing machine of removing slag and carry out the ball blast polishing;
6, heating before the finish forge, the automobile draw ring rough forge spare body 11 that is about to after ball blast is polished is put into the coal reverberatory furnace, is heated to 850 ℃ to 900 ℃, preferably is heated to 875 ℃;
7, finish forge, the automobile draw ring rough forge spare body 11 that is about to the heat after the ball blast polishing is put into the moulding of stamping machine mould finish forge immediately, obtains the automobile draw ring finish forge spare 2 of Fig. 5 and heat shown in Figure 6;
8, finish forge spare is cut edge, after even the automobile draw ring finish forge spare 2 of heat naturally cools to normal temperature, in stamping machine, dash the unnecessary neighboring 211 and the unnecessary inner rim 212 of the automobile draw ring finish forge spare body 21 that removes automobile draw ring finish forge spare 2, obtain Fig. 7 and automobile draw ring finish forge spare body 21 shown in Figure 8 with punch die;
9, finish forge spare body sanding and polishing is about to automobile draw ring finish forge spare body 21 and puts into sanding and polishing machine and carry out the ball blast polishing.
The used plant equipment of forging method of implementing high grade carbon steel hook of the present invention, ring parts is known.
Economy-combat grinding and polishing light obtains automobile draw ring finish forge spare body 21 and carries out turning again, and heat treatment etc. obtain finished product automobile draw ring.
The forging method of high grade carbon steel hook of the present invention, ring parts also can be used for the forging processing of other Fine Steel Casting iron machine components simple in structure, as long as change diel.
According to oneself describing the present invention property of embodiments of the invention and nonrestrictive description, but should be understood that under the situation that does not break away from relevant protection domain defined by the claims those skilled in the art can make change and/or revise.
Claims (2)
1, the forging method of a kind of high grade carbon steel hook, ring parts is characterized in that, order comprises the following steps:
(1) heating before the rough forge, the blank that is about to the Fine Steel Casting iron material is put into firing equipment, is heated to 920 ℃ to 980 ℃;
(2) remove the oxide skin of hot blank, be about to hot blank and put into the descale machine immediately and remove oxide skin;
(3) rough forge will remove the hot blank of oxide skin and put into the moulding of stamping machine mould rough forge immediately, obtain the rough forge spare of heat;
(4) rough forge spare is cut edge, even after the phase forging of heat naturally cools to normal temperature, dashes the unnecessary neighboring and the unnecessary inner rim of the rough forge spare body that removes rough forge spare with punch die in stamping machine, obtains rough forge spare body;
(5) rough forge spare body polishing ball blast is about to rough forge spare body and puts into the polishing machine of removing slag and carry out the ball blast polishing;
(6) heating before the finish forge, the rough forge spare body that is about to after ball blast is polished is put into firing equipment, is heated to 850 ℃ to 900 ℃;
(7) finish forge, the rough forge spare body that is about to the heat after ball blast is polished is put into the moulding of stamping machine mould finish forge immediately, obtains the automobile draw ring finish forge spare of heat;
(8) finish forge spare is cut edge, even after the ring finish forge spare of heat naturally cools to normal temperature, dashes the unnecessary neighboring and the unnecessary inner rim of the finish forge spare body that removes finish forge spare with punch die in stamping machine, obtains encircling finish forge spare body;
(9) finish forge spare body sanding and polishing is about to finish forge spare body and puts into sanding and polishing machine and carry out the ball blast polishing.
According to the described forging method of claim 1, it is characterized in that 2, the blank heating with the Fine Steel Casting iron material before the rough forge is heated to 950 ℃; Be heated to 875 ℃ before the finish forge.