CN1927558A - Manufacture method of inorganic heat-insulating material for building exterior wall - Google Patents
Manufacture method of inorganic heat-insulating material for building exterior wall Download PDFInfo
- Publication number
- CN1927558A CN1927558A CN 200610095160 CN200610095160A CN1927558A CN 1927558 A CN1927558 A CN 1927558A CN 200610095160 CN200610095160 CN 200610095160 CN 200610095160 A CN200610095160 A CN 200610095160A CN 1927558 A CN1927558 A CN 1927558A
- Authority
- CN
- China
- Prior art keywords
- various
- described method
- cement
- inorganic
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a new method of producing lagging material of external wall of buildings. It produces a light waterproof inorganic foaming sheet using the is ordinary silicate, sulfur-aluminates fast-drying cement and other special cement by the way of foaming, thereby achieve the purpose of heat insulation and overcoming the shortcomings of flammability and emitting toxic gases of other organic materials. The material is a new and friendly to environment insulation material of external wall of buildings.
Description
The present invention is by Portland cement, sulphate aluminium cement and other special cements etc. being foamed and water-proofing treatment with blowing agent, make light-weight foam sheet material, being mainly used in the exterior wall heat-insulation and heat-preservation field of industry and civil buildings.
Because worldwide energy crisis is serious day by day, various countries also more and more pay attention to energy savings at present.China has also proposed higher energy-conservation requirement to every profession and trade, present most of provinces and cities are in succession to the energy-conservation higher requirement of having made of building, also emerged in large numbers the external-wall heat-insulation material of a lot of various materials on the market, as inorganic material such as macromolecular materials such as polystyrene plates, granules of polystyrene thermal insulation mortar, polyurathamc sheet material, polyethylene foamed, expanded polypropylene and expanded perlite, mineral fibres cottons.But particularly when catching fire, building can produce a large amount of toxic gases because macromolecular material is inflammable, so its application has been subjected to very big restriction.And present most of inorganic heat insulation materials are because intensity is low, water absorption rate is high, and the reason such as harmful material that also contains that has makes it fail to be used widely.
The purpose of this invention is to provide a kind of novel inorganic heat insulation material production method, the product of producing is had not only can reach the heat-insulation and heat-preservation purpose but also can not produce dysgenic characteristics human body.
The present invention realizes by such mode: inorganic gel materials such as Portland cement, sulphate aluminium cement are mixed with sepiolite, flyash, blowing agent, waterproofing agent, other additives and water, pour into after stirring in the mould, require to cut into the sheet material of needs after the maintenance moulding according to difference.
The insulation material of method production is an inorganic material owing to what all use thus,, technological requirement not high, low production cost simple without any harmful effect and production equipment to human body.
Claims (9)
1, a kind of novel production technology that is used for the inorganic water-proof foaming plate of exterior-wall heat insulation, it is characterized in that inorganic gel material (1) is mixed (3) with inserts (2), adding waterproofing agent (4), blowing agent (5) and foam stabiliser (6) stir and pour moulding in the mould (7) into, cut into all size sheet material (8) after nature or steam curing.
2,, it is characterized in that described inorganic gel material (1) comprising: Portland cement, portland slag cement, Portland fly ash cement, composite Portland cement, gypsum, aluminium sulfate quick hardening cement and other various special cements according to the described method of claim 1.
3,, it is characterized in that described inserts (2) comprising: inorganic fillings and various reinforcers such as polypropylene fibre, polyster fibre and carbon fiber such as river sand, white clouds sand, flyash, various slag, quartz sand, limestone crushing sand, haydite, expanded perlite, expanded vermiculite, float stone, foam glass pearl according to the described method of claim 1.
4, according to the described method of claim 1, it is characterized in that described mixing (3) comprising: the artificial mixing, vertical mixer, horizontal mixer and other various types of mixers mix.
5,, it is characterized in that described waterproofing agent (4) comprising: various macromolecule emulsions, the macromolecule aqueous solution, organosilan, wax emulsion, the stearate aqueous solution, triethanolamine, iron chloride and other various waterproofing agents according to the described method of claim 1.
6, according to the described method of claim 1, it is characterized in that described blowing agent (5) comprising: anion surfactant, cationic surfactant, amphoteric surfactant, rosin soap, hydrogen peroxide, sodium acid carbonate and other materials that can produce gas or form bubble.
7,, it is characterized in that described foam stabiliser (6) comprising: the high molecular aqueous solution of various synthesizing water-solubilities, rosin soap, various surfactant and various water-soluble materials such as polyvinyl alcohol, polyacrylamide, cellulose according to the described method of claim 1.
8,, it is characterized in that described mould (7) comprising: the square that metal or nonmetal plate are made, rectangle, regular polygon cavity mould according to the described method of claim 1.
9,, it is characterized in that described all size sheet material (8) comprising: the sheet material of specifications such as the square of 1-6cm thickness, rectangle and regular polygon according to the described method of claim 1.