CN1900200A - Sprayed glue and its producing process - Google Patents
Sprayed glue and its producing process Download PDFInfo
- Publication number
- CN1900200A CN1900200A CN 200510035847 CN200510035847A CN1900200A CN 1900200 A CN1900200 A CN 1900200A CN 200510035847 CN200510035847 CN 200510035847 CN 200510035847 A CN200510035847 A CN 200510035847A CN 1900200 A CN1900200 A CN 1900200A
- Authority
- CN
- China
- Prior art keywords
- spray glue
- organic solvent
- grams
- thermoplastic elastomer
- rosin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of sprayed glue, which contains thermoplastic elastomer SBS 5-20 wt%, organic solvent 10-30 wt%, No. 6 extracting solvent oil 10-55 wt%, 801 resin 2-15 wt% and rosin 10-40 wt%. Its production process includes the following steps: 1. setting the organic solvent and one half of the No. 6 extracting solvent oil into the reaction kettle before starting the motor of the reaction kettle; 2. adding the thermoplastic elastomer SBS and the 801 resin into the reaction kettle and stirring for 3-4 hr; and 3. adding rosin and the rest No. 6 extracting solvent oil into the reaction kettle and stirring for one other 3-4 hr. The sprayed glue has no pollution, no harm to human body, high adhesion capacity, and other advantages, and may be used in producing sofa, swivel chair, folding screen, etc.
Description
[technical field]
The present invention relates to a kind of tackiness agent, especially relate to a kind of spray glue and manufacture craft thereof.
[background technology]
The thermoplastic elastomer SBS's solvent-borne type spray glue that occurs in the market, all different ratios contains triphen (benzene,toluene,xylene) and halocarbon class severe toxicity, high toxicity solvent, triphen belongs to carcinogenic substance, the halocarbon class can influence human body metabolism and cause liver to poison, no matter be Long contact time or ask contact in short-term, the acute and chronic poisoning that human body is caused in the capital to some extent causes serious pollution to surrounding environment simultaneously.And stickiness is low, easily come unglued, easy aging, non-refractory, cold-resistant.
[summary of the invention]
Technical problem to be solved by this invention is to provide a kind of its manufacture craft of spray glue, and is pollution-free, harmless, and stickiness strong, be difficult for coming unglued, be difficult for aging, high temperature resistant, cold-resistant.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is: a kind of spray glue is characterized in that: this spray glue contains by weight percentage: thermoplastic elastomer SBS 5-20%, organic solvent 10-30%, soybean extracting solvent no.6 10-55%, 801 resin 2-15%, rosin 10-40%.
Further improvement in the technical proposal is:
Described thermoplastic elastomer SBS is No. 411.
Described organic solvent is a methylene dichloride.
Described organic solvent is a trieline.
Described organic solvent is an acetone.
Described organic solvent is the mixture of methylene dichloride, trieline, acetone.
Also comprise staybelite 2-5% in the weight proportion of this spray glue.
Also comprise Virahol 1-3% in the weight proportion of this spray glue.
Also comprise Gum Rosin 1-5% in the weight proportion of this spray glue.
A kind of processing method of above-mentioned spray glue comprises the steps:
A, half of organic solvent and soybean extracting solvent no.6 total amount added reflection still, start reflection still motor;
B, thermoplastic elastomer SBS and 801 resins are added the reflection still respectively, stirred 3-4 hour;
C, adding rosin and remaining soybean extracting solvent no.6, restir 3-4 hour.
The invention has the beneficial effects as follows: spray glue of the present invention is pollution-free, harmless, and stickiness is strong, fast drying, can anti-height, little, the spraying of smell evenly, just sticking ability is strong, viscous force is lasting, ageing-resistant, solid content is high, save 10-30% than common like product consumption, correctly use harmless.
[embodiment]
Below in conjunction with embodiment the present invention is described further:
Embodiment one: preparation 3630 gram spray glue, and component and weight proportion are:
No. 411 thermoplastic elastomer SBS's 280 grams;
Methylene dichloride 350 grams;
Trieline 50 grams;
Acetone 50 grams;
Soybean extracting solvent no.6 1900 grams;
801 resins, 150 grams;
Rosin 850 grams.
Wherein methylene dichloride, trieline, acetone are organic solvent, can use wherein a kind of, two kinds or three kinds, the organic solvent total amount reach 450 the gram get final product.
Processing method is:
A, with organic solvent (methylene dichloride, trieline, acetone) and soybean extracting solvent no.6 total amount half promptly 950 grams add the reflection stills, start reflection still motor;
B, respectively thermoplastic elastomer SBS 280 gram and 801 resins, 150 grams are added the reflection stills, stirred 3-4 hour;
C, adding rosin 850 grams and remaining soybean extracting solvent no.6 950 grams, restir 3-4 hour.
Embodiment two: preparation 3770 gram spray glue, and component and weight proportion are:
No. 411 thermoplastic elastomer SBS's 260 grams;
Methylene dichloride 540 grams;
Trieline 60 grams;
Acetone 50 grams;
Soybean extracting solvent no.6 1740 grams;
801 resins, 70 grams;
Rosin 870 grams;
Staybelite 130 grams;
Virahol 50 grams.
Wherein methylene dichloride, trieline, acetone are organic solvent, can use wherein a kind of, two kinds or three kinds, the organic solvent total amount reach 650 the gram get final product.
Processing method is:
A, with organic solvent (methylene dichloride, trieline, acetone) and soybean extracting solvent no.6 total amount half promptly 870 grams add the reflection stills, start reflection still motor;
B, respectively thermoplastic elastomer SBS 260 gram and 801 resins, 70 grams are added the reflection stills, stirred 3-4 hour;
C, adding rosin 870 grams and remaining soybean extracting solvent no.6 870 grams, adding staybelite 130 grams, Virahol 50 restrain restir 3-4 hour.
Present embodiment has added staybelite and Virahol according to the Various Seasonal needs, can use in October to March.
Embodiment three: preparation 3680 gram spray glue, and component and weight proportion are:
No. 411 thermoplastic elastomer SBS's 260 grams;
Methylene dichloride 300 grams;
Trieline 50 grams;
Acetone 50 grams;
Soybean extracting solvent no.6 1950 grams;
801 resins, 100 grams;
Rosin 870 grams;
Gum Rosin 100 grams.
Wherein methylene dichloride, trieline, acetone are organic solvent, can use wherein a kind of, two kinds or three kinds, the organic solvent total amount reach 400 the gram get final product.
Processing method is:
A, with organic solvent (methylene dichloride, trieline, acetone) and soybean extracting solvent no.6 total amount half promptly 975 grams add the reflection stills, start reflection still motor;
B, respectively thermoplastic elastomer SBS 260 gram and 801 resins, 100 grams are added the reflection stills, stirred 3-4 hour;
C, adding rosin 870 grams and remaining soybean extracting solvent no.6 975 grams add Gum Rosin 100 grams, restir 3-4 hour again.
Present embodiment has added Gum Rosin according to the Various Seasonal needs, can use in April to June.
Claims (10)
1, a kind of spray glue is characterized in that: this spray glue contains by weight percentage: thermoplastic elastomer SBS 5-20%, organic solvent 10-30%, soybean extracting solvent no.6 10-55%, 801 resin 2-15%, rosin 10-40%.
2, spray glue as claimed in claim 1 is characterized in that: described thermoplastic elastomer SBS is No. 411.
3, spray glue as claimed in claim 1 is characterized in that: described organic solvent is a methylene dichloride.
4, spray glue as claimed in claim 1 is characterized in that: described organic solvent is a trieline.
5, spray glue as claimed in claim 1 is characterized in that: described organic solvent is an acetone.
6, spray glue as claimed in claim 1 is characterized in that: described organic solvent is the mixture of methylene dichloride, trieline, acetone.
7, spray glue as claimed in claim 1 is characterized in that: also comprise staybelite 2-5% in the weight proportion of this spray glue.
8, spray glue as claimed in claim 1 is characterized in that: also comprise Virahol 1-3% in the weight proportion of this spray glue.
9, spray glue as claimed in claim 1 is characterized in that: also comprise Gum Rosin 1-5% in the weight proportion of this spray glue.
10, a kind of processing method of spray glue as claimed in claim 1 is characterized in that: this method comprises the steps:
A, half of organic solvent and soybean extracting solvent no.6 total amount added reflection still, start reflection still motor;
B, thermoplastic elastomer SBS and 801 resins are added the reflection still respectively, stirred 3-4 hour;
C, adding rosin and remaining soybean extracting solvent no.6, restir 3-4 hour.