CN1884592A - Stepped quenching process and its apparatus suitable for bainite and martensite quenching - Google Patents
Stepped quenching process and its apparatus suitable for bainite and martensite quenching Download PDFInfo
- Publication number
- CN1884592A CN1884592A CN 200610089654 CN200610089654A CN1884592A CN 1884592 A CN1884592 A CN 1884592A CN 200610089654 CN200610089654 CN 200610089654 CN 200610089654 A CN200610089654 A CN 200610089654A CN 1884592 A CN1884592 A CN 1884592A
- Authority
- CN
- China
- Prior art keywords
- quenching
- nitrate
- groove
- bainite
- applicable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This invention involves a kind of step quenching process which is suitable for Bainitic and Martensite quenching and the equipment utilizing this step quenching process. The workflow includes: heating, quenching in low-temperature nitrate groove and isothermal; turn to oil grooves to cool down, wash and dry; turn to air furnace for isothermal temper. The above step quenching is performed in roller hearth furnace production line. After adjusting the technology parameter, this production line can undergo Bainitic step quenching and Martensite step quenching. This production line is composed mainly by roller hearth heating furnace, nitrate groove, oil groove, cleaner, dryer and temper furnace. This invention can improve the heat treatment quality; reduce the amount of nitrate and pollution. This production line can undergo normal Martensite quenching, Martensite step quenching and Bainitic step quenching, so to reduce investiment and increase the effeiciency.
Description
Technical field
The present invention relates to a kind of heat-treatment technology method, the especially a kind of stepped quenching process of bainite and marquench and equipment that is used for this stepped quenching process flow process of being applicable to belongs to metallic substance thermal treatment field.
Background technology
Metallic substance thermal treatment is the method that adopts heating and cooling, changes and improves the metallic substance performance, thereby improve the effective ways in its work-ing life.The metallic substance type of heat treatment is a lot, as, common marquench, martempering and bainitic hardening etc.Different quenching method will be equipped with different equipment, for example, the marquench operation generally is that part is heated in air-heating furnace, after part is heated to high temperature, quench cooled in oil groove or tank, obtain martensitic stucture, part is put into the tempering stove low-temperaturetempering again, China's past is adopted this kind technical process exactly to the thermal treatment of high-carbon-chromium bearing steel.This heat treating method technology is simple, and equipment falls behind, and quality is difficult for guaranteeing.After the nineties, China promotes the bainitic hardening technology of high-carbon-chromium bearing steel gradually.Because of bainite structure has better impelling strength and break resistance than martensitic stucture, can be widely used in rolling mill bearing, freight car bearing and automobile bearing etc.Bainitic hardening heating means and common marquench technical process are basic identical, but adopt different coolings and isothermal mode.Common marquench adopts oil cooling, and the cooling of bainitic hardening and isothermal carry out in nitrate solution, this kind method is that the part after the heating is directly quenched and isothermal in nitrate solution, the part easy deformation, all kinds of performance index of the bainite structure that is obtained are not ideal enough, simultaneously, its equipment simple pit furnace or box-type furnace heating and cooling and isothermals in the nitrate groove that opens wide of adopting more, pit furnace or box-type furnace equipment are outmoded, power consumption is serious, and nitrate solution is made up of Sodium Nitrite and saltpetre, therefore, currently used technical process exists more serious power consumption and problem of environmental pollution, can not adapt to the needs of production development; Simultaneously, different equipment is selected in different technical process for use, is unfavorable for the upgrading of renewal and renovation of equipment and equipment.
After the eighties, China is gradually from the external Equipment for Heating Processing of introducing a large amount of advanced persons, like that from Australia the roller bottom type that woods electric furnace company of association introduces is quenched, backfire product line as Wafagndian Bearing Factory and Luoyang Beaving Factory, be subjected to very much the welcome of domestic each Bearing Factory, and on the basis of digesting and assimilating, obtained popularization to a certain degree.But this equipment also is only limited to common martensite oil quenching, temper.Also have a kind of body turning style bainitic hardening production line, but also only limit to austempering, can not carry out marquench, therefore, also there is the problem of function singleness in present employed advanced heat-treatment production line.
Summary of the invention
The objective of the invention is to solve the existing quality of traditional thermal treatment process and be difficult for assurance, equipment power consumption greatly, waste is big, serious and the production line of environmental pollution uses and problem such as is limited to, and a kind of stepped quenching process method and automated production equipment thereof that is applicable to bainite and marquench is provided.
A kind of stepped quenching process that is applicable to bainite and marquench of the present invention, its technical process may further comprise the steps:
A. heating: heat-treatment part is heated to 820 ℃～880 ℃;
B. quench: the part after will heating is put into the low temperature nitrate groove rapidly and is quenched and isothermal, and the quenching temperature in nitrate groove is 160 ℃～240 ℃;
C. cooling: change the part behind the nitrate quenching in the oil groove cooling or air-cooled back water-cooled;
D. clean: cooled part is put into warm water tank clean;
E. tempering: the part after will cleaning changes isothermal tempering in the air furnace over to.
Wherein, in the described quenching step, the isothermal time of part in nitrate groove is 5～90 minutes.
In the cleaning step, the cleaning temperature of part in warm water tank is 50 ℃～80 ℃.
In the tempering step, the isothermal tempering temperature of part in air furnace is 160 ℃～240 ℃, and soaking time is 3～6 hours.
The present invention also provides a kind of equipment that is applicable to martensite and bainite marquenching, this equipment is that roller bottom type is used production line more, by the adjusting process parameter, can on this production line, carry out bainite marquenching and martempering, this production line is made of major equipments such as roller hearth type heating furnace, nitrate groove, oil groove, cleaning machine, dryer and tempering stoves, its transmission mechanism is a roller bar type transmission mechanism, wherein, nitrate groove is installed between process furnace and the oil groove, is provided with the lift quenching frame of band roller rod more than in the nitrate groove.
The stepped quenching process that is applicable to marquench and bainitic hardening provided by the present invention changes common marquench technology into martempering technology, is about to oil quenching and changes salt made from earth containing a comparatively high percentage of sodium chloride and the quenching of oily two-stage into; Change original bainite isothermal quenching technique into the bainite stepped quenching process, former useful nitrate groove isothermal is changed into use the air tempering furnace isothermal.The improvement of processing method has improved the thermal treatment quality of product, and the unanimity of technical process simultaneously also provides condition for the improvement of equipment.Therefore, aspect quenching apparatus, stove production line at the bottom of the existing roller is improved, make it can finish common marquench, martempering and bainite stepped quenching process.
Beneficial effect of the present invention is:
1. stepped quenching process of the present invention can guarantee surface hardness, the toughness reguirements of part, is out of shape for a short time, has improved the thermal treatment quality of part;
2. stepped quenching process flow process of the present invention is applicable to martempering and bainite marquenching, and technical process consistent reduced numerous and diverse on the heat treatment operation, simultaneously for equipment select for use and improvement provides condition;
3. austempering is improved to bainite marquenching of the present invention, it is fast to adopt hot nitrate quenching to have speed of cooling, the through hardening performance is good, characteristics such as each surface hardness of part is even, simultaneously former useful nitrate groove isothermal is changed into and use the air tempering furnace isothermal, reduce the salt made from earth containing a comparatively high percentage of sodium chloride usage quantity, reduced and pollute, improved production environment;
4. the improvement of stove production unit at the bottom of the pair roller, not only make bainite marquenching flow process realize automated operation, realized the multifunction of production line simultaneously, on a production line, can carry out common marquench, martempering and bainite marquenching respectively, reduce the investment of equipment, improved Working environment, improved working efficiency.
Description of drawings
Fig. 1 is the synoptic diagram that roller bottom type is used production line more among the present invention.
Fig. 2 is the enlarged view of A part among Fig. 1.
Fig. 3 is the enlarged view of B part among Fig. 1.
Among the figure: 1. roller hearth type heating furnace, 2. nitrate groove, 3. oil groove, 4. cleaning machine, 5. dryer, 6. tempering stove, 7. material platform, 8. air-exchanging chamber, 9. fog exhaust pipe, 10. quenching frame, 11. high pressure positive blower devices, 12. secondary feeders, 13. air-cooled, 14. discharging platforms.
Embodiment
The marquenching that is applicable to marquench and bainitic hardening of the present invention is carried out on production line in that roller bottom type shown in Figure 1 is many, referring to figs. 1 to Fig. 3, this production line is made of major equipments such as roller hearth type heating furnace 1, nitrate groove 2, oil groove 3, cleaning machine 4, dryer 5 and tempering stoves 6, its transmission mechanism is a roller bar type transmission mechanism, wherein, nitrate groove 2 is installed between roller hearth type heating furnace 1 and the oil groove 3, is provided with the lift quenching frame 10 of band roller rod more than in the nitrate groove 2.
Embodiment 1:
Present embodiment is a kind of bainite stepped quenching process, and whole technological process is carried out on production line in that roller bottom type shown in Figure 1 is many.Its technical process may further comprise the steps:
A. heat-treatment part is piled up on material platform 7, by roller bar type transmission mechanism part is sent in the roller hearth type heating furnace 1, this roller hearth type heating furnace 1 is the controllable atmosphere of nitrogen protection, and Heating temperature is 860 ℃～870 ℃, according to number of spare parts and size, soaking time is 0.5～3 hour;
B. the part after will heating is sent from the back door of roller hearth type heating furnace 1, puts into rapidly on the lift quenching frame 10 of nitrate groove 2 band roller rods, quenches and isothermal, and the quenching temperature in the nitrate groove is 220 ℃～240 ℃, and soaking time is 0.5～1.5 hour;
In the present embodiment, 4 stations are set in the nitrate groove 2, each station is respectively equipped with the lift quenching frame 10 of band roller rod, and each frame that quenches is installed in respectively on the bracing frame of nitrate groove top.One side of each frame that quenches is equipped with gear and tooth bar respectively, by being connected of gear and tooth bar driving the lifting in nitrate groove 2 of quenching frame 10.Also can between each lift quenching frame and bracing frame, install pneumatics, drive the lifting in nitrate groove of quenching frame by pneumatics.
Part moves forward by the roller rod on quenching frame 10, and isothermal rises to nitrate groove 2 tops and is sent to oil groove 3 tops by club to setting-up time.
C. part is put into oil groove 3 coolings rapidly;
D. the part behind the oil cooling is sent to and sends into drying shed 5 oven dry in the cleaning machine 4 after the cleaning, the temperature of warm water is 60 ℃～80 ℃ in the cleaning machine;
E. the part that will clean and dry changes isothermal tempering in the air furnace 6 over to by secondary feeder 12, and this tempering stove 6 is the double layer roller bottom type tempering stove, and tempering temperature is 220 ℃～240 ℃, and soaking time is 3～6 hours.
F. the part after the isothermal tempering is sent tempering stove 6 by roller bar type transport unit, is sent to discharging platform 14 after air-cooled through air-cooled 13, and whole process flow is finished.
Embodiment 2:
Present embodiment is a kind of martempering technology, and its technical process is with embodiment 1, and concrete processing parameter is: among the step a, the Heating temperature of heat-treatment part in roller hearth type heating furnace 1 is 820 ℃～860 ℃; Among the step b, the quenching temperature of part in nitrate groove 2 is 160 ℃～170 ℃ C, is incubated 5-10 minute; Among the step e, change the part after oil cooling and the cleaning in the air furnace 6 isothermal tempering, tempering temperature is 160 ℃～200 ℃, and soaking time is 3～5 hours.
Roller bottom type of the present invention is used in the apparatus for production line more, between oil groove 3 and cleaning machine 4, can install a high pressure positive blower device 11, for some part, can after nitrate groove quenches, not adopt in the oil groove and cool off, cool off and after high pressure positive blower device 11 is air-cooled, directly put into water.
The present invention is by the improvement to original marquench and bainitic hardening technical process, the roller bottom type that adopts advanced, automatization how with quench, backfire product line, by the thermal treatment process flow process of high-carbon-chromium bearing steel Gr15 and Gr18M being carried out test repeatedly, and its mechanical property contrasted, satisfy processing requirement fully.Simultaneously, by to roller bottom type many with quench, the improvement of backfire product line equipment, make on the production line and can carry out three kinds of thermal treatment process flow processs, comprise common marquench, martempering, bainite marquenching.Whole production line is controlled automatically by robot calculator, the controllable atmosphere of nitrogen protection, and advanced technology, device structure is reasonable, and production line is controlled by different technical process, and production process is automatically carried out.
Claims (9)
1, a kind of stepped quenching process that is applicable to bainite and marquench, it is characterized in that: described technical process may further comprise the steps:
A. heating: heat-treatment part is heated to 820 ℃～880 ℃;
B. quench: the part after will heating is put into the low temperature nitrate groove rapidly and is quenched and isothermal, and the quenching temperature in nitrate groove is 160 ℃～240 ℃;
C. cooling: change the part behind the nitrate quenching in the oil groove cooling or air-cooled back water-cooled;
D. clean: cooled part is put into warm water tank clean;
E. tempering: the part after will cleaning changes isothermal tempering in the air furnace over to.
2, a kind of stepped quenching process that is applicable to bainitic hardening or marquench according to claim 1 is characterized in that: in the described quenching step, the isothermal time of part in nitrate groove is 5～90 minutes.
3, a kind of stepped quenching process that is applicable to bainitic hardening or marquench according to claim 1 is characterized in that: in the described cleaning step, the cleaning temperature of part in warm water tank is 50 ℃～80 ℃.
4, a kind of stepped quenching process that is applicable to bainitic hardening or marquench according to claim 1 is characterized in that: in the described tempering step, the isothermal tempering temperature of part in air furnace is 160 ℃～240 ℃, and soaking time is 3～6 hours.
5, a kind of equipment that is applicable to bainite marquenching or martempering as claimed in claim 1, it is characterized in that: this equipment is that roller bottom type is used production line more, by the adjusting process parameter, can on this production line, carry out bainite marquenching and martempering, this production line is by roller hearth type heating furnace, nitrate groove, oil groove, cleaning machine, major equipment such as dryer and tempering stove constitutes, its transmission mechanism is a roller bar type transmission mechanism, wherein, nitrate groove is installed between process furnace and the oil groove, is provided with the lift quenching frame of band roller rod more than in the nitrate groove.
6, a kind of equipment that is applicable to bainite marquenching or martempering according to claim 5, it is characterized in that: 4 stations are set in the described nitrate groove, each station is respectively equipped with the lift quenching frame of band roller rod, and each frame that quenches is installed in respectively on the bracing frame of nitrate groove top.
7, a kind of equipment that is applicable to bainite marquenching or martempering according to claim 6, it is characterized in that: a side of the described frame that respectively quenches is equipped with gear and tooth bar respectively, by being connected of gear and tooth bar driving the lifting in nitrate groove of quenching frame.
8, a kind of equipment that is applicable to bainite marquenching or martempering according to claim 6, it is characterized in that: described respectively the quenching is equipped with pneumatics between frame and the bracing frame, drives the lifting in nitrate groove of quenching frame by pneumatics.
9, a kind of equipment that is applicable to bainite marquenching or martempering according to claim 5 is characterized in that: be equiped with the high pressure positive blower device between oil groove and cleaning machine.