CN1876914A - Manufacturing method for fabric capable of regulating temperature - Google Patents
Manufacturing method for fabric capable of regulating temperature Download PDFInfo
- Publication number
- CN1876914A CN1876914A CN200610089331.2A CN200610089331A CN1876914A CN 1876914 A CN1876914 A CN 1876914A CN 200610089331 A CN200610089331 A CN 200610089331A CN 1876914 A CN1876914 A CN 1876914A
- Authority
- CN
- China
- Prior art keywords
- lining
- water
- add
- temperature
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A method for preparation of face fabric with adjustable temperature is finished by three-channel procedures including weaving blended yarn containing Outlast air-handling fiber and blended yarn woven face fabric and dye-bleaching of face fabric. The invention adopts Outlast air-handling fiber to perform mixed spun with other fibers and they are woven to face fabric, which has flexible and comfortable hand feeling, and not only has the amenity of the cotton but also keeps the absorption and diffusion function of the Outlast air-handling fiber to the temperature, which makes the human body always in a soft and comfortable state.
Description
Technical field
The present invention relates to the manufacture method of underwear fabric, relate in particular to a kind of manufacture method that can regulate the lining of temperature.
Background technology
The current lining of making underwear on the market adopts materials such as gum sprayed cotton wadding material, no collodion flocculus, doughnut material, space wadding (claiming metal wool again), real silk silk floss, silkworm velvet more, it is too fat to move that these materials all exist outward appearance, sultry airtight, wear uncomfortable problem.
Summary of the invention
Technical problem to be solved by this invention provides the comfortableness of a kind of existing cotton, can play thermal effect again, can also be adjusted to the manufacture method of the lining of human comfort temperature to it according to variation of ambient temperature.
For solving the problems of the technologies described above, the present invention adopts following technical proposals: a kind of manufacture method that can regulate the lining of temperature, and it is that process is weaved blended yarn, blended yarn braiding lining, the three process of bleachinging and dyeing of lining is finished.
Details are as follows for three process:
A. weave blended yarn
The Outlast air-conditioning fiber of weight ratio 40-80% and other fibers of weight ratio 60-20% are carried out blending, make blended yarn.Described Outlast air-conditioning fiber is a kind of polypropylene acrylic fibers fiber with thermal conditioning function, uses the covert material of temperature-sensitive of microcapsules parcel in the fiber, and this material has and can absorb the function of storage and release heat with the form of latent heat.It can solid-state liquid state transform in variations in temperature mutually, therefrom reaches the effect of heat absorption, heat release.
Described other fiber is cotton or Mo Daier, and described Mo Daier is the environment-friendly type regeneration cellulose fibre.
Described blended yarn adopts and closely spins, and twist factor is 310-360.
B. blended yarn weaves lining
Use this blended yarn to be woven into the lining of reversible cloth, the grammes per square metre of lining is at 220-300g/m
2Between, the Outlast fiber will be knitted the side in direct and contact skin.
Described reversible cloth lining is that lining is organized in rib stitch, interlock or two-sided covering.
C. lining bleachinges and dyeing
The technological process of dyeing goes on foot and to form by floating the end, vital staining, acid dyeing, softness and drying five.
Concrete technological process is:
1. float at the end
At first, select to float end raw material, the described end raw material that floats that floats in the bottom technique flow process is compared with the weight of lining, and its percentage is respectively:
Penetrant m SK:0.3-0.5%;
Alkalescent agent 197:1.8-2.2%;
Chelating agent: 0.3-0.7%;
Hydrogen peroxide: 3-5%;
The weight ratio of lining and water is: 1: 10-12;
Secondly, it is as follows that it floats end process, in floating end container, the water and the water temperature that add 10-12 times of lining weight are 18-20 ℃, add lining then, then add 0.3-0.5% penetrant m SK and 0.3-0.7% chelating agent, add 1.8-2.2% weak base agent 197 again, the maintenance pH value is 9-10, rinsing 15-25 minute, with per minute 1-2 ℃ temperature speed water temperature progressively is heated to 96-98 ℃, stop the heating to water, put into the 3-5% hydrogen peroxide, keeping the time of water temperature is 55-65 minute, to float end liquid and drain, the water cleaning that adds 10-12 times of lining weight again after 10-20 minute is taken out lining stand-by;
2. vital staining
At first, select the vital staining raw material, the dyeing raw material in the described vital staining technological process is compared with the weight of floating the lining behind the end, and its percentage is respectively:
The red 3BS of Remazol (CIBA): 0.22-0.26%;
Yellow 3RS (CIBA): the 0.05-0.09% of Remazol;
Active blue FBN (light forever): 0.093-0.097%;
Soda ash: 10-14%;
Glauber salt: 30-50%;
Float that the weight ratio of lining and water is behind the end: 1: 10-12;
Secondly, its vital staining process is as follows, in the vital staining container, water and water temperature that adding 10-12 doubly floats the lining weight at the end are 18-20 ℃, add then and float lining at the end, then add the red 3BS of 0.22-0.26% Remazol, yellow 3RS of 0.05-0.09% Remazol and the active blue FBN of 0.093-0.097%, putting into the 30-50% glauber salt soaked 35-45 minute, with per minute 1-2 ℃ temperature speed water temperature progressively is heated to 55-65 ℃, add 10-14% soda ash again, the maintenance pH value is 9-10, keeping the time of water temperature is 55-65 minute, stops the heating to water, when treating that water temperature is reduced to 35-45 ℃, vital staining liquid is drained, add again water that 10-12 doubly floats the lining weight behind the end clean after 10-20 minute lining is taken out stand-by;
3. acid dyeing
At first, select the acid dyeing raw material, the weight of the lining behind the dyeing raw material in the described acid dyeing technological process and the vital staining is compared, and its percentage is respectively:
Polar yellow GN:0.0064-0.0068%;
The red B:0.03-0.07% in pula;
The blue R:0.034-0.038% in pula;
Acetic acid HAC:2-4%;
The weight ratio of lining and water is behind the vital staining: 1: 10-12;
Secondly, its acid dyeing process is as follows, in the acid dyeing container, the water and the water temperature that add the weight of the lining behind the 10-12 times of vital staining are 18-20 ℃, add lining behind the vital staining then, then add 0.0064-0.0068% polar yellow GN, the blue R in red B in 0.03-0.07% pula and 0.034-0.038% pula, soaked 15-25 minute, add 2-4% acetic acid HAC again, the maintenance pH value is 6-6.2, with per minute 1-2 ℃ temperature speed water temperature progressively is heated to 96-98 ℃, keeping the time of water temperature is 25-35 minute, stop the heating to water, acid dyeing liquid is drained, the water cleaning that adds the 10-12 times of lining weight behind the vital staining again after 10-20 minute is taken out lining stand-by;
4. soft
At first, select softener, the weight of the lining after the softener in the described soft technological process and the acid dyeing is compared, and its percentage is respectively:
Increase bullet softener: 2.2-2.7%;
The weight ratio of lining and water is after the acid dyeing: 1: 10-12;
Secondly, its soft process is as follows, in container, the water and the water temperature that add the weight of the lining after the 10-12 times of acid dyeing are 18-20 ℃, add lining after the acid dyeing then, water temperature progressively is heated to 35-40 ℃, add 2.2-2.7% again and increase the bullet softener with per minute 1-2 ℃ temperature, the maintenance pH value is 6.4-6.6, keeping the time of water temperature is 15-25 minute, stops the heating to water, soaks 5-10 minute, lining after the softness is taken out the dehydration of carrying out 8-10 minute, take out stand-by then;
5. oven dry
Lining after the softness is put into the oscillatory type dryer, and the temperature of dryer is controlled at 90-95 ℃,
The speed of a motor vehicle be adjusted into 8-10 rice/minute, both finished the overall process of bleachinging and dyeing of lining.
The present invention has adopted Outlast air-conditioning fiber and other fiber to carry out blending, and be woven into lining, and soft, comfortable, the comfortableness of existing cotton, kept of the effect of Outlast air-conditioning fiber again, made human body be in a kind of cosy state all the time temperature absorption or diffusion diffusion.
The specific embodiment
Embodiment 1
A kind of manufacture method that can regulate the lining of temperature, it is that process is weaved blended yarn, blended yarn braiding lining, the three process of bleachinging and dyeing of lining is finished.
Details are as follows for three process:
A. weave blended yarn
The Outlast air-conditioning fiber of weight ratio 40% and other fibers of weight ratio 60% are carried out blending, make blended yarn;
Described other fiber is cotton;
Described blended yarn adopts and closely spins, and twist factor is 310;
B. blended yarn weaves lining
Use this blended yarn to be woven into the lining of reversible cloth, the grammes per square metre of lining is at 220g/m
2, the Outlast fiber will be knitted the side in direct and contact skin;
Described reversible cloth lining is the rib stitch lining;
C. lining bleachinges and dyeing
The technological process of dyeing goes on foot and to form by floating the end, vital staining, acid dyeing, softness and drying five.
Concrete technological process is:
1. float at the end
At first, select to float end raw material, the described end raw material that floats that floats in the bottom technique flow process is compared with the weight of lining, and its percentage is respectively:
Penetrant m SK:0.3%;
Alkalescent agent 197:1.8%;
Chelating agent: 0.3%;
Hydrogen peroxide: 3%;
The weight ratio of lining and water is: 1: 10;
Secondly, it is as follows that it floats end process, in floating end container, the water and the water temperature that add 10 times of lining weight are 18 ℃, add lining then, then add 0.3% penetrant m SK and 0.3% chelating agent, add 1.8% weak base agent 197 again, keeping pH value is 9, rinsing 15 minutes, temperature speed with 1 ℃ of per minute progressively is heated to 96 ℃ with water temperature, stop the heating to water, put into 3% hydrogen peroxide, keeping the time of water temperature is 55 minutes, to float end liquid and drain, the water cleaning that adds 10 times of lining weight again after 10 minutes is taken out lining stand-by;
2. vital staining
At first, select the vital staining raw material, the dyeing raw material in the described vital staining technological process is compared with the weight of floating the lining behind the end, and its percentage is respectively:
The red 3BS of Remazol (CIBA): 0.22%;
The yellow 3RS (CIBA) of Remazol: 0.05%;
Active blue FBN (light forever): 0.093%;
Soda ash: 10%;
Glauber salt: 30%;
Float that the weight ratio of lining and water is behind the end: 1: 10;
Secondly, its vital staining process is as follows, in the vital staining container, adding 10 times of water and water temperatures of floating the lining weight behind the end is 18 ℃, add then and float lining at the end, then add the red 3BS of 0.22% Remazol, yellow 3RS of 0.05% Remazol and 0.093% active blue FBN, put into 30% glauber salt and soaked 35 minutes, water temperature progressively is heated to 55 ℃, add 10% soda ash again with the temperature speed of 1 ℃ of per minute, keeping pH value is 9, keeping the time of water temperature is 55 minutes, stops the heating to water, when treating that water temperature is reduced to 35 ℃, vital staining liquid is drained, add again 10 times of water that float the lining weight behind the end clean after 10 minutes lining is taken out stand-by;
3. acid dyeing
At first, select the acid dyeing raw material, the weight of the lining behind the dyeing raw material in the described acid dyeing technological process and the vital staining is compared, and its percentage is respectively:
Polar yellow GN:0.0064%;
The red B:0.03% in pula;
The blue R:0.034% in pula;
Acetic acid HAC:2%;
The weight ratio of lining and water is behind the vital staining: 1: 10;
Secondly, its acid dyeing process is as follows, in the acid dyeing container, the water and the water temperature that add the weight of the lining behind 10 times of vital stainings are 18 ℃, add lining behind the vital staining then, then add 0.0064% polar yellow GN, the blue R in red B in 0.03% pula and 0.034% pula, soaked 15 minutes, add 2% acetic acid HAC again, keeping pH value is 6, with the temperature speed of 1 ℃ of per minute water temperature progressively is heated to 96 ℃, keeping the time of water temperature is 25 minutes, stop the heating to water, acid dyeing liquid is drained, the water cleaning that adds 10 times of lining weight behind the vital staining again after 10 minutes is taken out lining stand-by;
4. soft
At first, select softener, the weight of the lining after the softener in the described soft technological process and the acid dyeing is compared, and its percentage is respectively:
Increase the bullet softener: 2.2%;
The weight ratio of lining and water is after the acid dyeing: 1: 10;
Secondly, its soft process is as follows, in container, the water and the water temperature that add the weight of the lining after 10 times of acid dyeings are 18 ℃, add lining after the acid dyeing then, water temperature progressively is heated to 35 ℃, add 2.2% again and increase the bullet softener with the temperature of 1 ℃ of per minute, keeping pH value is 6.4, keeping the time of water temperature is 15 minutes, stops the heating to water, soaks 5 minutes, lining after the softness is taken out the dehydration of carrying out 8 minutes, take out stand-by then;
5. oven dry
Lining after the softness is put into the oscillatory type dryer, and the temperature of dryer is controlled at 90 ℃, and the speed of a motor vehicle is adjusted into 8 meters/minute, has both finished the overall process of bleachinging and dyeing of lining.
Embodiment 2
A kind of manufacture method that can regulate the lining of temperature, it is that process is weaved blended yarn, blended yarn braiding lining, the three process of bleachinging and dyeing of lining is finished.
Details are as follows for three process:
A. weave blended yarn
The Outlast air-conditioning fiber of weight ratio 80% and other fibers of weight ratio 20% are carried out blending, make blended yarn;
Described other fiber is Mo Daier;
Described blended yarn adopts and closely spins, and twist factor is 360;
B. blended yarn weaves lining
Use this blended yarn to be woven into the lining of reversible cloth, the grammes per square metre of lining is at 300g/m
2, the Outlast fiber will be knitted the side in direct and contact skin;
Described reversible cloth lining is the interlock lining;
C. lining bleachinges and dyeing
The technological process of dyeing goes on foot and to form by floating the end, vital staining, acid dyeing, softness and drying five.
Concrete technological process is:
1. float at the end
At first, select to float end raw material, the described end raw material that floats that floats in the bottom technique flow process is compared with the weight of lining, and its percentage is respectively:
Penetrant m SK:0.5%;
Alkalescent agent 197:2.2%;
Chelating agent: 0.7%;
Hydrogen peroxide: 5%;
The weight ratio of lining and water is: 1: 12;
Secondly, it is as follows that it floats end process, in floating end container, the water and the water temperature that add 12 times of lining weight are 20 ℃, add lining then, then add 0.5% penetrant m SK and 0.7% chelating agent, add 2.2% weak base agent 197 again, keeping pH value is 10, rinsing 25 minutes, temperature speed with 2 ℃ of per minutes progressively is heated to 98 ℃ with water temperature, stop the heating to water, put into 5% hydrogen peroxide, keeping the time of water temperature is 65 minutes, to float end liquid and drain, the water cleaning that adds 12 times of lining weight again after 20 minutes is taken out lining stand-by;
2. vital staining
At first, select the vital staining raw material, the dyeing raw material in the described vital staining technological process is compared with the weight of floating the lining behind the end, and its percentage is respectively:
The red 3BS of Remazol (CIBA): 0.26%;
The yellow 3RS (CIBA) of Remazol: 0.09%;
Active blue FBN (light forever): 0.097%;
Soda ash: 14%;
Glauber salt: 50%;
Float that the weight ratio of lining and water is behind the end: 1: 12;
Secondly, its vital staining process is as follows, in the vital staining container, adding 12 times of water and water temperatures of floating the lining weight behind the end is 20 ℃, add then and float lining at the end, then add the red 3BS of 0.26% Remazol, yellow 3RS of 0.09% Remazol and 0.097% active blue FBN, put into 50% glauber salt and soaked 45 minutes, water temperature progressively is heated to 65 ℃, add 14% soda ash again with the temperature speed of 2 ℃ of per minutes, keeping pH value is 10, keeping the time of water temperature is 65 minutes, stops the heating to water, when treating that water temperature is reduced to 45 ℃, vital staining liquid is drained, add again 12 times of water that float the lining weight behind the end clean after 20 minutes lining is taken out stand-by;
3. acid dyeing
At first, select the acid dyeing raw material, the weight of the lining behind the dyeing raw material in the described acid dyeing technological process and the vital staining is compared, and its percentage is respectively:
Polar yellow GN:0.0068%;
The red B:0.07% in pula;
The blue R:0.038% in pula;
Acetic acid HAC:4%;
The weight ratio of lining and water is behind the vital staining: 1: 12;
Secondly, its acid dyeing process is as follows, in the acid dyeing container, the water and the water temperature that add the weight of the lining behind 12 times of vital stainings are 20 ℃, add lining behind the vital staining then, then add 0.0068% polar yellow GN, the blue R in red B in 0.07% pula and 0.038% pula, soaked 25 minutes, add 4% acetic acid HAC again, keeping pH value is 6.2, with the temperature speed of 2 ℃ of per minutes water temperature progressively is heated to 98 ℃, keeping the time of water temperature is 35 minutes, stop the heating to water, acid dyeing liquid is drained, the water cleaning that adds 12 times of lining weight behind the vital staining again after 20 minutes is taken out lining stand-by;
4. soft
At first, select softener, the weight of the lining after the softener in the described soft technological process and the acid dyeing is compared, and its percentage is respectively:
Increase the bullet softener: 2.7%;
The weight ratio of lining and water is after the acid dyeing: 1: 12;
Secondly, its soft process is as follows, in container, the water and the water temperature that add the weight of the lining after 12 times of acid dyeings are 20 ℃, add lining after the acid dyeing then, water temperature progressively is heated to 40 ℃, add 2.7% again and increase the bullet softener with the temperature speed of 2 ℃ of per minutes, keeping pH value is 6.6, keeping the time of water temperature is 25 minutes, stops the heating to water, soaks 10 minutes, lining after the softness is taken out the dehydration of carrying out 10 minutes, take out stand-by then;
5. oven dry
Lining after the softness is put into the oscillatory type dryer, and the temperature of dryer is controlled at 95 ℃, and the speed of a motor vehicle is adjusted into 10 meters/minute, has both finished the overall process of bleachinging and dyeing of lining.
Embodiment 3
A kind of manufacture method that can regulate the lining of temperature, it is that process is weaved blended yarn, blended yarn braiding lining, the three process of bleachinging and dyeing of lining is finished.
Details are as follows for three process:
A. weave blended yarn
The Outlast air-conditioning fiber of weight ratio 60% and other fibers of weight ratio 40% are carried out blending, make blended yarn;
Described other fiber is cotton;
Described blended yarn adopts and closely spins, and twist factor is 335;
B. blended yarn weaves lining
Use this blended yarn to be woven into the lining of reversible cloth, the grammes per square metre of lining is at 260g/m
2, the Outlast fiber will be knitted the side in direct and contact skin;
Described reversible cloth lining is that lining is organized in two-sided covering;
C. lining bleachinges and dyeing
The technological process of dyeing goes on foot and to form by floating the end, vital staining, acid dyeing, softness and drying five.
Concrete technological process is:
1. float at the end
At first, select to float end raw material, the described end raw material that floats that floats in the bottom technique flow process is compared with the weight of lining, and its percentage is respectively:
Penetrant m SK:0.4%;
Alkalescent agent 197:2%;
Chelating agent: 0.5%;
Hydrogen peroxide: 4%;
The weight ratio of lining and water is: 1: 11;
Secondly, it is as follows that it floats end process, in floating end container, the water and the water temperature that add 11 times of lining weight are 19 ℃, add lining then, then add 0.4% penetrant m SK and 0.5% chelating agent, add 2% weak base agent 197 again, keeping pH value is 9.5, rinsing 20 minutes, temperature speed with 1.5 ℃ of per minutes progressively is heated to 97 ℃ with water temperature, stop the heating to water, put into 4% hydrogen peroxide, keeping the time of water temperature is 60 minutes, to float end liquid and drain, the water cleaning that adds 11 times of lining weight again after 15 minutes is taken out lining stand-by;
2. vital staining
At first, select the vital staining raw material, the dyeing raw material in the described vital staining technological process is compared with the weight of floating the lining behind the end, and its percentage is respectively:
The red 3BS of Remazol (CIBA): 0.24%;
The yellow 3RS (CIBA) of Remazol: 0.07%;
Active blue FBN (light forever): 0.095%;
Soda ash: 12%;
Glauber salt: 40%;
Float that the weight ratio of lining and water is behind the end: 1: 11;
Secondly, its vital staining process is as follows, in the vital staining container, adding 11 times of water and water temperatures of floating the lining weight behind the end is 19 ℃, add then and float lining at the end, then add the red 3BS of 0.24% Remazol, yellow 3RS of 0.07% Remazol and 0.095% active blue FBN, put into 40% glauber salt and soaked 40 minutes, water temperature progressively is heated to 60 ℃, add 12% soda ash again with the temperature speed of 1.5 ℃ of per minutes, keeping pH value is 9.5, keeping the time of water temperature is 60 minutes, stops the heating to water, when treating that water temperature is reduced to 40 ℃, vital staining liquid is drained, add again 11 times of water that float the lining weight behind the end clean after 15 minutes lining is taken out stand-by;
3. acid dyeing
At first, select the acid dyeing raw material, the weight of the lining behind the dyeing raw material in the described acid dyeing technological process and the vital staining is compared, and its percentage is respectively:
Polar yellow GN:0.0066%;
The red B:0.05% in pula;
The blue R:0.036% in pula;
Acetic acid HAC:3%;
The weight ratio of lining and water is behind the vital staining: 1: 11;
Secondly, its acid dyeing process is as follows, in the acid dyeing container, the water and the water temperature that add the weight of the lining behind 11 times of vital stainings are 19 ℃, add lining behind the vital staining then, then add 0.0066% polar yellow GN, the blue R in red B in 0.05% pula and 0.036% pula, soaked 20 minutes, add 3% acetic acid HAC again, keeping pH value is 6.1, with the temperature speed of 1.5 ℃ of per minutes water temperature progressively is heated to 97 ℃, keeping the time of water temperature is 30 minutes, stop the heating to water, acid dyeing liquid is drained, the water cleaning that adds 11 times of lining weight behind the vital staining again after 15 minutes is taken out lining stand-by;
4. soft
At first, select softener, the weight of the lining after the softener in the described soft technological process and the acid dyeing is compared, and its percentage is respectively:
Increase the bullet softener: 2.5%;
The weight ratio of lining and water is after the acid dyeing: 1: 11;
Secondly, its soft process is as follows, in container, the water and the water temperature that add the weight of the lining after 11 times of acid dyeings are 19 ℃, add lining after the acid dyeing then, water temperature progressively is heated to 37 ℃, add 2.5% again and increase the bullet softener with the temperature of 1.5 ℃ of per minutes, keeping pH value is 6.5, keeping the time of water temperature is 20 minutes, stops the heating to water, soaks 7 minutes, lining after the softness is taken out the dehydration of carrying out 9 minutes, take out stand-by then;
5. oven dry
Lining after the softness is put into the oscillatory type dryer, and the temperature of dryer is controlled at 93 ℃, and the speed of a motor vehicle is adjusted into 9 meters/minute, has both finished the overall process of bleachinging and dyeing of lining.
Claims (8)
1, a kind of manufacture method that can regulate the lining of temperature, it comprises weaves blended yarn, blended yarn braiding lining, lining bleaching and dyeing three process, it is characterized in that: details are as follows for three process:
A. weave blended yarn
The Outlast air-conditioning fiber of weight ratio 40-80% and other fibers of weight ratio 60-20% are carried out blending, make blended yarn;
B. blended yarn weaves lining
Use this blended yarn to be woven into the lining of reversible cloth, the grammes per square metre of lining is at 220-300g/m
2Between, the Outlast fiber will be knitted the side in direct and contact skin;
C. lining bleachinges and dyeing
The technological process of dyeing goes on foot and to form by floating the end, vital staining, acid dyeing, softness and drying five.
2, a kind of manufacture method that can regulate the lining of temperature according to claim 1, it is characterized in that: described other fiber is cotton or Mo Daier, and described blended yarn adopts and closely spins, and twist factor is 310-360.
3, a kind of manufacture method that can regulate the lining of temperature according to claim 1 is characterized in that: the reversible cloth lining is that rib stitch, interlock, two-sided covering are organized lining.
4, a kind of manufacture method that can regulate the lining of temperature according to claim 1, it is characterized in that: the described end process of floating is: at first, end raw material is floated in selection, and the described end raw material that floats that floats in the bottom technique flow process is compared with the weight of lining, and its percentage is respectively:
Penetrant m SK:0.3-0.5%;
Alkalescent agent 197:1.8-2.2%;
Chelating agent: 0.3-0.7%;
Hydrogen peroxide: 3-5%;
The weight ratio of lining and water is: 1: 10-12;
Secondly, it is as follows that it floats end process, in floating end container, the water and the water temperature that add 10-12 times of lining weight are 18-20 ℃, add lining then, then add 0.3-0.5% penetrant m SK and 0.3-0.7% chelating agent, add 1.8-2.2% weak base agent 197 again, the maintenance pH value is 9-10, rinsing 15-25 minute, with per minute 1-2 ℃ temperature speed water temperature progressively is heated to 96-98 ℃, stop the heating to water, put into the 3-5% hydrogen peroxide, keeping the time of water temperature is 55-65 minute, to float end liquid and drain, the water cleaning that adds 10-12 times of lining weight again after 10-20 minute is taken out lining stand-by.
5, a kind of manufacture method that can regulate the lining of temperature according to claim 1, it is characterized in that: described vital staining process is: at first, select the vital staining raw material, dyeing raw material in the described vital staining technological process is compared with the weight of floating the lining behind the end, and its percentage is respectively:
The red 3BS of Remazol (CIBA): 0.22-0.26%;
Yellow 3RS (CIBA): the 0.05-0.09% of Remazol;
Active blue FBN (light forever): 0.093-0.097%;
Soda ash: 10-14%;
Glauber salt: 30-50%;
Float that the weight ratio of lining and water is behind the end: 1: 10-12;
Secondly, its vital staining process is as follows, in the vital staining container, water and water temperature that adding 10-12 doubly floats the lining weight at the end are 18-20 ℃, add then and float lining at the end, then add the red 3BS of 0.22-0.26% Remazol, yellow 3RS of 0.05-0.09% Remazol and the active blue FBN of 0.093-0.097%, putting into the 30-50% glauber salt soaked 35-45 minute, with per minute 1-2 ℃ temperature speed water temperature progressively is heated to 55-65 ℃, add 10-14% soda ash again, the maintenance pH value is 9-10, keeping the time of water temperature is 55-65 minute, stops the heating to water, when treating that water temperature is reduced to 35-45 ℃, vital staining liquid is drained, add again water that 10-12 doubly floats the lining weight behind the end clean after 10-20 minute lining is taken out stand-by.
6, a kind of manufacture method that can regulate the lining of temperature according to claim 1, it is characterized in that: described acid dyeing is floated end process and is: at first, select the acid dyeing raw material, the weight of the lining behind the dyeing raw material in the described acid dyeing technological process and the vital staining is compared, and its percentage is respectively:
Polar yellow GN:0.0064-0.0068%;
The red B:0.03-0.07% in pula;
The blue R:0.034-0.038% in pula;
Acetic acid HAC:2-4%;
The weight ratio of lining and water is behind the vital staining: 1: 10-12;
Secondly, its acid dyeing process is as follows, in the acid dyeing container, the water and the water temperature that add the weight of the lining behind the 10-12 times of vital staining are 18-20 ℃, add lining behind the vital staining then, then add 0.0064-0.0068% polar yellow GN, the blue R in red B in 0.03-0.07% pula and 0.034-0.038% pula, soaked 15-25 minute, add 2-4% acetic acid HAC again, the maintenance pH value is 6-6.2, with per minute 1-2 ℃ temperature speed water temperature progressively is heated to 96-98 ℃, keeping the time of water temperature is 25-35 minute, stop the heating to water, acid dyeing liquid is drained, the water cleaning that adds the 10-12 times of lining weight behind the vital staining again after 10-20 minute is taken out lining stand-by.
7, a kind of manufacture method that can regulate the lining of temperature according to claim 1, it is characterized in that: described soft process is: at first, select softener, the weight of the lining after the softener in the described soft technological process and the acid dyeing is compared, and its percentage is respectively:
Increase bullet softener: 2.2-2.7%;
The weight ratio of lining and water is after the acid dyeing: 1: 10-12;
Secondly, its soft process is as follows, in container, the water and the water temperature that add the weight of the lining after the 10-12 times of acid dyeing are 18-20 ℃, add lining after the acid dyeing then, water temperature progressively is heated to 35-40 ℃, add 2.2-2.7% again and increase the bullet softener with per minute 1-2 ℃ temperature, the maintenance pH value is 6.4-6.6, keeping the time of water temperature is 15-25 minute, stops the heating to water, soaks 5-10 minute, lining after the softness is taken out the dehydration of carrying out 8-10 minute, take out stand-by then.
8, a kind of manufacture method that can regulate the lining of temperature according to claim 1, it is characterized in that: described drying course is:
Lining after the softness is put into the oscillatory type dryer, and the temperature of dryer is controlled at 90-95 ℃, the speed of a motor vehicle be adjusted into 8-10 rice/minute, both finished the overall process of bleachinging and dyeing of lining.