CN1876364A - Stainless steel, aluminum composite honeycomb panel and processing method - Google Patents
Stainless steel, aluminum composite honeycomb panel and processing method Download PDFInfo
- Publication number
- CN1876364A CN1876364A CN 200510050025 CN200510050025A CN1876364A CN 1876364 A CN1876364 A CN 1876364A CN 200510050025 CN200510050025 CN 200510050025 CN 200510050025 A CN200510050025 A CN 200510050025A CN 1876364 A CN1876364 A CN 1876364A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- aluminium
- aluminum composite
- board
- honeycomb core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to stainless steel, aluminum -composite honeycombed sheet and preparing process, comprising upper board, lower board, and honeycomb core between upper and lower board. Said upper board and lower board is composite-layer of stainless steel and aluminum sheet, honeycomb core is composite -layer of stainless steel and aluminum sheet or composite -layer of aluminum board, stainless board and aluminum board. The upper and lower board and honeycomb core is composite two-layer or three-layer stainless steel and aluminum board, the honeycomb sheet is equipped with aluminum board and stainless board, and it is characterized by increased mechanical intensity, fire resistant of stainless board and smooth surface. The honeycomb core employs aluminum heating to soften braze welding, and the braze welding of upper and lower board and honeycomb core applies aluminum sheet to soften welding, and the connection is characterized by high intensity.
Description
Technical field
The present invention relates to cellular board, also relate to the processing method of cellular board simultaneously, be mainly used in the building inner, external wall art work and as the art work in the ship, in the automobile.
Background technology
The basic structure of cellular board is between plate and the lower panel honeycomb core to be arranged in the above, and existing cellular board can be divided into honeycomb card board, aluminum honeycomb panel by the manufactured materials difference.Honeycomb card board is mainly used in pallet, the packing of product, and its shortcoming is water funk, inflammable; Aluminum honeycomb panel is mainly used in building decoration, and as metope, ceiling etc., the major defect of its existence is that mechanical strength is lower, and fire resistance is relatively poor.And existing honeycomb card board and aluminum honeycomb panel be when making honeycomb core, glue bond on process, heats operations such as pressurization, cutting, stretching and make, and wherein gluing needs coating adhesive, causes environmental pollution.
Summary of the invention
The objective of the invention is provides a kind of mechanical strength height in order to overcome the shortcoming of prior art, and fire resistance is good, the stainless steel of good looking appearance, aluminum composite honeycomb panel.
Not gluing when another object of the present invention provides a kind of manufacturing honeycomb, the processing method of free of contamination stainless steel, aluminum composite honeycomb panel
The technical scheme of stainless steel of the present invention, aluminum composite honeycomb panel is: top panel, lower panel are arranged, honeycomb core is arranged between the upper and lower panel, it is characterized in that described top panel and lower panel are compound two-layer of corrosion resistant plate and aluminium sheet, honeycomb core is compound three layers of corrosion resistant plate and aluminium sheet compound two-layer or aluminium sheet, corrosion resistant plate, aluminium sheet.The stainless steel of the technical program, aluminum composite honeycomb panel, its upper and lower panel and honeycomb core are compound two-layer of corrosion resistant plate and aluminium sheet or three layers, aluminium sheet is not only arranged in cellular board, and corrosion resistant plate arranged again, compared with the prior art, the one, mechanical strength increases, and the 2nd, corrosion resistant plate is high temperature resistant, smooth surface, good looking appearance.Be mainly used in the decoration of inner, external wall, perhaps decoration of ship inner room compartment and automobile inside pool etc.
The processing method of stainless steel of the present invention, aluminum composite honeycomb panel, it is characterized in that getting corrosion resistant plate at first respectively and aluminium sheet carries out overlapping, be pressed into stainless steel, aluminum composite plate through adding, again stainless steel, aluminum composite plate are made stainless steel, aluminium honeycomb core by heating pressurization soldering, cutting, stretching, stick stainless steel, aluminum composite plate on the two sides of honeycomb core, be heated to 500-600 ℃, pressurization simultaneously becomes stainless steel, aluminum composite honeycomb panel by the softening back soldering of aluminium.Honeycomb core and whole cellular board manufacturing are processed through soldering, and pollution-free without gluing, fastness is good, the intensity height.
Stainless steel of the present invention, the processing method of aluminum composite honeycomb panel, get corrosion resistant plate at first respectively and aluminium sheet is two-layer or aluminium sheet by another kind of honeycomb core, corrosion resistant plate, aluminium sheet carries out overlapping for three layers, be pressed into stainless steel through adding, composite plate that aluminium is two-layer or aluminium, stainless steel, the composite plate that aluminium is three layers, again aluminium, stainless steel, the composite plate that aluminium is three layers is by heating pressurization soldering, cutting, aluminium is made in stretching, stainless steel, aluminium honeycomb core, stainless steel is sticked on two sides at honeycomb core, aluminum composite plate, be heated to 500-600 ℃, pressurization simultaneously becomes stainless steel by the softening back soldering of aluminium, aluminum composite honeycomb panel.
Description of drawings
Fig. 1 is stainless steel of the present invention, a kind of structural representation of aluminum composite honeycomb panel;
Fig. 2 is the another kind of example schematic in stainless steel of the present invention, aluminum composite honeycomb panel cross section.
The specific embodiment the invention discloses a kind of stainless steel, aluminum composite honeycomb panel and processing method, the honeycomb core 2 that composite honeycomb board mainly contains between top panel 1, lower panel 3 and the upper and lower panel is formed, its major technology is characterised in that described top panel 1 and lower panel 3 are compound two-layer of corrosion resistant plate and aluminium sheet, and honeycomb core is compound three layers of corrosion resistant plate and aluminium sheet compound two-layer or aluminium sheet, corrosion resistant plate, aluminium sheet.As shown in Figure 1, honeycomb core 2 is that corrosion resistant plate 2 ' " mutually compound is two-layer made with aluminium sheet 2.As shown in Figure 2, top panel 1 is that corrosion resistant plate 1 ' " mutually compound is two-layer made with aluminium sheet 1.As shown in Figure 2, lower panel 3 is that corrosion resistant plate 3 ' " mutually compound is two-layer made with aluminium sheet 3.As shown in Figure 2, honeycomb core 2 is that three layers of aluminium sheets 2 ", corrosion resistant plate 2 ', aluminium sheet 2 " are compound made.Fig. 1, Fig. 2 only are two embodiment, in actual product, not limited by accompanying drawing.
The processing method of stainless steel of the present invention, aluminum composite honeycomb panel, get corrosion resistant plate and aluminium sheet at first respectively and carry out overlaid together, be pressed into stainless steel, aluminum composite plate through adding, stainless steel, aluminum composite plate can be two-layer, also can be three layers, hot-forming as requested.Again stainless steel, aluminum composite plate are made stainless steel, aluminium honeycomb core by heating pressurization soldering, cutting, stretching, wherein soldering heating pressurization is exactly to two composite plates (every Manufactured two-layer or three layers stainless steel, aluminum composite plate) pressurization of section between heating has, section is linked to each other, the section gluing is mutually bonding between the replacement prior art, the composite plate that a section is linked to each other is cut, is stretched and make honeycomb core again, the cutting here stretches also identical with prior art, only is that heating pressurization soldering replaces the prior art gluing.After making honeycomb core, stick stainless steel, aluminum composite plate the two sides of honeycomb core (above and below), as shown in Figure 2, be heated to 500-600 ℃, pressurization simultaneously becomes stainless steel, aluminum composite honeycomb panel by the softening back soldering of aluminium.
Another kind of processing method about honeycomb core is: get the two-layer or aluminium sheet of corrosion resistant plate and aluminium sheet at first respectively, corrosion resistant plate, aluminium sheet carries out overlapping for three layers, be pressed into stainless steel through adding, composite plate that aluminium is two-layer or aluminium, stainless steel, the composite plate that aluminium is three layers, again aluminium, stainless steel, the composite plate that aluminium is three layers is by heating pressurization soldering, cutting, aluminium is made in stretching, stainless steel, aluminium honeycomb core, stainless steel is sticked on two sides at honeycomb core, aluminum composite plate, be heated to 500-600 ℃, pressurization simultaneously becomes stainless steel by the softening back soldering of aluminium, aluminum composite honeycomb panel.
Claims (3)
1, stainless steel, aluminum composite honeycomb panel, top panel, lower panel are arranged, honeycomb core is arranged between the upper and lower panel, it is characterized in that described top panel and lower panel are compound two-layer of corrosion resistant plate and aluminium sheet, honeycomb core is compound three layers of corrosion resistant plate and aluminium sheet compound two-layer or aluminium sheet, corrosion resistant plate, aluminium sheet.
2, the processing method of stainless steel as claimed in claim 1, aluminum composite honeycomb panel, it is characterized in that getting corrosion resistant plate at first respectively and aluminium sheet carries out overlapping, be pressed into stainless steel, aluminum composite plate through adding, again stainless steel, aluminum composite plate are made stainless steel, aluminium honeycomb core by heating pressurization soldering, cutting, stretching, stick stainless steel, aluminum composite plate on the two sides of honeycomb core, be heated to 500-600 ℃, pressurization simultaneously becomes stainless steel, aluminum composite honeycomb panel by the softening back soldering of aluminium.
3, stainless steel as claimed in claim 1, the processing method of aluminum composite honeycomb panel, it is characterized in that getting at first respectively corrosion resistant plate and aluminium sheet is two-layer or aluminium sheet, corrosion resistant plate, aluminium sheet carries out overlapping for three layers, be pressed into stainless steel through adding, composite plate that aluminium is two-layer or aluminium, stainless steel, the composite plate that aluminium is three layers, again aluminium, stainless steel, the composite plate that aluminium is three layers is by heating pressurization soldering, cutting, aluminium is made in stretching, stainless steel, aluminium honeycomb core, stainless steel is sticked on two sides at honeycomb core, aluminum composite plate, be heated to 500-600 ℃, pressurization simultaneously becomes stainless steel by the softening back soldering of aluminium, aluminum composite honeycomb panel.