CN108952000A - A kind of gradient color aluminum honeycomb mirror surface plate module and its preparation process - Google Patents
A kind of gradient color aluminum honeycomb mirror surface plate module and its preparation process Download PDFInfo
- Publication number
- CN108952000A CN108952000A CN201810939628.6A CN201810939628A CN108952000A CN 108952000 A CN108952000 A CN 108952000A CN 201810939628 A CN201810939628 A CN 201810939628A CN 108952000 A CN108952000 A CN 108952000A
- Authority
- CN
- China
- Prior art keywords
- aluminum honeycomb
- profile
- module
- honeycomb panel
- stainless steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of gradient color aluminum honeycomb mirror surface plate module and its preparation processes.The module includes aluminum honeycomb panel, the front side of aluminum honeycomb panel is equipped with stainless steel mirror board, other bread of aluminum honeycomb panel are wrapped with aluminium sheet, the two sides up and down of aluminum honeycomb panel and it is respectively arranged on the left side and the right side one/profile of profile two, two/profile of profile one, when two or more modules connect, profile one and profile two between adjacent block cooperate.Preparation process are as follows: be uniformly coated with polyurethane adhesive on the inside of stainless steel faceplate, aluminium sheet；Aluminum honeycomb panel is put into the aluminium sheet for coating polyurethane adhesive, stainless steel mirror board is then covered with, forms module；Graded films are sticked after module is cold-pressed, and are dried, finally installation installation profile.Lines sense of the present invention is clear, beautiful design, and highlights the stereovision of whole metope gradient color effect, ensure that consumer product uniqueness, visual effect are good.
Description
Technical field
The present invention relates to a kind of gradient color aluminum honeycomb mirror surface plate module and its preparation processes, for industries such as advertising signboards
In.
Background technique
With social progress and development, the aesthetic conceptions of people require to have stepped up with visual effect, stainless steel mirror
Plate clearly becomes clear as mirror, with more and more extensive in all trades and professions, but stainless steel mirror is decorated on whole exterior wall
Panel generally does base layer support using reinforcing rib, bracket etc., it may appear that and it is uneven, influence Integral decoration effect, such as integral wall
Face, which is done, smooth will increase cost.Aluminum honeycomb is a kind of new decorative material, has surface, intensity height, green ring
The characteristics such as guarantor now produce stable structure using aluminum honeycomb material cooperation, and product integral smoothness height is unlikely to deform, and has gradient color
Effect stainless steel mirror plate module, meets the aesthetic effect of integrated curtain-wall.
Summary of the invention
Problem to be solved by this invention is how to make one kind both to have guaranteed that product structure stablized guarantee product entirety again
Flatness height is unlikely to deform and has the stainless steel mirror plate module of gradient color effect, meets the aesthetic effect of integrated curtain-wall.
To solve the above-mentioned problems, the technical solution of the present invention is to provide a kind of gradient color aluminum honeycomb mirror surface plate module,
It is characterized in that, including aluminum honeycomb panel, the front side of aluminum honeycomb panel is equipped with stainless steel mirror board, and stainless steel mirror plate surface is covered with gradual change
Film, other bread of aluminum honeycomb panel are wrapped with aluminium sheet, and the two sides up and down of aluminum honeycomb panel are respectively equipped with profile one, profile two, aluminum honeycomb
Plate is respectively arranged on the left side and the right side one/profile of profile two, two/profile of profile one, adjacent when two or more modules connect
Profile one and profile two between module cooperate；The cross section of profile one is equipped with the branch for connecting with aluminum honeycomb panel side
Leg one, the supporting leg two for being connect with aluminum honeycomb panel back, supporting leg three and groove for being connect with metope, profile two it is transversal
Face be equipped with the supporting leg four for connect with aluminum honeycomb panel back, the supporting leg five for being connect with aluminum honeycomb panel side and be used for it is recessed
The supporting leg six that slot matches.
Preferably, the aluminium sheet on the outside of the aluminum honeycomb panel is integrally formed.
Preferably, the profile one, profile two are connected and fixed by screw one and aluminium sheet, aluminum honeycomb panel.
Preferably, the edge of the stainless steel mirror board extends around along aluminum honeycomb panel surface.
It is highly preferred that being equipped with glue one between the extension of the stainless steel mirror board and the aluminium sheet on the outside of aluminum honeycomb panel.
It is highly preferred that the width that the stainless steel mirror board is more than the extension of aluminium sheet outer rim is 4mm.
It is highly preferred that the end of the supporting leg five of the profile two connects the bottom of a U-shaped portion, when two modules connect,
The both ends of the U-shaped portion are respectively held against the extension of the stainless steel mirror board of two modules.
It is highly preferred that being filled with rubber item in the U-shaped portion, the opening of U-shaped portion is equipped with glue two.
Preferably, when installation, the supporting leg three and the metope steelframe of installation metope of the profile one are connected and fixed.
It is highly preferred that the supporting leg three is connected and fixed with metope steelframe by screw two.
Preferably, when one or more modules are connected with each other and are mounted on the installation metope, outside the module of outside
The profile one or profile two of edge are replaced by L-type bending part, and one side of L-type bending part is fixedly connected with module, another side and installation
Metope is fixedly connected.
It is highly preferred that the L-type bending part is fixedly connected by screw two with installation metope on one side, another side passes through riveting
Nail is fixedly connected with the aluminium sheet of module bottom, aluminum honeycomb panel.
It is highly preferred that the outside of the L-type bending part is equipped with bound edge sealing plate.
The present invention also provides a kind of preparation processes of above-mentioned gradient color aluminum honeycomb mirror surface plate module, which is characterized in that packet
Include following steps:
Step 1: selection needs the aluminium sheet of specification, by its surrounding bending；
Step 2: selection needs the aluminum honeycomb panel of specification according to the specification of the aluminium sheet after bending；
Step 3: selection needs the stainless steel mirror board of specification, it is uniformly coated on the inside of stainless steel faceplate, aluminium sheet
Polyurethane adhesive；
Step 4: aluminum honeycomb panel is put into the aluminium sheet for coating polyurethane adhesive, it is then covered with stainless steel mirror board, forms mould
Block；
Step 5: module is put into cold press, it is ensured that product is smooth, indeformable, glue solidifies completely；
Step 6: wiping solidification after module stainless steel mirror plate surface, guarantee its free from dust, without particle, without flash；
Step 7: sticking graded films, and remove moisture content after stainless steel mirror plate surface is uniformly sprayed and reconciles water, it is ensured that
Surface free from dust, without particle, bubble-free；
Step 8: the module that graded films will be posted, baking oven drying is put into, it is ensured that surface free from dust, without particle, bubble-free；
Step 9: the Modular surface pasting protective film of drying is formed complete module；
Step 10: surrounding installation profile one, profile two or the L-type bending part in module are needed according to installation, in installation L-type
The bottom installation kit banding plate edge sealing of bending part.
Preferably, the polyurethane adhesive in the third step uses SY8409 ceramic tile aluminum honeycomb panel polyurethane adhesive.
Preferably, the pressure of cold press is 2~3MPa in the 5th step, and room temperature lay-by time is 24 hours after cold pressing
More than.
Preferably, the reconciliation water in the 7th step is water and white cat board Multifunctional kitchen detergent with the weight of 1000:5
Amount is than mixed mixture.
Preferably, the design parameter dried in the 8th step are as follows: 55~65 DEG C of oven temperature, drying time is 48 small
When more than.
The present invention uses a kind of gradient color aluminum honeycomb mirror board manufacture craft, and aluminum honeycomb has surface, green, ring
The performances such as guarantor, energy-saving decoration are strong, and light weight, intensity height, stable structure, resisting wind press capacity are good, prevent fires, is shockproof are a kind of new
The ornament materials of type, meets the technological effect demand of different clients different product, whole wall surface levelling, and module is directly set with module
There is a lines sense for receiving glue, lines sense is clear, beautiful design, and highlights the stereovision of whole metope gradient color effect, ensure that visitor
Family product is unique, and visual effect is good.Technique of the invention is advanced rationally, enhances the market competitiveness, produces significant warp
Ji benefit.
Detailed description of the invention
Fig. 1 is the main view of gradient color aluminum honeycomb mirror surface plate module provided by the invention；
Fig. 2 is the cross-sectional view in the face X-X in Fig. 1；
Fig. 3 is the partial enlarged view of I part in Fig. 2；
Fig. 4 is the partial enlarged view of II part in Fig. 2；
Fig. 5 is the cross-sectional view in the face Y-Y in Fig. 1；
Fig. 6 is the partial enlarged view of III part in Fig. 5；
Fig. 7 is the partial enlarged view of IV part in Fig. 5；
Fig. 8 is the cross-sectional view of aluminium sheet 3；
Fig. 9 is the main view when present invention is mounted on installation metope；
Figure 10 is the cross-sectional view in the face C-C in Fig. 9；
Figure 11 is the partial enlarged view of V part in Figure 10；
Figure 12 is the partial enlarged view of VI part in Figure 10；
Figure 13 is the partial enlarged view of VII part in Figure 10.
Specific embodiment
In order to make the present invention more obvious and understandable, hereby with preferred embodiment, and attached drawing is cooperated to be described in detail below.
Embodiment
It as shown in figs 1-9, is a kind of gradient color aluminum honeycomb mirror surface plate module provided by the invention comprising aluminum honeycomb panel 2,
The front side of aluminum honeycomb panel 2 is equipped with stainless steel mirror board 1, and 1 surface of stainless steel mirror board is covered with graded films, aluminum honeycomb panel 2 it is other
Bread is wrapped with aluminium sheet 3, and aluminium sheet 3 is integrally formed.The two sides up and down of aluminum honeycomb panel 2 are respectively equipped with one A of profile, two B of profile, aluminium bee
Nest plate 2 is respectively arranged on the left side and the right side one A of profile, two B of profile；The cross section of one A of profile be equipped with for 2 side of aluminum honeycomb panel
The supporting leg 1 of connection, the supporting leg 27 for being connect with 2 back of aluminum honeycomb panel, supporting leg 38 and groove for being connect with metope
The cross section of 9, two B of profile is equipped with supporting leg 4 18 for connect with 2 back of aluminum honeycomb panel, is used for and 2 side of aluminum honeycomb panel company
The supporting leg 5 19 connect and the supporting leg 6 10 for being matched with groove 9.The supporting leg 1 of one A of profile, supporting leg 27, two B of profile
Supporting leg 4 18, supporting leg 5 19 are connected and fixed by screw 1 with aluminium sheet 3, aluminum honeycomb panel 2.The edge edge of stainless steel mirror board 1
2 surface of aluminum honeycomb panel extend around.It is set between the aluminium sheet 3 in 2 outside of extension and aluminum honeycomb panel of stainless steel mirror board 1
There is glue 1.Stainless steel mirror board 1 is more than that the width of the extension of 3 outer rim of aluminium sheet is 4mm.The supporting leg 5 19 of two B of profile
End connects the bottom of a U-shaped portion 20, and when two modules connect, the both ends of the U-shaped portion 20 are respectively held against two modules not
The extension of rust steel mirror panel 1.Rubber item 14 is filled in U-shaped portion 20, the opening of U-shaped portion 20 is equipped with glue 2 13.Installation
When, the supporting leg 38 and the metope steelframe 12 of installation metope of one A of profile is connected and fixed by screw 2 11.The present embodiment use from
One E of module, two F of module, three G of module under are sequentially connected, and two B of profile on the downside of three G of module is by 15 generation of L-type bending part
It replaces, one side of L-type bending part 15 is fixedly connected with metope steelframe 12 by screw 2 11, and another side passes through rivet 16 and module bottom
Aluminium sheet 3, the aluminum honeycomb panel 2 in portion are fixedly connected.The outside of L-type bending part 15 is equipped with bound edge sealing plate 17.
The preparation process of above-mentioned gradient color aluminum honeycomb mirror surface plate module the following steps are included:
Step 1: selection needs the aluminium sheet 3 of specification, by its surrounding bending；
Step 2: selection needs the aluminum honeycomb panel 2 of specification according to the specification of the aluminium sheet 3 after bending；
Step 3: selection needs the stainless steel mirror board 1 of specification, it is uniform in the inside of stainless steel faceplate 1, aluminium sheet 3
Coat polyurethane adhesive (using SY8409 ceramic tile aluminum honeycomb panel polyurethane adhesive)；
Step 4: aluminum honeycomb panel 2 is put into the aluminium sheet 3 for coating polyurethane adhesive, it is then covered with stainless steel mirror board 1, shape
At module；
Step 5: module is put into cold press, the pressure of cold press is 2~3MPa, and room temperature lay-by time is after cold pressing
24 hours or more, it is ensured that product is smooth, indeformable, glue solidifies completely；
Step 6: 1 surface of stainless steel mirror board of the module after wiping solidification, guarantees its free from dust, without particle, hairless
Side；
Step 7: 1 surface of stainless steel mirror board uniformly spray reconcile water (water and white cat board Multifunctional kitchen detergent with
The mixture of the weight ratio mixing of 1000:5) after, graded films are sticked, and remove moisture content, it is ensured that surface free from dust, without particle, nothing
Bubble；
Step 8: the module that graded films will be posted, put into baking oven drying (55~65 DEG C of oven temperature, drying time 48
Hour or more), it is ensured that surface free from dust, without particle, bubble-free；
Step 9: the Modular surface pasting protective film of drying is formed complete module；
Step 10: needing surrounding installation one A of profile, two B of profile or the L-type bending part 15 in module according to installation, pacifying
17 edge sealing of bottom installation kit banding plate of L-type bending part 15 is filled, specifically:
It is needed that one A of profile, supporting leg 1, supporting leg 27 screw 1 and module are installed in the top of each module according to installation
It is connected and fixed, and in junction gluing 1；Following installation two B of profile, supporting leg 4 18, the screw 1 of supporting leg 5 19 and module connect
Fixation is connect, and in junction gluing 1.
One A of profile is installed on the module left side, supporting leg 1, supporting leg 27 are connected and fixed with screw 1 with module, and are being connected
Locate gluing 1；Two B of profile is installed on the right, and supporting leg 4 18, supporting leg 5 19 are connected and fixed with screw 1 with module, and in junction
Gluing 1.
Step 11: the supporting leg 38 of one A of profile of one top E of module and metope steelframe 12 are used spiral shell when installing with metope
It follows closely 2 11 to be connected and fixed, the supporting leg 6 10 and the groove 9 of one A of profile of two top F of module of one E of module following two B of profile is right
It inserts, the supporting leg 38 of one A of profile of two F of module is equally connected and fixed with the screw 2 11 of metope steelframe 12；In one bottom E of module
Two B of profile U-shaped portion 20 in be put into rubber item 14, blend compounds 2 13 are closed, the mounting means phase of the profile of each module two sides
Together, three G of module is installed using same method；The bottom of three G of module is installed by L-type bending part 15, one side and metope steelframe 12
It is connected and fixed with screw 2 11, another side is connected and fixed with rivet 16 and three G of module, bottom installation kit banding plate according to demand
17, the outer rim of outermost module is respectively mounted L-type bending part 15.
Claims (14)
1. a kind of gradient color aluminum honeycomb mirror surface plate module, which is characterized in that including aluminum honeycomb panel (2), the front side of aluminum honeycomb panel (2)
Equipped with stainless steel mirror board (1), stainless steel mirror board (1) surface is covered with graded films, and other bread of aluminum honeycomb panel (2) are wrapped with aluminium
Plate (3), the two sides up and down of aluminum honeycomb panel (2) are respectively equipped with profile one (A), profile two (B), the left and right sides of aluminum honeycomb panel (2)
It is respectively equipped with profile one (A)/profile two (B), profile two (B)/profile one (A), it is adjacent when two or more modules connect
Profile one (A) and profile two (B) between module cooperate；The cross section of profile one (A) be equipped with for aluminum honeycomb panel (2)
Supporting leg one (6), supporting leg two (7), the supporting leg for being connect with metope for being connect with aluminum honeycomb panel (2) back of side connection
Three (8) and groove (9), the cross section of profile two (B) is equipped with the supporting leg four (18) for connecting with aluminum honeycomb panel (2) back, use
In the supporting leg five (19) being connect with aluminum honeycomb panel (2) side and the supporting leg six (10) for being used to match with groove (9).
2. gradient color aluminum honeycomb mirror surface plate module as described in claim 1, which is characterized in that the stainless steel mirror board (1)
Edge extend around along aluminum honeycomb panel (2) surface.
3. gradient color aluminum honeycomb mirror surface plate module as claimed in claim 2, which is characterized in that the stainless steel mirror board (1)
Extension and aluminum honeycomb panel (2) on the outside of aluminium sheet (3) between be equipped with glue one (5).
4. gradient color aluminum honeycomb mirror surface plate module as claimed in claim 2, which is characterized in that the stainless steel mirror board (1)
Width more than the extension of aluminium sheet (3) outer rim is 4mm.
5. gradient color aluminum honeycomb mirror surface plate module as claimed in claim 2, which is characterized in that the supporting leg of the profile two (B)
The bottom of the end connection one U-shaped portion (20) of five (19), when two modules connect, the both ends of the U-shaped portion (20) are respectively held against
The extension of the stainless steel mirror board (1) of two modules.
6. gradient color aluminum honeycomb mirror surface plate module as claimed in claim 5, which is characterized in that filling in the U-shaped portion (20)
Have rubber item (14), the opening of U-shaped portion (20) is equipped with glue two (13).
7. gradient color aluminum honeycomb mirror surface plate module as described in claim 1, which is characterized in that when installation, the profile one (A)
Supporting leg three (8) and install metope metope steelframe (12) be connected and fixed.
8. gradient color aluminum honeycomb mirror surface plate module as described in claim 1, which is characterized in that one or more module phases
When connecting and being mounted on the installation metope, the profile one (A) or profile two (B) of the outer rim of outside module are by L-type bending part
(15) it replaces, one side of L-type bending part (15) is fixedly connected with module, and another side is fixedly connected with installation metope.
9. gradient color aluminum honeycomb mirror surface plate module as claimed in claim 8, which is characterized in that the L-type bending part (15)
Outside is equipped with bound edge sealing plate (17).
10. a kind of preparation process of gradient color aluminum honeycomb mirror surface plate module described in any one of claim 1-9, feature exist
In, comprising the following steps:
Step 1: selection needs the aluminium sheet (3) of specification, by its surrounding bending；
Step 2: selection needs the aluminum honeycomb panel (2) of specification according to the specification of the aluminium sheet (3) after bending；
Step 3: selection needs the stainless steel mirror board (1) of specification, it is equal in the inside of stainless steel faceplate (1), aluminium sheet (3)
It is even to coat polyurethane adhesive；
Step 4: aluminum honeycomb panel (2) is put into the aluminium sheet (3) for coating polyurethane adhesive, it is then covered with stainless steel mirror board (1),
Form module；
Step 5: module is put into cold press, it is ensured that product is smooth, indeformable, glue solidifies completely；
Step 6: wiping solidification after module stainless steel mirror board (1) surface, guarantee its free from dust, without particle, without flash；
Step 7: sticking graded films, and remove moisture content, it is ensured that table after stainless steel mirror board (1) surface uniformly sprays and reconciles water
Face free from dust, without particle, bubble-free；
Step 8: the module that graded films will be posted, baking oven drying is put into, it is ensured that surface free from dust, without particle, bubble-free；
Step 9: the Modular surface pasting protective film of drying is formed complete module；
Step 10: surrounding installation profile one (A), profile two (B) or the L-type bending part (15) in module are needed according to installation,
Bottom installation kit banding plate (17) edge sealing of L-type bending part (15) is installed.
11. the preparation process of gradient color aluminum honeycomb mirror surface plate module as claimed in claim 10, which is characterized in that the third
Polyurethane adhesive in step uses SY8409 ceramic tile aluminum honeycomb panel polyurethane adhesive.
12. the preparation process of gradient color aluminum honeycomb mirror surface plate module as claimed in claim 10, which is characterized in that the described 5th
The pressure of cold press is 2~3MPa in step, and room temperature lay-by time is 24 hours or more after cold pressing.
13. the preparation process of gradient color aluminum honeycomb mirror surface plate module as claimed in claim 10, which is characterized in that the described 7th
Reconciliation water in step is the mixture that water is mixed with white cat board Multifunctional kitchen detergent with the weight ratio of 1000:5.
14. the preparation process of gradient color aluminum honeycomb mirror surface plate module as claimed in claim 10, which is characterized in that the described 8th
The design parameter dried in step are as follows: 55~65 DEG C of oven temperature, drying time is 48 hours or more.