CN1869299B - Spinning fine spinning blended by milk fibre and making method thereof - Google Patents
Spinning fine spinning blended by milk fibre and making method thereof Download PDFInfo
- Publication number
- CN1869299B CN1869299B CN200610086668A CN200610086668A CN1869299B CN 1869299 B CN1869299 B CN 1869299B CN 200610086668 A CN200610086668 A CN 200610086668A CN 200610086668 A CN200610086668 A CN 200610086668A CN 1869299 B CN1869299 B CN 1869299B
- Authority
- CN
- China
- Prior art keywords
- spinning
- fibre
- silk
- twist
- milk fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a spinning fine count blending with milk fiber. It includes the following steps: cutting off the silk into bulk fiber and the length is 50-60mm, reversion is 18-25%, and oil content is 2-3%, cultivating for 8-24 hours until fully penetrating. The fine combing fiber length is 40-50mm, and spun yarn twist is 850-1600T/M, twist coefficient is 85-130, taking bulk fiber mixing,adding wool cream according to 1:3, and making yarn after taking slivering, forespinning and post spinning processes. The invention has the advantages of natural, green, healthy keeping, low cost, good heat keeping, etc.
Description
One, technical field
The present invention relates to a kind of spinning fine spinning and preparation method of blended by milk fibre, belong to field of textiles.
Two, background technology
Cashmere fiber has exquisiteness, softness, slides characteristics such as glutinous, be that other fiber is incomparable, but its further popularization also has certain limitation.Reason: first: pure fleece fabrics costs an arm and a leg, and can not accepted by consumers in general on market.Second: the cashmere monofilament strength is lower, is not suitable for spinning the too yarn of high-count.So just be unfavorable for that pure cashmere product further develops.
Three, summary of the invention
The technical problem that the present invention solves is: provide a kind of natural, green, health care, health, cost low, antibiotic property is strong; Thermal property is good; Have good moisture absorption, lead moistly, wear smooth, ventilative; Soft, slim and graceful, elegant; Outward appearance gracefulness, luxurious; The fabric lines exquisiteness that is made into, clear, product is more frivolous, the spinning fine spinning of a kind of blended by milk fibre of environmental protection.
Technical solution:
The present invention adopts milk fibre and natural protein fibre cashmere, the mixed spinning of silk to form, and the number scope is 100/2-180/2, wherein milk fibre content 10-50%, silk content 20-70%, cashmere content 10--60%, single twist 850-1600T/M is more than the powerful 70-200CN; Two twist per unit 450-1600T/M are more than the powerful 160-400CN.
Processing step:
(1) and hair technology be: earlier the silk bar is cut into bulk fibre, raw material is carried out bulk fibre mix, added and crude oil water by 1: 3, the sheared length of silk bar is 50-60MM;
(2) and suede technology be: and back suede moisture regain fully permeates profit for 18-25%, oil content 2-3% and back hair health 8-24 hour;
(3) carding machine carries out combing, and the yarn fibre length is 40-50MM, and the spun yarn twist is 850-1600T/M, and twist factor is 85-130;
(4) again through the system bar, preceding spin and after spin operation spinning resultant yarn.
The present invention also can make bar respectively with milk fibre, silk fiber, cashmere fiber, passes through silver mixing again, precedingly spin, after spin operation spinning resultant yarn.
Be used to weave knitted underwear, woven fabric and spinning scarf, tippet, the printed scarf series of products.
Advantage of the present invention:
Milk protein fiber is the grade textiles raw material of a kind of new type natural, green, health care, health, it is the casein protein that extracts from milk, and contain more than the 10 kind of amino acid favourable in the casein protein, so the health-care function that can play the nutrition skin, lubricate the skin and muscle to human body.Key property has: good skin-friendly, skin care; Good moisture retention, milk protein fiber have the natural insulation factor NMF of protein, and the hydroxyl that contains in the molecular structure of the insulation factor can clench hydrone more, therefore can keep skin moisture content, makes skin softness, smooth, and wrinkle reduces; Antibiotic property; Thermal property is good; Good moisture absorption, lead moistly, wear smooth, ventilative; Soft, slim and graceful, elegant; Outward appearance gracefulness, luxurious; The fabric lines exquisiteness that is made into high grade yarn, clear is particularly suitable for wearing next to the skin, and is the fabulous lining of making high-grade underwear and shirt.
The spinning fine spinning of blended by milk fibre of the present invention, be characterized in: it is the perfect combination by two kinds of five-star protein fibres and a kind of new green environment protection, health fiber, by its woven fabric, knitting series products mainly contains underwear, and preparing development product has: frivolous product spring and summer; Underlinen fabric, scarf, tippet, high grade yarn printed scarf etc.It is smooth that these products have cloth cover, bright and clean, and drapability is good, and winter, the product dress was warming, flexible; Summer, the product dress was frivolous, softness, and absorbing sweat, ventilative is incomparable comfortable, expensive goods of general clothes.
Four, the specific embodiment
The spinning process of milk fibre and cashmere, silk blending:
At present, we adopt two kinds of methods spinning milk fibres and cashmere, silk blended yarn.First kind: utilize the spinning of cotton type and wool type mixing device,, strand is sheared by the number of institute's yarn at wool blending step, make them become the bulk fibre state, sheared length is 55MM, milk fibre, and cashmere fiber, silk fiber consumption mix in the ratio of customer requirement, shredding, and by adding at 1: 3 and crude oil water and back suede get damp again and is generally 23%, oil content 2.5%, after mixing, health 12-20 hour again.Make strip through carding process, grilling mechanism bar makes fiber parallel, straight, reduces crotch; By combing process, short flannel is removed, make various fibers fully obtain mixing, according to the difference of institute's yarn number, the yarn fibre length generally is controlled at 45MM.Again through the multiple tracks gill box with strip further and close, drawing-off, make fiber more parallel, straight, make strip more even, and progressively take out long drawing-down, yarn is ready uniformly in order to spin.Further drawing-off through rove, spinning process makes strip more and more thinner, and adds the suitable twist, and according to the difference that institute spins and props up, the twist is 850-1600T/M, makes its spinning count that reaches technological requirement, makes single thread.Again through winder, doubling, twist thread, with two single thread and close, twist two yarns, according to the difference that institute spins and props up, two twist per units are 450-1600T/M.Technological process: and hair-carding (carding machine)-a pin-two pins-combing-three pin-four pin-five pin-six pin-head also (drawing frame)-two also-three also-rove-spun yarn-winder-doubling-double twisting.Above carding machine, drawing frame, Speed frames, fine spining machine are cotton type equipment, and all the other are wool type equipment.
Second kind: utilize cotton type and wool type mixing device, at wool blending step, milk fibre, silk fiber, cashmere fiber are carried out respectively and suede, and add the profit of 1: 3 ratio respectively, and through carding process, the grilling operation, combing process, make strip respectively,, several strips are mixed also according to the desired ratio of client, through the multiple tracks grilling, with strip and close and drawing-off, and take out long drawing-down, make fiber parallel straight, and make the fibre length of yarn satisfy technological requirement, pass through rove, spun yarn again, network is also twisted with the fingers operation, is spun into required yarn.
The index of the spun yarn of milk fibre that we spun and cashmere, silk blending is up to state standards, and more than the single thread force 70-180CN, more than the powerful 160-380CN of two yarns, more than the elongation 7-15%, bar is done CV%15-23%.
Embodiment:
Example: blended yarn 20135/2, raw materials used is 23% cashmere, 27% spun silk, 50% milk fibre, utilizes cotton type and wool type mixing device spinning to form.The milk fibre intermediate length is 52MM, and fineness is 14.3 μ M; The spun silk bar is sheared according to 55MM, and middle long 45MM is about fineness 12 μ M; Long 33MM in the cashmere is about fineness 15.5 μ M.Milk fibre, silk, cashmere fiber are mixed, and 1: the 3 ratio refueling water and the 18-20% that afterwards gets damp again, oil content 1.8-2%; Through carding machine, two reason grillings, combing process is made strip, the yarn fibre length is 43MM, again through four road grillings, and three road draftings, rove, spun yarn is spun into single thread, and twist 1200T/M is more than the powerful 120CN, extend more than 13%, through winder, doubling, twist thread, twist with the fingers two yarns, twist 660T/M, more than the powerful 260CN, elongation is spun into 135/2 more than 9%.
With 135/2 weaving yarns knitted underwear and summer T-shirt and vest series of products, vehicle 24G circular knitting machine, density 34 orders/INCH, 185 grams/every square metre, about every cover underwear 350 grams, about every 70-100 gram of product in summer. these products, wear frivolous, soft and smooth, absorbing sweat is ventilative, flexible, easily washing, easily nursing.
Claims (3)
1. the spinning fine spinning of blended by milk fibre, it is characterized in that: adopt milk fibre and natural protein fibre cashmere, the mixed spinning of silk to form, the number scope is 100/2-180/2, milk fibre content 10-50% wherein, silk content 20-70%, cashmere content 10--60%, single twist 850-1600T/M is more than the powerful 70-200CN; Two twist per unit 450-1600T/M are more than the powerful 160-400CN.
2. the spinning fine spinning preparation method of blended by milk fibre according to claim 1 is characterized in that, adopts following processing step:
(1) and hair technology: earlier the silk bar is cut into bulk fibre, the sheared length of silk bar is 50-60MM; Cashmere, silk, milk fibre is mixed in proportion and add and crude oil water by 1: 3 oil-water ratio, require and back suede moisture regain for 18-25%, oil content 2-3% and after suede health 12-20 hour, profit is fully permeated;
(2) combing: requiring the yarn fibre length is 40-50MM;
(3) spinning process: requiring the spun yarn twist is 850-1600T/M, and twist factor is 85-130;
(4) twisting technique: two twist per units are 450-1600T/M.
3. according to the spinning fine spinning preparation method of claims 1 described blended by milk fibre, it is characterized in that: at wool blending step, milk fibre, silk fiber, cashmere fiber are carried out respectively and suede, and add the profit of 1: 3 ratio respectively, and through carding process, the grilling operation, combing process, make strip respectively, pass through silver mixing again, precedingly spin, after spin operation spinning resultant yarn.